片状铋/钒酸铋复合催化剂的制备及其光催化性能

doi:10.11962/1006-4990.2020-0064

摘要/Abstract

摘要：

用溶剂热法合成了一系列不同铋含量的片状铋/钒酸铋（Bi/BiVO₄）复合光催化剂。采用X射线衍射（XRD）、X射线光电子能谱（XPS）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）、紫外-可见漫反射光谱（UV-vis DRS）、电感耦合等离子发射光谱（ICP-OES）、氮气吸附脱附和光电流响应等技术对所制备的催化剂进行了表征。通过氙灯下光催化降解亚甲基蓝的性能来评价样品的光催化活性,实验结果表明铋的自掺杂能显著提高钒酸铋的光催化活性。最后,通过自由基捕获实验对铋/钒酸铋光催化机理进行了探讨。

关键词: 钒酸铋, 复合半导体, 光催化, 染料降解

Abstract:

A series of sheet-like Bi/BiVO₄ composite photocatalysts with different Bi contents were synthesized using solvo-thermal method.The prepared catalysts were characterized by using X-ray diffraction（XRD）,X-ray photoelectron spectro-scopy（XPS）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,ultraviolet-visible diffuse reflec-tion spectroscopy（UV-Vis DRS）,inductively coupled plasma optical emission spectroscopy（ICP-OES）,nitrogen adsorp-tion-desorption analysis and photocurrent response measurements.The photocatalytic performance of the sample was assessed by photodecomposition of methylene blue（MB） under xenon lamp irradiation.The results showed that the photocatalytic ac-tivity of BiVO₄ was enhanced significantly with Bi self-doping.Finally,the photocatalytic reaction mechanism of Bi/BiVO₄ composite was discussed by free radical capture experiments.

Key words: bismuth vanadate, composite semiconductor, photocatalysis, dye degradation

中图分类号:

O643.36

冯飞,李书文,汪铁林,王为国,王存文. 片状铋/钒酸铋复合催化剂的制备及其光催化性能[J]. 无机盐工业, 2021, 53(1): 107-112.

Feng Fei,Li Shuwen,Wang Tielin,Wang Weiguo,Wang Cunwen. Synthesis and photocatalytic performance of sheet-like Bi/BiVO₄ composite catalyst[J]. Inorganic Chemicals Industry, 2021, 53(1): 107-112.

图/表 13

图1

图2

图3

图4

表1

图5

图6

图7

图8

图9

图10

图11

图12

参考文献 22

[1]	Fakhrul R S M, Tau S L, Sufian S, et al. Exploring the role of elec-tron-hole scavengers on optimizing the photocatalytic performance of BiVO₄[J]. Materials Today:Proceedings, 2018,5(10):21703-21709.
[2]	Kudo A, Omori K, Kato H. A novel aqueous process for preparation of crystal form-controlled and highly crystalline BiVO₄ powder from layered vanadates at room temperature and its photocatalytic and photophysical properties[J]. Journal of the American Chemical So-ciety, 1999,121(49):11459-11467.
[3]	Obregón S, Colón G. On the different photocatalytic performance of BiVO₄ catalysts for methylene blue and rhodamine B degradation[J]. Journal of Molecular Catalysis A:Chemica, 2013,376:40-47.
[4]	Wang Min, Wang Qiming, Guo Peizhi, et al. In situ fabrication of nanoporous BiVO₄/Bi₂S₃ nanosheets for enhanced photoelectroche-mical water splitting[J]. Journal of Colloid and Interface Science, 2019,534:338-342.
[5]	Gao Shan, Gu Bingchuan, Jiao Xingchen, et al. Highly efficient and exceptionally durable CO₂ photoreduction to methanol over frees-tanding defective single-unit-cell bismuth vanadate layers[J]. Jour-nal of the American Chemical Society, 2017,139(9):3438-3445.
[6]	Shi Weidong, Yan Yan, Xu Yan. Microwave-assisted synjournal of nano-scale BiVO₄ photocatalysts and their excellent visible-light-driven photocatalytic activity for the degradation of ciprofloxacin[J]. Chemical Engineering Journal, 2013,215/216:740-746.
[7]	Liu Guoshuai, Liu Suwen, Lu Qifang, et al. Synjournal of monoclinic BiVO₄ microribbons by sol-gel combined with electrospinning pro-cess and photocatalytic degradation performances[J]. Journal ofSol-Gel Science and Technology, 2014,70(1):24-32.
[8]	刘利, 王亚飞, 崔文权, 等. 钒酸铋的制备及可见光降解罗丹明B的研究[J]. 无机盐工业, 2013,45(8):60-62.
[9]	Wang Zeli, Huang Xiaolei, Wang Xuesen. Recent progresses in the design of BiVO₄-based photocatalysts for efficient solar water splitt-ing[J]. Catalysis Today, 2019,335:31-38.
[10]	Eda S, Fujishima M, Tada H. Low temperature-synjournal of BiVO₄ nanorods using polyethylene glycol as a soft template and the visi-ble-light-activity for copper acetylacetonate decomposition[J]. Applied Catalysis B:Environmental, 2012,125:288-293.
[11]	Zhu Yunqing, Muhammad W S, Wang Chuanyi. Insight into therole of Ti³+ in photocatalytic performance of shuriken-shaped BiVO₄/TiO_2-x heterojunction[J]. Applied Catalysis B:Environmental, 2017,203:526-532.
[12]	黄文迪, 孙静, 申婷婷, 等. Co-BiVO₄异质结光催化剂的制备及其性能[J]. 化工进展, 2017,36(11):4080-4086.
[13]	Gao Yangqin, Li Yandong, Yang Guoqing, et al. Fe₂TiO₅ as an effi-cient Co-catalyst to improve the photoelectrochemical water spli-tting performance of BiVO₄[J]. ACS Applied Materials & Interfac-es, 2018,10(46):39713-39722.
[14]	Cao Shaowen, Zhen Yin, Barber J, et al. Preparation of Au-BiVO₄ heterogeneous nanostructures as highly efficient visible-light pho-tocatalysts[J]. ACS Applied Materials & Interfaces, 2012,4(1):418-423.
[15]	Zhao Zaiwang, Zhang Wendong, Sun Yanjuan, et al. Bi cocatalyst/Bi₂MoO₆ microspheres nanohybrid with SPR-promoted visible-light photocatalysis[J]. The Journal of Physical Chemistry C, 2016,120(22):11889-11898.
[16]	Jing Qifeng, Feng Xinyan, Zhao Xiaojun, et al. Bi/BiVO₄ chainlike hollow microstructures:synjournal,characterization,and application as visible-light-active photocatalysts[J]. ACS Applied Nano Mate-rials, 2018,1(6):2653-2661.
[17]	Kruk M, Jaroniec M. Gas adsorption characterization of ordered or-ganic-inorganic nanocomposite materials[J]. Chemistry of Materi-als, 2001,13(10):3169-3183.
[18]	Jo W J, Jang J, Kong K, et al. Phosphate doping into monoclinic BiVO₄ for enhanced photoelectrochemical water oxidation activi-ty[J]. Angewandte Chemie International Edition, 2012,51(13):3147-3151.
[19]	Boda M A, Shah M A. Fabrication of ZnFe₂O₄/TiO₂ nanotube array composite to harness the augmented photocurrent density under vi-sible light[J]. Applied Physics A, 2018,124(1):55.
[20]	Huang Zhenfeng, Zou Jijun, Lun Pan, et al. Synergetic promotion on photoactivity and stability of W₁₈O₄₉/TiO₂ hybrid[J]. Applied Catalysis B:Environmental, 2014,147:167-174.
[21]	Fan Dong, Li Qiuyan, Sun Yanjuan, et al. Noble metal-like behavior of plasmonic Bi particles as a cocatalyst deposited on (BiO)₂CO₃ microspheres for efficient visible light photocatalysis[J]. ACS Ca-talysis, 2014,4(12):4341-4350.
[22]	Jing Qifeng, Feng Xinyan, Pan Jiangling, et al. Facile synjournal Bi/BiVO₄ composite ellipsoids with highphotocatalytic activity[J]. Dalton Transactions, 2018,47(8):2602-2609.

催化剂	比表面积/ （m²·g^-1）	孔容/ （cm³·g^-1）	孔径/ nm	n（Bi）/n（V）
BiVO₄	13.708 0	0.082 696	24.144 32	1.21
2-BiVO₄	13.731 1	0.079 239	22.263 1	—
3-BiVO₄	13.782 2	0.073 714	21.406 57	—
4-BiVO₄	9.872 8	0.049 779	20.196 73	1.37

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会