以浓厚卤水为原料制备半水硫酸钙晶须的研究

doi:10.11962/1006-4990.2019-0312

Abstract

Abstract:

Calcium sulfate hemihydrate whisker with high length/diameterm（L/D） ratio was prepared from high concentration brine abandoned in the production process of sea salt industry.The effects of material concentration,crystal growth promoter concentration,reaction time,reaction temperature and reaction stirring rate on the preparation of calcium sulfate hemihydrate whisker were investigated.The prepared calcium sulfate hemihydrate whisker was characterized and confirmed by powder X-ray diffractometer and scanning electron microscope.Through the orthogonal experimental,the optimum conditions were con-firmed as follows：material mass fraction of 3%,crystal growth aid mass fraction of 3%,reaction time of 7 h,reaction tempera-ture of 130 ℃ and reaction stirring rate of 30 r/min.Under this condition,calcium sulfate hemihydrate whiskers with the L/D ratio of 400 were produced.The technology has the advantages of low production cost,environment friendly and stablity.The prepared calcium sulfate hemihydrate whisker with average L/D ratio of 400 is easy to produce industrially.

Key words: dense brine, Calcium sulfate hemihydrate whiskers, length/diameter（L/D） ratio

CLC Number:

TQ132.32

Tang Na,Hei Yunhao,Wu Tengfei,Xiang Jun,Du Wei,Zhang Lei. Study on preparation of hemihydrate calcium sulfate whisker from dense brine[J]. Inorganic Chemicals Industry, 2020, 52(4): 88-92.

Figures/Tables 10

References 14

[1]	Fan H, Song X, Liu T , et al. Effect of Al ³+ on crystal morphology and size of calcium sulfate hemihydrate:Experimental and molecular dynamics simulation study [J]. Journal of Crystal Growth, 2018,495:29-36. doi: 10.1016/j.jcrysgro.2018.05.013
[2]	Fan H, Song X, Xu Y , et al. Insights into the modification for impro-ving the surface property of calcium sulfate whisker:Experimental and DFT simulation study[J]. Applied Surface Science, 2019,478:594-600. doi: 10.1016/j.apsusc.2019.01.161
[3]	Han Q, Luo K, Li H , et al. Influence of disodium hydrogen phosphate dodecahydrate on hydrothermal formation of hemihydrate calcium sulfate whiskers[J]. Particuology, 2014,17:131-135. doi: 10.1016/j.partic.2013.10.002
[4]	Liu C, Zhao Q, Wang Y , et al. Surface modification of calcium sul-fate whisker prepared from flue gas desulfurization gypsum[J]. App-lied Surface Science, 2016,360:263-269.
[5]	Luo K, Li C, Xiang L , et al. Influence of temperature and solution composition on the formation of calcium sulfates[J]. Particuology, 2010,8(3):240-244. doi: 10.1016/j.partic.2010.01.005
[6]	崔益顺 . 磷石膏制备硫酸钙晶须的研究[J]. 无机盐工业, 2010,42(9):49-50.
[7]	Mao X, Song X, Lu G , et al. Effect of additives on the morphology of calcium sulfate hemihydrate:Experimental and molecular dynamics simulation studies[J]. Chemical Engineering Journal, 2015,278:320-327.
[8]	Miao M, Feng X, Wang G , et al. Direct transformation of FGD gyps-um to calcium sulfate hemihydrate whiskers: Preparation, simula-tions, and process analysis[J]. Particuology, 2015,19(2):53-59.
[9]	Sun H, Tan D, Peng T , et al. Preparation of calcium sulfate whisker by atmospheric acidification method from flue gas desulfurization gypsum[J]. Procedia Environmental Sciences, 2016,31:621-626.
[10]	Tan H, Dong F, Liu J . Morphology control of calcium sulfate hemi-hydrates and application in size screening iron/sulfur of jarosite sediment[J]. Journal of Physics and Chemistry of Solids, 2018,112:239-245.
[11]	Teng W, Wang J, Wu J , et al.Rapid synjournal of alpha calcium sul-fate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste[J].Journal of Crystal Gro-wth, 2018,496/497:24-30.
[12]	黄哲元, 董发勤, 张伟 . 硫酸钙晶须的制备进展[J]. 无机盐工业, 2009,41(8):6-8.
[13]	刘崇峻 . 药物水合物结晶热力学及转晶过程研究[D]. 天津:天津大学, 2013.
[14]	方羊 . 水热法制备半水硫酸钙晶须及其长径比的可控研究[D]. 合肥:合肥工业大学, 2017.

序号	检测项目	检测方法	国标
1	Ca²⁺	滴定法	GB/T 13025.6—2012
2	Na⁺	滴定法	GB/T 13025.8—2012
3	Cl^-	滴定法	GB/T 13025.5—2012
4	SO₄^2-	滴定法	GB/T 13025.8—2012
5	K⁺	滴定法	QB/T 4445—2012
6	Mg²⁺	滴定法	GB/T 13025.6—2012
7	色度	稀释倍数法	GB/T 11903—1989
8	COD	化学需氧量（COD）测定仪	GB/T 32208—2015

水平	因素
水平	A w（物料)/%	B 时间/h	C w（晶型助长剂)/%	D转速/ （r·min^-1）	E 温度/℃
1	2	6	2	30	125
2	3	7	3	60	130
3	4	8	4	90	135

实验号	因素					长径比
实验号	A	B	C	D	E	长径比
1	1	1	3	1	2	98
2	1	3	1	2	2	89
3	2	2	2	1	2	401
4	3	3	3	1	3	81
5	1	1	1	1	1	67
6	2	1	1	3	3	77
7	1	2	1	2	3	71
8	1	1	2	1	3	44
9	1	3	2	3	1	42
10	3	1	1	3	2	56
11	1	2	3	3	1	48
12	2	3	1	1	1	39
13	2	1	3	2	1	25
14	3	2	1	1	1	83
15	3	1	2	2	1	68
16	1	2	2	2	2	168
K₁	627	435	482	813	372
K₂	542	771	723	421	812
K₃	288	251	252	223	273
k₁	78	62	69	116	53
k₂	136	154	145	84	162
k₃	72	63	63	56	68
R	64	92	82	60	109

[1]	YAN Xin, LIU Hailu, LIU Baolin, LIU Yi, LIU Yanyang. Research on key technologies and mechanisms of green nano calcium carbonate production [J]. Inorganic Chemicals Industry, 2025, 57(1): 71-76.
[2]	ZHANG Jianle, CAO Yapeng, ZU Minghua, ZHANG Zhikun, LIU Yumin, HAN Jilong. Study on morphology of calcium carbonate controlled by sodium dodecyl sulfate and amino acid double template [J]. Inorganic Chemicals Industry, 2025, 57(1): 58-63.
[3]	WANG Jie, ZHAO Xubo, TANG Yong, QIN Lingyi, CHEN Xiaopeng, LIAO Dankui, TONG Zhangfa, WANG Linlin. Preparation and structural characterization of high specific surface area calcium hydroxide by wet digestion of quicklime [J]. Inorganic Chemicals Industry, 2024, 56(12): 104-112.
[4]	LUO Ya, ZHOU Rong, LÜ Li, YANG Jie, TANG Shengwei, ZHANG Tao. Study on crystallization and filtration properties of calcium sulfate for treating industrial waste sulfuric acid with calcium carbonate [J]. Inorganic Chemicals Industry, 2024, 56(12): 127-133.
[5]	YANG Yuqing, LUO Aiwen, WANG Jie, WU Chenjie, QU Jun, XU Zhigao, DU Dongyun, CAO Yanmin. Study on solidification of soluble phosphorus in phosphogypsum by Ca/Al/La LDH [J]. Inorganic Chemicals Industry, 2024, 56(12): 134-141.
[6]	LI Xuelian, TANG Zihan, XU Jie, LI Xiong. Study on performance of calcium sulfate whisker/SBS composite modified asphalt [J]. Inorganic Chemicals Industry, 2024, 56(9): 82-89.
[7]	LI Yuxing, ZHANG Jincai, CHENG Fangqin. Research progress of preparation and growth mechanism of various crystalline nano-calcium carbonate [J]. Inorganic Chemicals Industry, 2024, 56(5): 1-10.
[8]	CHEN Feng, FENG Kang, LI Ming, SHEN Haojie, TIAN Chengtao, TANG Yuan, LI Zhili, HE Dongsheng. Application of organically modified calcium sulfate whiskers in asphalt modification [J]. Inorganic Chemicals Industry, 2024, 56(3): 125-130.
[9]	XIONG Shuang, YAN Jinsheng, ZHOU Zhou, ZHOU Baodi, CHEN Xiaopeng, TONG Zhangfa. Effect of reaction conditions of quicklime digestion on properties of calcium hydroxide [J]. Inorganic Chemicals Industry, 2023, 55(12): 50-58.
[10]	GUO Ze, ZHANG Pengfei, YANG Fan, ZHANG Hanquan, LU Manman. Preparation of β-hemihydrate gypsum by phosphogypsum roasting [J]. Inorganic Chemicals Industry, 2023, 55(10): 106-113.
[11]	DU Guanggang, HE Tong, XU Zehui, LIU Lei. Study on properties of calcium oxide in SCA under different calcination conditions [J]. Inorganic Chemicals Industry, 2023, 55(10): 35-41.
[12]	LIU Yue, ZHENG Qiang, XING Jiabin, XING Run, MA Yali, JIA Songyan, LI Xue. Study on process and application of high-performance calcium hydroxide prepared by dry digestion from limestone [J]. Inorganic Chemicals Industry, 2023, 55(10): 42-49.
[13]	CHEN Xiaoqing, ZHOU Jian′an, WANG Yi, HAN Juan, WANG Bao, PEI Peiyan. Study on decomposition characteristic of limestone powder in high temperature flue gas of converter [J]. Inorganic Chemicals Industry, 2023, 55(10): 70-77.
[14]	CHEN Qi, LIAO Dankui, ZHANG Qingnian, YAN Jinsheng, HUANG Yu, CHEN Xiaopeng, TONG Zhangfa. Fast and efficient determination of quicklime activity by conductivity method [J]. Inorganic Chemicals Industry, 2023, 55(9): 114-120.
[15]	ZHANG Jinjun, GUO Linlin, LIU Bojing, FENG Shuang, SHI Qi. Study on preparation of needle-like shaped CaCO₃ from calcium carbide slag [J]. Inorganic Chemicals Industry, 2023, 55(7): 103-108.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on preparation of hemihydrate calcium sulfate whisker from dense brine

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 10

References 14

Related Articles 15

Metrics

Comments

Recommended 0