自拟合纳米二氧化钛催化污水处理剂的研究与开发

doi:10.11962/1006-4990.2019-0047

摘要/Abstract

摘要：

利用硫酸法钛白粉副产稀硫酸与钛原料生产硫酸钛溶液,再与碱性印染污水中和,自拟合生成超细纳米二氧化钛颗粒,催化氧化分解污水中的有机物,减少现有芬顿法过氧化氢的用量70%。采用紫外光催化氧化,全部替代过氧化氢的用量,污水中的化学需氧量（COD）去除率提高14.5%,达到94.5%。开发了钛白粉生产废硫酸作为印染污水处理的经济方法,耦合了2个相关行业“冗余”的化学资源和化学能源,做到了低成本、经济的纳米二氧化钛催化剂的生产合成,降低了印染污水处理的生产费用,效果显著。

关键词: 高级氧化, 催化分解, 污水处理, 二氧化钛

Abstract:

The by-prodnct dilute sulfuric from the production of TiO₂ by sulfuric acid was used to prepare Ti（SO₄）₂ solution reacted with titanian as raw material.The titanium sulfate solution was neutralized with alkaline printing and dyeing wastewater.Then the ultrafine nano-sized TiO₂ powders was self-fitted and obtained.The TiO₂ powders were used to catalyze,oxidize and decompose the organic material in sewage,and reduced the amount of hydrogen peroxide in the existing Fenton method by 70%.Using UV-photocatalytic oxidation,the amount of hydrogen peroxide was all replaced,the COD removal rate in sewage increased by 14.5% and reached 94.5%.The economical method of production of waste sulphuric acid from titanium dioxide for the treatment of printing and dyeing wastewater was developed,which was coupled with the redundant chemical resources and chemical energy of two related industries.Thus the goal of economicproduction of nano-sized titanium dioxide catalyst was achieved,the production cost of printing and dyeing wastewater treatment was reduced,and the effect was remarkable.

Key words: super oxidation, catalytic decomposition, sewage treatment, titanium dioxide

中图分类号:

TQ134.11

龚家竹,陆祥芳,吴宁兰,邵国雄. 自拟合纳米二氧化钛催化污水处理剂的研究与开发[J]. 无机盐工业, 2020, 52(5): 59-64.

Gong Jiazhu,Lu Xiangfang,Wu Ninglan,Shao Guoxiong. Research and development of self-fitting nano-sized titanium dioxide catalytic wastewater treatment agent[J]. Inorganic Chemicals Industry, 2020, 52(5): 59-64.

图/表 18

表1

表2

表3

表4

表5

表6

图1

图2

图3

图4

表7

图5

图6

图7

图8

图9

图10

图11

参考文献 15

[1]	龚家竹 . 钛白粉生产工艺技术进展[J]. 无机盐工业, 2012,44(8):1-4.
[2]	龚家竹 . 硫酸法钛白粉酸解工艺技术的回顾与展望[J]. 无机盐工业, 2014,46(7):1-7,42.
[3]	龚家竹 . 硫酸法钛白生产废硫酸循环利用技术回顾与展望[J]. 硫酸工业, 2016, No.1:67-72.
[4]	龚家竹, 于奇志 . 纳米二氧化钛的现状与发展[J]. 无机盐工业, 2006,38(7):8-10.
[5]	龚家竹, 李欣 . 硫酸法钛白粉生产技术面临循环经济促进法存在的问题与解决办法[J]. 无机盐工业, 2009,41(8):15-17.
[6]	Kranthi Kumar Akurati . Synbook of TiO₂ based nanoparticles for photocatalytic applications[M]. Duisburg-Essen:Cuvillier Verlag Göttingen, 2008.
[7]	李大成, 周大利, 刘恒 , 等. 纳米TiO₂的特性[J]. 四川有色金属, 2002(3):45-47.
[8]	任成军, 李大成, 钟本和 , 等. 影响TiO₂光催化活性的因素及提高其活性的措施[J]. 四川有色金属, 2004(4):36-39.
[9]	任成军, 钟本和, 周大利 , 等. 水热法制备高活性TiO₂光催化剂的研究进展[J]. 四川有色金属, 2004(5):42-44.
[10]	Duyvesteyn W, Sabacky B, Verhulst D , et al. Process aqueous titanium chloride solution to ultrafine titanium dioxide：US,6440383[P]. 2002-08-27.
[11]	Meng X G, Dadachov M, George P . Korfiutis.methods of preparing surface activeted titanium oxide product and of using same in water treatment processes：US,6919029[P]. 2005-05-19.
[12]	Bygott C, Ries M and Kinniard S P . Photocatalytic rutil titanium dioxide：US,7521039[P]. 2009-08-21.
[13]	Ralf-Johan Lamminmaki, Esa Latva-Nirva and Riitta Linho . Methods of preparing well dispersable macrocrystalline titanium oxide product,the producte,and the use thereof：US,8182602[P]. 2012-05-22.
[14]	龚家竹 . 一种自拟合纳米催化污水处理剂的生产方法:中国,201910060630.3[P]. 2019-01-23.
[15]	GONG Jiazhu . Production method of self fitting nano catalytic wastewater treatment agent:US,16278728[P]. 2019-02-19.

废水类型	pH	COD/ （mg·L^-1）	BOD₅/ （mg·L^-1）	ρ（SS）/ （mg·L^-1）	ρ（NH₃-N）/ （mg·L^-1）	色度/ 倍
退煮漂废水	10~13	1 900	800	200	—	—
染色废水	8~10	500	300	250	10	500
丝光废水	10~13	800	300	200	—	—
印花废水	8~10	1 000	400	250	10	400
设备冲洗废水	8~10	1 000	200	300	—	—
后整理废水	8~10	300	150	150	—	—
混合水废水	9~11	1 200	500	240	45	200

洗水检测/ mL	w（Fe）（TiO₂干基）/10^-6	w（Fe）（TiO₂干基）/10^-6	打浆浓度/ （g·L^-1）	密度/ （g·cm^-3）
≤10	≤30	≤80	350	1.64
0.1 mol/L高锰酸钾溶液	以单质铁计（金红石）	以单质铁计（锐钛型）	以TiO₂计

编号	主要组成/%			密度/ （g·cm^-3）
编号	w（H₂SO₄）	w（FeSO₄）	w[Ti（SO₄）₂]	密度/ （g·cm^-3）
1	20.75	9.08	1.08	1.260
2	20.07	9.46	1.51	1.265

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会