氧缺陷C3N5复合混凝土涂层的制备及光催化性能研究

doi:10.19964/j.issn.1006-4990.2024-0447

Abstract

Abstract:

The oxygen-deficient nitrogen-rich carbon nitride（C₃N₅-O） photocatalyst was prepared by a simple high-temperature thermal polymerization method.The phase composition，elemental composition，unpaired electrons，spectral absorption，photoelectron-hole recombination and electrochemical properties of the photocatalyst were characterized by X-ray diffraction（XRD），X-ray photoelectron spectroscopy（XPS），electron paramagnetic resonance spectroscopy（EPR），UV-vis diffuse reflectance spectroscopy（UV-vis DRS），photoluminescence spectroscopy（PL），transient photocurrent spectroscopy（TPC） and electrochemical impedance spectroscopy（EIS）.The C₃N₅-O photocatalyst showed excellent photocatalytic activity and stability.The degradation rate of rhodamine B（RhB） by C₃N₅-O photocatalyst reached 97.49% after visible light irradiation for 60 min，which was 1.49 times that of pure C₃N₅.After 10 cycles，it still showed excellent photocatalytic activity，and the degradation rate was still higher than 96%.Portland cement，water and C₃N₅-O photocatalyst were uniformly mixed and uniformly applied to the surface of concrete matrix by brushing method to prepare C₃N₅-O composite concrete coating.The optimum doping amount of C₃N₅-O was 1.5%（mass fraction）.The coating had good photocatalytic performance and stability.The degradation rate of RhB reached 97.31% within 60 min under visible light irradiation，and the degradation rate of RhB was 96.94% after 10 cycles.The hydration products，thermal weight loss and pores of the coatings were analyzed by XRD，thermogravimetric analysis（TGA） and pore size distribution（BJH）.The effect of C₃N₅-O incorporation on cement hydration was studied.The incorporation of C₃N₅-O promoted the hydration process of cement through the nucleation effect and filling effect，promoted the formation of hydration products，and improved the compressive strength of the matrix，the compressive strength of concrete cured for 28 d was increased by 8.51%.

Key words: nitrogen rich carbon nitride, oxygen defects, photocatalysis, concrete coating, rodamine B

CLC Number:

TQ127.16

HAN Qing, HAN Xiaoyong. Study on preparation and photocatalytic properties of oxygen deficient C₃N₅ composite concrete coating[J]. Inorganic Chemicals Industry, 2025, 57(7): 134-142.

Figures/Tables 14

Fig.1

Fig.2

Fig.3

Table 1

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

Fig.11

Fig.12

Fig.13

References 24

[1]	LIU Guanyu， FEI Hailiang， ZHANG Jiaxu，et al.Enhancement mechanism for mechanical and water purification performance of piezo-photocatalytic recycled aggregate pervious concrete containing hydrophobic BiOI/BaTiO₃ ［J］.Chemical Engineering Journal，2024，493：152596.
[2]	林元明，林佳福，熊晓立，等.TiO₂改标性钢渣基透水混凝土的力学和NO _x 降解性能研究［J］.硅酸盐通报，2024，43（1）：191-199.
	LIN Yuanming， LIN Jiafu， XIONG Xiaoli，et al.Mechanical and NO _x degradation performance of TiO₂ modified steel slag-based permeable concrete［J］.Bulletin of the Chinese Ceramic Society，2024，43（1）：191-199.
[3]	XIA Dongtao， XIA Pan， HU Junan，et al.Optimization of mechanical properties of pervious recycled concrete using polypropylene fiber and waterborne epoxy resin［J］.Structures，2024，63：106372.
[4]	CHEN Shoukai， ZHOU Jingfei， LIU Junguo，et al.Sustainable ecological pervious concrete（SEPC） based on modified corn-cob coarse aggregate：Crushing morphology，strength，pore properties，and durability［J］.Construction and Building Materials，2024，426：136194.
[5]	YAGHMOUR E， QAMAR M ABU， NAITO C，et al.Pressure drop and heat transfer properties for normal weight and lightweight pervious concrete［J］.Construction and Building Materials，2024，425：135947.
[6]	KHAN M A， AHMAD J， KHAN H A，et al.High strength rubberized porous concrete for sustainable pavements：Engineering properties and life cycle assessment［J］.Journal of Cleaner Production，2024，451：142012.
[7]	唐贝.ZnO/g-C₃N₄异质结光催化材料的制备及对吡啶的降解［J］.无机盐工业，2024，56（4）：133-142.
	TANG Bei.Preparation of ZnO/g-C₃N₄ heterojunction photocatalytic material and its degradation of pyridine［J］.Inorganic Chemicals Industry，2024，56（4）：133-142.
[8]	ZHANG Junlei， TAO Hengcong， WU Shanshan，et al.Enhanced durability of nitric oxide removal on TiO₂（P25） under visible light：Enabled by the direct Z-scheme mechanism and enhanced structure defects through coupling with C₃N₅ ［J］.Applied Catalysis B：Environmental，2021，296：120372.
[9]	LIU Tianyu， YANG Guojiang， WANG Wei，et al.Preparation of C₃N₅ nanosheets with enhanced performance in photocatalytic methylene blue（MB） degradation and H2-evolution from water splitting［J］.Environmental Research，2020，188：109741.
[10]	YIN Hongfei， YUAN Chunyu， LV Huijun，et al.The interface design of（0D/2D/1D） AgI/BiOI/C₃N₅ dual Z-scheme heterostructures with efficient visible-light-driven photocatalytic activity［J］.Separation and Purification Technology，2023，308：122815.
[11]	GUJRAL H S， SINGH G， YANG J H，et al.Mesoporous titanium carbonitride derived from mesoporous C₃N₅ for highly efficient hydrogen evolution reaction［J］.Carbon，2022，195：9-18.
[12]	DU Xing， LIU Qianqian， CHENG Miao，et al.Single-atom Pt decorated g-C₃N₅ nanorods as highly efficient photocatalyst for H₂ evolution and wastewater purification［J］.International Journal of Hydrogen Energy，2024，53：353-363.
[13]	LONG Jieqing， WEI Liang， HUANG Haizan，et al.Facile fabrication of biochar-coupled g-C₃N₅/C and its enhanced photocatalytic properties［J］.Journal of Physics and Chemistry of Solids，2022，171：111029.
[14]	MA Zhanqiang， GUO Wei， ZHANG Kaiyue，et al.Liquid exfoliation of bulk g-C₃N₅ to nanosheets for improved photocatalytic antibacterial activity［J］.Environmental Science and Pollution Research International，2023，30（26）：69486-69498.
[15]	邵宗涵，肖柯，赵宇，等.磷掺杂氮缺陷g-C₃N₄的合成及其光催化性能研究［J］.化工新型材料，2024，52（3）：214-219.
	SHAO Zonghan， XIAO Ke， ZHAO Yu，et al.Synthesis of phosphorus-doped nitrogen-deficient g-C₃N₄ and its photocatalytic performance［J］.New Chemical Materials，2024，52（3）：214- 219.
[16]	董永浩，马爱琼，李金叶，等.热剥离法制备含缺陷g-C₃N₄纳米片及光催化性能［J］.稀有金属，2021，45（1）：47-54.
	DONG Yonghao， MA Aiqiong， LI Jinye，et al.Preparation of defective g-C₃N₄ nanosheets by thermal exfoliation and its photocatalytic performance［J］.Chinese Journal of Rare Metals，2021，45（1）：47-54.
[17]	贺晓宇.基于氮化碳的光催化水泥混凝土制备与性能研究［J］.公路，2020，65（10）：292-296.
	HE Xiaoyu.Preparation and properties of photocatalytic cement concrete based on carbon nitride［J］.Highway，2020，65（10）：292-296.
[18]	WANG Lei， CHEN Ruijie， ZHANG Zhiqiang，et al.Constructing direct Z-scheme heterojunction g-C₃N₅/BiOBr for efficient photocatalytic CO₂ reduction with H₂O［J］.Journal of Environmental Chemical Engineering，2023，11（2）：109345.
[19]	DENG Yaocheng， LI Ling， ZENG Hao，et al.Unveiling the origin of high-efficiency charge transport effect of C₃N₅/C₃N₄ homojunction for activating peroxymonosulfate to degrade atrazine under visible light［J］.Chemical Engineering Journal，2023，457：141261.
[20]	李书文，周严，汪铁林.BiVO₄/rGO复合物的制备及其光催化还原CO₂研究［J］.无机盐工业，2019，51（11）：82-87.
	LI Shuwen， ZHOU Yan， WANG Tielin.Study on preparation and photocatalysis-reduction for CO₂ of BiVO₄/rGO composite［J］.Inorganic Chemicals Industry，2019，51（11）：82-87.
[21]	WANG Yin， LEI Shulai， ZHANG Xin，et al.First-principles study of nitrogen defect g-C₃N₄/WS₂ heterojunction on photocatalytic activity［J］.Current Applied Physics，2022，39：70-76.
[22]	杨文博，吴潘，何坚，等.升温速率对尿素热解制g-C₃N₄光催化剂构效影响研究［J］.无机盐工业，2022，54（4）：169- 174.
	YANG Wenbo， WU Pan， HE Jian，et al.Study on effect of heating rate on structure-activity of g-C₃N₄ photocatalyst by pyrolysis of urea［J］.Inorganic Chemicals Industry，2022，54（4）：169-174.
[23]	YIN Hongfei， YUAN Chunyu， LV Huijun，et al.Fabrication of 2D/1D Bi₂WO₆/C₃N₅ heterojunctions for efficient antibiotics remo- val［J］.Powder Technology，2023，413：118083.
[24]	SHEN Yuanyuan， JIANG Long， SHEN Peiliang，et al.Development of photocatalytic carbonation coating for concrete：Enhancement of air quality and sequestration of CO₂ ［J］.Cement and Concrete Composites，2024，145：105308.

样品	原子数比
样品	C/N	C/H	C/O
C₃N₅	0.645	2.552	16.415
C₃N₅-O	0.646	2.561	10.582

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on preparation and photocatalytic properties of oxygen deficient C₃N₅ composite concrete coating

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 14

References 24

Related Articles 15

Metrics

Comments

Recommended 0

[1]	WANG Xiaoyu, DU Ruicheng, LI Yan, YANG Shuyan. Research advances in optimization and modification of TiO₂-based nanomaterials [J]. Inorganic Chemicals Industry, 2025, 57(7): 24-34.
[2]	ZHAO Yanyan, TIAN Zhuangzhuang. Study on preparation and visible light degradation performance of g-C₃N₄ loaded nano-Ag composites [J]. Inorganic Chemicals Industry, 2025, 57(6): 114-122.
[3]	LIN Shashan, WANG Xiazhong. Study on preparation of MoS₂/g-C₃N₄ composite loaded photocatalytic concrete and its activity [J]. Inorganic Chemicals Industry, 2025, 57(6): 123-132.
[4]	ZHU Jianjun, LIU Peiting, HAN Wenbo, WANG Jing. Study on preparation and visible⁃light photocatalytic properties of TiO₂/g-C₃N₄/Ag₃PO₄heterojunction [J]. Inorganic Chemicals Industry, 2025, 57(5): 116-124.
[5]	ZHANG Dian. Degradation performance analysis of S-scheme activated carbon supported g-C₃N₄/TiO₂ photocatalytic concrete [J]. Inorganic Chemicals Industry, 2025, 57(4): 118-127.
[6]	SHI Wangfang, ZHANG Yongsheng. Study on NO _x degradation performance of concrete-based non-metallic boron doped nitrogen-rich carbon nitride [J]. Inorganic Chemicals Industry, 2025, 57(3): 116-123.
[7]	LI Zihan, ZHANG Jiaqi, LI Shizhuo, LI Xinyu, LIU Shaozhuo, WANG Yihao, HAO Yucui, LIU Jian, LI Yanhua. Study on synthesis and catalytic mechanism of CdS/g-C₃N₄composite photocatalyst [J]. Inorganic Chemicals Industry, 2025, 57(3): 124-132.
[8]	SUN Qinghao, LI Keyan, GUO Xinwen. Study on photocatalytic benzyl alcohol oxidation coupled with hydrogen production over Pd/ZnIn₂S₄ nanosheets [J]. Inorganic Chemicals Industry, 2025, 57(1): 113-119.
[9]	LIU Guangming. Study on photocatalytic and mechanical properties of C₃N₅/NH₂-MIL-125（Ti） modified concrete mortar [J]. Inorganic Chemicals Industry, 2025, 57(1): 120-128.
[10]	ZHANG Guoqiang, RONG Xilin, XIAO Zhenfang, XUE Ziran, CHENG Hao, FENG Jun, LIU Quan, LU Yao, HUANG Wenyi. Study on preparation and photocatalytic properties of bagasse carbon aerogels loaded with zinc oxide nanoparticles [J]. Inorganic Chemicals Industry, 2024, 56(8): 131-138.
[11]	WANG Yawen, WANG Fangfang, GENG Siyu, JU Jia, CHEN Lei, CHEN Changdong. Study on preparation and photocatalytic performance of SrTiO₃-SrWO₄ [J]. Inorganic Chemicals Industry, 2024, 56(7): 143-149.
[12]	LIU Min, HUANG Xiu, ZHANG Liyuan. Research progress of S-type heterojunction photocatalysts [J]. Inorganic Chemicals Industry, 2024, 56(7): 18-27.
[13]	LI Jiangpeng, ZHANG Huibin. Synergistic degradation of methylene blue by photo-Fenton and photocatalytic with 3D porous LaFeO₃/CeO₂/SrTiO₃ [J]. Inorganic Chemicals Industry, 2024, 56(5): 141-148.
[14]	TANG Bei. Preparation of ZnO/g-C₃N₄ heterojunction photocatalytic material and its degradation of pyridine [J]. Inorganic Chemicals Industry, 2024, 56(4): 133-142.
[15]	HUANG Jianan, LU Xiaoyu, WANG Mitang. Effect of Ba-La co-doping on degradation of methylene blue dye by TaON [J]. Inorganic Chemicals Industry, 2024, 56(2): 146-151.

Study on preparation and photocatalytic properties of oxygen deficient C3N5 composite concrete coating