一氧化碳脱毒铬渣制备水泥矿物掺合料

doi:10.11962/1006-4990.2020-0366

Abstract

Abstract:

The influence of the addition ratio of chromium slag detoxified by carbon monoxide off-gas on the compressive strength,bending strength and setting time of concrete test samples were experimentally studied.The leaching concentrations of total chromium（Cr） and hexavalent chromium Cr（Ⅵ）were determined,and their effective diffusion co-efficient D and diffu-sion factor L were calculated by semi-dynamic leaching experiment.The results showed that the detoxified chromium slag after fine grinding could meet the requirement of cement mineral admixture.With the increase of adding ratio,the setting time of mortar were extended,the compressive and bending strength were declined,but all the experimental groups meet the strength grade requirements of C60.The D value of Cr（Ⅵ） and total Cr in the sample was 10^-10~10^-9,L value was more than 9,and the migration ability was very low,which proved that the preparation of mineral admixtures was a safe and effective resource disposal method for detoxified chromium slag.

Key words: dolomite, buffer system, vaterite, calcium carbonate, detoxified chromium residue, mineral admixture, carbon monoxide, cement

CLC Number:

He Liwei,Zhou Xuejin,Ning Ping. Preparation of cement mineral admixture from chromium slag detoxified by carbon monoxide[J]. Inorganic Chemicals Industry, 2021, 53(5): 73-77.

Figures/Tables 15

Fig.1

Table 1

Table 2

Fig.2

Fig.3

Table 3

Fig.1

Fig.4

Fig.5

Fig.2

Table 4

Fig.6

Fig.7

Fig.8

Fig.9

References 26

[6]	Fu Lianhua, Qi Chao, Hu Yanru, et al. Cellulose/vaterite nanocom-posites:Sonochemical synjournal,characterization,and their appli-cation in protein adsorption[J]. Materials Science & Engineering C, 2019,96:426-435.
[7]	Wang Xiaoqiang, Wu Congmeng, Tao Kai, et al. Influence of oval-bumin on CaCO₃ precipitation during in vitro biomineralization[J]. Journal of Physical Chemistry B, 2010,114(16):5301. doi: 10.1021/jp1008237 pmid: 20369864
[8]	Liu Y, Cui Y J, Mao H Y, et al. Calcium carbonate crystallization in the presence of casein[J]. Crystal Growth & Design, 2012,12(10):4720-4726. doi: 10.1021/cg3005213
[9]	Porter A L, Wilson W J. Manufacture of precipitated calcium carbona-te of improved color and stable crystalline form：US,6132696A[P]. 2000-10-17.
[10]	黄文艺, 马蓝宇, 程昊, 等. 氯化铝对碳酸钙结晶形貌的影响[J]. 无机盐工业, 2018,50(1):20-23.
[1]	纪柱. 中国铬盐近五十年发展概况[J]. 无机盐工业, 2010,42(12):1-15.
[11]	Di Profio Gianluca, Salehi Shabnam Majidi, Caliandro Rocco, et al. Bioinspired synjournal of CaCO₃ superstructures through a novel hy-drogel composite membranes mineralization platform:A comprehe-nsive view[J]. Advanced Materials, 2016,28(4):610-616. doi: 10.1002/adma.201504608
[2]	Walawska B, Kowalski Z. Model of technological alternatives of pro-duction of sodium chromate(Ⅵ) with the use of chromic wastes[J]. Waste Management, 2000,20(8):711-723. doi: 10.1016/S0956-053X(00)00038-6
[3]	Hori M, Shozugawa K, Matsuo M. Hexavalent chromium pollution caused by dumped chromium slag at the urban park in Tokyo[J]. Journal of Material Cycles & Waste Management, 2015,17(1):201-205.
[12]	郑天文, 陈雪梅. 球霰石碳酸钙微球的合成及其机理[J]. 材料科学与工程学报, 2018(3):358-364
[13]	Loïc Dupont, François Portemer, the late Michel Figlarz. Synjournal and study of a well crystallized CaCO₃ vaterite showing a new habi-tus[J]. Journal of Materials Chemistry, 1997,7(5):797-800. doi: 10.1039/a607761g
[4]	Matern K, Weigand H, Singh A, et al. Environmental status of gro-undwater affected by chromite ore processing residue(COPR) dum-psites during pre-monsoon and monsoon seasons[J]. Environmental Science & Pollution Research, 2017,24(4):3582-3592.
[14]	Dmitry V V, Alexander I P, Michelle P, et al. Matrix polyelectrolyte microcapsules:New system for macromoleculeen-capsulation[J]. Langmuir, 2004,20(8):3398-3406. doi: 10.1021/la036177z
[5]	刘帅霞. 两段式还原工艺解毒铬渣技术研究[D]. 上海:东华大学, 2013.
[6]	Li Y, Cundy A B, Feng J, et al. Remediation of hexavalent chromium contamination in chromite ore processing residue by sodium dithio-nite and sodium phosphate addition and its mechanism[J]. Journal of Environmental Management, 2017,192(5):100-106. doi: 10.1016/j.jenvman.2017.01.031
[15]	陈佩圆, 胡秀平, 孙龙, 等. 快速沉淀法制备高分散高纯度球霰石晶体[J]. 人工晶体学报, 2019,48(3):114-118.
[7]	Panneerselvam P, Choppala G, Kunhikrishnan A, et al. Potential of novel bacterial consortium for the remediation of chromium contam-ination[J]. Water,Air,and Soil Pollution, 2013,224(12):211-221.
[16]	Ramesh T N, Inchara S A, Pallavi K. Para-amino benzoic acid-me-diated synjournal of vaterite phase of calcium carbonate[J]. Journal of Chemical Sciences, 2015,127(5):843-848. doi: 10.1007/s12039-015-0849-3
[17]	邹俭鹏, 杨洪志, 肖平, 等. 微纳分级结构碳酸钙中空微球的可控制备[J]. 无机材料学报, 2016,31(7):711-718.
[8]	Chen J, Wang Y, Zhou S, et al. Reduction/immobilization processes of hexavalent chromium using metakaolin-based geopolymer[J]. Jour-nal of Environmental Chemical Engineering, 2016,4(2):2084-2089.
[9]	何力为, 李彬, 宁平, 等. 利用一氧化碳工业废气解毒铬渣的方法及条件优化[J]. 环境工程学报, 2018,12(9):195-204.
[18]	Hu Qiaona, Zhang Jiaming, Henry Teng, et al. Growth process and crystallographic properties of ammonia-induced vaterite[J]. Ame-rican Mineralogist, 2015,97(8/9):1437-1445.
[10]	Bagheri A, Nazari A. Compressive strength of high strength class C fly ash-based geopolymers with reactive granulated blast furnace slag aggregates designed by Taguchi method[J]. Materials & De-sign, 2014,54(2):483-490.
[11]	He L, Li B, Ning P, et al. Chromium slag detoxification by carbon monoxide off-gases and optimization of detoxification parameters by Box-Behnken design[J]. Journal of Material Cycles and Waste Management, 2019,22(3):111-122. doi: 10.1007/s10163-019-00918-1
[12]	白智韬, 邱桂博, 彭犇, 等. 高碳铬铁渣基微晶玻璃体系调控分析[J]. 环境工程, 2019,37(1):158-163.
[13]	方久华, 杨峰, 左明扬, 等. 玻璃配合料中铬渣最大允许用量研究[J]. 无机盐工业, 2015,47(1):18-21.
[14]	冯勇, 韩艳丽. 钢渣混凝土抗硫酸盐、镁盐侵蚀性能的实验分析[J]. 硅酸盐通报, 2015,34(11):3345-3351.
[15]	Jagupilla S C, Moon D H, Wazne M, et al. Effects of particle size and acid addition on the remediation of chromite ore processing re-sidue using ferrous sulfate[J]. Journal of Hazardous Materials, 2009,168(1):121-128. doi: 10.1016/j.jhazmat.2009.02.012 pmid: 19272700
[16]	Chrysochoou M, Fakra S C, Marcus M A, et al. Microstructural an-alyses of Cr(Ⅵ) speciation in chromite ore processing residue (COPR)[J]. Environmental Science & Technology, 2009,43(14):5461-5466. doi: 10.1021/es9005338
[17]	GB/T 17671—1999 水泥胶砂强度实验[S].
[18]	GB/T 7023—2011 低、中水平放射性废物固化体标准浸出实验方法[S].
[19]	HJ/T 299—2007 固体废物浸出毒性浸出方法硫酸硝酸法[S].
[20]	GB/T 15555.4—1995 固体废物六价铬的测定二苯碳酰二肼分光光度法[S].
[21]	HJ 687—2014 固体废物六价铬的测定碱消解/火焰原子吸收分光光度法[S].
[22]	HJ/T 301—2007 铬渣污染治理环境保护技术规范(暂行)[S].
[23]	GB/T 203—2008 用于水泥中的粒化高炉矿渣[S].
[24]	GB/T 2847—2005 用于水泥中的火山灰质混合材料[S].
[25]	GB 175—2007 通用硅酸盐水泥[S].
[26]	Dutre V, Vandecasteele C. An evaluation of the solidification/stabi-lization of industrial arsenic containing waste using extraction and semi-dynamic leach tests[J]. Waste Management, 1996,16(7):625-631. doi: 10.1016/S0956-053X(97)00003-2

编号	m（水泥）/g	m（铬渣）/g	m（标准砂）/g	说明
0	450	0	1 350	对照
A-1	405	45	1 350	10%
A-2	360	90	1 350	20%
A-3	315	135	1 350	30%
A-4	270	180	1 350	0%

编号	初凝时间	终凝时间	编号	初凝时间	终凝时间
0	217	252	A-3	227	294
A-1	218	275	A-4	230	295
A-2	221	289

编号	Cr（Ⅵ）平均有效扩散系数D/（cm²·s^-1）	Cr（Ⅵ）浸出因子L	编号	总Cr平均有效扩散系数 D/（cm²·s^-1）	总Cr 浸出因子L
A-1	3.57×10^-10	9.63	A-1	1.56×10^-10	10.27
A-2	4.63×10^-10	9.53	A-2	3.58×10^-10	9.61
A-3	7.43×10^-10	9.36	A-3	2.89×10^-10	9.74
A-4	1.48×10^-9	9.11	A-4	2.14×10^-10	9.84

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Preparation of cement mineral admixture from chromium slag detoxified by carbon monoxide

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 15

References 26

Related Articles 15

Metrics

Comments

Recommended 0

[1]	SHI Yunpeng, GUO Ze, ZHANG Hanquan, LU Manman. Study on treatment of ammonia nitrogen wastewater by roasted phosphorus tailings [J]. Inorganic Chemicals Industry, 2025, 57(3): 94-100.
[2]	ZHANG Jinjun, GUO Linlin, MIAO Chengpeng, LI Xingyu, PANG Yaheng, YANG Rongkai, YU Yasen. Study on preparation of spherical calcium carbonate for coating fillers based on carbide slag as raw materials [J]. Inorganic Chemicals Industry, 2025, 57(2): 113-119.
[3]	BAI Xingxing, LI Hanfei, TANG Yong, ZHANG Jun, ZHU Guangkai, LI Lishuo, TONG Zhangfa. Study on preparation of cellulose based hydrogel doped with nano-calcium carbonate and its adsorption properties of copper ions [J]. Inorganic Chemicals Industry, 2025, 57(2): 83-91.
[4]	ZHANG Jianle, CAO Yapeng, ZU Minghua, ZHANG Zhikun, LIU Yumin, HAN Jilong. Study on morphology of calcium carbonate controlled by sodium dodecyl sulfate and amino acid double template [J]. Inorganic Chemicals Industry, 2025, 57(1): 58-63.
[5]	YAN Xin, LIU Hailu, LIU Baolin, LIU Yi, LIU Yanyang. Research on key technologies and mechanisms of green nano calcium carbonate production [J]. Inorganic Chemicals Industry, 2025, 57(1): 71-76.
[6]	CHENG Ziyang, CHEN Guofu. Early hydration kinetics research of nano-SiO₂ and cement composite cementitious materials [J]. Inorganic Chemicals Industry, 2024, 56(7): 80-87.
[7]	TU Yanping, BAI Dengxian, CHENG Shukai, XIE Junjie, HUANG Zhiliang, CHEN Guofu. Effect of high temperature modification of mineral powder and quicklime on properties of phosphogypsum cement based materials [J]. Inorganic Chemicals Industry, 2024, 56(6): 94-101.
[8]	LI Yuxing, ZHANG Jincai, CHENG Fangqin. Research progress of preparation and growth mechanism of various crystalline nano-calcium carbonate [J]. Inorganic Chemicals Industry, 2024, 56(5): 1-10.
[9]	LI Keke, XUE Jiangwei, WANG Luwei, GUAN Xuemao. Effect of MgAl-layered double hydroxides on properties of high-iron low-calcium portland cement [J]. Inorganic Chemicals Industry, 2024, 56(4): 57-63.
[10]	YU Zhou, HE Zhaoyi, TANG Liang, HE Sheng, XIAO Haixin, XIAO Yixun. Study on preparation and microscopic properties of typical sulfate solid waste composite cementitious materials [J]. Inorganic Chemicals Industry, 2024, 56(4): 90-97.
[11]	WANG Ruting, ZHAO Xiaorong, HUANG Xuquan, WANG Haojie, XUE Fei, CAI Jiawei. Research on preparation and early performance of mixed phase phosphogypsum-based cementing materials [J]. Inorganic Chemicals Industry, 2024, 56(3): 98-104.
[12]	YUAN Xing, DONG Wenyan, WANG Mingshun, CHENG Dilan, AO Xianquan. Effect of metallic ions on dispersion behavior of dolomite mineral particles [J]. Inorganic Chemicals Industry, 2024, 56(2): 44-50.
[13]	JIANG Lilong, LI Jianqiu, YANG Lin, ZHANG Qinggang. Study on performance of concrete with high-Mg phosphate tailing as mineral admixture [J]. Inorganic Chemicals Industry, 2024, 56(1): 90-95.
[14]	CHEN Yanmeng, MO Huiling, ZHONG Jiamei, YANG Pengfei, LAN Junfeng. Study on preparation process of porous calcium carbonate by carbonization [J]. Inorganic Chemicals Industry, 2023, 55(8): 102-108.
[15]	ZHANG Jinjun, GUO Linlin, LIU Bojing, FENG Shuang, SHI Qi. Study on preparation of needle-like shaped CaCO₃ from calcium carbide slag [J]. Inorganic Chemicals Industry, 2023, 55(7): 103-108.