工业石膏的资源化利用途径与展望

doi:10.19964/j.issn.1006-4990.2020-0558

摘要/Abstract

摘要：

电力、钢铁、磷肥等工业生产过程中产生大量副产石膏,如不能妥善处理而将其大量搁置,不仅造成环境污染,而且导致资源浪费。副产石膏的无害化、大综化、高质化利用,已经成为工业发展中的热点话题。对国内工业副产品石膏中脱硫石膏和磷石膏在水泥、建材、农业、化工等领域应用和技术开发现状进行了总结,并对未来工业石膏资源化利用提出了建议。以工业石膏为原料制备硫酸联产水泥、铁酸钙以及转铵法制备硫酸的工业路线具有可行性,有望实现脱硫石膏和磷石膏的大规模利用。

关键词: 脱硫石膏, 磷石膏, 天然石膏, 综合利用

Abstract:

A large amount of by-product gypsum is produced in the process of industrial production,such as electric power,iron and steel,phosphate fertilizer,etc.If it cannot be properly treated and put it aside in large quantities,it will not only cause environmental pollution but also lead to waste resources.The harmless,comprehensive and high-quality utilization of by-pro-duct gypsum has become a topical focus in industrial development.The application and technical development status of desul-furization gypsum and phosphogypsum in cement,building materials,agriculture and chemical industry were summarized,and the suggestions for the resource utilization of industrial gypsum in the future were put forward.In this paper,it was pointed out that industrial routes such as preparing sulphuric acid co-production cement,calcium ferrite and conversion of ammonium to sulphuric acid by industrial gypsum were feasible,which would expect to realize the large-scale utilization of desulphuriza-tion gypsum and phosphogypsum.

Key words: desulfurization gypsum, phosphogypsum, natural gypsum, comprehensive utilization

中图分类号:

TQ132.32

刘林程,左海滨,许志强. 工业石膏的资源化利用途径与展望[J]. 无机盐工业, 2021, 53(10): 1-9.

Liu Lincheng,Zuo Haibin,Xu Zhiqiang. Resource utilization approach of industrial gypsum and its prospect[J]. Inorganic Chemicals Industry, 2021, 53(10): 1-9.

图/表 8

图1

表1

图2

表2

图3

表3

图4

图5

参考文献 60

[1]	张凡凡, 陈超, 张西兴, 等. 不同来源石膏的性能特点与应用分析[J]. 无机盐工业, 2017, 49(8):10-13.
[2]	李逸晨. 石膏行业的发展现状及趋势[J]. 硫酸工业, 2019(11):1-7,13.
[3]	裴晋鹏. 火电厂脱硫石膏的综合利用[J]. 科技创新导报, 2019(28):51-52.
[4]	卢兰萍, 李阳, 王稷良, 等. 脱硫石膏综合利用的现状与分析[J]. 粉煤灰综合利用, 2019(3):95-98.
[5]	刘小杰, 李建鹏, 吕庆, 等. 脱硫石膏综合利用的现状与展望[J]. 化工环保, 2017, 37(6):611-615.
[6]	Koralegedara N H, Pinto P X, Dionysiou D D, et al. Recent advances in flue gas desulfurization gypsum processes and applications-A review[J]. Journal of Environmental Management, 2019, 251.Doi: 10.1016/j.jenvman.2019.109572.
[7]	Butali T, Wolf W, Amaya P. The utilization of flue-gas desulfuriza-tion materials[J]. Coal Combustion Products(CCP′s), 2017(6):155-184.
[8]	韩青, 罗康碧, 李沪萍, 等. 磷石膏开发利用现状[J]. 化工科技, 2012, 20(1):53-58.
[9]	梅毅, 段东成, 杨亚斌, 等. 磷石膏的综合利用及其竞争力分析[J]. 无机盐工业, 2011, 43(8):1-5.
[10]	李国鹏. 磷石膏综合利用技术难点探讨[J]. 硫酸工业, 2019(10):20-21.
[11]	秦玲. 新修订的固体废物污染环境防治法9月施行[J]. 中国设备工程, 2020(10):1.
[12]	Liu S, Fang P, Ren J, et al. Application of lime neutralised phosp-hogypsum in supersulfated cement[J]. Journal of Cleaner Produc-tion, 2020, 272.Doi: 10.1016/j.jclepro.2020.122660.
[13]	Jin Z, Ma B, Su Y, et al. Effect of calcium sulphoaluminate cement on mechanical strength and waterproof properties of beta-hemihy-drate phosphogypsum[J]. Construction and Building Materials, 2020, 242.Doi: 10.1016/j.conbuildmat.2020.118198.
[14]	Zeng L, Bian X, Zhao L, et al. Effect of phosphogypsum on physio-chemical and mechanical behaviour of cement stabilized dredged soil from Fuzhou,China[J]. Geomechanics for Energy and the En-vironment, 2021(25).Doi: 10.1016/j.gete.2020.100195.
[15]	尤彩霞, 李军, 孙娜, 等. 电厂脱硫石膏制水泥缓凝剂二水石膏的研究[J]. 无机盐工业, 2019, 51(12):71-74.
[16]	莫奕新, 庞建勇, 黄金坤, 等. 粉煤灰-脱硫石膏复合水泥土渗透性试验研究[J]. 新型建筑材料, 2018, 45(1):122-125.
[17]	Sun H, Qian J, Yang Y, et al. Optimization of gypsum and slag con-tents in blended cement containing slag[J]. Cement and Concrete Composites, 2020, 112.Doi: 10.1016/j.cemconcomp.2020.103674.
[18]	潘洪祥, 张昺榴, 赵德强, 等. 磷石膏-熟料-粉煤灰道路基层水泥的生产与应用[J]. 新世纪水泥导报, 2019, 25(3):68-72.
[19]	周维. 烧结脱硫石膏用作水泥缓凝剂的研究[J]. 混凝土世界, 2020(5):74-78.
[20]	徐亚玲, 孙振平, 朱永明, 等. 一种以脱硫石膏为激发剂的高强混凝土及其制备方法:中国,102452814[P]. 2012-05-16.
[21]	杨志强, 陈晴, 郭清春, 等. 磷石膏在水泥生产中的应用现状与展望[J]. 硅酸盐通报, 2016, 35(9):2860-2865.
[22]	Zhang Y, Yu P, Pan F, et al. The synergistic effect of AFt enhance-ment and expansion in Portland cement-aluminate cement-FGD gypsum composite cementitious system[J]. Construction and Build-ing Materials, 2018, 190:985-994.
[23]	Gracioli B, Angulski Da Luz C, Beutler C S, et al. Influence of the calcination temperature of phosphogypsum on the performance of supersulfated cements[J]. Construction and Building Materials, 2020, 262.Doi: 10.1016/j.conbuildmat.2020.119961.
[24]	柯岩波. 脱硫石膏在水泥生产使用中的几点措施[J]. 中国水泥, 2016(3):101-102.
[25]	边成利, 时焕岗, 包文运, 等. 脱硫石膏热处理制备注浆成型模具[J]. 无机盐工业, 2020, 52(2):54-57.
[26]	李亮. 利用脱硫石膏制备发泡轻质材料的研究[J]. 无机盐工业, 2018, 50(11):49-52.
[27]	娄有信, 杨子, 徐惠国. 高强脱硫石膏砌块的制备及微观结构研究[J]. 辽宁师范大学学报:自然科学版, 2019, 42(1):83-87.
[28]	宋昊, 崔学坤. Na⁺、K⁺、Mg²⁺对纸面石膏板粘结性能的影响[J]. 建材世界, 2016, 37(1):30-32.
[29]	Yang L, Jing M, Lu L, et al. Effects of modified materials prepared from wastes on the performance of flue gas desulfurization gypsum-based composite wall materials[J]. Construction and Building Ma-terials, 2020, 257.Doi: 10.1016/j.conbuildmat.2020.119519.
[30]	张欣欣. 新型脱硫石膏砌块的制备及其性能研究[J]. 矿冶, 2019, 28(2):65-67.
[31]	戴丽聪. 利用脱硫石膏制备粉刷石膏砂浆[J]. 商品混凝土, 2019(10):62-64.
[32]	Zhao Y, Li Y, Wang S, et al. Combined application of a straw layer and flue gas desulphurization gypsum to reduce soil salinity and alkalinity[J]. Pedosphere, 2020, 30(2):226-235.
[33]	Yang Z, Zhang Q, Liang L, et al. Remediation of heavily saline-so-dic soil with flue gas desulfurization gypsum in Arid-Inland China[J]. Soil Science and Plant Nutrition, 2018, 64(4):526-534.
[34]	Wang Y, Shi L. The effects of modified flue gas desulfurization resi-due on growth of sweet potato and soil amelioration[J]. Water,Air,& Soil Pollution, 2015, 226(8).Doi: 10.1007/s11270-015-2508-1.
[35]	da Costa C H M, Crusciol C A C. Long-term effects of lime and pho-sphogypsum application on tropical no-till soybean-oat-sorghum rotation and soil chemical properties[J]. European Journal of Agro-nomy, 2016, 74:119-132.
[36]	Crusciola C A C, Artigiania A C C A, Arfb O, et al. Soil fertility,plant nutrition,and grain yield of upland rice affected by surface application of lime,silicate,and phosphogypsum in a tropicalno-till system[J]. Catena, 2016, 137:87-99.
[37]	Hentati O, Abrantes N, Caetano A L, et al. Phosphogypsum as a soil fertilizer:Ecotoxicity of amended soil and elutriates to bacteria,invertebrates,algae and plants[J]. Journal of Hazardous Materi-als, 2015, 294:80-89.
[38]	Tirado-Corbalá R, Slater B K, Dick W A, et al. Hydrologic proper-ties and leachate nutrient responses of soil columns collected from gypsum-treated fields[J]. Soil and Tillage Research, 2013, 134:232-240.
[39]	Baligar V, Clark R, Korcak R, et al. Flue gas desulfurization pro-duct use on agricultural land[J]. Advances in Agronomy, 2011, 111:51-86.
[40]	Kammoun M, Ghorbel I, Charfeddine S, et al. The positive effect of phosphogypsum-supplemented composts on potato plant growth in the field and tuber yield[J]. Journal of Environmental Manageme-nt, 2017, 200:475-483.
[41]	陈闽子, 佟琦, 韩树民. 磷石膏、粉煤灰在硅钙硫肥料生产中的应用[J]. 中国资源综合利用, 2003(9):9-11.
[42]	陈平, 田宇, 胡成. 盐溶液种类和浓度对α-半水脱硫石膏合成的影响[J]. 无机盐工业, 2020, 52(10):130-134.
[43]	程雲, 林美庆, 赵敏. 脱硫石膏制备半水石膏晶须的研究[J]. 无机盐工业, 2016, 48(2):63-67.
[44]	罗冰, 陈秋菊. 工业副产石膏制备石膏晶须的研究进展[J]. 学术论坛, 2019(11):35-37.
[45]	周华锋, 张肖肖, 李响. 磷石膏制备硫酸钙晶须的工艺研究[J]. 硅酸盐通报, 2017, 36(6):2090-2094.
[46]	林艳, 彭同江, 孙红娟, 等. 石膏晶须的制备方法与应用[J]. 人工晶体学报, 2017, 46(4):705-711.
[47]	汪潇, 金彪, 王宇斌, 等. 阴离子在脱硫石膏晶须水热结晶中的作用机理[J]. 高等学校化学学报, 2020, 41(3):473-480.
[48]	王艾文, 陈德玉, 黄滔. 磷石膏常压无氯盐溶液法制备硫酸钙晶须[J]. 非金属矿, 2020, 43(4):84-87.
[49]	谢晴, 蒋美雪, 彭同江, 等. 磷石膏常压酸化法制备无水硫酸钙晶须的实验研究[J]. 人工晶体学报, 2019, 48(6):1060-1066.
[50]	Gao J, Li Q, Liu F. Calcium sulfate whisker prepared by flue gas desulfurization gypsum:A physical-chemical coupling production process[J]. Chinese Journal of Chemical Engineering, 2020, 28(8):2221-2226.
[51]	Sun H, Tan D, Peng T, et al. Preparation of calcium sulfate whisker by atmospheric acidification method from flue gas desulfurization gypsum[J]. Procedia Environmental Sciences, 2016, 31:621-626.
[52]	Guan Q, Tang H, Sun W, et al. Insight into influence of glycerol on preparing α-CaSO₄·1/2H₂O from flue gas desulfurization gypsum in glycerol-water solutions with succinic acid and NaCl[J]. Indu-strial & Engineering Chemistry Research, 2017, 56(35).Doi: 10.1021/acs.iecr.7b02067.
[53]	郑绍聪, 余强, 谢刚, 等. 用盐酸溶解工业磷石膏重结晶法制备硫酸钙晶须[J]. 湿法冶金, 2016, 35(6):488-491.
[54]	Song W, Zhou J, Wang B, et al. Production of SO₂ gas:new and ef-ficient utilization of flue gas desulfurization gypsum and pyrite re-sources[J]. Industrial & Engineering Chemistry Research, 2019, 58(44):20450-20460.
[55]	Zheng S, Ning P, Ma L, et al. Reductive decomposition of phospho-gypsum with high-sulfur-concentration coal to SO₂ in an inert atmo-sphere[J]. Chemical Engineering Research and Design, 2011, 89(12):2736-2741.
[56]	王艳梅, 刘梅堂, 孙华, 等. 磷石膏转氨法制硫酸技术原理与过程评价[J]. 化工进展, 2015, 34:196-201.
[57]	黄岳元, 赵天成, 张粉艳, 等. 磷石膏废渣生产硫酸钾新工艺研究—Ⅰ.磷石膏废渣制备硫酸铵工艺[J]. 西北大学学报:自然科学版, 2001(4):315-318.
[58]	许春凤, 邓跃全, 董发勤, 等. 磷石膏固相球磨制备硫酸铵的研究[J]. 非金属矿, 2010, 33(3):62-65.
[59]	苏航, 左海滨, 赵骏. 石膏在高温下的分解脱硫研究[J]. 无机盐工业, 2019, 51(7):68-73.
[60]	Zhao J, Su H, Zuo H, et al. The mechanism of preparation calcium ferrite from desulfurization gypsum produced in sintering[J]. Jour-nal of Cleaner Production, 2020, 267.Doi: 10.1016/j.jclepro.2020.122002.

原料	w（CaO）	w（SiO₂）	w（Al₂O₃）	w（SO₃）	w（Fe₂O₃）
天然石膏	31.12	2.38	0.82	35.16	0.35
脱硫石膏	31.42	3.12	1.38	44.72	0.34
原料	w（MgO）	w（K₂O）	w（Na₂O）	烧失率
天然石膏	4.39	≤0.3	≤0.15	23.85
脱硫石膏	0.35	≤0.4	≤0.10	18.04

w（SO₃）	w（CaO）	w（SiO₂）	w（Al₂O₃）	w（MnO）	w（Fe₂O₃）	w（MgO）
32.20	28.63	17.06	0.236	≤0.1	0.212	≤0.03
w（K₂O）	w（Na₂O）	w（P₂O₅）	w（F）	w（水）	w（其他）	pH
≤0.1	≤0.1	0.70	≤0.5	18.84	1.441	3.11

类型	方法	反应物	反应温度/℃	产物	优点（O）和缺点（X）
相转变法	水热法	石膏	120 （高压）	半水合物（HH）	纯度高（O）条件苛刻（X）
	盐溶液法	石膏、 HCl、CaCl₂	98~101	HH	常压条件（O）污染环境（X）
	盐溶液法	石膏、 H₂SO₄、CaCl₂	102~120	HH	常压条件（O）污染环境（X）
	有机溶剂法	石膏、甘油	110	HH	常压条件（O）高成本（X）
结晶法	结晶法	石膏、无机酸	70~110	二水合物（DH）	杂质去除（O）低性能（X）

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会