CuO@HHSS催化剂制备及催化还原对硝基苯酚性能

doi:10.11962/1006-4990.2020-0424

摘要/Abstract

摘要：

在水热合成复合二氧化硅空心球（HHSS）基础上,以硝酸铜为原料,采用超声辅助浸渍法制备出高分散CuO@HHSS复合催化剂。采用X射线衍射（XRD）、氮气吸附-脱附、X射线光电子能谱（XPS）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）等表征手段对合成催化剂的形貌和结构进行了表征。结果表明：CuO@HHSS催化剂依然保持HHSS的层次纳米中空结构;CuO颗粒高度分散在HHSS表面,而且复合催化剂具有较高的比表面积（488.9 m²/g）。以对硝基苯酚（4-NP）的催化还原反应作为反应模型,考察了CuO和CuO@HHSS催化剂对4-NP还原的催化性能。结果表明：在不同对硝基苯酚浓度下CuO@HHSS展现出优异的催化性能,在200 s内催化硼氢化钠（NaBH₄）将4-NP转化为对氨基苯酚（4-AP）。

关键词: CuO@HHSS, 高分散, 比表面积, 对硝基苯酚, 催化还原

Abstract:

On the basis of preparing hollow silica sphere（HHSS） by hydrothermal method,CuO@HHSS composite catalysts were prepared with copper nitrate as raw material by ultrasonic assisted-impregnation method.The morphology and structure of the prepared catalyst were characterized by means of X-ray diffraction（XRD）,nitrogen adsorption and desorption,X-ray photoelectron spectroscopy（XPS）,scanning electron microscopy（SEM） and transmission electron microscopy（TEM） etc..Results showed that the CuO@HHSS catalyst still maintained the hierarchical nano hollow structure of HHSS.CuO particles were highly dispersed on the HHSS surface,which showed a high specific surface area（488.9 m²/g）.The catalytic reduction reaction of p-nitrophenol（4-NP） was used as a model reaction to investigate the catalytic performance of CuO and CuO@HHSS catalysts for reduction of 4-NP.The results revealed that CuO@HHSS had excellent catalytic performance at different 4-NP concentrations and catalyze NaBH₄ to convert 4-NP to p-aminophenol（4-AP） within 200 s.

Key words: CuO@HHSS, highly dispersed, high specific surface area, p-nitrophenol, catalytic reduction

中图分类号:

TQ131.21

陈猛,杨万亮,段英男,田蒙奎. CuO@HHSS催化剂制备及催化还原对硝基苯酚性能[J]. 无机盐工业, 2020, 52(12): 92-97.

Chen Meng,Yang Wanliang,Duan Yingnan,Tian Mengkui. Preparation of CuO@HHSS catalyst and its catalytic properties for reduction of p-nitrophenol[J]. Inorganic Chemicals Industry, 2020, 52(12): 92-97.

图/表 12

图1

图2

图3

图4

表1

图5

图6

图7

图8

表2

表3

表4

参考文献 20

[1]	李俊生, 徐靖, 罗建武, 等. 硝基苯环境效应的研究综述[J]. 生态环境学报, 2009,18(2):771-776.
[2]	Zhang Z, Shao C, Zou P, et al. In situ assembly of well-dispersed gold nanoparticles on electrospun silica nanotubes for catalytic reduction of 4-nitrophenol[J]. Chemical Communications, 2011,47(13):3906-3908. pmid: 21336412
[3]	李菁, 张颖, 韩恩山, 等. 氧化铜作锂离子电池负极材料的制备及性能研究[J]. 无机盐工业, 2013,45(2):60-62.
[4]	Hong Q, Cao Y, Xu J, et al. Self-powered ultrafast broadband photo-detector based on p-n heterojunctions of CuO/Si nanowire array[J]. ACS Applied Materials & Interfaces, 2014,6(23):20887-20894. doi: 10.1021/am5054338 pmid: 25383662
[5]	Rahman M M, Ahammad A J S, Jin J, et al. A comprehensive review of glucose biosensors based on nanostructured metal-oxides[J]. Sensors, 2010,10(5):4855-4886. doi: 10.3390/s100504855 pmid: 22399911
[6]	Zabilskiy M, Djinovic P, Erjavec B, et al. Small CuO clusters on CeO₂ nanospheres as active species for catalytic N₂O decomposition[J]. Applied Catalysis B:Environmental, 2015,163:113-122.
[7]	Mandlimath T R, Gopal B. Catalytic activity of first row transition metal oxides in the conversion of p-nitrophenol to p-aminophenol[J]. Journal of Molecular Catalysis A:Chemical, 2011,350(1):9-15.
[8]	陶淼, 于少明, 李奈, 等. 高活性氧化铜的制备工艺研究[J]. 无机盐工业, 2016,48(1):31-34.
[9]	Cotea V V, Luchian C E, Bilba N, et al. Mesoporous silica SBA-15,a new adsorbent for bioactive polyphenols from red wine[J]. Analytica Chimica Acta, 2012,732:180-185. doi: 10.1016/j.aca.2011.10.019 pmid: 22688050
[10]	Fihri A, Cha D, Bouhrara M, et al. Fibrous nano-silica(KCC-1)-supported palladium catalyst:suzuki coupling reactions under sustainable conditions[J]. Chemsuschem, 2012,5(1):85-89. doi: 10.1002/cssc.201100379 pmid: 22086867
[11]	Yang W, Li B. Facile fabrication of hollow silica nanospheres and their hierarchical self-assemblies as drug delivery carriers through a new single-micelle-template approach[J]. Journal of Materials Chemistry B, 2013,1(19):2525-2532. doi: 10.1039/c3tb20086h pmid: 32261053
[12]	Zheng W, Yang W, He G, et al. Facile synjournal of extremely small Ag₃PO₄ nanoparticles on hierarchical hollow silica sphere (HHSS)for the enhanced visible-light photocatalytic property and stability[J]. Colloids and Surfaces A, 2019,571:1-8.
[13]	Yang W, Xiao X, Lu R, et al. Synjournal of novel TiO₂ /BiOCl@HHSS composites and its photocatalytic activity enhancement under simu-lated sunlight[J]. RSC Advances, 2016,6(103):101242-101249.
[14]	Liu M, Wu L, Han J, et al. Facile synjournal of palladium nanoparti-cles on hierarchical hollow silica spheres and its catalytic proper-ties in suzuki-reaction[J]. Royal Society Open Science, 2018, 5(9):180545. doi: 10.1098/rsos.201184 pmid: 33204472
[15]	Chen M, Cui J, Wang Y, et al. Amine modified nano-sized hierarc-hical hollow system for highly effective and stable oxidative-adso-rptive desulfurization[J]. Fuel, 2020,266:116960.
[16]	Zhang L, Song F, Wu Y, et al. A novel amino and carboxyl functionalized mesoporous silica as an efficient adsorbent for nickel(Ⅱ)[J]. Journal of Chemical and Engineering Data, 2019,64(1):176-188.
[17]	Lv J, Wang A, Ma X, et al. One-pot synjournal of porous Pt-Au nanodendrites supported on reduced graphene oxide nanosheets toward catalytic reduction of 4-nitrophenol[J]. Journal of Materials Chemistry A, 2015,3(1):290-296.
[18]	沈洁, 叶少琛, 金磊, 等. 石墨烯负载钴纳米粒子催化还原4-硝基苯酚[J]. 精细化工, 2019,36(9):1850-1856.
[19]	Huang C, Ye W, Liu Q, et al. Dispersed Cu₂O octahedrons on h-BN nanosheets for p-nitrophenol reduction[J]. ACS Applied Materials & Interfaces, 2014,6(16):14469-14476. doi: 10.1021/am5037737 pmid: 25046693
[20]	Sahoo P K, Panigrahy B, Bahadur D. Facile synjournal of reduced graphene oxide/Pt-Ni nanocatalysts:their magnetic and catalytic properties[J]. RSC Advances, 2014,4(89):48563-48571.

催化剂	比表面积/（m²·g^-1）	孔容/（cm³·g^-1）	平均孔径/nm
CuO	2.1	0.011	—
HHSS	752.6	1.750	9.95
CuO@HHSS	488.9	1.058	7.81
SiO₂	237.2	0.842	14.21
CuO@SiO₂	189.4	0.653	11.26

催化剂	速率常数k₁	t_1/2/s	R²
CuO	0.001 8	385.1	0.983
CuO@HHSS	0.016 0	43.3	0.946
CuO@SiO₂	0.006 0	115.5	0.962

c（4-NP）/（mmol·L^-1）	t/s	c（4-NP）/（mmol·L^-1）	t/s
0.10	200	0.05	80
0.08	140	0.01	20

催化剂	完全反应时间/s	催化剂	完全反应时间/s
CuO@HHSS^本文	200	Cu₂O@h-BV^[19]	720
Co-graphene^[18]	480	RGO/Pt-Ni^[20]	1 080

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会