水热法可控制备NiMoO4纳米片微球及其超级电容器性能

doi:10.19964/j.issn.1006-4990.2021-0249

摘要/Abstract

摘要：

以硝酸镍和钼酸钠为原料,聚乙烯吡咯烷酮为结构导向剂,采用水热-热处理方法在镍网基底上制备了NiMoO₄纳米片微球。通过XRD、Raman、SEM以及TEM测试表征了所得NiMoO₄纳米片微球的结构与形貌。测试结果表明,三维微/纳分级结构的β-NiMoO₄纳米片微球的直径范围为2.3~3.0 μm,且纳米片微球是由厚度约为16 nm的纳米片相互交错而成。研究分析了β-NiMoO₄纳米片微球的生长机理。电化学测试结果表明,NiMoO₄纳米片微球电极在6 mol/L KOH电解液中、1 A/g电流密度下的比电容高达1 161.8 F/g,这可归因于其独特的三维微/纳分级结构在电荷存储过程中可提供更多的氧化还原反应活性位点。另外,NiMoO₄纳米片微球电极的分级结构可减缓充放电循环过程中的体积变化,保持结构的稳定性,使其在20 A/g大电流密度下,循环2 000次后的电容保持率为82.2%,展现出良好的循环性能。

关键词: NiMoO₄纳米片微球, 结构导向, 超级电容器, 电化学性能

Abstract:

NiMoO₄ nanosheets-based microspheres were successfully fabricated on nickel foam substrate through hydro-thermal method combined with an annealing post-treatment,using nickel nitrate and sodium molybdate as raw materials and polyvinyl pyrrolidone as structure directing agent.The structure and morphology of the obtained NiMoO₄ nanosheets-based microspheres were characterized by XRD,Raman,SEM and TEM.The test results showed that the β-NiMoO₄ nanosheets-based microspheres with three-dimensional micro/nano hierarchical structure and a diameter of 2.3~3.0 μm,was consisted of numerous interlaced nanosheets with thickness of about 16 nm.The growth mechanism of β-NiMoO₄ nanosheets-based mi-crospheres was studied.Electrochemical tests showed NiMoO₄ nanosheets-based microspheres electrode exhibited high spe-cific capacitance of 1 161.8 F/g at current density of 1 A/g in 6 mol/L KOH electrolyte,which was attributed to the unique features of three-dimensional micro/nano hierarchical structure that could provide more redox active sites during the charge storage process.Additionally,this hierarchical structure of NiMoO₄ nanosheets-based microspheres electrode could alleviate the volume variation during the charge/discharge cycling process and maintain the stability of the structure.Thus,NiMoO₄ na-nosheets-based microspheres electrode showed a capacitance retention of 82.2% after 2 000 cycles at a large current density of 20 A/g,indicating good cycling stability.

Key words: NiMoO₄ nanosheets-based microspheres, structure directing, supercapacitors, elctrochemical performance

中图分类号:

TQ138.1

赵志超,王洪林,王侠,孙刚,赵翠莲,孙楠楠. 水热法可控制备NiMoO₄纳米片微球及其超级电容器性能[J]. 无机盐工业, 2022, 54(2): 60-64.

ZHAO Zhichao,WANG Honglin,WANG Xia,SUN Gang,ZHAO Cuilian,SUN Nannan. Controllable preparation of NiMoO₄ nanosheets-based microspheres by hydrothermal method and their supercapacitor properties[J]. Inorganic Chemicals Industry, 2022, 54(2): 60-64.

图/表 5

图1

图2

图3

图4

图5

参考文献 19

[1]	SIMON P, GOGOTSI Y. Perspectives for electrochemical capacitors and related devices[J]. Nature Materials, 2020, 19(11):1151-1163. doi: 10.1038/s41563-020-0747-z
[2]	LI J, HAN K, WANG D, et al. Fabrication of high performance struc-tural N-doped hierarchical porous carbon for supercapacitors[J]. Carbon, 2020, 164:42-50. doi: 10.1016/j.carbon.2020.03.044
[3]	GAO X, LIU X, WU D, et al. Significant role of Al in ternary layered double hydroxides for enhancing electrochemical performance of fl-exible asymmetric supercapacitor[J]. Advanced Functional Materi-als, 2019, 29(36).Doi: 10.1002/adfm.201903879. doi: 10.1002/adfm.201903879
[4]	罗惜情, 王同振, 江苗苗, 等. 二硫化镍/氢氧化镍空心球的制备及其电容器性能研究[J]. 无机盐工业, 2019, 51(12):35-38.
[5]	HUANG J, XIAO Y, PENG Z, et al. Co₃O₄ supraparticle-based bub-ble nanofiber and bubble nanosheet with remarkable electrochemi-cal performance[J]. Advanced Science, 2019, 6(12).Doi: 10.1002/advs.201900107. doi: 10.1002/advs.201900107
[6]	CHEN Y, CAI K, LIU C, et al. High-performance and breathable po-lypyrrole coated air-laid paper for flexible all-solid-state supercapa-citors[J]. Advanced Energy Materials, 2017, 7(21).Doi: 10.1002/aenm.201701247. doi: 10.1002/aenm.201701247
[7]	WANG T, CHEN H C, YU F, et al. Boosting the cycling stability of transition metal compounds-based supercapacitors[J]. Energy Stor-age Materials, 2019, 16:545-573.
[8]	PENG S, LI L, WU H B, et al. Controlled growth of NiMoO₄ nanosheet and nanorod arrays on various conductive substrates as advanced electrodes for asymmetric supercapacitors[J]. Advanced Energy Ma-Materials, 2015, 5(2).Doi: 10.1002/aenm.201401172. doi: 10.1002/aenm.201401172
[9]	CHEN D, LU M, LI L, et al. Hierarchical core-shell structural NiMoO₄@NiS₂/MoS₂ nanowires fabricated via an in situ sulfurization method for high performance asymmetric supercapacitors[J]. Journal of Ma-terials Chemistry A, 2019, 7(38):21759-21765.
[10]	ZHOU G, XU L, HU G, et al. Nanowires for electrochemical energy storage[J]. Chemical Reviews, 2019, 119(20):11042-11109. doi: 10.1021/acs.chemrev.9b00326
[11]	HUANG J, PENG Z, XIAO Y, et al. Hierarchical nanosheets/walls structured carbon-coated porous vanadium nitride anodes enable wide-voltage-window aqueous asymmetric supercapacitors with high energy density[J]. Advanced Science, 2019, 6(16).Doi: 10.1002/advs.201900550. doi: 10.1002/advs.201900550
[12]	MONEEB A M, ALABDULRAHMAN A M, BAGABAS A A, et al. Bimetallic single-source precursor for the synjournal of pure nano-crystalline room temperature-stabilized β-NiMoO₄[J]. Ceramics International, 2016, 42(1):1366-1372. doi: 10.1016/j.ceramint.2015.09.076
[13]	CAO Z, ZHANG D J, XU C Y, et al. A novel enzyme-free glucose sensor based on nicke[J]. International Journal of Electrochemical Science, 2015, 10:3152-3159.
[14]	JOTHI P R, SHANTHI K, SALUNKHE R R, et al. Synjournal and characterization of α-NiMoO₄ nanorods for supercapacitor-applica-tion[J].European Journal of Inorganic Chemistry, 2015(22):3694-3699.
[15]	JOTHI P R, KANNAN S, G V.Enhanced methanol electro-oxida-tion over in-situ carbon and graphene supported one dimensional NiMoO₄ nanorods[J]. Journal of Power Sources, 2015, 277:350-359. doi: 10.1016/j.jpowsour.2014.11.137
[16]	徐斌, 余林, 叶文锦, 等. 不同形貌二氧化锰的制备及其电化学性能研究[J]. 无机盐工业, 2017, 49(10):42-45.
[17]	CHEN Y, CHEN Y, HU P, et al. The effects of PVP surfactant in the direct and indirect hydrothermal synjournal processes of ceria nano-structures[J]. Ceramics International, 2016, 42(16):18516-18520. doi: 10.1016/j.ceramint.2016.08.189
[18]	WANG C, XI Y, HU C, et al. β-NiMoO₄ nanowire arrays grown on carbon cloth for 3D solid asymmetry supercapacitors[J]. RSC Ad- vances, 2015, 5(129):107098-107104.
[19]	张硕嘉, 杨玉彬, 唐宇, 等 .高活性 Fe₂O₃@Ni复合电极制备及电化学性能研究[J]. 无机盐工业, 2019, 51(7):24-27.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会

水热法可控制备NiMoO₄纳米片微球及其超级电容器性能

Controllable preparation of NiMoO₄ nanosheets-based microspheres by hydrothermal method and their supercapacitor properties

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 5

参考文献 19

相关文章 15

Metrics

本文评价

推荐阅读 10

[1]	梁群芳,许雪棠,王凡. 基于阴离子交换反应的NiMn-LDH电极电容性能提升研究[J]. 无机盐工业, 2022, 54(2): 38-44.
[2]	简梦奇,张堃,谢鑫,陈锡勇. 磷酸锰锂锂离子电池正极材料研究进展[J]. 无机盐工业, 2021, 53(9): 18-23.
[3]	沈威,王思楠,梁雪梅,韦金云,潘玉洁,农甜甜,周燕,谭学才,黄在银. 纳米MOFs及其衍生物在超级电容器中的研究进展[J]. 无机盐工业, 2021, 53(6): 79-86.
[4]	张豪,王立艳,李英奇,肖姗姗,毕菲,赵丽. 泡沫镍表面原位生长纳米花锌钴氢氧化物电极材料及电化学性能研究[J]. 无机盐工业, 2021, 53(5): 61-65.
[5]	王月香,邵兰燕,徐天男,蔡彩红,袁俊生,张英武. 垃圾焚烧飞灰中氯元素存在形态及深度脱氯的研究[J]. 无机盐工业, 2021, 53(5): 78-83.
[6]	李璐,高长青,刘怡琳,王雪,李建生,刘炳光. 氮杂化介孔碳制备方法及在超级电容器中的应用进展[J]. 无机盐工业, 2021, 53(3): 24-29.
[7]	包科杰,路凌然. 新能源汽车电池负极材料的制备与性能研究[J]. 无机盐工业, 2021, 53(3): 54-59.
[8]	程丽群,左付山. 新能源汽车电池用无镁储氢合金的制备与性能研究[J]. 无机盐工业, 2021, 53(11): 71-76.
[9]	张亚锋,李宏伟,赵志坚. 无人机用锂离子电池正极材料Li_1.20Mn_0.54Ni_0.13Co_0.13O₂的Mo⁶⁺掺杂改性研究[J]. 无机盐工业, 2021, 53(11): 81-85.
[10]	佘翔,刘冬梅,李雪. 电动汽车用La-Fe-B储氢合金的制备与电化学性能研究[J]. 无机盐工业, 2021, 53(10): 64-69.
[11]	范庆科,孟庆华,罗凤钰. 汽车锂电池正极材料的制备与性能研究[J]. 无机盐工业, 2021, 53(1): 44-49.
[12]	臧毅华,盛春光,吴巍,刘宗园,李阳,陈赞. 含氟体系合成分子筛膜的研究进展[J]. 无机盐工业, 2020, 52(7): 12-17.
[13]	董丽坤,贾永卿. 石墨烯负载纳米二硫化钴的制备及其在锂离子电池方面的应用研究[J]. 无机盐工业, 2020, 52(7): 55-58.
[14]	李通,史云斌,刘庆彬,何爽. 硒掺杂改性新能源汽车锂电池正极材料的结构与电化学性能[J]. 无机盐工业, 2020, 52(2): 17-22.
[15]	张硕嘉，杨玉彬，唐宇，迟莉萍，徐冰. 高活性Fe2O3@Ni复合电极制备及电化学性能研究[J]. 无机盐工业, 2019, 51(7): 24-27.

首 页