球形碳酸钙的控制合成研究

doi:10.11962/1006-4990.2019-0035

Abstract

Abstract: Spherical calcium carbonate（calcite） crystals were prepared by co precipitation method with boric acid as control agent，calcium chloride and sodium carbonate as raw materials.The effects of the concentration of control agent，reaction tem perature，reaction time and reactant concentration on the particle size and morphology of calcium carbonate were investigated. Results showed that when the concentration of boric acid was 0.4 mol/L，the concentration of calcium chloride was 0.1 mol/L，the dropping rate of saturated sodium carbonate solution at 20 ℃ was 4.9 mL/min，the reaction time was 60 min，the aging time was 60 min，the reaction temperature was 50 ℃ and the amount of substance ratio of calcium chloride to sodium carbo nate was 1∶1，the prepared spherical calcium carbonate particles were uniform in size and the average particle size was 1.57 μm.

Key words: spherical calcium carbonate；co precipitation method；boric acid；calcite

CLC Number:

TQ132.32

Tan Tingting1，2，3，Zhong Jianchu1，2，3. Study on controllable synthesis of spherical calcium carbonate[J]. Inorganic Chemicals Industry, 2019, 51(12): 30-34.

[1]	Zhang Bin,Xiao Xiao,Han Yunjiao,Zhang Yuanyuan,Yu Hongwei. Study on third-step infrared spectroscopy of calcium carbonate [J]. Inorganic Chemicals Industry, 2021, 53(1): 97-101.
[2]	Yang Xiaohong,Xue Xishi,Zhang Lulu,Chang Jun. Kinetics study of calcium leaching from electrolytic manganese residue by hydrochloric acid [J]. Inorganic Chemicals Industry, 2021, 53(1): 82-86.
[3]	Chen Hongqiong,Ma Hang. Industrial test on control of free acid in granular tripe superphosphate [J]. Inorganic Chemicals Industry, 2021, 53(1): 59-61.
[4]	Cao Weiwen,Li Jun,Chen Ming,Yu Yinrong,Liao Xiaoting. Study on agglomeration process during crystallization of calcium hydrogen phosphate and its main affecting impurity thereof [J]. Inorganic Chemicals Industry, 2021, 53(1): 50-53.
[5]	Chang Yuefan,Zhang Huijie,Wang Shanshan,Xue Yongqiang. Controllable preparation of nano-calcium carbonate with different particle sizes [J]. Inorganic Chemicals Industry, 2020, 52(12): 29-33.
[6]	Zhang Dongxue,Yang Baojun,Chen Yujia,Wang Bainian,Shao Zongqi. Preparation of calcium sulfate dihydrate whiskers from leachate of phosphate ore by hydrochloric acid [J]. Inorganic Chemicals Industry, 2020, 52(11): 37-42.
[7]	Li Zhixin,Xu Kaidong,Zhou Hao,Wang Jina,Zhang Jianwu,Guo Gaowei. Study on composite admixtures modified salt gypsum [J]. Inorganic Chemicals Industry, 2020, 52(11): 75-78.
[8]	Zhou Jianwei,Cheng Baojun,Yu Baoying,Ma Pengfei,He Pingxian. Effect of heat-treated desulfurized gypsum on properties of super sulfated cement [J]. Inorganic Chemicals Industry, 2020, 52(11): 79-85.
[9]	Yang Quancheng,Gong Zhiming,Mao Yanyu,Li Xiaodong,Zhang Yancheng,Shi Changsheng,Zeng Ming. Preparation of mesoporous calcium silicate with alumina-extracted coal gangue by hydrothermal method [J]. Inorganic Chemicals Industry, 2020, 52(11): 86-90.
[10]	Wang Yubin,Zhang Lu,Mao Xinyu,Wang Wangbo,Dang Weiben. Effect mechanism of hydroxide ions on morphology of calcium sulfate hemihydrate crystals [J]. Inorganic Chemicals Industry, 2020, 52(11): 20-23.
[11]	Liu Baoshu,Hao Zhigang,Ma Yongshan,Liu Runjing,Hu Yongqi. Trend analysis and review of calcium carbonate production in China for the past 60 years [J]. Inorganic Chemicals Industry, 2020, 52(10): 37-43.
[12]	Zhao Shihao,Lin Xihua,Ma Pengfei,Yuan Yijin,Gao Yuxin,Zhang Ping,Zhou Dali. Study on formulation calculation of phosphogypsum-based composite cementitious materials based on expansion and failure of critical AFt [J]. Inorganic Chemicals Industry, 2020, 52(9): 91-95.
[13]	Wang Xiaoxiong,Zhang Jiangang,Zhang Wenjing,Chen Ye. Removal of calcium chloride from crude phosphoric acid by hydrochloric acid method [J]. Inorganic Chemicals Industry, 2020, 52(8): 17-19.
[14]	Zhang Yulu,Wang Ye,Yang Lin,Yang Xiushan,Wang Xinlong. Preparation of high purity calcium oxide combined with sulfuric acid from fluorine gypsum decomposed by sulfur [J]. Inorganic Chemicals Industry, 2020, 52(7): 70-73.
[15]	Yan Xin. Research and production of colorful nano-sized calcium carbonate [J]. Inorganic Chemicals Industry, 2020, 52(5): 53-55.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on controllable synthesis of spherical calcium carbonate

RichHTML

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Metrics

Comments

Recommended 10