电导率法快捷高效测定生石灰活性度

doi:10.19964/j.issn.1006-4990.2022-0674

Abstract

Abstract:

In order to overcome the shortcomings of the methods for determining the activity of quicklime by the titration method of hydrochloric acid and the temperature rise rate method，such as the large amount of reagents，restricted conditions and complicated operation，a method for the determination of the conductivity of quicklime activity with less reagents，simple operation and suitable for different activity levels was proposed.The effects of stirring time，stirring speed，solution temperature and the ratio of quicklime to water on the correspondence between the activity of quicklime and the conductivity of the solution were investigated，and the most suitable conditions for the linear relationship between the activity of quicklime and the conductivity were investigated.The results showed that the optimum conditions for the determination of the lime activity were：stirring time of 12 min，solution temperature of 25 ℃，stirring speed of 200 r/min，and the dosage of lime and water of 1 g，1 000 mL.The linear relationship between the lime activity and the solution conductivity was A=（σ-0.565 7）/0.012 46，and the fitted linear correlation coefficient was R²=0.993 1.Compared with the hydrochloric acid titration method specified in the current standard（YB/T 105—2014），this method had the advantages of saving time，drugs，energy consumption and easy operation.The maximum relative deviation between this method and hydrochloric acid titration method was 0.366%，the precision was completely reliable and could be used for industrial promotion.

Key words: lime, calcium oxide, conductivity, activity

CLC Number:

TQ132.32

CHEN Qi, LIAO Dankui, ZHANG Qingnian, YAN Jinsheng, HUANG Yu, CHEN Xiaopeng, TONG Zhangfa. Fast and efficient determination of quicklime activity by conductivity method[J]. Inorganic Chemicals Industry, 2023, 55(9): 114-120.

Figures/Tables 11

Fig.1

Fig.2

Table 1

Fig.3

Table 2

Table 3

Fig.4

Fig.5

Table 4

Fig.6

Table 5

References 20

1	SAKR M， EL-SAWWAF M， AZZAM W，et al.Improvement of shear strength and compressibility of soft clay stabilized with lime columns［J］.Innovative Infrastructure Solutions，2021，6（3）：1-20.
2	ADIGOPULA V K， BOGI REDDY C， GARG A，et al.Laboratory investigation of modified subgrade clay soil mix with steel slag and lime using static and dynamic test approach［J］.International Journal of Geotechnical Engineering，2022，16（10）：1211-1220.
3	ZANIN M， LAMBERT H， DU PLESSIS C A.Lime use and functionality in sulphide mineral flotation：A review［J］.Minerals Engineering，2019，143：105922.
4	YAN Zhiming， LI Zushu， SANJEEV M，et al.Value in use of lime in BOF steelmaking process［J］.Ironmaking & Steelmaking，2022，49（1）：42-48.
5	HATA Y， ISHIHARA M， HIRUMA S，et al.Recent progress in the development of disinfectants from scallop shell-derived calcium oxide for clinical and daily use［J］.Biocontrol Science，2021，26（3）：129-135.
6	吴鹏辉.生石灰与熟石灰在生活垃圾焚烧发电厂的应用研究［J］.中国资源综合利用，2022，40（8）：61-63.
	WU Penghui.Application study of quicklime and slaked lime in domestic waste incineration power plant［J］.China Resources Comprehensive Utilization，2022，40（8）：61-63.
7	QASWAR M， LI Dongchu， HUANG Jing，et al.Interaction of liming and long-term fertilization increased crop yield and phosphorus use efficiency（PUE） through mediating exchangeable cations in acidic soil under wheat-maize cropping system［J］.Scientific Reports，2020，10：19828.
8	BANKOVIĆ-ILIĆ I B， MILADINOVIĆ M R， STAMENKOVIĆ O S，et al.Application of nano CaO-based catalysts in biodiesel synthesis［J］.Renewable and Sustainable Energy Reviews，2017，72：746-760.
9	CAO Mingli， MING Xing， HE Kaiyu，et al.Effect of macro-，micro -and nano-calcium carbonate on properties of cementitious composites：A review［J］.Materials，2019，12（5）：781.
10	MA Jianping， JI Junrong， YASEEN M，et al.A promising strategy for the large-scale preparation of spherical calcium carbonate by efficiently using carbon dioxide［J］.Journal of CO₂ Utilization，2022，63：102136.
11	YANG Aimei， HUANG Zhiqin， ZHU Yong，et al.Preparation of nano-sized calcium carbonate in solution mixing process［J］.Journal of Crystal Growth，2021，571：126247.
12	王耀宣，袁爱群，周泽广，等.球霰石型纳米碳酸钙椭球形颗粒的合成［J］.无机盐工业，2020，52（1）：54-58.
	WANG Yaoxuan， YUAN Aiqun， ZHOU Zeguang，et al.Prepration of vaterite nano-sized CaCO₃ with elipse ball-like［J］.Inorganic Chemicals Industry，2020，52（1）：54-58.
13	常越凡，张慧捷，王珊珊，等.不同粒度纳米碳酸钙的可控制备［J］.无机盐工业，2020，52（12）：29-33.
	CHANG Yuefan， ZHANG Huijie， WANG Shanshan，et al.Controllable preparation of nano-calcium carbonate with different particle sizes［J］.Inorganic Chemicals Industry，2020，52（12）：29-33.
14	颜鑫，卢云峰.轻质系列碳酸钙关键技术［M］.北京：化学工业出版社，2016：42-44.
15	郭汉杰.活性石灰生产理论与工艺［M］.北京：化学工业出版社，2014：188-220.
16	王玉龙，郭临军.石灰活性度酸碱滴定测定法的优化［J］.耐火与石灰，2010，35（6）：13-14.
	WANG Yulong， GUO Linjun.Optimization of acid-base nitration measuring method for lime reactivity［J］.Refractories & Lime，2010，35（6）：13-14.
17	中华人民共和国工业和信息化部.冶金石灰物理检验方法：YB/T 105—2014［S］.北京：冶金工业出版社，2014.
18	郝素菊，张玉柱，蒋武锋，等.温升速率法测定高活性石灰的活性度［J］.冶金分析，2008，28（8）：19-22.
	HAO Suju， ZHANG Yuzhu， JIANG Wufeng，et al.Temperature rising rate method for measurement of activity of high active li-me［J］.Metallurgical Analysis，2008，28（8）：19-22.
19	张宇，祁晓玉，冯梦瑶，等.电导率调控介孔二氧化硅增透膜透过性能的研究［J］.无机盐工业，2022，54（8）：80-84.
	ZHANG Yu， QI Xiaoyu， FENG Mengyao，et al.Study on permeability of mesoporous silica antireflective film regulated by conductivity［J］.Inorganic Chemicals Industry，2022，54（8）：80-84.
20	YANG Lietai， PABALAN R T， JUCKETT M R.Deliquescence relative humidity measurements using an electrical conductivity method［J］.Journal of Solution Chemistry，2006，35（4）：583-604.

搅拌时间/min	R²	搅拌时间/min	R²
6	0.977 7	15	0.983 3
9	0.982 8	18	0.982 3
12	0.984 0

溶液温度/℃	R²	溶液温度/℃	R²
20.0	0.981 5	27.5	0.983 0
22.5	0.982 8	30	0.984 0
25.0	0.985 4

活性度 A_exp./mL	电导率σ/（mS·cm^-1）							式（1）计算值 A_cal_. /mL	绝对偏差/mL	相对偏差/%
活性度 A_exp./mL	1	2	3	4	5	6	平均值	式（1）计算值 A_cal_. /mL	绝对偏差/mL	相对偏差/%
219.0	3.23	3.34	3.28	3.27	3.33	3.30	3.292	218.8	0.2	0.091 3
327.9	4.64	4.65	4.67	4.69	4.47	4.70	4.637	326.7	1.2	0.366 0
403.6	5.61	5.71	5.52	5.50	5.49	5.65	5.580	402.4	1.2	0.297 5

[1]	MAO Shize. Study on microwave roasting-activated coal gangue to improve sulfate corrosion resistance of concrete [J]. Inorganic Chemicals Industry, 2025, 57(3): 86-93.
[2]	WANG Wei, GUO Lihui, REN Siqian, HUA Chunfeng, WU Yuanting, LIU Hulin, WANG Zhao. Study on modification of inorganic activators and their active excitation on sulfur fixing ash [J]. Inorganic Chemicals Industry, 2024, 56(7): 135-142.
[3]	XIANG Quanjin, QUAN Xuejun, LI Li, WANG Haibo, CHEN Xinhong, LI Ping. Formation rules and emission reduction method of sublimed sulfur in acidolysis exhaust gas of titanium concentrate [J]. Inorganic Chemicals Industry, 2024, 56(7): 96-103.
[4]	TU Yanping, BAI Dengxian, CHENG Shukai, XIE Junjie, HUANG Zhiliang, CHEN Guofu. Effect of high temperature modification of mineral powder and quicklime on properties of phosphogypsum cement based materials [J]. Inorganic Chemicals Industry, 2024, 56(6): 94-101.
[5]	DONG Mingzhe, LI Kexin, YE Xiushen, MA Zhen, LI Shengting, LI Quan, WU Zhijian. Study on electrochemical properties of magnesium chloride molten salt hydrates [J]. Inorganic Chemicals Industry, 2024, 56(2): 51-56.
[6]	WANG Jie, ZHAO Xubo, TANG Yong, QIN Lingyi, CHEN Xiaopeng, LIAO Dankui, TONG Zhangfa, WANG Linlin. Preparation and structural characterization of high specific surface area calcium hydroxide by wet digestion of quicklime [J]. Inorganic Chemicals Industry, 2024, 56(12): 104-112.
[7]	WANG Chen, HE Wei, SUN Mengyuan. Research on preparation of nano-bismuth oxide-enhanced chloride/magnesium oxide composites and their thermophysical properties [J]. Inorganic Chemicals Industry, 2024, 56(12): 120-126.
[8]	XU Xijun, LIN Jianfeng, LUO Xiongwei, ZHAO Jingwei, HUO Yanping. Recent progress of NASICON-type Na₁₊_x Zr₂Si _x P_3-_x O₁₂ solid electrolyte for sodium metal batteries [J]. Inorganic Chemicals Industry, 2024, 56(11): 1-14.
[9]	QIN Ye, LIU Chang, HAN Song, WANG Shuo. Study on conductivity of electrolyte in aqueous Zn-Mn battery [J]. Inorganic Chemicals Industry, 2024, 56(11): 132-138.
[10]	LI Qiang, YOU Xiaomin, SHE Xuefeng, JIANG Zeyi, XUE Qingguo, WANG Jingsong. Effect of calcination temperature and carbon structure on compressive strength of CaO-containing carbon pellets [J]. Inorganic Chemicals Industry, 2023, 55(9): 43-49.
[11]	KANG Le, JING Maoxiang, LI Donghong, HU Xinyu, JIA Chunyan. Study on preparation and electrochemical performance of lithium aluminate nanorods modified solid electrolyte [J]. Inorganic Chemicals Industry, 2023, 55(8): 65-70.
[12]	WANG Yue, FANG Guoxiang, ZHANG Daoming, WANG Weicheng. Effect of nanosilica on gelling properties of hydraulic lime [J]. Inorganic Chemicals Industry, 2023, 55(7): 75-80.
[13]	JIA Yuhong, HU Zhongpan, WANG Kunyuan, HAN Jingfeng, WEI Yingxu, LIU Zhongmin. Co anchored on silanol nests of S-1 zeolite for propane dehydrogenation to propylene [J]. Inorganic Chemicals Industry, 2023, 55(5): 121-127.
[14]	ZHANG Xing,XU Jie,WANG Zibing,HOU Peng,HE Long,LIU Huan. Effect of feedstock particle size on kinetics of limestone thermal decomposition reaction [J]. Inorganic Chemicals Industry, 2023, 55(2): 79-84.
[15]	XIONG Shuang, YAN Jinsheng, ZHOU Zhou, ZHOU Baodi, CHEN Xiaopeng, TONG Zhangfa. Effect of reaction conditions of quicklime digestion on properties of calcium hydroxide [J]. Inorganic Chemicals Industry, 2023, 55(12): 50-58.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Fast and efficient determination of quicklime activity by conductivity method

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 11

References 20

Related Articles 15

Metrics

Comments

Recommended 0