硅灰、粉煤灰对矿渣基地质聚合物性能的影响

doi:10.19964/j.issn.1006-4990.2024-0471

Abstract

Abstract:

In this study，silica fume and fly ash used to improve the mechanical properties，hydration reaction and microstructure of slag-based geopolymer were disscussed.The effects of different proportions of silica fume and fly ash on the mechanical properties of the geopolymer mortar were studied，and the hydration mechanism and microstructure were analyzed by XRD，FTIR and SEM.The research showed that the effect of 10% silica fume and 1.2 and 25% sodium silicate was the best，and the compressive strength of 3，7 d and 28 d could reach 54，68 MPa and 72 MPa，while the effect of fly ash was poor，and the effect of 3，7 d and 28 d was better when the content was 10% and 1.2 and 25% of sodium silicate.The strength was 53，58 MPa and 62 MPa respectively.The addition of silica ash filled the pores of the geopolymer of the slag-based，and a large amount of SiO₂ reacted with OH^-，resulting in the Si—O bond fracture reaction to form calcium silicate aluminate hydrate［C-（A）-S-H］ and sodium silicate aluminate hydrate［N-（A）-S-H］ gels，which improved the mechanical properties，hydration reaction and microstructure of the geopolymer of the slag-based.However，excess silica ash would restrict the formation of gel，resulting in decreased compressive strength.The compressive strength of pure slag ground geopolymer for 7 d and 28 d was increased by 23.6%，9.1% respectively.Due to the activity and low calcium content of fly ash，the incorporation of fly ash hindered the hydration reaction of the geopolymer in the slag-based and the microscopic cracks were larger.Therefore，the combination of silica fume and slag could produce the high strength geopolymer cementing materias.

Key words: slag-based geopolymer, silica fume, fly ash, mechanical property, microscopic property

CLC Number:

TQ528.7

FENG Hao, QIN Meng, HE Zhaoyi, BI Yanli, SONG Yu, DU Youcheng. Effect of silica fume and fly ash on properties of slag-based geopolymer[J]. Inorganic Chemicals Industry, 2025, 57(11): 91-99.

Figures/Tables 14

Table 1

Fig.1

Table 2

Table 3

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

Table 4

References 15

[1]	乔京生，王旭影，王冠泓，等.粒化高炉矿渣微粉固化淤泥质土的动力特性及微观机理［J］.硅酸盐通报，2021，40（7）：2306-2312.
	QIAO Jingsheng， WANG Xuying， WANG Guanhong，et al.Dynamic characteristics and microscopic mechanism of muddy clay solidified by ground granulated blast-furnace slag［J］.Bulletin of the Chinese Ceramic Society，2021，40（7）：2306-2312.
[2]	RAMEZANIANPOUR A A， MOEINI M A.Mechanical and durability properties of alkali activated slag coating mortars containing nanosilica and silica fume［J］.Construction and Building Materials，2018，163：611-621.
[3]	GAO X， YU Q L， BROUWERS H J H.Reaction kinetics，gel character and strength of ambient temperature cured alkali activated slag-fly ash blends［J］.Construction and Building Materials，2015，80：105-115.
[4]	李晨，孙川，刘松玉.粒化高炉矿渣微粉对固化土特性影响研究［J］.地下空间与工程学报，2013，9（S2）：1827-1832.
	LI Chen， SUN Chuan， LIU Songyu.The effects of GGBS on the engineering properties of stabilized soil［J］.Chinese Journal of Underground Space and Engineering，2013，9（S2）：1827-1832.
[5]	TU Wenlin， FANG Guohao， DONG Biqin，et al.Behaviour of alkali-activated fly ash-slag paste at elevated temperatures：An experimental study［J］.Cement and Concrete Composites，2024，147：105438.
[6]	孙佳.钠/钾水玻璃激发矿渣基地质聚合物的泛碱研究［D］.南宁：广西大学，2019.
	SUN Jia.Pan-alkali study of sodium/potassium sodium silicate excited slag base polymers［D］.Nanning：Guangxi University，2019.
[7]	詹疆淮.碱激发偏高岭土—矿渣复合胶凝材料体积稳定性研究［D］.银川：宁夏大学，2023.
	ZHAN Jianghuai.Study on volume stability of alkali-excited meta-kaolinite-slag composite cementing materials［D］.Yin chuan：Ning-xia university，2023.
[8]	FANG Shuai， LAM E S S， LI Bo，et al.Effect of alkali contents，moduli and curing time on engineering properties of alkali activated slag［J］.Construction and Building Materials，2020，249：118799.
[9]	RAVIKUMAR D， NEITHALATH N.Reaction kinetics in sodium silicate powder and liquid activated slag binders evaluated using isothermal calorimetry［J］.Thermochimica Acta，2012，546：32-43.
[10]	CUI Yong， WANG Dongmin， WANG Yiren，et al.Effects of the n（H₂O：Na₂O_eq） ratio on the geopolymerization process and microstructures of fly ash-based geopolymers［J］.Journal of Non-Crystalline Solids，2019，511：19-28.
[11]	OZER I， SOYER-UZUN S.Relations between the structural characteristics and compressive strength in metakaolin based geopolymers with different molar Si/Al ratios［J］.Ceramics International，2015，41（8）：10192-10198.
[12]	ZHANG Yunsheng， SUN Wei， CHEN Qianli，et al.Synthesis and heavy metal immobilization behaviors of slag based geopoly-mer［J］.Journal of Hazardous Materials，2007，143（1/2）：206-213.
[13]	姚力豪，王彦平，陈昶旭，等.硅灰对粉煤灰-矿渣基地质聚合物性能的影响［J］.新型建筑材料，2022，49（5）：48-52.
	YAO Lihao， WANG Yanping， CHEN Changxu，et al.Effect of silica fume on properties of fly ash-slag based geopolymer［J］.New Building Materials，2022，49（5）：48-52.
[14]	ANDERSEN M D， JAKOBSEN H J， SKIBSTED J.Characterization of white Portland cement hydration and the C-S-H structure in the presence of sodium aluminate by 27Al and ²⁹Si MAS NMR spectroscopy［J］.Cement and Concrete Research，2004，34（5）：857-868.
[15]	KORPA A， DERVISHI S， VOLAVSEK J，et al. ²⁹Si and ²⁷Al MAS NMR assessment of the C-（A-） S-H nanomolecular structure of Ultra-High-Performance Concrete（UHPC） modified with pyrogenic oxides［J］.Journal of the Indian Chemical Society，2022，99（6）：100443.

成分	w（SiO₂）	w（Al₂O₃）	w（Fe₂O₃）	w（CaO）	w（SO₃）	w（MgO）	w（K₂O）	w（MnO）	w（P₂O₅）	w（其他）
矿渣	28.22	13.52	0.38	50.82	2.45	0.62	0.44	0.26	—	1.20
粉煤灰	54.31	27.23	6.52	5.33	2.10	1.47	0.50	—	0.86	0.57
硅灰	96.86	0.36	0.09	0.75	0.28	0.39	0.36	0.19	0.52	0.10

编号	S∶F∶SF	水玻璃模数	水玻璃掺量/%	编号	S∶F∶SF	水玻璃模数	水玻璃掺量/%	编号	S∶F∶SF	水玻璃模数	水玻璃掺量/%	编号	S∶F∶SF	水玻璃模数	水玻璃掺量/%
A1	100∶0∶0	1.0	20	C1	70∶30∶0	1.0	20	E1	90∶0∶10	1.0	20	G1	50∶0∶50	1.0	20
A2			25	C2			25	E2			25	G2			25
A3			30	C3			30	E3			30	G3			30
A4		1.2	20	C4		1.2	20	E4		1.2	20	G4		1.2	20
A5			25	C5			25	E5			25	G5			25
A6			30	C6			30	E6			30	G6			30
A7		1.4	20	C7		1.4	20	E7		1.4	20	G7		1.4	20
A8			25	C8			25	E8			25	G8			25
A9			30	C9			30	E9			30	G9			30
B1	90∶10∶0	1.0	20	D1	50∶50∶0	1.0	20	F1	70∶0∶30	1.0	20
B2			25	D2			25	F2			25
B3			30	D3			30	F3			30
B4		1.2	20	D4		1.2	20	F4		1.2	20
B5			25	D5			25	F5			25
B6			30	D6			30	F6			30
B7		1.4	20	D7		1.4	20	F7		1.4	20
B8			25	D8			25	F8			25
B9			30	D9			30	F9			30

样品	共振峰位置/Hz	归属	相对峰面积	聚合度/ %
A5-28 d	-81.82	SiQ¹（1Al）	100.00	47.79
	-85.38	SiQ²（2Al）	64.58
	-89.12	SiQ³	34.78
	-89.92	SiQ⁴	28.95
E5-28 d	-82.07	SiQ¹（1Al）	100.00	51.30
	-84.60	SiQ²（2Al）	82.87
	-88.69	SiQ³	35.85
	-91.14	SiQ⁴	28.95

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Effect of silica fume and fly ash on properties of slag-based geopolymer

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 14

References 15

Related Articles 15

Metrics

Comments

Recommended 0

[1]	ZHANG Yu. Study on effect of polycarboxylate superplasticizer grafted with graphene oxide on properties of cement mortar [J]. Inorganic Chemicals Industry, 2025, 57(9): 46-52.
[2]	QIAO Zixuan, ZHANG Runfeng, LIU Tong, FU Xinyu, YANG Hongjian. Effect of kaolin content on properties of magnesium oxy sulfate cement [J]. Inorganic Chemicals Industry, 2025, 57(5): 32-38.
[3]	LIU Xinlong, YANG Zhenyu, HAO He, LIU Shuxin, WU Chenyang, WANG Xingli, MA Qingqing. Study on shaped 4A zeolite synthesized with aluminum extraction residue by fly ash [J]. Inorganic Chemicals Industry, 2025, 57(3): 78-85.
[4]	LI Chao, WANG Liping, GAO Guimei, ZHANG Yunfeng, HONG Yu, LIU Darui, XU Lijun, CUI Yongjie. Study on reaction mechanism of acid leaching lithium from circulating fluidized bed fly ash [J]. Inorganic Chemicals Industry, 2025, 57(3): 101-107.
[5]	LI Changjiang, GUAN Xuemao, LIU Xiaoxing, ZHANG Neng, LUO Jintao. Study on early hydration and mechanism of Bayer red mud and fly ash geopolymer [J]. Inorganic Chemicals Industry, 2025, 57(11): 83-90.
[6]	ZHAO Feiyan, ZHANG Xiaodong, DU Yanxia, WANG Qiang, LI Xiaoyan. Preparation technology and research progress of fly ash ceramsite [J]. Inorganic Chemicals Industry, 2024, 56(4): 16-23.
[7]	LI Kuai, LI Zhaoshuai, DONG Tingxuan, LI Dan, GUO Shengwei, HAN Fenglan. Study on effect of wet magnetic separation on distribution of Fe and heavy metal in fly ash [J]. Inorganic Chemicals Industry, 2024, 56(4): 98-104.
[8]	LI Qiaoyun, HUANG Xiuxing, WEI Wenye, CHEN Zhen. Study on adsorption of methylene blue by activated carbon with acid/alkali synergistically modified fly ash [J]. Inorganic Chemicals Industry, 2024, 56(3): 131-136.
[9]	ZHAO Shiyong, XIAO Yuchen, MA Qingqing, YANG Zhenni, WANG Jizhen, FAN Xiaoping. Study on adsorption of Cu（Ⅱ） on 4A zeolite synthesized by aluminum extraction residue by fly ash [J]. Inorganic Chemicals Industry, 2024, 56(10): 127-134.
[10]	LI Wen, WANG Wenxiang, FANG Hongsheng, WU Pingxiao. Study on effect mechanism of silicon-aluminum additives on stabilization of heavy metals in fly ash by mechanochemical stabilization method [J]. Inorganic Chemicals Industry, 2023, 55(4): 84-91.
[11]	LI Yunfei, LIU Shuqing, TANG Shengwei, ZHANG Tao. Preparation of α-hemihydrate gypsum in Mg-Na mixed salt solution system under atmospheric pressure [J]. Inorganic Chemicals Industry, 2023, 55(11): 100-106.
[12]	DU Changqing, WANG Zhangxuan, TONG Teng, LIU Xiaofan, LIU Liang. Study on dispersion of silica fume/graphene oxide in hardened cement paste [J]. Inorganic Chemicals Industry, 2023, 55(11): 115-120.
[13]	SUN Zhigao, WU Yuan, YANG Xingchun, ZHANG Dongliang, WANG Mitang. Preparation and properties of high-magnesium nickel slag-fly ash based geopolymer [J]. Inorganic Chemicals Industry, 2023, 55(11): 139-146.
[14]	YANG Hongjun, WANG Min, GE Haiwen, QIAO Youmin, QIAO Ziyang. Study on recycling process of potassium from calcium aluminate fly ash [J]. Inorganic Chemicals Industry, 2023, 55(10): 121-127.
[15]	LI Sen, WANG Jin, WANG Yingying, CAI Mingfang. Synthesis and modification of NaA zeolite and its application in polyurethane system [J]. Inorganic Chemicals Industry, 2023, 55(10): 78-85.