铂金镍纳米合金的制备研究进展

doi:10.19964/j.issn.1006-4990.2022-0464

摘要/Abstract

摘要：

铂基催化材料在燃料电池阳极催化剂和脱氢反应领域具有较大的应用前景，目前的纯铂和二元铂基催化剂并不能满足电催化领域的需求，新的三元铂基催化材料不断涌现。其中Pt-Au-Ni纳米合金催化剂在降低贵金属含量，增强催化活性，消除铂催化剂易中毒等方面具有较大的潜力。综述了近年来Pt-Au-Ni合金纳米材料的制备方法，包括液相合成法、种子生长法、化学蚀刻法等制备方法，对现有的制备方法进行了总结。在酸性环境下，合金催化剂容易出现Ni的溶解，降低催化剂的活性，甚至造成催化剂的失效，因此提出了金属间化合物催化剂可能是解决方法，为Pt-Au-Ni纳米合金的研究提供思路。

关键词: Pt-Au-Ni合金, 贵金属合金, 纳米粒子, 催化剂

Abstract:

Platinum-based catalytic materials have excellent applications in fuel cell anode catalysts and dehydrogenation reactions.The current pure platinum and binary platinum-based catalysts cannot meet the needs of the electrocatalytic field，and new ternary platinum-based catalytic materials are constantly emerging.Among them，Pt-Au-Ni nanoalloy catalysts have great potential in reducing the content of precious metals，enhancing catalytic activity，and eliminating the poisoning of platinum catalysts.The preparation methods of Pt-Au-Ni alloy nanoparticles in recent years were reviewed，including the lliquid phase synthesis，seed growth，chemical etching，etc.The existing preparation methods were summarized.In acidic environments，the alloy catalysts were prone to Ni dissolution，which could reduce the catalyst activity and even cause catalyst failure.Therefore，intermetallic compound catalysts had been proposed as a possible solution，providing ideas for the research of Pt-Au-Ni nanoalloys.

Key words: Pt-Au-Ni alloy, precious metal alloys, nanoparticle, catalyst

中图分类号:

TQ138.26

马超, 胡洁琼, 谢明, 陈永泰, 张巧, 陈松, 方继恒, 邱乐祺. 铂金镍纳米合金的制备研究进展[J]. 无机盐工业, 2023, 55(9): 26-32.

MA Chao, HU Jieqiong, XIE Ming, CHEN Yongtai, ZHANG Qiao, CHEN Song, FANG Jiheng, QIU Leqi. Research progress of preparation of Pt-Au-Ni nanoalloys[J]. Inorganic Chemicals Industry, 2023, 55(9): 26-32.

图/表 4

参考文献 52

1	骆明川，孙英俊，秦英楠，等.维度调控策略提升铂基纳米晶氧还原催化研究进展（英文）［J］.物理化学学报，2018，34（4）：361-376.
	LUO Mingchuan， SUN Yingjun， QIN Yingnan，et al.Boosting oxygen reduction catalysis by tuning the dimensionality of Pt-based nanostructures［J］.Acta Physico-Chimica Sinica，2018，34（4）：361-376.
2	YI Qingfeng， LI Lei， YU Wenqiang，et al.Hydrothermal synthesis of titanium-supported PtIrRu/Ti electrode and its electrocatalytic activity［J］.Journal of Alloys and Compounds，2008，466（1/2）：52-58.
3	FENG Jiuju， HE Lili， FANG Rui，et al.Bimetallic PtAu superlattice arrays：Highly electroactive and durable catalyst for oxygen reduction and methanol oxidation reactions［J］.Journal of Power Sources，2016，330：140-148.
4	WANG Xiaoxia， SOKOLOWSKI J， LIU Hui，et al.Pt alloy oxygen-reduction electrocatalysts：Synthesis，structure，and property［J］.Chinese Journal of Catalysis，2020，41（5）：739-755.
5	MARTIN S， JENSEN J O， LI Q，et al.Feasibility of ultra-low Pt loading electrodes for high temperature proton exchange membrane fuel cells based in phosphoric acid-doped membrane［J］.International Journal of Hydrogen Energy，2019，44（52）：28273-28282.
6	ASAL Y M， AL-AKRAA I M， MOHAMMAD A M，et al.Design of efficient bimetallic Pt-Au nanoparticle-based anodes for direct formic acid fuel cells［J］.International Journal of Hydrogen Energy，2019，44（7）：3615-3624.
7	REN Xuefeng， LV Qianyuan， LIU Lifen，et al.Current progress of Pt and Pt-based electrocatalysts used for fuel cells［J］.Sustainable Energy & Fuels，2020，4（1）：15-30.
8	MA Zhong， CANO Z P， YU Aiping，et al.Enhancing oxygen reduction activity of Pt-based electrocatalysts：From theoretical mechanisms to practical methods［J］.Angewandte Chemie International Edition，2020，59（42）：18334-18348.
9	WANG Deli， XIN H L， HOVDEN R，et al.Structurally ordered intermetallic platinum-cobalt core-shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts［J］.Nature Materials，2013，12（1）：81-87.
10	LIU Zhufang， JACKSON G S， EICHHORN B W.Tuning the CO-tolerance of Pt-Fe bimetallic nanoparticle electrocatalysts through architectural control［J］.Energy & Environmental Science，2011，4（5）：1900.
11	CHUNG D Y， JUN S W， YOON G，et al.Highly durable and active PtFe nanocatalyst for electrochemical oxygen reduction reaction［J］.Journal of the American Chemical Society，2015，137（49）：15478-15485.
12	SUN S， MURRAY C B， WELLER D，et al.Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattic- es［J］.Science，2000，287（5460）：1989-1992.
13	LEONARD B M， ZHOU Qin， WU Diane，et al.Facile synthesis of PtNi intermetallic nanoparticles：Influence of reducing agent and precursors on electrocatalytic activity［J］.Chemistry of Materials，2011，23（5）：1136-1146.
14	WANG Yameng， ZOU Liangliang， HUANG Qinghong，et al.3D carbon aerogel-supported PtNi intermetallic nanoparticles with high metal loading as a durable oxygen reduction electrocataly-st［J］.International Journal of Hydrogen Energy，2017，42（43）：26695-26703.
15	MARKOVIC N M.Structural-effects in electrocatalysis Oxygen reduction on the gold single crystal electrodes with（110） and （111） orientations［J］.Journal of Electroanalytical Chemistry，1984，165：105-120.
16	GASTEIGER H A， KOCHA S S， SOMPALLI B，et al.Activity benchmarks and requirements for Pt，Pt-alloy，and non-Pt oxygen reduction catalysts for PEMFCs［J］.Applied Catalysis B：Environmental，2005，56（1/2）：9-35.
17	HARUTA M， DATÉ M.Advances in the catalysis of Au nanoparticles［J］.Applied Catalysis A：General，2001，222（1/2）：427- 437.
18	ZHANG J， VUKMIROVIC M B， SASAKI K，et al.Mixed-metal Pt monolayer electrocatalysts for enhanced oxygen reduction kinetics［J］.Journal of the American Chemical Society，2005，127（36）：12480-12481.
19	BIAN Ting， ZHANG Hui， JIANG Yingying，et al.Epitaxial growth of twinned Au-Pt core-shell star-shaped decahedra as highly durable electrocatalysts［J］.Nano Letters，2015，15（12）：7808-7815.
20	ZHANG Lili， DING Liangxin， CHEN Hongbin，et al.Self-supported PtAuP alloy nanotube arrays with enhanced activity and stability for methanol electro-oxidation［J］.Small，2017，13（17）：1604000.
21	彭程，程璇，张颖，等.直接甲醇燃料电池中阳极催化剂的研究进展［J］.电源技术，2003，27（5）：470-474.
	PENG Cheng， CHENG Xuan， ZHANG Ying，et al.Recent progress in anode catalysts of direct methanol fuel cells［J］.Chinese Journal of Power Sources，2003，27（5）：470-474.
22	KIM H Y， JOO S H.Recent advances in nanostructured intermetallic electrocatalysts for renewable energy conversion reactio-ns［J］.Journal of Materials Chemistry A，2020，8（17）：8195-8217.
23	BHUNIA K， KHILARI S， PRADHAN D.Trimetallic PtAuNi alloy nanoparticles as an efficient electrocatalyst for the methanol electrooxidation reaction［J］.Dalton Transactions，2017，46（44）：15558-15566.
24	SHI Qiurong， ZHU Chengzhou， FU Shaofang，et al.One-pot fabrication of mesoporous core-shell Au@PtNi ternary metallic nano particles and their enhanced efficiency for oxygen reduction reaction［J］.ACS Applied Materials & Interfaces，2016，8（7）：4739-4744.
25	LU Aolin， WU Zhipeng， CHEN Binghui，et al.From a Au-rich core/PtNi-rich shell to a Ni-rich core/PtAu-rich shell：An effective thermochemical pathway to nanoengineering catalysts for fuel cells［J］.Journal of Materials Chemistry A，2018，6（12）：5143-5155.
26	WU Zhifu， SU Yaqiong， HENSEN E J M，et al.Highly stable Pt₃Ni nanowires tailored with trace Au for the oxygen reduction reaction［J］.Journal of Materials Chemistry A，2019，7（46）：26402-26409.
27	DUTTA A， OUYANG Jianyong.Ternary NiAuPt nanoparticles on reduced graphene oxide as catalysts toward the electrochemical oxidation reaction of ethanol［J］.ACS Catalysis，2015，5（2）：1371-1380.
28	CHEN Tingwen， HUANG Weifeng， KANG Jianxin，et al.Cycling potential engineering surface configuration of sandwich Au@Ni@PtNiAu for superior catalytic durability［J］.Nano Energy，2018，52：22-28.
29	SHEN Liuliu， ZHANG Guirong， MIAO Shu，et al.Core-shell nanostructured Au@Ni _m Pt₂ electrocatalysts with enhanced activity and durability for oxygen reduction reaction［J］.ACS Catalysis，2016，6（3）：1680-1690
30	KANG Yijin， SNYDER J， CHI Miaofang，et al.Multimetallic core/interlayer/shell nanostructures as advanced electrocatalysts［J］.Nano Letters，2014，14（11）：6361-6367.
31	ZHANG Min， MIAO Shu， XU Boqing.Core@shell nanostructured Au-d@Ni _m Pt _m for electrochemical oxygen reduction reaction：Effect of the core size and shell thickness［J］.Catalysis Science & Technology，2019，9（17）：4668-4677.
32	KANG Jianxin， CHEN Tingwen， ZHANG Dongfeng，et al.PtNiAu trimetallic nanoalloys enabled by a digestive-assisted process as highly efficient catalyst for hydrogen generation［J］.Nano Energy，2016，23：145-152.
33	CHANG Jinfa， FENG Ligang， LIU Changpeng，et al.Ni₂P enhances the activity and durability of the Pt anode catalyst in direct methanol fuel cells［J］.Energy & Environmental Science，2014，7（5）：1628-1632.
34	FAN Liangdong， ZHU Bin， CHEN Mingming，et al.High performance transition metal oxide composite cathode for low temperature solid oxide fuel cells［J］.Journal of Power Sources，2012，203：65-71.
35	PEI An， RUAN Luna， LIU Bingqian，et al.Ultra-low Au decorated PtNi alloy nanoparticles on carbon for high-efficiency electro-oxidation of methanol and formic acid［J］.International Journal of Hydrogen Energy，2020，45（43）：22893-22905.
36	LIU Zhipan， HU P.General rules for predicting where a catalytic reaction should occur on metal surfaces：A density functional theory study of C—H and C—O bond breaking/making on flat，stepped，and kinked metal surfaces［J］.Journal of the American Chemical Society，2003，125（7）：1958-1967.
37	LU Xianmao，AU L， MCLELLAN J，et al.Fabrication of cubic nanocages and nanoframes by dealloying Au/Ag alloy nanoboxes with an aqueous etchant based on Fe（NO₃）₃ or NH₄OH［J］.Nano Letters，2007，7（6）：1764-1769.
38	WU Yuen， WANG Dingsheng， ZHOU Gang，et al.Sophisticated construction of Au islands on Pt-Ni：An ideal trimetallic nanoframe catalyst［J］.Journal of the American Chemical Society，2014，136（33）：11594-11597
39	SHVIRO M， POLANI S， ZITOUN D.Hollow octahedral and cuboctahedral nanocrystals of ternary Pt-Ni-Au alloys［J］.Nanoscale，2015，7（32）：13521-13529.
40	KIM S W， KIM M， LEE W Y，et al.Fabrication of hollow palladium spheres and their successful application to the recyclable heterogeneous catalyst for suzuki coupling reactions［J］.Jour-nal of the American Chemical Society，2002，124（26）：7642- 7643.
41	ZHANG Hui， JIN Mingshang， LIU Hongyang，et al.Facile synthesis of Pd-Pt alloy nanocages and their enhanced performance for preferential oxidation of CO in excess hydrogen［J］.ACS Nano，2011，5（10）：8212-8222.
42	LAL S， LINK S， HALAS N J.Nano-optics from sensing to waveguiding［J］.Nature Photonics，2007，1（11）：641-648.
43	KOH S， STRASSER P.Electrocatalysis on bimetallic surfaces： Modifying catalytic reactivity for oxygen reduction by voltammetric surface dealloying［J］.Journal of the American Chemical Society，2007，129（42）：12624-12625.
44	MAYRHOFER K J J， HARTL K， JUHART V，et al.Degradation of carbon-supported Pt bimetallic nanoparticles by surface segregation［J］.Journal of the American Chemical Society，2009，131（45）：16348-16349.
45	NAJAFISHIRTARI S， BRESCIA R， GUARDIA P，et al.Nanoscale transformations of alumina-supported AuCu ordered phase nanocrystals and their activity in CO oxidation［J］.ACS Catalysis，2015，5（4）：2154-2163.
46	GALEANO C， MEIER J C， PEINECKE V，et al.Toward highly stable electrocatalysts via nanoparticle pore confinement［J］.Journal of the American Chemical Society，2012，134（50）：20457-20465.
47	WANG Dingsheng， LI Yadong.Bimetallic nanocrystals：Liquid-phase synthesis and catalytic applications［J］.Advanced Materials，2011，23（9）：1044-1060.
48	FERRANDO R， JELLINEK J， JOHNSTON R L.Nanoalloys：From theory to applications of alloy clusters and nanoparticles［J］.Chemical Reviews，2008，108（3）：845-910.
49	LI Qing， WU Liheng， WU Gang，et al.New approach to fully ordered fct-FePt nanoparticles for much enhanced electrocatalysis in acid［J］.Nano Letters，2015，15（4）：2468-2473.
50	EL-DEEB H， BRON M.Microwave-assisted polyol synthesis of PtCu/carbon nanotube catalysts for electrocatalytic oxygen reduction［J］.Journal of Power Sources，2015，275：893-900.
51	胡洁琼，谢明，陈永泰，等.Au-Pt-Ni三元催化剂体系纳米相图的研究进展［J］.材料导报，2020，34（S2）：1338-1343.
	HU Jieqiong， XIE Ming， CHEN Yongtai，et al.Research progress on the nanophase diagram of Au-Pt-Ni catalyst system［J］.Materials Reports，2020，34（S2）：1338-1343.
52	SCHMIDT J， MARQUES M R G， BOTTI S，et al.Recent advances and applications of machine learning in solid-state materials science［J］.NPJ Computational Materials，2019，5. Doi：10.1038/s41524-019-0221-0.

[1]	汪敏娟, 王重庆. 新型反应器在纳米颗粒制备中的应用研究进展[J]. 无机盐工业, 2024, 56(3): 19-27.
[2]	靳苏娜, 吕瑞亮. 非均相催化臭氧氧化处理工业废水的研究进展[J]. 无机盐工业, 2024, 56(3): 28-38.
[3]	陈星亮, 范文娟, 常会, 黄海平, 蒋志强. Fe³⁺协同Ni基金属-有机框架提升电催化析氧反应活性的研究[J]. 无机盐工业, 2024, 56(2): 152-158.
[4]	金声势, 刘凯杰, 刘秋文, 张一波, 杨向光. 磷酸改性CeO₂纳米棒负载Pt催化剂催化丙烷燃烧性能的研究[J]. 无机盐工业, 2024, 56(1): 141-148.
[5]	郭子妮, 屈吉艳, 罗建洪. 不同禁带宽度催化剂协同低温等离子体氧化NO _x[J]. 无机盐工业, 2023, 55(9): 126-133.
[6]	刘伟, 许岩, 陈永生, 孙春晖, 张景成, 朱金剑, 刘洋. 碱土金属对铜/三氧化二铝酯加氢催化剂性能的影响[J]. 无机盐工业, 2023, 55(9): 140-144.
[7]	杨博, 梁志燕, 刘文元, 曹嘉真, 刘昕玥, 邢明阳. 钼基催化材料在水污染控制领域的应用研究进展[J]. 无机盐工业, 2023, 55(8): 1-12.
[8]	马致远, 吕大伟, 王辉, 靳南南, 朱金剑, 张景成. THDS-2/3型催化剂在加氢精制装置扩能改造中的工业应用[J]. 无机盐工业, 2023, 55(8): 140-144.
[9]	陈俊雪, 莫建欣, 周治宇, 李中林, 王丁, 李玉平, 胡拥军, 将学先, 李义兵. NaFe _x Cr _y （SO₄）₂（OH）₆的合成及电化学性能研究[J]. 无机盐工业, 2023, 55(8): 71-76.
[10]	王延苏, 刘国柱, 于海斌. 铂基丙烷脱氢催化剂研究进展[J]. 无机盐工业, 2023, 55(7): 1-9.
[11]	鲁琴, 方伟, 赵雷. 石墨化碳修饰碳化稻壳泡沫的制备及光热水蒸发性能[J]. 无机盐工业, 2023, 55(7): 122-129.
[12]	贾育红, 胡忠攀, 王坤院, 韩晶峰, 魏迎旭, 刘中民. S-1分子筛羟基窝锚定钴用于丙烷脱氢制丙烯[J]. 无机盐工业, 2023, 55(5): 121-127.
[13]	李通, 尹宏峰. 层状硅酸镍纳米管催化剂的可控制备及其催化性能研究[J]. 无机盐工业, 2023, 55(5): 128-136.
[14]	张永坤, 常洋, 李孝国, 刘岩, 杏长鑫, 郜金平, 肖家旺, 侯章贵. HZSM-5催化剂改性及其催化苯与低浓度乙烯反应的中试研究[J]. 无机盐工业, 2023, 55(5): 137-142.
[15]	冯效迁, 赵艺霖, 赵永华, 张启俭, 王欢, 孟庆润. 改性蒙脱土基催化剂研究进展[J]. 无机盐工业, 2023, 55(5): 24-30.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会