无机盐工业 ›› 2016, Vol. 48 ›› Issue (9): 61-.

传统加热酸溶性钛渣实验研究

刘钱钱1，廖雪峰1，陈菓1，2，陈沪飞1，张利波1，彭金辉1，2

1.微波能工程应用及装备技术国家地方联合工程实验室，非常规冶金省部共建教育部重点实验室，昆明
理工大学冶金与能源工程学院，云南昆明 650093；2.云南省高校民族地区资源清洁转化重点实验室，
云南省跨境民族地区生物质资源清洁利用国际联合研究中心，云南民族大学

出版日期:2016-09-10 发布日期:2016-09-18

Experimental study on acid soluble titanium slag by traditional heating

Liu Qianqian1，Liao Xuefeng1，Chen Guo1，2，Chen Hufei1，Zhang Libo1，Peng Jinhui1，2

1.National Local Joint Engineering Laboratory of Engineering Applications of Microwave Energy and Equipment Technology，
Key Laboratory of Unconventional Metallurgy，Ministry of Education，School of Metallurgy and Energy Engineering，Kunming
University of Science and Technology，Kunming 650093，China；2.Key Laboratory of Resource Clean Conversion in Ethnic
Regions，Education Department of Yunnan，Joint Research Centre for International Cross-border Ethnic Regions Biomass
Clean Utilization in Yunnan，Yunnan Minzu University

Online:2016-09-10 Published:2016-09-18

摘要/Abstract

摘要： 以酸溶性钛渣为原料，对其进行传统加热氧化焙烧实验研究。考察了焙烧温度及保温时间对样品中二氧化钛、硫、碳含量的影响。结果表明：随着焙烧温度升高，氧化焙烧过程中低价钛、铁以及氧化亚铁的氧化使物料总量增加，而钛总量不变，导致焙烧后物料中二氧化钛含量随着焙烧温度的升高而降低；随着保温时间增加，各成分的氧化反应进行得更彻底，物料中二氧化钛的含量不断降低；随着焙烧温度的升高及保温时间的增加，碳与硫的脱除效果明显，其含量不断降低。

关键词: 酸溶性钛渣, 传统加热, 氧化焙烧, 二氧化钛

Abstract: The traditional heating oxidation roasting experiment research with acid soluble titanium slag as the raw material was carried out.The influences of different roasting temperature and holding time on the contents of titanium dioxide，carbon， and sulfur in the samples were investigated.The results indicated that: with the increase of roasting temperature，because the low valence titanium，Fe，and FeO took place oxidation reactions，and made the total amount of sample increase but the over- all titanium content did not change，so the content of TiO2 decreased；with the increase of holding time，the content of TiO2 decreased continuously because the reactions of each component became more thoroughly；investigated the influences of different roasting temperatures and holding times on carbon and sulfur contents in the samples，the results showed that with the increase of temperature and holding time，carbon and sulfur removal effect was obvious，and the contents decreased with temperature and time increase.

Key words: acid soluble titanium slag, traditional heating, oxidation roasting, titanium oxide

中图分类号:

TQ134.11

刘钱钱, 廖雪峰, 陈菓, 陈沪飞, 张利波, 彭金辉. 传统加热酸溶性钛渣实验研究[J]. 无机盐工业, 2016, 48(9): 61-.

LIU Qian-Qian, LIAO Xue-Feng, CHEN Guo, CHEN Hu-Fei, ZHANG Li-Bo, PENG Jin-Hui. Experimental study on acid soluble titanium slag by traditional heating[J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(9): 61-.

[1]	张树立,徐旭鹏,陈书锐,刘黔蜀,王本菊. 钒掺杂二氧化钛光催化活性研究[J]. 无机盐工业, 2020, 52(8): 93-97.
[2]	赵扬,贺素姣,何璐红. 柔性钙钛矿太阳能电池的制备及性能研究[J]. 无机盐工业, 2020, 52(7): 52-54.
[3]	庆朋辉,董玉明,王兴润,朱开生,牛仁杰,孟静娟,陈小红,陈辉霞,张红玲,徐红彬. 铬铁矿无钙焙烧铬渣的深度提铬与无害化处理[J]. 无机盐工业, 2020, 52(6): 63-67.
[4]	龚家竹,陆祥芳,吴宁兰,邵国雄. 自拟合纳米二氧化钛催化污水处理剂的研究与开发[J]. 无机盐工业, 2020, 52(5): 59-64.
[5]	朱佳新,熊裕华,郭锐. 二氧化钛光催化剂改性研究进展[J]. 无机盐工业, 2020, 52(3): 23-27.
[6]	王子楠,陈葵,朱家文,张玉荣,林发蓉,周晓葵. 晶种和盐处理剂对煅烧过程中二氧化钛晶型转变的影响[J]. 无机盐工业, 2020, 52(3): 45-50.
[7]	陈雯,龙翔,李海艳,杨辉,贾贵发,金娅秋. 激光粒度仪测定气相氧化法二氧化钛粒径的研究[J]. 无机盐工业, 2020, 52(2): 69-71.
[8]	胡敏,郭嘉,吴华东,张林锋. N-Zn/TiO₂光催化氧化脱硫废液中亚硫酸钠的研究[J]. 无机盐工业, 2020, 52(10): 151-156.
[9]	徐元盛,李建伟,马炎,李国旺,张茂亮,单雪强. 硫化镉-二氧化钛/分子筛复合光催化材料制备及性能研究[J]. 无机盐工业, 2019, 51(6): 83-87.
[10]	高雅男. 二氧化钛-钒酸铋复合材料光催化降解布洛芬的研究[J]. 无机盐工业, 2019, 51(6): 88-91.
[11]	鲁杰,吴华东,马尚,张林锋,严才成,郭嘉. 镍系催化剂的制备、表征及其甲烷化性能的研究[J]. 无机盐工业, 2019, 51(5): 78-81.
[12]	王硕,白丽明. 钇沉积的二氧化钛-SBA-15纳米催化剂制备及其应用[J]. 无机盐工业, 2019, 51(3): 77-81.
[13]	庆朋辉1，2，3，张红玲1，2，石义朗4，蔡再华4，梅海军5，徐红彬1，2. 添加剂对铬铁矿氧化焙烧过程的影响[J]. 无机盐工业, 2019, 51(12): 26-29.
[14]	路瑞芳，吴健春，刘婵. 钛液水解工艺对金红石二氧化钛消色力的影响[J]. 无机盐工业, 2019, 51(12): 44-48.
[15]	张洪光1，王国薇2，孙革1，许凤1，李红梅1，李爽1，付双1. 二氧化钛发光与光催化性能关系的研究[J]. 无机盐工业, 2019, 51(12): 94-96.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会

传统加热酸溶性钛渣实验研究

Experimental study on acid soluble titanium slag by traditional heating

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10

首 页

传统加热酸溶性钛渣实验研究

Experimental study on acid soluble titanium slag by traditional heating

可视化

引用本文

使用本文

首页