磷酸铁锂废粉硫酸氢钠焙烧回收工艺研究

doi:10.19964/j.issn.1006-4990.2022-0314

摘要/Abstract

摘要：

随着磷酸铁锂电池新能源车产销量迅速增长，如何有效回收废旧磷酸铁锂动力电池并实现有价金属的资源化利用已成为研究热点。提出一种钠盐辅助焙烧磷酸铁锂废粉和水浸回收锂盐的工艺。在氧气气氛中磷酸铁锂废粉与一水硫酸氢钠反应生成硫酸钠锂、磷酸铁、三氧化二铁，然后通过选择性浸出、分离、沉淀得到纯度高达99.58%的磷酸锂、纯度达到99.6%的磷酸铁。对一水硫酸氢钠与磷酸铁锂废粉质量比、氧化焙烧温度、焙烧保温时间和焙烧产物水浸时间等工艺条件进行了研究，结果表明一水硫酸氢钠与磷酸铁锂废粉质量比为1.6、氧化焙烧温度为600 ℃、焙烧保温时间为60 min、焙烧产物室温水浸时间为70 min为最佳回收工艺参数，在此条件下锂离子浸出率为98.7%。该工艺在温和条件下实现了有价金属的选择性回收，有助于废旧磷酸铁锂电池资源化利用。

关键词: 磷酸铁锂废粉, 硫酸氢钠, 焙烧, 回收, 磷酸锂

Abstract:

With the rapid growth of the production and sales of lithium iron phosphate battery new energy vehicles，how to effectively recycle the waste lithium iron phosphate power batteries and realize the resource utilization of their valuable metals has become a research hotspot.The process of sodium salt assisted roasting of lithium iron phosphate waste powder and water leaching to recover lithium salt was proposed.In oxygen atmosphere，lithium iron phosphate waste powder was reacted with NaHSO₄·H₂O to produce LiNaSO₄，FePO₄ and Fe₂O₃，and then Li₃PO₄ with a purity of 99.58% and FePO₄ with a purity of 99.6% were obtained through selective leaching，separation and precipitation.The process conditions such as the mass ratio of NaHSO₄·H₂O to waste LFP（lithium iron phosphate），the oxidative roasting temperature，the roasting holding time and the water immersion time of roasted products were studied.The results showed that the mass ratio of NaHSO₄·H₂O to waste LFP powder was 1.6，oxidative roasting at 600℃ for 60 min，and the roasted product was immersed in water for 70 min at room temperature，which were the best recovery process parameters，and the lithium ion leaching rate was 98.7%.In this process，the selective recovery of valuable metals was realized under mild conditions，which was helpful for the resource utilization of waste lithium iron phosphate batteries.

Key words: waste lithium iron phosphate powder, sodium bisulfate, roasting, recovery, lithium phosphate

中图分类号:

X705

陈昱珏, 张梁军, 旷焕, 蒋漫文, 肖利. 磷酸铁锂废粉硫酸氢钠焙烧回收工艺研究[J]. 无机盐工业, 2023, 55(3): 113-117.

CHEN Yujue, ZHANG Liangjun, KUANG Huan, JIANG Manwen, XIAO Li. Study on roasting and recovery process of waste lithium iron phosphate powder with sodium bisulfate[J]. Inorganic Chemicals Industry, 2023, 55(3): 113-117.

图/表 9

图1

图2

表1

图3

表2

表3

表4

图4

图5

参考文献 20

1	郭举，贾双珠.水热法一步合成磷酸铁锂及其性能研究[J].无机盐工业，2020，52（6）:36-40.
	GUO Ju， JIA Shuangzhu.Study on the one-step hydrothermal synthesis of LiFePO₄ and its properties[J].Inorganic Chemicals Industry，2020，52（6）:36-40.
2	张克杰，陈鹏，谢旺旺，等.磷酸铁锂优缺点及改性研究进展[J].无机盐工业，2018，50（6）:13-17.
	ZHANG Kejie， CHEN Peng， XIE Wangwang，et al.Progress in modification of lithium iron phosphate and its advantages and disadvantages[J].Inorganic Chemicals Industry，2018，50（6）:13-17.
3	吴小龙，王晨麟，陈曦，等.废旧锂离子电池市场规模及回收利用技术[J].环境科学与技术，2020，43（S2）:179-183.
	WU Xiaolong， WANG Chenlin， CHEN Xi，et al.Market scale and recycling technology of waste lithium-ion batteries[J].Environmental Science & Technology，2020，43（S2）:179-183.
4	TAO Shengdong， LI Jian， WANG Lihua，et al.A method for recovering Li₃PO₄ from spent lithium iron phosphate cathode material through high-temperature activation[J].Ionics，2019，25（12）:5643-5653.
5	BI Haijun， ZHU Huabing， ZU Lei，et al.Environment-friendly technology for recovering cathode materials from spent lithium iron phosphate batteries[J].Waste Management & Research:the Journal of the International Solid Wastes and Public Cleansing Association，ISWA，2020，38（8）:911-920.
6	王甲泰，赵段，马莲花，等.锂离子电池正极材料磷酸铁锂的研究进展[J].无机盐工业，2020，52（4）:18-22.
	WANG Jiatai， ZHAO Duan， MA Lianhua，et al.Research progress of LiFePO₄ cathode materials for Li-ion battery[J].Inorganic Chemicals Industry，2020，52（4）:18-22.
7	YANG Yongxia， ZHENG Xiaohong， CAO Hongbin，et al.A closed-loop process for selective metal recovery from spent lithium iron phosphate batteries through mechanochemical activation[J].ACS Sustainable Chemistry & Engineering，2017，5（11）:9972-9980.
8	WANG Mengmeng， LIU Kang， DUTTA S，et al.Recycling of lithium iron phosphate batteries:Status，technologies，challenges，and prospects[J].Renewable and Sustainable Energy Reviews，2022，163.Doi:10.1016/j.rser.2022.112515.
9	WANG Dahui， ZHANG Xiaodong， CHEN Huaijing，et al.Separation of Li and Co from the active mass of spent Li-ion batteries by selective sulfating roasting with sodium bisulfate and water leaching[J].Minerals Engineering，2018，126:28-35.
10	SUN Sen， YU Xiaoping， LI Mingli，et al.Green recovery of lithium from geothermal water based on a novel lithium iron phosphate electrochemical technique[J].Journal of Cleaner Production，2020，247.Doi:10.1016/j.jclepro.2019.119178.
11	LI Huan， XING Shengzhou， LIU Yu，et al.Recovery of lithium，iron，and phosphorus from spent LiFePO₄ batteries using stoichiometric sulfuric acid leaching system[J].ACS Sustainable Chemistry & Engineering，2017，5（9）:8017-8024.
12	高洁，夏永高.一种从废旧磷酸铁锂电池中回收锂的方法以及回收锂和磷酸铁的方法:中国，111675203A[P].2021-12-14.
13	ZHANG Beilei， QU Xin， CHEN Xiang，et al.A sodium salt-assisted roasting approach followed by leaching for recovering spent LiFePO₄ batteries[J].Journal of Hazardous Materials，2022，424.Doi:10.1016/j.jhazmat.2021.127586.
14	LI Haoyu， YE Hua， SUN Mingcang，et al.Process for recycle of spent lithium iron phosphate battery via a selective leaching-precipitation method[J].Journal of Central South University，2020，27（11）:3239-3248.
15	MAHANDRA H， GHAHREMAN A.A sustainable process for selective recovery of lithium as lithium phosphate from spent LiFePO₄ batteries[J].Resources，Conservation and Recycling，2021，175.Doi:10.1016/j.resconrec.2021.105883.
16	魏永刚，曲国瑞，王华，等.一种从废旧锂离子电池中火法回收锂的方法:中国，113061725A[P].2021-07-02.
17	FORTE F， PIETRANTONIO M， PUCCIARMATI S，et al.Lithium iron phosphate batteries recycling:An assessment of current status[J].Critical Reviews in Environmental Science and Technology，2021，51（19）:2232-2259.
18	SHENTU Huajian， XIANG Bo， CHENG Yajun，et al.A fast and efficient method for selective extraction of lithium from spent lithium iron phosphate battery[J].Environmental Technology & Innovation，2021，23.Doi:10.1016/j.eti.2021.101569.
19	王炼，王建波，陈梦君，等.废锂电池破碎及碱浸除铝特性[J].环境科学与技术，2017，40（S2）:102-106.
	WANG Lian， WANG Jianbo， CHEN Mengjun，et al.Shear breaking and Al removing by alkaline leachate for spent lithium batteries[J].Environmental Science & Technology，2017，40（S2）:102-106.
20	蒋伟.二水磷酸铁脱水工艺研究[J].安徽化工，2019，45（3）:59-61.
	JIANG Wei.Dehydration of ferric phosphate dihydrate[J].Anhui Chemical Industry，2019，45（3）:59-61.

样品	各元素质量分数/%
样品	Li	Al	Fe	Cu	P	C	F
LFP废粉	3.47	12.37	26.71	0.12	14.58	4.87	0.29

样品	各元素质量分数/%
样品	Fe	Al	Cu	P	F
水浸渣	43.061 5	0.104 4	0.154 1	15.622 1	0.301 5

样品	主要成分质量分数/%
样品	Li₃PO₄	Al	Fe	Na	SO₄^2-	Cu
磷酸锂产品	99.58	0.008 8	0.006	0.13	0.20	0.000 1

[1]	唐迪,王俊雄,陈稳,季冠军,马骏,周光敏. 退役锂离子电池正极材料直接回收的研究现状和展望[J]. 无机盐工业, 2023, 55(1): 15-25.
[2]	周诗雨,何婷,付彤彤,郭子睿,顾帅,于建国. 退役锂离子电池湿法回收生命周期和经济评价[J]. 无机盐工业, 2023, 55(1): 26-32.
[3]	戎西林,崔葆,黄秋梅,崔美佳,程昊,冯军,黄文艺. 甘蔗渣纤维素基碳气凝胶的制备及吸附性能研究[J]. 无机盐工业, 2022, 54(9): 126-135.
[4]	周蕾,袁永顺,李璐,刘炳光,李建生. 废旧锂离子电池制备锂离子筛及其应用研究进展[J]. 无机盐工业, 2022, 54(8): 33-39.
[5]	丁勇,冯晓锐,鲁相杰,高小琴,冯燕,何艳. 羰基镍粉焙烧制备高纯度微米氧化亚镍粉体的研究[J]. 无机盐工业, 2022, 54(4): 119-122.
[6]	郭春平,周有池,文小强,刘雯雯,洪侃,黄叶钿. 磷酸锂渣制备电池级碳酸锂工艺研究[J]. 无机盐工业, 2022, 54(3): 82-86.
[7]	何婷,孔娇,崔景植,陈志豪,付彤彤,郭子睿,顾帅,于建国. 退役锂离子电池电化学还原浸出及热力学研究[J]. 无机盐工业, 2022, 54(12): 34-43.
[8]	曾彦捷,徐同飞,黄子良,陈志鹏,刘旭东,易美桂. 焙烧-水化络合法脱除镁废渣中钙杂质的研究[J]. 无机盐工业, 2022, 54(11): 118-123.
[9]	孙双双,仲剑初,王洪志. 铜冶炼废渣脱硅工艺研究[J]. 无机盐工业, 2021, 53(9): 83-87.
[10]	张耀滔,李军,陈明,郑卓超. 碱法回收湿法磷酸萃余渣中五氧化二磷的研究[J]. 无机盐工业, 2021, 53(7): 86-91.
[11]	欧健,李天祥,隋岩峰,吴强,黄林川,朱静. 工业含氟废气处理及资源回收的概述[J]. 无机盐工业, 2021, 53(5): 39-46.
[12]	李玉录,周飞,杨萍,冯军强,黄德明,林倩. 硝酸酸解焙烧磷精矿过程五氧化二磷分解率及伴生碘的迁移分布研究[J]. 无机盐工业, 2021, 53(4): 38-42.
[13]	阎振宗,王东. 贵州天柱重晶石回转窑还原焙烧生产工艺研究[J]. 无机盐工业, 2021, 53(4): 73-75.
[14]	贺晓莹,李晨,王鹏飞,蒋凌云,臧甲忠,吴青. 硫化钠沉淀法从含铑溶液中富集铑工艺研究[J]. 无机盐工业, 2021, 53(4): 81-85.
[15]	肖亦寒,曹建新,刘飞,易芸. 焙烧温度对MnZnO_x物化性质及催化性能的影响[J]. 无机盐工业, 2021, 53(4): 95-100.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会