聚氯化铝残渣制备CaFeAl-LDO及其对甲基橙的吸附

doi:10.19964/j.issn.1006-4990.2020-0648

摘要/Abstract

摘要：

采用聚氯化铝生产中的压滤残渣（PACR）制备CaFeAl-LDO吸附剂,对吸附剂的结构、形貌等进行表征,并考察该吸附剂对甲基橙的吸附效果。结果表明,制备的吸附剂焙烧前具有类水滑石的结构,焙烧后其表面变得疏松多孔,有明显的断层及裂痕。BET分析数据显示,CaFeAl-LDO较PACR比表面积增大近1.5倍,FTIR分析也表明CaFeAl-LDO有效融合了Ca-Al和Ca-Fe型吸附剂的特征峰。吸附实验效果表明,CaFeAl-LDO吸附剂最佳焙烧温度为750 ℃,对甲基橙的吸附符合二级吸附动力学模型,吸附后的LDO经高温焙烧后可以循环使用至少5次。

关键词: 聚氯化铝, CaFeAl-LDO, 吸附, 甲基橙

Abstract:

CaFeAl-LDO was prepared by pressure filtration residue（PACR） from polyaluminum chloride production.The structure and morphology of the adsorbent were characterized,and the adsorption effect of adsorbent on methyl orange was investigated.The results showed that the prepared adsorbent had hydrotalcite like structure before calcination,and its surface became loose and porous with obvious faults and cracks after calcination.BET analysis data showed that the specific surface area of CaFeAl-LDO was 1.5 times larger than that of PACR.FTIR also showed that CaFeAl-LDO effectively integrated the characteristic peaks of Ca-Al and Ca-Fe adsorbents.The results of adsorption experiments showed that the best calcination temperature of CaFeAl-LDO adsorbent was 750 ℃,and the adsorption of methyl orange conformed to the second-order adsorp-tion kinetic model,and the CaFeAl-LDO could be recycled for at least 5 times after being calcined at high temperature.

Key words: polyaluminum chloride, CaFeAl-LDO, adsorption, methyl orange

中图分类号:

TQ133.1

韩晓刚,闵建军,顾一飞,刘转年. 聚氯化铝残渣制备CaFeAl-LDO及其对甲基橙的吸附[J]. 无机盐工业, 2021, 53(10): 81-85.

Han Xiaogang,Min Jianjun,Gu Yifei,Liu Zhuannian. Preparation of CaFeAl-LDO from polyaluminum chloride residue and its adsorption for methyl orange[J]. Inorganic Chemicals Industry, 2021, 53(10): 81-85.

图/表 12

表1

图1

图2

图3

表2

图4

图5

图6

图7

图8

表3

图9

参考文献 18

[1]	Ali R M, Hassaan M A, Elkatory M R. Towards potential removal of malachite green from wastewater:Adsorption process optimization and prediction[J]. Materials Science Forum, 2020, 1008:213-221. doi: 10.4028/www.scientific.net/MSF.1008
[2]	Abdelrahman E A. Synjournal of zeolite nanostructures from waste aluminum cans for efficient removal of malachite green dye from aqueous media[J]. Journal of Molecular Liquids, 2018, 253:72-82. doi: 10.1016/j.molliq.2018.01.038
[3]	刘剑, 朱秋香, 谭雄文, 等. 改性活性炭对甲基橙的吸附[J]. 过程工程学报, 2016, 16(2):222-227.
[4]	王恩文, 叶绘英, 余红英. 铝硅酸盐矿物/石墨复合材料吸附甲基橙性能研究[J]. 采矿技术, 2018, 18(4):80-86.
[5]	尚建平, 刘锐, 覃孝平, 等. 改性凹凸棒土负载铜和稀土催化氧化印染废水[J]. 化工进展, 2020, 39(S2):434-439.
[6]	王向辉, 杨雪, 王闯, 等. 改性椰壳生物炭对甲基橙的吸附效果与机制[J]. 科学技术与工程, 2020, 20(27):11371-11377.
[7]	刘剑, 王若瑄, 鄢瑛, 等. Fe-NaA分子筛膜的制备及催化湿式H₂O₂氧化甲基橙溶液[J]. 环境科学学报, 2019, 39(8):2543-2549.
[8]	陈毅挺, 方润, 黄露, 等. 废水中甲基橙的电化学降解[J]. 化工环保, 2018, 38(5):524-528.
[9]	Lu Y S, Zhang Z W, Xu Y F, et al. CaFeAl mixed oxide derived het-erogeneous catalysts for transesterification of soybean oil to biodie-sel[J]. Bioresource Technology, 2015, 190:438-441. doi: 10.1016/j.biortech.2015.02.046
[10]	张璐虹, 唐有根, 张丽, 等. MgAl-LDH吸附甲基橙性能研究[J]. 功能材料, 2012, 43(18):2469-2472.
[11]	兰天石, 徐晶晶, 张钰, 等. MgAl水滑石的制备及其对甲基橙的吸附[J]. 山东化工, 2019, 48(20):23-24.
[12]	韩晓刚, 刘转年, 陆亭伊, 等. 改性聚氯化铝残渣吸附剂制备及其除磷性能[J]. 无机盐工业, 2019, 51(4):59-62.
[13]	韦世强. 铝酸钙渣提取氧化铝的试验研究[J]. 轻金属, 2012(12):9-11.
[14]	Wang B, Li S, Tian S, et al. A new solid base catalyst for the trans-esterification of rapeseed oil to biodiesel with methanol[J]. Fuel, 2013, 104:698-703. doi: 10.1016/j.fuel.2012.08.034
[15]	张冠华, 陈语芙, 孟跃, 等. AuCu/ZnAl-LDO复合光催化剂的制备及其光催化性能[J]. 无机化学学报, 2020, 36(5):875-884.
[16]	Zhang P, Qian G, Xu Z P, et al. Effective adsorption of sodium do-decylsulfate (SDS) by hydrocalumite(CaAl-LDH-Cl) induced by self-dissolution and re-precipitation mechanism[J]. Journal of Colloid & Interface Science, 2012, 367(1):264-271.
[17]	韩晓刚, 刘转年, 陆亭伊, 等. 改性聚氯化铝残渣吸附剂的制备及对亚甲基蓝的吸附[J]. 印染助剂, 2019, 36(6):21-24.
[18]	刘转年, 邵华帆, 韩晓刚, 等. 煤基聚苯胺对苯酚废水的吸附性能和机理研究[J]. 洁净煤技术, 2018, 24(1):136-141.

吸附剂	S_BET/ （m²·g^-1）	S_Langmuir/ （m²·g^-1）	孔容/ （cm³·g^-1）	孔径/ nm
PACR	782.2	964.8	0.47	19.35
CaFeAl-LDO	1161.8	1534.6	0.59	21.50

吸附剂	q_e/ （mg·g^-1）	Lagergren一级动力学			二级动力学
吸附剂	q_e/ （mg·g^-1）	k₁/ （L·min^-1）	q_e.c/ （mg·g^-1）	R²	k₂/ （g·mg^-1·min^-1）	q_e.c/ （mg·g^-1）	R²
CaFeAl- LDO	35.17	0.041 4	33.46	0.968	0.001 7	38.26	0.994
PACR	10.59	0.063 2	7.25	0.896	0.025 8	10.37	0.998

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会