氢氧化镁与七水硫酸镁水热法合成碱式硫酸镁晶须

doi:10.19964/j.issn.1006-4990.2023-0047

Abstract

Abstract:

To obtain the high-quality basic magnesium sulfate whiskers，magnesium hydroxide and magnesium sulfate heptahydrate were used to prepare basic magnesium sulfate whiskers with the hydrothermal method.The influences of hydrothermal parameters on whisker morphology were investigated，which included the molar ratio of magnesium sulfate heptahydrate to magnesium hydroxide，hydrothermal time，stirring speed，addition amount of magnesium sulfate heptahydrate，and hydrothermal temperature.The whisker products were characterized by the various instruments of X-ray diffractometry（XRD），scanning electron microscopy（SEM），transmission electron microscopy（TEM），selected area electron diffraction（SAED），and Fourier-transform infrared spectrum（FT-IR）.The results showed that the optimized process parameters were as following：the molar ratio of magnesium sulfate heptahydrate to magnesium hydroxide was 3∶1，hydrothermal time was 2 h，stirring speed was 400 r/min，addition amount of magnesium sulfate heptahydrate was 4.93 g，hydrothermal temperature was 180 ℃ and the reaction medium of water was 80 mL.The products synthesized at the optimized conditions were mainly fibrous whiskers.The aspect ratio of fibrous whisker was more than 160 with the diameter of 300~500 nm and the length of 80~100 µm.Therefore，the optimization of the process parameters could effectively improve the dispersion and aspect ratio of basic magnesium sulfate whiskers.

Key words: basic magnesium sulfate whisker, hydrothermal method, morphology, magnesium hydroxide, magnesium sulfate heptahydrate

CLC Number:

TQ132.2

JIANG Demin, LI Shunmei, Li Qingqing, Chen Yuxin, LIU Daijun. Hydrothermal synthesis of basic magnesium sulfate whiskers from magnesium hydroxide and magnesium sulfate heptahydrate[J]. Inorganic Chemicals Industry, 2023, 55(12): 74-81.

Figures/Tables 10

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

References 36

1	NAKAMURA Y， OKITA K， KUDO D， et al. Magnesium hydroxide nanoparticles kill exponentially growing and persister escherichia coli cells by causing physical damage［J］. Nanomaterials， 2021， 11（6）：1584. doi: 10.3390/nano11061584
2	JIANG Demin， YANG Yuhan， HUANG Chentao， et al. Removal of the heavy metal ion nickel（Ⅱ） via an adsorption method using flower globular magnesium hydroxide［J］. Journal of Hazardous Materials， 2019， 373：131-140. doi: S0304-3894(19)30103-7 pmid: 30909138
3	WETTELAND C L， DE JESUS SANCHEZ J， SILKEN C A， et al. Dissociation of magnesium oxide and magnesium hydroxide nano-particles in physiologically relevant fluids［J］. Journal of Nanoparticle Research， 2018， 20（8）：215. doi: 10.1007/s11051-018-4314-3
4	JIANG Demin， WANG Fang， LAN Bo， et al. Efficient treatment of anthraquinone dye wastewater by adsorption using sunflower torus-like magnesium hydroxide microspheres［J］. Korean Journal of Chemical Engineering， 2020， 37（3）：434-447. doi: 10.1007/s11814-019-0455-z
5	YUAN Qinghua， YANG Wei， MA Zhuwen， et al. Tobacco stalk flour/magnesium oxysulfate whiskers reinforced hybrid composites of recycled polypropylene：Mechanical and thermal and antibacterial properties［J］. Polymers， 2022， 14（4）：815. doi: 10.3390/polym14040815
6	ZOU Sai， DANG Li， LI Yawei， et al. Inorganic-organic dual modification of magnesium borate whisker by magnesium hydrate and dodecyl dihydrogen phosphate and its effect on the fire safety and mechanical properties of epoxy resin［J］. Applied Surface Science， 2022， 589：153064. doi: 10.1016/j.apsusc.2022.153064
7	LI Na， LI Zhi， LIU Zhiqi， et al. Magnesium hydroxide micro-whiskers as super-reinforcer to improve fire retardancy and mechanical property of epoxy resin［J］. Polymer Composites， 2022， 43（4）：1996-2009. doi: 10.1002/pc.v43.4
8	CHEN Xi， QIU Tian. Natural rubber composites reinforced with basic magnesium oxysulfate whiskers：Processing and ultraviolet resistance/flame retardant properties［J］. Polymer Testing， 2020， 81：106271. doi: 10.1016/j.polymertesting.2019.106271
9	ZHOU Xiaochen， ZHANG Yao， JIANG Guodong. Surface modification of magnesium oxysulfate whisker based on SiO₂@silane coupling agent and SiO₂@polydopamine double-layer structure for reinforcing HDPE［J］. Materials， 2022， 15（9）：3272. doi: 10.3390/ma15093272
10	ZOU Sai， LAN Shengjie， DANG Li， et al. Controllable fabrication of a hybrid containing dodecyl dihydrogen phosphate modified magnesium borate whisker/hydrated alumina for enhancing the fire safety and mechanical properties of epoxy resin［J］. RSC Advances， 2022， 12（12）：7422-7432. doi: 10.1039/d1ra08289b pmid: 35424671
11	ZHAO Xueni， YANG Jianjun， XIN Hua， et al. Improved dispersion of SiC whisker in nano hydroxyapatite and effect of atmospheres on sintering of the SiC whisker reinforced nano hydroxyapatite composites［J］. Materials Science and Engineering：C， 2018， 91：135-145.
12	YANG Yuanyi， DENG Yi. Mechanical properties of hybrid short fibers reinforced oil well cement by polyester fiber and calcium carbonate whisker［J］. Construction and Building Materials， 2018， 182：258-272. doi: 10.1016/j.conbuildmat.2018.06.110
13	JAGTAP P， SETHURAMAN V A， KUMAR P. Critical evaluation of relative importance of stress and stress gradient in whisker growth in Sn coatings［J］. Journal of Electronic Materials， 2018， 47（9）：5229-5242. doi: 10.1007/s11664-018-6391-6
14	LI Guanghui， FANG Li， ZHANG Xin， et al. Utilization of the MgO-rich residue originated from ludwigite ore：Hydrothermal synthesis of MHSH whiskers［J］. Minerals， 2017， 7（8）：138. doi: 10.3390/min7080138
15	ZHOU Zhengzhi， SUN Qunhui， HU Zeshan， et al. Nanobelt formation of magnesium hydroxide sulfate hydrate via a soft chemistry process［J］. The Journal of Physical Chemistry B， 2006， 110（27）：13387-13392. doi: 10.1021/jp0612228
16	YU Ri， PEE J H， KIM H T， et al. Effect of MgSO₄/MgO on the synthesis of 5Mg（OH）₂·MgSO₄·3H₂O whiskers using one-step ambient pressure［J］. Journal of the Korean Ceramic Society， 2013， 50（3）：201-205. doi: 10.4191/kcers.2013.50.3.201
17	GAO Chuanhui， LI Xianguo， FENG Lijuan， et al. Preparation and thermal decomposition of 5Mg（OH）₂·MgSO₄·2H₂O nanowhiskers［J］. Chemical Engineering Journal， 2009， 150（2/3）：551- 554. doi: 10.1016/j.cej.2008.12.029
18	蒙红平，王会强，罗艳. 碱式硫酸镁晶须增强阻燃聚氯乙烯性能研究［J］. 塑料科技， 2020， 48（12）：41-44.
	MENG Hongping， WANG Huiqiang， LUO Yan. Study on properties of flame retardant PVC reinforced by basic magnesium sulfate whisker［J］. Plastics Science and Technology， 2020， 48（12）：41-44.
19	GONG Juan， GUO Weihong， WANG Kai， et al. Surface modification of magnesium hydroxide sulfate hydrate whiskers and its toughness and reinforcement for polyvinyl chloride［J］. Polymer Composites， 2018， 39（10）：3676-3685. doi: 10.1002/pc.v39.10
20	朱云鹏，李庆华，沈芳，等. 石墨烯/碱式硫酸镁晶须/PVC复合材料的制备及性能表征［J］. 塑料科技， 2020， 48（3）：7-12.
	ZHU Yunpeng， LI Qinghua， SHEN Fang， et al. Preparation and property characterization of graphene/basic magnesium sulfate whisker/PVC composites［J］. Plastics Science and Technology， 2020， 48（3）：7-12.
21	刘艳丽，杨玮婧，李磊，等. 碱式硫酸镁晶须的改性及在改善聚丙烯复合材料阻燃性能上的应用［J］. 化学工程师， 2022， 36（9）：85-88.
	LIU Yanli， YANG Weijing， LI Lei， et al. Modification of basic magnesium sulfate whiskers and its application in improving the flame retardant properties of polypropylene composites［J］. Che-Engineer mical， 2022， 36（9）：85-88.
22	DANG Li， NAI Xueying， DONG Yaping， et al. Functional group effect on flame retardancy，thermal，and mechanical properties of organophosphorus-based magnesium oxysulfate whiskers as a flame retardant in polypropylene［J］. RSC Advances， 2017， 7（35）：21655-21665. doi: 10.1039/C7RA02863F
23	TANG Zhilei， ZHU Chaoliang， FAN Faying， et al. Green synthesis of the excellent magnesium oxysulfate whiskers under controlled reaction conditions［J］. Materials Chemistry and Physics， 2017， 195：143-148. doi: 10.1016/j.matchemphys.2017.04.014
24	党力，乃学瑛，董亚萍，等. 微波法快速制备碱式硫酸镁晶须［J］. 人工晶体学报， 2016， 45（1）：21-27，34.
	DANG Li， NAI Xueying， DONG Yaping， et al. Rapid synthesis of magnesium oxysulfate whisker by microwave method［J］. Journal of Synthetic Crystals， 2016， 45（1）：21-27，34.
25	吴健松，肖应凯，梁海群，等. 丁醇-变频微波-水热法制备优质碱式硫酸镁晶须及表征［J］. 人工晶体学报， 2009， 38（1）：285-289.
	WU Jiansong， XIAO Yingkai， LIANG Haiqun， et al. Butanol-frequency microwave-hydrothermal synthesis and characterization of high-quality hydrous magnesium oxysulfate whiskers［J］. Journal of Synthetic Crystals， 2009， 38（1）：285-289.
26	MA Xinlong， NING Guoqing， QI Chuanlei， et al. One-step synthesis of basic magnesium sulfate whiskers by atmospheric pressure reflux［J］. Particuology， 2016， 24：191-196. doi: 10.1016/j.partic.2015.03.004
27	ZHU Donghai， NAI Xueying， LAN Shengjie， et al. Surface modification of magnesium hydroxide sulfate hydrate whiskers using a silane coupling agent by dry process［J］. Applied Surface Science， 2016， 390：25-30. doi: 10.1016/j.apsusc.2016.08.033
28	ZHAO Wenpeng， GAO Chuanhui， WANG Ting， et al. Effect of alcohols additives on hydrothermal formation of magnesium hydroxide sulfate hydrate whiskers［J］. Crystal Research and Technology， 2015， 50（8）：676-681. doi: 10.1002/crat.v50.8
29	NING Xinkuang， WU Chengyou， CHEN Hongdu. Preparation and characterization of novel 5Mg（OH）₂·MgSO₄·7H₂O whiskers［J］. Materials， 2022， 15（22）：8018. doi: 10.3390/ma15228018
30	HUANG Meiying， JIANG Demin. Hydrothermal Preparation of Magnesium Oxysulfate Whiskers ［J］. 2021， 48（4）：1089-1100.
31	薛建荣，钟宏，高俊，等. 水热法合成碱式硫酸镁晶须［J］. 无机盐工业， 2011， 43（5）：30-32.
	XUE Jianrong， ZHONG Hong， GAO Jun， et al. Hydrothermal-controlled synthesis of basic magnesium sulfate whiskers［J］. Inorganic Chemicals Industry， 2011， 43（5）：30-32.
32	YUE Tao， GAO Shiyang， ZHU Lixia， et al. Crystal growth and crystal structure of magnesium oxysulfate 2MgSO₄·Mg（OH）₂·2H₂O［J］. Journal of Molecular Structure， 2002， 616（1/2/3）：247-252. doi: 10.1016/S0022-2860(02)00347-2
33	白丽梅，孙志雅，祝洪武，等. 无水硫酸镁对氧化镁水热产物的影响［J］. 硅酸盐通报， 2017， 36（11）：3595-3600.
	BAI Limei， SUN Zhiya， ZHU Hongwu， et al. Effects of anhydrous magnesium sulfate on magnesium oxide hydrothermal products［J］. Bulletin of the Chinese Ceramic Society， 2017， 36（11）：3595-3600.
34	YAN Xiaoxing， XU Dongli， XUE Dongfeng. SO₄ ^2- ions direct the one-dimensional growth of 5Mg（OH）₂·MgSO₄·2H₂O［J］. Acta Materialia， 2007， 55（17）：5747-5757. doi: 10.1016/j.actamat.2007.06.023
35	JIANG Demin， YU Qinghang， HUANG Chengtao， et al. Preparation of mesoporous spherical magnesium hydroxide particles via the static self-assembled method［J］. Journal of Molecular Structure， 2019， 1175：858-864. doi: 10.1016/j.molstruc.2018.08.058
36	韩跃新，李丽匣，印万忠，等. 碱式硫酸镁晶须的表面改性［J］. 东北大学学报（自然科学版）， 2009， 30（1）：133-136.
	HAN Yuexin， LI Lixia， YIN Wanzhong， et al. On the surface modification of basic magnesium sulfate whiskers［J］. Journal of Northeastern University（Natural Science）， 2009， 30（1）：133-136.

[1]	CHEN Zhangxu, FU Minglian, ZHU Danchen, ZHENG Bingyun. Preparation of carbon/graphite carbon nitride composites and their methylene blue removal performance [J]. Inorganic Chemicals Industry, 2023, 55(3): 134-139.
[2]	XIONG Shuang, YAN Jinsheng, ZHOU Zhou, ZHOU Baodi, CHEN Xiaopeng, TONG Zhangfa. Effect of reaction conditions of quicklime digestion on properties of calcium hydroxide [J]. Inorganic Chemicals Industry, 2023, 55(12): 50-58.
[3]	LI Yunfei, LIU Shuqing, TANG Shengwei, ZHANG Tao. Preparation of α-hemihydrate gypsum in Mg-Na mixed salt solution system under atmospheric pressure [J]. Inorganic Chemicals Industry, 2023, 55(11): 100-106.
[4]	LU Yang,WANG Jing,HE Lijie,WANG Fudong,ZHANG Jiaming. Research progress on preparation of magnesium aluminate spinel powders and it in field of luminescent material [J]. Inorganic Chemicals Industry, 2022, 54(9): 39-46.
[5]	PANG Hongchang,WANG Zhiyu,TIAN Peng,NING Guiling. Study on synthesis and properties of two component magnesium based flame retardant by“one?pot method” [J]. Inorganic Chemicals Industry, 2022, 54(8): 54-58.
[6]	JIANG Tiantian,XU Xuetang,WANG Fan. Research on growth and supercapacitance of NiCo based electrode materials regulated by halogen ions [J]. Inorganic Chemicals Industry, 2022, 54(8): 66-73.
[7]	CHANG Chenggong,WEN Jing,DONG Jinmei,ZHENG Weixin,YAN Fengyun,XIAO Xueying. Effect of carbonization on evolution process of microstructure of magnesium oxychloride cement [J]. Inorganic Chemicals Industry, 2022, 54(6): 61-65.
[8]	XI Yuping,LUO Zhihuan. Effect of hydride carrier LaMg₂Ni on hydrogen storage properties of Mg₂Ni alloy for automobile [J]. Inorganic Chemicals Industry, 2022, 54(5): 61-66.
[9]	LI Xiao,ZHAO Yuxiang,LI Bo,ZOU Xingwu,WANG Shuxuan. Study on controllable synthesis of spherical strontium fluoride [J]. Inorganic Chemicals Industry, 2022, 54(5): 67-71.
[10]	LU Zheng,CHEN Kunfeng,XUE Dongfeng. Study on large-scale preparation and electrochemical properties of high thermal stabilized α-Fe₂O₃ [J]. Inorganic Chemicals Industry, 2022, 54(3): 45-50.
[11]	PEI Yinchang,MO Shengpeng,XIE Qinglin,CHEN Nanchun. Study on mechanism of zeolite A synthesized from stellerite zeolite by two-step hydrothermal method [J]. Inorganic Chemicals Industry, 2022, 54(11): 59-64.
[12]	QI Yuanhao,WU Jinxiu,LIU Zhaogang,HU Yanhong,FENG Fushan,LI Jianfei,WANG Xin,LIU Conglin. Preparation and characterization of anhydrous calcium sulfate whisker [J]. Inorganic Chemicals Industry, 2022, 54(10): 109-115.
[13]	FAN Tianbo,HU Tingting,HAN Dongxue,JIA Xiaohui,ZHAO Yibo,WANG Xin′an,GUO Hongfan,LI Li,LIU Yunyi. Preparation of micro-nano round flake magnesium hydroxide from calcined dolomite powder [J]. Inorganic Chemicals Industry, 2022, 54(1): 29-33.
[14]	KONG Huimin,ZOU Laixi,LIU Yuan,CAO Yuwei,LIN Yanjun,LUO Xianping. Study on preparation of hexagonal plates of magnesium hydroxide by light-burned magnesium oxide [J]. Inorganic Chemicals Industry, 2022, 54(1): 39-44.
[15]	LI Zheng,HU Meng,DOU Yan,CUI Peng,SHEN Hao,ZHENG Zhiyin,LIU Rong. Effect of sodium oxalate on stability of calcium sulfate hemihydrate crystal [J]. Inorganic Chemicals Industry, 2022, 54(1): 62-65.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Hydrothermal synthesis of basic magnesium sulfate whiskers from magnesium hydroxide and magnesium sulfate heptahydrate

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 10

References 36

Related Articles 15

Metrics

Comments

Recommended 0