废铅酸蓄电池中二氧化铅还原技术研究进展

摘要/Abstract

摘要： 废铅酸蓄电池中的二氧化铅（PbO2）是一种两性氧化物，主要呈酸性，性质比较稳定，难以回收利用，但其含量仅次于硫酸铅，其还原回收率对铅的总回收率具有重大影响，使得人们对废铅酸蓄电池中二氧化铅的还原技术愈加重视。对国内外废铅酸蓄电池回收技术中二氧化铅的还原方法及研究现状进行了综述，分析了各种方法的优缺点，指出湿法还原优于火法还原，尤其是用草酸还原二氧化铅的方法比较理想，对环境无污染，并具有工业应用价值，值得做进一步的试验研究。

关键词: 废铅酸蓄电池, 二氧化铅, 还原

Abstract: The PbO2 in spent lead acid battery is an amphoteric compound with prevalent acidic properties.It′s difficult to be recycled because of its stability.But the reduction rate of PbO2 has a significant influence on the total recycle rate of Pb in the spent lead acid battery because the content of PbO2 is only less than PbSO4.Therefore，more attention has been paid to the reduction technology of PbO2 in the spent lead acid battery.The methods to reduce PbO2 in the process of recycling spent lead acid battery and present study status were reviewed.The advantages and disadvantages of each method were analyzed.It was indicated that hydrometallurgical reduction was much better than pyrometallurgical reduction，especially the method of reducing lead dioxide by oxalic acid which was no pollution to the environment and had high value in industrial application was more ideal and worth further experimental investigation.

Key words: spent lead acid battery, PbO2, reduction

中图分类号:

TQ134.33

邱德芬, 柯昌美, 王茜, 陈珊, 刘芳芳. 废铅酸蓄电池中二氧化铅还原技术研究进展[J]. 无机盐工业, 2014, 46(3): 15-.

QIU De-Fen, KE Chang-Mei, WANG Qian, CHEN Shan, LIU Fang-Fang. Research progress of reduction technology for PbO2 from spent lead acid battery[J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(3): 15-.

[1]	龚鹏,张兵,刘思浩. 失活商用SCR催化剂的再生与资源化利用现状[J]. 无机盐工业, 2021, 53(1): 14-17.
[2]	李建生,于韶梅,王欣,祖晓冬,刘炳光. 石墨烯制备中的无机氧化剂和无机还原剂[J]. 无机盐工业, 2020, 52(8): 6-10.
[3]	王珏,石启福,周骏宏,赵增懿,王富龙. 亚磷酸镁制备初步研究[J]. 无机盐工业, 2020, 52(6): 50-53.
[4]	王冬斌,梁精龙,邓孝纯,王晶. 锂资源提取与回收及锂制备工艺研究现状[J]. 无机盐工业, 2020, 52(6): 8-12.
[5]	张晓,程婷,陈晨,王津南,陈刚,邓琴,王磊. 紫外/亚硫酸钠体系对2,4,6-三溴酚的脱溴效果及机理[J]. 无机盐工业, 2020, 52(12): 69-74.
[6]	陈猛,杨万亮,段英男,田蒙奎. CuO@HHSS催化剂制备及催化还原对硝基苯酚性能[J]. 无机盐工业, 2020, 52(12): 92-97.
[7]	张岩岩,刘永鹤,李东红,王毅. 氮化铝粉末的制备及扩大实验研究[J]. 无机盐工业, 2020, 52(11): 56-59.
[8]	李朴芳,穆林,王社斌. 碳热还原/熔融分离废SCR催化剂中有价金属[J]. 无机盐工业, 2020, 52(1): 93-98.
[9]	李积升1，2，魏明2. 以天青石矿为原料生产高纯硫酸锶工艺研究[J]. 无机盐工业, 2019, 51(12): 61-64.
[10]	韩佳锡，蓝邦，周子昊，余林，孙明. 亚铁离子刻蚀α-MnO2纳米棒的制备及其氧还原性能的研究[J]. 无机盐工业, 2019, 51(11): 73-77.
[11]	李书文，周严，汪铁林. BiVO4/rGO复合物的制备及其光催化还原CO2研究[J]. 无机盐工业, 2019, 51(11): 82-87.
[12]	刘冠良，刘鹏，余林，孙明，程高. 氮掺杂科琴黑碳材料的制备及电催化氧还原性能研究[J]. 无机盐工业, 2019, 51(10): 84-88.
[13]	邓月, 魏光涛, 李仲民, 王艺志, 邵鲁华, 龙影红, 张琳叶. 氢氛还原法制备氧化铁/膨润土复合材料及其表征研究[J]. 无机盐工业, 2016, 48(8): 30-.
[14]	田喜强, 赵东江, 马松艳, 迟彩霞, 董艳萍, 田军, 乔秀丽. NiCo2S4化合物对氧还原的电催化性能[J]. 无机盐工业, 2016, 48(8): 74-.
[15]	张翔, 段建榜, 李瑞歌, 陈淼, 卢艳洁. 炼钙还原渣和煤矸石制备聚合氯化铝的研究[J]. 无机盐工业, 2016, 48(4): 66-.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会