BiOBr/UiO-66-（COOH）2复合材料制备及光催化性能研究

doi:10.19964/j.issn.1006-4990.2021-0138

摘要/Abstract

摘要：

为提高传统光催化材料BiOBr和UiO-66-（COOH）₂的性能和对可见光的吸收强度,以及它们的光催化活性和光催化效率,通过简单的溶剂热法制备了一种新型复合光催化剂BiOBr/UiO-66-（COOH）₂。运用X射线衍射光谱（XRD）、扫描电镜（SEM）、透射电镜（TEM）、红外光谱（FT-IR）、光致发光（PL）光谱、N₂吸附-脱附、紫外-可见漫反射光谱（UV-Vis DRS）和电化学等手段对其进行表征,并对其光催化降解甲基橙的效率进行了研究。结果表明,相对于单一的BiOBr材料,与UiO-66-（COOH）₂复合之后的BiOBr/UiO-66-（COOH）₂催化剂保留了原有材料的结构,相应的比表面积增大,对可见光的吸收强度增强。将BiOBr/UiO-66-（COOH）₂用于光催化降解甲基橙,在氙灯照射120 min后,甲基橙的降解率达到70%,分别约为纯UiO-66-（COOH）₂和BiOBr的3.68倍和1.43倍,光催化活性显著提高,光催化降解过程符合一级反应动力学规律。

关键词: 溶剂热法, 复合材料, 光催化, 染料降解

Abstract:

In order to improve the performance of BiOBr and UIO-66-（COOH）₂ photocatalytic materials and the absorption intensity of visible light,as well as their photocatalytic activity and efficiency,a new type of composite photocatalyst BiOBr/UiO-66-（COOH）₂ was prepared by simple solvothermal method.The sample was characterized by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,fourier transform infrared spectroscopy（FT-IR）,photoluminescence（PL）,N₂ absorption-desorption,UV-visual diffuse reflectance spectroscopy（UV-vis DRS） and elec-trochemistry.The photocatalytic activity of BiOBr/UiO-66-（COOH）₂ was investigated in the degradation efficiency of methyl orange.The results showed that after modifying BiOBr with UiO-66-（COOH）₂,BiOBr/UiO-66-（COOH）₂ retained the struc-ture of original materials.Moreover,with the increasing of the corresponding specific surface area,the visible light absorption of the sample increased.Under xenon lamp irradiation for 120 minutes,the degradation rate of BiOBr/UiO-66-（COOH）₂ to methyl orange was as high as 70%,which was about 3.68 times and 1.43 times of pure UiO-66-（COOH）₂ and BiOBr.The activity of the composite was significantly improved,and the photocatalytic degradation process was conformed to the law of first-order reaction kinetics.

Key words: solvothermal method, composite material, photocatalysis, dye degradation

中图分类号:

O614.53

熊芸,陈新,张静,邓妮艳,张权,刘生鹏,孙国锋. BiOBr/UiO-66-（COOH）₂复合材料制备及光催化性能研究[J]. 无机盐工业, 2021, 53(12): 150-155.

XIONG Yun,CHEN Xin,ZHANG Jing,DENG Niyan,ZHANG Quan,LIU Shengpeng,SUN Guofeng. Preparation and photocatalytic properties of BiOBr/UiO-66-（COOH）₂ composite materials[J]. Inorganic Chemicals Industry, 2021, 53(12): 150-155.

图/表 9

图1

图2

图3

图4

图5

图6

图7

图8

图9

参考文献 22

[1]	ZHAO Wanyue, DING Tong, WANG Yating, et al. Decorating Ag/ AgCl on UiO-66-NH₂:Synergy between Ag plasmons and hetero- structure for the realization of efficient visible light photocataly- sis[J]. Chinese Journal of Catalysis, 2019, 40(8):1187-1197.
[2]	LIMVORAPITUX Rungmai, CHEN Haoyuan, MENDONCA Ma- tthew, et al. Elucidating the mechanism of the UiO-66-catalyzed sulfide oxidation:activity and selectivity enhancements through ch- anges in the node coordination environment and solvent[J]. Cataly- sis Science & Technology, 2018, 9(2):327-335.
[3]	LUO Tian, ZHANG Jianling, LI Wei, et al. Metal-organic framework stabilized CO₂/water interfacial route for photocatalytic CO₂ conver- sion[J]. ACS Applied Materials & Interfaces, 2017, 9:41594-41598.
[4]	陈小浪. 新型光催化纳米材料的制备及其氧化NO和产氢性能的研究[D]. 上海:上海师范大学, 2018.
[5]	冯飞, 李书文, 汪铁林, 等. 片状铋/钒酸铋复合催化剂的制备及其光催化性能[J]. 无机盐工业, 2021, 53(1):107-112.
[6]	冯胜雷, 刘方华, 付翔, 等. TiO₂/g-C₃N₄光催化材料的制备及其可见光降解性能研究[J]. 化工新型材料, 2020, 48(11):99-102,107.
[7]	CAO Jing, XU Benyan, LUO Bangde, et al. Novel BiOI/BiOBr het- erojunction photocatalysts with enhanced visible light photocatalytic properties[J]. Catalysis Communications, 2011, 13(1):63-68.
[8]	GUO Junqiu, LIAO Xin, LEE Ming-Hsien, et al. Experimental and DFT insights of the Zn-doping effects on the visible-light photoca- talytic water splitting and dye decomposition over Zn-doped BiOBr photocatalysts[J]. Applied Catalysis B:Environmental, 2018, 243:502-512.
[9]	KONG Liang, JIANG Zheng, LAI Henry H, et al. Unusual reactivity of visible-light-responsive AgBr-BiOBr heterojunction photocataly- sts[J]. Journal of Catalysis, 2012, 293:116-125.
[10]	ZHANG Xinxin, LI Ruiping, JIA Manke, et al. Degradation of cipro- floxacin in aqueous bismuth oxybromide (BiOBr) suspensions un- der visible light irradiation:A direct hole oxidation pathway[J]. Chemical Engineering Journal, 2015, 274:290-297.
[11]	ZHANG Xi, ZHANG Lizhi, XIE Tengfeng, et al. Low-temperature synjournal and high visible-light-induced photocatalytic activity of BiOI/TiO₂ heterostructures[J]. The Journal of Physical Chemistry C, 2009, 113(17):7371-7378.
[12]	于吉行, 俞俊, 薛晓雅, 等. 金属有机骨架UiO-66在催化领域的应用[J]. 化工进展, 2019, 38(增刊1):144-151.
[13]	WANG Rong, GU Lina, ZHOU Jianjian, et al. Quasi-polymeric me- tal-organic framework UiO-66/g-C₃N₄ heterojunctions for enhan- ced photocatalytic hydrogen evolution under visible light irradia- tion[J]. Advanced Materials Interfaces, 2015, 2(10).Doi: 10.1002/admi.201500037.
[14]	YE Liqun, LIU Jinyan, JIANG Zhuo, et al. Facets coupling of BiOBr- g-C₃N₄ composite photocatalyst for enhanced visible-light-driven photocatalytic activity[J]. Applied Catalysis B:Environmental, 2013, 142-143(Complete):1-7.
[15]	CHAVAN Sachin M, SHEARER Greig C, SVELLE Stian, et al. Sy njournal and characterization of amine-functionalized mixed-ligand metal-organic frameworks of UiO-66 topology[J]. Inorganic Chemi- stry, 2014, 53(18):9509-9523.
[16]	SINGH Pardeep, SONU, RAIZADA Pankaj, et al. Enhanced photo- catalytic activity and stability of AgBr/BiOBr/graphene heterojunc- tion for phenol degradation under visible light[J]. Journal of Saudi Chemical Society, 2019, 23(5):586-599.
[17]	RAGON Florence, CAMPO Betiana, YANG Qingyuan, et al. Acic- functionalized UiO-66(Zr) MOFs and their evolution after intra- framework cross-linking:Structural features and sorption properti- es[J]. Journal of Materials Chemistry A, 2015, 3(7):3294-3309.
[18]	任勇, 潘越, 刘德蓉, 等. Rh/UiO-66-NH₂催化1,4-丁炔二醇加氢性能研究[J]. 应用化工, 2019, 48(1):136-139,144.
[19]	朱帅汝. BiOBr/MOF复合材料的制备与光催化性能的研究[D]. 宁波:宁波大学, 2018.
[20]	杨黄根, 陈渊, 王治伟, 等. 多孔柿饼状BiOBr光催化剂的简易溶剂热法合成[J]. 无机化学学报, 2020, 36(2):333-344.
[21]	ZHU Guiliang, SHENG Feng, SHAO Cong, et al. One-pot synjournal of C-dots modified TiO₂ nanosheets/UiO-66-NH₂ with improved photocatalytic activity under visible light[J]. Ceramics Internatio- nal, 2020, 46(2):2530-2537.
[22]	YAN Yuxiang, YANG Hua, YI Zao, et al. Direct Z-scheme CaTiO₃@BiOBr composite photocatalysts with enhanced photodegradation of dyes[J]. Environmental Science and Pollution Research, 2019, 26(28):29020-29031.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会

BiOBr/UiO-66-（COOH）₂复合材料制备及光催化性能研究

Preparation and photocatalytic properties of BiOBr/UiO-66-（COOH）₂ composite materials

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 9

参考文献 22

相关文章 15

Metrics

本文评价

推荐阅读 0

[1]	史王芳, 张永胜. 混凝土基非金属硼掺杂富氮氮化碳降解NO _x 性能研究[J]. 无机盐工业, 2025, 57(3): 116-123.
[2]	李子罕, 张佳琦, 李世卓, 李欣雨, 刘少卓, 王一豪, 郝玉翠, 刘剑, 李彦华. CdS/g-C₃N₄复合光催化剂的合成及催化机理研究[J]. 无机盐工业, 2025, 57(3): 124-132.
[3]	孙庆昊, 李克艳, 郭新闻. Pd/ZnIn₂S₄纳米片光催化苯甲醇氧化耦合产氢的研究[J]. 无机盐工业, 2025, 57(1): 113-119.
[4]	刘光明. C₃N₅/NH₂-MIL-125（Ti）改性混凝土砂浆光催化和力学性能研究[J]. 无机盐工业, 2025, 57(1): 120-128.
[5]	张飞刚, 刘中利. CuO/g-C₃N₄复合材料在有机染料降解和超级电容器中的应用研究[J]. 无机盐工业, 2025, 57(1): 129-136.
[6]	石萌轲, 范赵亚, 岳峰, 张硕, 孟阳, 张宏忠. 空气中CO₂电辅助式光催化高选择性转化的研究[J]. 无机盐工业, 2024, 56(9): 154-163.
[7]	孙延龙, 袁广胜, 王红军. 基于钯修饰的介孔TiO₂纳米棒高效光降解四环素的研究[J]. 无机盐工业, 2024, 56(9): 147-153.
[8]	张国强, 戎西林, 肖振芳, 薛自然, 程昊, 冯军, 刘泉, 陆瑶, 黄文艺. 甘蔗渣碳气凝胶负载纳米氧化锌的制备及其光催化性能研究[J]. 无机盐工业, 2024, 56(8): 131-138.
[9]	李曌, 尹优优, 刘晨辉, 王访, 高冀芸. 二维碳化钛/氧化锌纳米颗粒的制备及其乙醇气敏性能研究[J]. 无机盐工业, 2024, 56(8): 33-39.
[10]	王雅雯, 王芳芳, 耿司宇, 鞠佳, 陈雷, 陈常东. SrTiO₃-SrWO₄的制备及其光催化性能研究[J]. 无机盐工业, 2024, 56(7): 143-149.
[11]	刘敏, 黄秀, 张理元. S型异质结光催化剂的研究进展[J]. 无机盐工业, 2024, 56(7): 18-27.
[12]	李江朋, 张慧斌. 三维多孔LaFeO₃/CeO₂/SrTiO₃光芬顿和光催化协同脱色亚甲基蓝[J]. 无机盐工业, 2024, 56(5): 141-148.
[13]	唐贝. ZnO/g-C₃N₄异质结光催化材料的制备及对吡啶的降解[J]. 无机盐工业, 2024, 56(4): 133-142.
[14]	周旋, 李梦锐, 陈一尘, 樊辉强, 王宾, 袁刚. 镍基磷化物复合材料在催化电解水析氢性能提升方面的研究进展[J]. 无机盐工业, 2024, 56(4): 8-15.
[15]	黄佳楠, 陆啸宇, 王觅堂. 钡镧共掺杂对TaON降解亚甲基蓝染料的影响[J]. 无机盐工业, 2024, 56(2): 146-151.

首 页