二氧化钛-钒酸铋复合材料光催化降解布洛芬的研究

Abstract

Abstract:

In order to synthesize the performance of TiO₂ and BiVO₄ photo-catalysts,a TiO₂-BiVO₄ composite photo-catalyst was prepared.And using ibuprofen as the target degradation product,the performance of TiO₂-BiVO₄ composite photo-catalyst was compared with that of TiO₂ and BiVO₄ photo-catalysts.TiO₂ photo-catalyst was prepared by gelatin method using butyl ti-tanate as raw material and adding anhydrous ethanol,hydrochloric acid and deionized water.BiVO₄ photo-catalyst and TiO₂-BiVO₄composite photo-catalyst were prepared with five water bismuth nitrate[Bi（NO₃） ₃·5H₂O] and ammonium vanadate （NH₄VO₃） asraw material by adding concentrated nitric acid and sodium hydroxide.This preparation method was simple and efficient.Under visible light irradiation,the photo-catalytic degradation of ibuprofen was carried out by using three kinds pho to-catalysts of TiO₂,BiVO₄ and TiO₂-BiVO₄ composite,and the photo-catalytic degradation of ibuprofen was also carried out by combining three kinds of photo-catalysts with hydrogen peroxide respectively.The photo-catalytic properties of the three photo-catalysts were investigated.The results showed that under the condition of no hydrogen peroxide addition,the photo-catalytic properties of the three photo-catalysts were from TiO₂-BiVO₄ composite photo-catalyst,TiO₂ photo-catalyst to BiVO₄ photo-catalyst in descending order.After adding electron capture agent H₂O₂,the efficiency of photo-catalyst degradation of ibuprofen was improved,the recombination velocity of electron hole pair was reduced,and the photo-catalytic performance of the three photo-catalysts was TiO₂-BiVO₄ composite,BiVO₄ and TiO₂ in descending order.

Key words: TiO₂, BiVO₄, TiO₂-BiVO₄composite, ibuprofen, photo-catalytic properties

CLC Number:

Gao Yanan. Photo-catalyst degradation of ibuprofen by TiO₂-BiVO₄ composites[J]. Inorganic Chemicals Industry, 2019, 51(6): 88-91.

Figures/Tables 5

References 8

[1]	孟璐, 马兰 . 布洛芬及其衍生物的合成进展[J]. 黑龙江科技信息, 2012(9): 2, 86.
[2]	陈玉花, 王俊峰, 常洋 , 等. 关于布洛芬缓释胶囊有关物质检测方法的研究[J]. 黑龙江畜牧兽医, 2016(9):273-276.
[3]	杨大伟, 王帆 . 液相色谱-质谱联用法对非法制剂中的布洛芬检测分析[J]. 黑龙江科技信息, 2012(4):13.
[4]	郭宇, 金玉家 . 负载型二氧化钛光催化材料的制备及其光催化性能研究[J]. 光谱学与光谱分析, 2015,35(6):1677-1681.
[5]	李家贵, 韦庆敏, 罗志辉 , 等. TiO₂/BiVO₄复合光催化剂的合成及其光催化性能研究[J]. 材料导报B:研究篇, 2014,28(5):46-49.
[6]	刘利, 王亚飞, 崔文权 , 等. 钒酸铋的制备及可见光降解罗丹明B的研究[J]. 无机盐工业, 2013,45(8):60-62.
[7]	李富华, 孔青青, 康亚璞 , 等. BiVO₄联合H₂O₂或K₂S₂O₈光催化降解布洛芬[J]. 环境工程学报, 2016,10(10):5380-5386.
[8]	王周, 石建新, 彭敏 , 等. 钒酸铋黄色颜料的制备——推荐一个无机化学教学实验[J]. 大学化学, 2016,31(6):53-57.

[1]	ZHAN Hongren, TIAN Feng, ZHANG Xianzhen, MA Yugui, KOU Liping, LIU Peng. Experimental study on preparation of high performance foam glass ceramics from waste rock wool [J]. Inorganic Chemicals Industry, 2024, 56(1): 96-101.
[2]	SONG Zhijia, WANG Suisui, KUANG Qin. Hollow Cu-doped TiO₂ for enhancing photocatalytic CO₂ reduction performance [J]. Inorganic Chemicals Industry, 2023, 55(8): 45-50.
[3]	CHEN Zhangxu, ZHU Danchen, FU Minglian. Study on preparation of g-C₃N₄/TiO₂composites and application for rhodamine B removal [J]. Inorganic Chemicals Industry, 2023, 55(7): 130-136.
[4]	XU Xiaobing,LI Xu,YANG Xu,XU Xiaoyong. Effect of firing temperature on properties of MgO-TiO₂ composite inorganic ceramic microfilter membrane support [J]. Inorganic Chemicals Industry, 2022, 54(8): 85-89.
[5]	YANG Shuang,ZHAO Siqin,YANG Huiying. Research progress on photocatalysis by bismuth?based semiconductor composite TiO₂ [J]. Inorganic Chemicals Industry, 2022, 54(6): 38-45.
[6]	HOU Yan,GAO Chengjuan,WU Xizhe,ZI Xuechi,XIE Lu,YANG Haizheng,YAN Yuxing. Theoretical study on effect of nitrogen doping on photoelectric properties of rutile TiO₂ [J]. Inorganic Chemicals Industry, 2022, 54(6): 90-95.
[7]	ZHANG Farong,FAN Tiantian,GUO Yanyun,LI Lu,LIU Bingguang,LI Jiansheng. Research progress on self-cleaning film materials [J]. Inorganic Chemicals Industry, 2022, 54(4): 74-80.
[8]	FU Yong,XU Wenqi,ZHAO Qiang,RAN Ruiquan,LI Jun,JIN Yang. Study on preparation of silver-doped titanium dioxide/activated carbon composite material and its photocatalytic performance [J]. Inorganic Chemicals Industry, 2022, 54(2): 117-122.
[9]	Liu Xingyu,Jia Yuanyuan,Wu Shufeng,Tang Zhonghua,Zhang Peng,Liu Junqiang,Pu Xin. Research progress of Ce-based SCR denitration catalysts [J]. Inorganic Chemicals Industry, 2021, 53(8): 15-20.
[10]	Zhang Lan,Tan Haolei,Ma Huizhong,Luo Aoxiang,Wang Jiping. Study on preparation and photocatalytic performance of nano-TiO₂films co-doped with nickel and carbon [J]. Inorganic Chemicals Industry, 2021, 53(4): 107-111.
[11]	WU Lina,ZHANG Xiangjun,LIN Qingxian. Synthesis and antibacterial performance of γ-Fe₂O₃/sorbic acid/Ag-TiO₂ [J]. Inorganic Chemicals Industry, 2021, 53(12): 156-162.
[12]	SHI Suqi,ZHANG Shouchen,ZHANG Dijia,NING Guiling,YE Junwei. Study on crystal facet regulation of bismuth vanadate and its degradation properties of tetracycline antibiotics [J]. Inorganic Chemicals Industry, 2021, 53(11): 114-121.
[13]	Zhang Aiwen,Chong Yanzhu,Gao Guanjun. Preparation of Ag modified TiO₂ nano-fiber by electrostatic spinning for MB photo-degradation [J]. Inorganic Chemicals Industry, 2021, 53(10): 125-128.
[14]	Zhang Wei,Wang Dandan,Tian Zhongqing. Preparation and photoelectric properties of CuO/BiVO₄ heterojunction films [J]. Inorganic Chemicals Industry, 2020, 52(7): 99-102.
[15]	Zhu Jiaxin,Xiong Yuhua,Guo Rui. Research progress in modification of TiO₂ photocatalyst [J]. Inorganic Chemicals Industry, 2020, 52(3): 23-27.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Photo-catalyst degradation of ibuprofen by TiO₂-BiVO₄ composites

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 5

References 8

Related Articles 15

Metrics

Comments

Recommended 0

Photo-catalyst degradation of ibuprofen by TiO2-BiVO4 composites