水相法制备双乙二酸硼酸锂的中试工艺研究

doi:10.11962/1006-4990.2019-0605

Abstract

Abstract:

The double oxalate lithium borate（LiBOB） was prepared by aqueous-phase method.The effect of material ratio,reaction temperature,reaction time and amount of crystallization solvent on the product quality under the condition of pilot test was studied.The result of products was confirmed by FTIR,TG-DSC and XRD.The pilot plant had achieved a production scale of 10 t/a at present.The experimental results showed the optimum operating parameters which were material ratio（the amount-of-substance ratio of oxalic acid to lithium carbonate to boric acid） of 4∶2∶1.1,reaction temperature of 80 ℃,reaction time of 8 h,the concentration amount（the mass ratio of residual solvent to total solvent mass） of about 80% in the process of concentration and crystallization,and the addition amount of crystallization agent of 4 times of the product mass.The dynamic drying was adopted for 8 h.After analysis,the quality of the product prepared by this process exceeded the level of the market products.

Key words: double oxalate lithium borate, aqueous-phase method, crystallization agent

CLC Number:

TQ131.11

Liu Yanrui,Song Congcong,Shi Guizhen,Wang Kun. The study of double oxalate lithium borate preparation technology by aqueous phase method[J]. Inorganic Chemicals Industry, 2020, 52(10): 100-105.

Figures/Tables 18

References 11

[1]	Fan Lizhen, Xing Taofeng, Rafi Awan. Studies on lithium bis(oxalato)-borate/propylene carbonate-based electrolytes for Li-ion batteries[J]. Ionics, 2011,17(6):491-494.
[2]	王艳菊, 乔庆东, 李琪, 等. 双乙二酸硼酸锂的合成及性能研究[J]. 化工新型材料, 2015,43(10):193-195.
[3]	平平. 锂离子电池热失控与火灾危险性分析及高安全性电池体系研究[D]. 合肥:中国科学技术大学, 2014.
[4]	邓凌峰, 陈洪, 魏银烨. 锂离子电池电解质锂盐双乙二酸硼酸锂的制备与性能[J]. 材料导报, 2009,23(S1):295-298.
[5]	宋洋, 赵连海, 梁子雷, 等. 双乙二酸硼酸锂在液态电解质中的研究进展[J]. 无机盐工业, 2009,41(10):11-14.
[6]	赵本好. 一种应用于电池电解液中环保型添加剂的性能研究[J]. 电池工业, 2017,21(3):9-11.
[7]	李世友, 马培华, 滕祥国, 等. 锂离子电池电解质的新型锂盐——双乙二酸硼酸锂[J]. 化学进展, 2007(5):695-699.
[8]	Swiderska-Mocek A, Naparstek D. Physical and electrochemical properties of lithium bis(oxalate)borate-organic mixed electrolytes in Li-ion batteries[J]. Electrochimica Acta, 2016,204:69-77.
[9]	Ulrich Wietelmann,Uwe Lischka,Marion Wegner, Lithium bisox alatoborate,the production thereof and its use as a conducting salt：US,6506516B1[P]. 2003-01-14.
[10]	张玥, 袁莉, 刘锦平, 等. 锂离子电池用双草酸硼酸锂的固相合成[J]. 无机盐工业, 2011,43(4):42-44.
[11]	陈姚, 杨倩韵, 于欣伟, 等. 两步法合成锂离子电池用双草酸硼酸锂[J]. 电池, 2016,46(5):251-254.

温度/℃	溶解度/g	温度/℃	溶解度/g
10	6.08	60	44.5
30	14.3	70	65.0
40	21.5	80	84.5
50	31.4	90	119.8

温度/℃	溶解度/g	温度/℃	溶解度/g
10	3.57	60	14.51
20	5.04	70	16.73
30	6.60	80	23.75
40	8.72	90	30.38
50	11.54	100	40.25

氧化剂Y加入量（氧化剂与产品质量比）	纯度/ %	Cl含量/ （mg·kg^-1）	色度/ APHA	浊度/NTU	SO₄^2-含量/ （mg·kg^-1）
1/2 000	99.32	1	80	2	0.2
1/1 500	99.50	1	80	2	0.2
1/1 000	99.79	1	15	2	0.2
1/800	99.10	22	15	2	19.0

项目	名称	单价/ （万元·t^-1）	所需用量/ t	成本/ 万元
原材料	二水草酸	0.48	1.30	0.62
	碳酸锂	6.00	0.21	1.26
	硼酸	0.42	0.32	0.14
	LY07	1.00	10（损耗1 t）	1.00
	LY05	0.80	5（损耗0.5 t）	0.40
直接人工费用（7人）				7.00
制造费用	辅材			0.50
	设备折旧			0.50
	电			0.80
	维修			0.30
	液氮			0.80
总成本				13.32

λ/cm^-1	振动类型	λ/cm^-1	振动类型
1 813.75、 1 777.00	C=O的离域或定域震动	1 016.30	O—B—O的伸缩振动
1 747.80	C=O的伸缩振动	983.21、956.43	O—B—O的不伸缩振动
1 638.87	COO—的不对称伸缩振动	709.82	COO—的变形振动
1 441.73	COO—的对称伸缩振动	617.15	B—O的变形振动
1 365.56	B—O的伸缩振动	478.92	BO₄键的振动
1 304.81	C—O—B—O—C的伸缩振动

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

The study of double oxalate lithium borate preparation technology by aqueous phase method

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 18

References 11

Related Articles 15

Metrics

Comments

Recommended 0

批次	二水草酸投料量/kg	硼酸投料量/kg	碳酸锂投料量/kg	理论产量/kg	实际产量/kg	产品收率/%
QLC-1	100	24.5	16.11	76.94	75.40	98.0
QLC-2	100	24.5	16.11	76.94	75.30	97.8
QLC-3	100	24.5	16.11	76.94	75.36	97.9
QLC-4	100	24.5	16.11	76.94	75.42	97.9
QLC-5	100	24.5	16.11	76.94	75.30	97.9
QLC-6	100	24.5	16.11	76.94	75.48	98.1
QLC-7	100	24.5	16.11	76.94	76.02	98.8
QLC-8	100	24.5	16.11	76.94	75.41	98.0
QLC-9	100	24.5	16.11	76.94	75.35	97.9
QLC-10	100	24.5	16.11	76.94	75.29	97.8

[1]	MA Jingyuan, LI Yan, ZHOU Hanjie, LI Jiangang. Research progress of PEO based organic/inorganic composite solid electrolyte [J]. Inorganic Chemicals Industry, 2025, 57(3): 1-8.
[2]	JIANG Minghui, ZHANG Liqing, PANG Meijing, LIU Chao. Research progress of ion channels for achieving monovalent cation sieving [J]. Inorganic Chemicals Industry, 2025, 57(3): 9-17.
[3]	LI Chao, WANG Liping, GAO Guimei, ZHANG Yunfeng, HONG Yu, LIU Darui, XU Lijun, CUI Yongjie. Study on reaction mechanism of acid leaching lithium from circulating fluidized bed fly ash [J]. Inorganic Chemicals Industry, 2025, 57(3): 101-107.
[4]	SONG Jiaxi, JI Renfei, CHEN Jun, LIN Sen, YU Jianguo. Research on characteristics analysis and pretreatment on deeply deactivated power battery ternary cathode materials [J]. Inorganic Chemicals Industry, 2025, 57(2): 44-49.
[5]	KONG Lingjie, LI Guangbi, XIE Jiahao, YANG Xinhui, BAI Xiaoqin. Research progress on lithium extraction technology from salt lake brine [J]. Inorganic Chemicals Industry, 2025, 57(1): 14-26.
[6]	ZHANG Shanshan, ZENG Yule, ZHANG Ting, LIN Sen, LIU Chenglin. Research progress of cathode pre-lithiation technology for lithium-ion batteries [J]. Inorganic Chemicals Industry, 2025, 57(1): 1-13.
[7]	ZHAO Runze, QIAN A′niu. Research progress of lithium recovery for spent lithium-ion batteries and preparation in battery-grade lithium carbonate [J]. Inorganic Chemicals Industry, 2024, 56(12): 70-78.
[8]	FU Yu, ZHANG Boshuang, YANG Jianmao, LIU Jianyun. Research progress of lithium manganese oxide materials in electrochemical lithium extraction applications [J]. Inorganic Chemicals Industry, 2024, 56(12): 62-69.
[9]	GE Jianhua, XIE Minyan, OUYANG Quansheng, SHAO Jiaojing. Advances in regeneration processes of cathode materials for spent power batteries [J]. Inorganic Chemicals Industry, 2024, 56(12): 79-87.
[10]	WANG Ruirui, ZHU Chaoliang, MU Bing, MA Wanxia, FAN Jie, XU Guowang, SHI Yifei, DENG Xiaochuan, QING Binju. Preparation of cubic manganese carbonate by hydrothermal method and its application in extraction of lithium [J]. Inorganic Chemicals Industry, 2024, 56(12): 94-103.
[11]	CHENG Chunchun, LI Yulong, ZHANG Zhiqiang, ZUO Shuo, QIN Donglan, ZHOU Na, WANG Jiaqin. Study on agglomeration phenomenon and regulation method of lithium carbonate crystal prepared from potassium carbonate [J]. Inorganic Chemicals Industry, 2024, 56(10): 47-54.
[12]	MA Shuqing, LI Changwen, SHI Chenglong, QIN Yaru. Kinetic study of lithium extraction from solution with iron-based ionic liquid system [J]. Inorganic Chemicals Industry, 2024, 56(9): 60-66.
[13]	TIAN Peng, ZHANG Haoran, XU Jingang, MOU Chenxi, XU Qianjin, NING Guiling. Study on aluminum sol modified anode and cathode materials for lithium ion batteries [J]. Inorganic Chemicals Industry, 2024, 56(9): 44-53.
[14]	ZHU Zongjiang, WANG Gang, WEI Yuanfeng, TANG Yanhong, KAKUTA Cheng, LIU Chengbin. Research progress and prospect of resourceful recycling technology of electrolyte from decommissioned lithium⁃ion battery [J]. Inorganic Chemicals Industry, 2024, 56(7): 11-17.
[15]	SU Baocai, ZHANG Qin, XIE Yuanjian, CAI Pingxiong, PAN Yuanfeng. Advances in synthesis methods and structural modification of LiMnFePO₄ materials [J]. Inorganic Chemicals Industry, 2024, 56(7): 28-36.

批号	纯度/ %	H₂O含量/ （mg·kg^-1）	色度/ APHA	浊度/ NTU	Ca含量/ （mg·kg^-1）	Fe含量/ （mg·kg^-1）
生产产品	99.79	16	15	2	0.2	1.2
市售产品	99.17	53	15	2	3.1	5.4