粉煤灰基地质聚合物微球吸附水中铜（Ⅱ）的研究

doi:10.19964/j.issn.1006-4990.2022-0033

摘要/Abstract

摘要：

以粉煤灰为原料，以氢氧化钾溶液为碱激发剂，将二者按照优化配比（氧化钾与氧化铝物质的量比为1.5、水与氧化钠物质的量比为18）混合均匀后，采用悬浮固化法制备粉煤灰基地质聚合物微球，将微球用于吸附含铜废水中的铜（Ⅱ）。通过X射线衍射（XRD）仪、比表面积与孔径分析仪、BT-99型水质分析仪对微球进行了表征，探究了吸附时间、微球用量、吸附温度、铜（Ⅱ）溶液pH、铜（Ⅱ）溶液质量浓度等因素对微球吸附铜（Ⅱ）的影响。结果表明，粉煤灰基地质聚合物微球较粉煤灰原料具有更大的孔径和比表面积，具有更好的对铜（Ⅱ）的吸附效果，在最优条件下[微球用量为0.20 g、溶液pH为5、铜（Ⅱ）初始质量浓度为100 mg/L、溶液体积为100 mL、吸附温度为40 ℃、吸附时间为24 h]微球对铜（Ⅱ）的吸附量为45.62 mg/g、去除率达到91.46%，吸附过程遵循准二级动力学方程。

关键词: 粉煤灰, 地质聚合物, 微球, 吸附, 铜（Ⅱ）

Abstract:

Fly ash was used as a raw material，potassium hydroxide solution was used as an alkali activator，and the mixture was uniform according to the optimized ratio[n（K₂O）/n（Al₂O₃）=1.5，n（H₂O）/n（Na₂O）=18].The fly ash-based geoploymer microspheres were prepared by suspension solidification method，and it was used to adsorb Cu²⁺ from wastewater containing copper.The microspheres were characterized by X-ray diffraction（XRD），specific surface area and aperture analyzer，BT-99 water quality analyzer.The effects of time，dosage，temperature，pH value，concentration and other factors on the adsorption of Cu²⁺ on the microspheres were explored.The results showed that the fly ash-based geoploymer microspheres had larger pore size，specific surface area and better adsorption effect than fly ash.Under the optimal conditions（dosage of microspheres was 0.20 g，pH of solution was 5，initial mass concentration of Cu²⁺ was 100 mg/L，volume of solution was 100 mL，adsorption temperature was 40 ℃，and adsorption time was 24 h），the adsorption capacity of Cu²⁺ by microspheres was 45.62 mg/g，and the removal rate was 91.46%.The adsorption process was followed the pseudo-second-order kinetic equation.

Key words: fly ash, geoploymer, microspheres, adsorption, Cu²⁺

中图分类号:

李巧云,贺艳. 粉煤灰基地质聚合物微球吸附水中铜（Ⅱ）的研究[J]. 无机盐工业, 2022, 54(12): 113-118.

LI Qiaoyun,HE Yan. Study on adsorption of Cu²⁺ in water by fly ash-based geopolymer microspheres[J]. Inorganic Chemicals Industry, 2022, 54(12): 113-118.

图/表 10

表1

图1

图2

图3

图4

图5

图6

图7

图8

图9

参考文献 16

1	王夏芳. 铜离子对环境危害现状及对策研究[J]. 国土与自然资源研究, 2015(1)：55-57.
	WANG Xiafang. The dangers of copper ions on the environment and research on countermeasure[J]. Territory ＆ Natural Resour-Study ces, 2015(1)：55-57.
2	AWUAL M R. Novel ligand functionalized composite material for efficient copper（Ⅱ） capturing from wastewater sample[J]. Composites Part B：Engineering, 2019, 172: 387-396.
3	廖妮. 磁性硅藻土的制备及对铜离子的吸附能力研究[J]. 化学工程与装备, 2019(3)：13-15.
	LIAO Ni. Study on preparation of magnetic diatomite and its adsorption capacity for copper ions[J]. Chemical Engineering & Equi-pment, 2019(3)：13-15.
4	葛圆圆. 偏高岭土地质聚合物基重金属离子吸附剂的制备及其性能研究[D].南宁：广西大学, 2015.
	GE Yuanyuan. Fabrication of metakaolin geopolymer-based adsorbents and their applied performance for heavy metal retention[D].Nanning：Guangxi University, 2015.
5	KENG P S, LEE S L, HA S T, et al. Removal of hazardous heavy metals from aqueous environment by low-cost adsorption materials[J]. Environmental Chemistry Letters, 2014, 12(1)：15-25.
6	SUTIRMAN Z A, RAHIM E A, SANAGI M M, et al. New efficient chitosan derivative for Cu（Ⅱ） ions removal：Characterization and adsorption performance[J]. International Journal of Biological Mac- romolecules, 2020, 153: 513-522.
7	李巧云, 贺艳, 徐梦雪, 等. 地质聚合物基无机膜去除水中钙、镁离子的研究[J]. 功能材料, 2017, 48(1)：1215-1220.
	LI Qiaoyun, HE Yan, XU Mengxue, et al. Study on the removal of Ca²⁺ and Mg²⁺ in water by the geopolymer-based inorganic membrane[J]. Journal of Functional Materials, 2017, 48(1)：1215-1220.
8	唐青. 悬浮固化法制备球形地质聚合物的研究及应用[D]. 南宁：广西大学, 2018.
	TANG Qing. Studies on preparation of spherical geopolymer using suspension solidification and its application[D].Nanning：Guan-gxi University, 2018.
9	SU Qiaoqiao, YANG Sijie, HE Yan, et al. Prepared self-growing supported nickel catalyst by recovering Ni（Ⅱ） from metal wastewater using geopolymer microspheres[J]. Journal of Hazardous Materials, 2020, 389.Doi：10.1016/j.jhazmat.2019.121919 . doi: 10.1016/j.jhazmat.2019.121919
10	SU Qiaoqiao, YE Quan, DENG Liang, et al. Prepared self-growth supported copper catalyst by recovering Cu（Ⅱ） from wastewater using geopolymer microspheres[J]. Journal of Cleaner Production, 2020, 272.Doi：10.1016/j.jclepro.2020.122571 . doi: 10.1016/j.jclepro.2020.122571
11	唐青, 崔学民, 贺艳, 等. 地质聚合物及其在重金属废水处理中的应用[J]. 现代技术陶瓷, 2016, 37(4)：253-269.
	TANG Qing, CUI Xuemin, HE Yan, et al. Geopolymer：research progress and its applications in removing heavy metal from water[J]. Advanced Ceramics, 2016, 37(4)：253-269.
12	李巧云. 偏高岭土基地质聚合物无机膜的制备及其对自来水的处理[D]. 南宁：广西大学, 2017.
	LI Qiaoyun. Preparation of metakaolin-based geopolymer inorganic membrane and its treatment for tap water[D]. Nanning：Guangxi University, 2017.
13	苏俏俏. 地聚物基吸附剂与催化剂载体微球回收利用重金属的研究[D].南宁：广西大学, 2020.
	SU Qiaoqiao. Study of recovery and utilization of heavy metal by adsorbent and catalyst supports microspheres from geopolymer[D].Nanning：Guangxi University, 2020.
14	WU Qiong, CHEN Jie, CLARK M, et al. Adsorption of copper to different biogenic oyster shell structures[J]. Applied Surface Science, 2014, 311: 264-272.
15	王英明, 姜亮, 董彦博, 等. 粉煤灰基地质聚合物制备及其对Cu²⁺的吸附性能[J]. 洁净煤技术, 2018, 24(5)：120-125, 131.
	WANG Yingming, JIANG Liang, DONG Yanbo, et al. Preparation condition and Cu²⁺ adsorption properties of fly ash based geopolymer[J]. Clean Coal Technology, 2018, 24(5)：120-125, 131.
16	于岩. 新型水相吸附材料[M].北京：科学出版社, 2016.

[1]	赵飞燕, 张小东, 杜艳霞, 王强, 李小燕. 粉煤灰陶粒的制备技术及研究进展[J]. 无机盐工业, 2024, 56(4): 16-23.
[2]	李快, 栗照帅, 董庭轩, 李丹, 郭生伟, 韩凤兰. 湿法磁选对粉煤灰中铁和重金属元素的分布影响研究[J]. 无机盐工业, 2024, 56(4): 98-104.
[3]	徐梦瑶, 张欣, 何琨鹏, 何坚, 蒋炜. 锆钇废料制备氧化钇和磷酸锆吸附剂及其性能评价[J]. 无机盐工业, 2024, 56(3): 116-124.
[4]	李巧云, 黄修行, 韦文业, 陈振. 活性炭协同酸/碱改性粉煤灰对亚甲基蓝的吸附研究[J]. 无机盐工业, 2024, 56(3): 131-136.
[5]	赵闯, 陈自浩, 张博宇, 李犇, 靳凤英, 李滨, 孙振海, 郭春垒. 分子筛吸附剂对不同类型柴油吸附分离性能的研究[J]. 无机盐工业, 2024, 56(3): 80-85.
[6]	贺翌鹏, 熊晨曦, 王一平, 李军, 金央. 室温制备铁基有机金属框架吸附三价砷的研究[J]. 无机盐工业, 2024, 56(2): 111-120.
[7]	李阳, 娄飞健, 隋鑫, 李克艳, 刘飞, 郭新闻. 氨基功能化气相二氧化硅材料的制备及其吸附二氧化碳性能研究[J]. 无机盐工业, 2024, 56(2): 38-43.
[8]	柳富杰, 何倩, 苏龙, 蒋才云. 海藻酸钠表面功能化磁性生物炭对亚甲基蓝的吸附特性[J]. 无机盐工业, 2024, 56(2): 65-73.
[9]	张丽, 张丹, 潘红艳, 董永刚, 李文飞, 秦红. 磷酸法低灰分活性炭的制备研究[J]. 无机盐工业, 2024, 56(2): 95-103.
[10]	严振, 邱兆富, 金锡标, 王远, 刘畅, 杨骥. 4A分子筛负载Ce和γ-Fe₂O₃去除水中Sb（Ⅲ）和Sb（Ⅴ）的研究[J]. 无机盐工业, 2024, 56(1): 81-89.
[11]	王梦迪, 罗瑾, 吴巍, 周靖辉, 王静, 孙彦民, 于海斌. 微反应法制备γ-Al₂O₃及其对甲基橙的吸附性能研究[J]. 无机盐工业, 2023, 55(9): 66-74.
[12]	周世奇, 王涛, 敬方梨, 罗仕忠. 硝酸镁改性碳分子筛分离氮气/甲烷的性能研究[J]. 无机盐工业, 2023, 55(9): 75-80.
[13]	李超, 王丽萍, 戴崟, 高桂梅, 张云峰, 洪雨, 许立军, 崔永杰. 高硅渣碱熔水热合成13X分子筛及吸附铅铜锌离子研究[J]. 无机盐工业, 2023, 55(9): 88-93.
[14]	杨博, 梁志燕, 刘文元, 曹嘉真, 刘昕玥, 邢明阳. 钼基催化材料在水污染控制领域的应用研究进展[J]. 无机盐工业, 2023, 55(8): 1-12.
[15]	王颖南, 绳琳琳, 黄娟, 黄占斌. 燃煤炉渣吸附水中铅的性能研究[J]. 无机盐工业, 2023, 55(8): 109-115.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会