共沸回流法制备α-半水石膏工艺研究

doi:10.19964/j.issn.1006-4990.2021-0597

Abstract

Abstract:

In order to eliminate the harm of by-product gypsum to the environment and improve the utilization value of by-product gypsum，the azeotropic reflux method was used to take industrial waste acid gypsum as raw material to obtain α-hemihydrate gypsum through slurry preparation，azeotropic solvent addition，crystal conversion reaction，and suction drying，and the best synthesis process of α-hemihydrate gypsum was explored.The product was characterized by X-ray diffractometer（XRD） and scanning electron microscope（SEM）.The effects of azeotropic solvent concentration，temperature，solid-liquid ratio，and pH on the conversion process of by-product gypsum，the composition and structure of the conversion product were mainly researched，and the best experimental conditions were obtained through single-factor experiments and orthogonal experiments.The results showed that when the concentration of azeotropic solvent was 70%，the crystal transition temperature was 120 ℃，the solid-to-liquid ratio was 1∶6，the pH was 5，and the reaction time was 3 h，the aspect ratio could be about 1∶1，and flexural resistance could be obtained.The α-hemihydrate gypsum with a strength（2 h） of 5.6 MPa and a drying compressive strength of 43 MPa met the α40 strength grade of JC/T 2038—2010“α-type high-strength gypsum”.

Key words: by-product gypsum, α-hemihydrate gypsum, azeotropic reflux method, azeotropic solvent

CLC Number:

TQ177.373

XU Cheng,SHENG Jiefa,HAO Yuning,WU Binghui,MA Xiaoming,LIU Jianwu,YAN Shenghu,ZHANG Yue. Study on process of preparing α-hemihydrate gypsum by azeotropic reflux method[J]. Inorganic Chemicals Industry, 2022, 54(7): 117-123.

Figures/Tables 21

Table 1

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

Fig.11

Fig.12

Fig.13

Fig.14

Fig.15

Table 2

Table 3

Fig.16

Fig.17

Table 4

References 15

1	崔玉民，殷榕灿.染料废水处理方法研究进展［J］.科技导报，2021，39（18）：79-87.
	CUI Yumin， YIN Rongcan.The progress of treatment methods of dye wastewater［J］.Science & Technology Review，2021，39（18）：79-87.
2	李崇，周俊，刘瑶，等.我国废硫酸产生及综合利用现状［J］.过程工程学报，2018，18（S1）：24-34.
	LI Chong， ZHOU Jun， LIU Yao，et al.Emission and comprehensive utilization of spent sulfuric acid in China［J］.The Chinese Journal of Process Engineering，2018，18（S1）：24-34.
3	卢静昭，赵斌，陈学青，等.利用脱硫石膏制备高品质二水石膏［J］.人工晶体学报，2016，45（1）：97-103.
	LU Jingzhao， ZHAO Bin， CHEN Xueqing，et al.Preparation of the high-quality gypsum by dihydrate FGD［J］.Journal of Synthetic Crystals，2016，45（1）：97-103.
4	杨林，张冰，周杰，等.磷石膏制备α型高强石膏及其转化过程研究［J］.建筑材料学报，2014，17（1）：147-152.
	YANG Lin， ZHANG Bing， ZHOU Jie，et al.Preparation of α-high strength gypsum using phosphogypsum and transformation of phosphogypsum to α-high strength gypsum［J］.Journal of Building Materials，2014，17（1）：147-152.
5	汪潇，曹博伦，金彪，等.添加剂调控半水石膏晶体生长研究进展［J］.硅酸盐学报，2020，48（1）：94-103.
	WANG Xiao， CAO Bolun， JIN Biao，et al.Using additives to control crystal growth of hemihydrate gypsum-A short review［J］.Journal of the Chinese Ceramic Society，2020，48（1）：94-103.
6	胡成，向玮衡，陈平，等.丁二酸对水热合成α-半水脱硫石膏微晶形貌及力学强度的影响［J］.无机盐工业，2021，53（4）：76-80.
	HU Cheng， XIANG Weiheng， CHEN Ping，et al.Effects of succinic acid on crystallite morphology and mechanical strength of α-hemihydrate desulfurized gypsum synthesized by hydrothermal method［J］.Inorganic Chemicals Industry，2021，53（4）：76-80.
7	LU Wenda， MA Baoguo， SU Ying，et al.Preparation of α-hemihydrate gypsum from phosphogypsum in recycling CaCl₂ solution［J］.Construction and Building Materials，2019，214：399-412.
8	陈平，田宇，胡成.盐溶液种类和浓度对α-半水脱硫石膏合成的影响［J］.无机盐工业，2020，52（10）：130-134.
	CHEN Ping， TIAN Yu， HU Cheng.Effect of type and concentration of salt solution on synthesis of α-semi-water desulfurization gypsum［J］.Inorganic Chemicals Industry，2020，52（10）：130-134.
9	LUO Zhao， HAN Fenglan， HUANG Xinhua.Alpha hemihydrate gypsum preparationed by atmospheric pressure salt solution method
	process route［J］.Applied Mechanics and Materials，2013，327：23-27.
10	桂苗苗，丛钢.脱硫石膏蒸压法制α半水石膏的研究［J］.重庆建筑大学学报，2001，23（1）：62-65，81.
	GUI Miaomiao， CONG Gang.Study on the α-hemihydrate gypsum made by desulphogypsum through autoclave process［J］.Journal of Chongqing Jianzhu University，2001，23（1）：62-65，81
11	罗东燕，邱树恒，陈霏，等.用蒸压法将磷石膏制备α半水石膏的研究［J］.新型建筑材料，2015，42（9）：23-26，46.
	LUO Dongyan， QIU Shuheng， CHEN Fei，et al.Preparation of alpha hemihydrate gypsum from phosphogypsum by autoclave met-
	hod［J］.New Building Materials，2015，42（9）：23-26，46.
12	彭家惠，瞿金东，张建新，等.EDTA吸附特性及其对α半水脱硫石膏晶形的影响［J］.材料研究学报，2011，25（6）：566-572.
	PENG Jiahui， QU Jindong， ZHANG Jianxin，et al.Adsorption characteristics of EDTA on α-hemihydrate desulfurization gypsum surface and its influence on crystal morphology［J］.Chinese Journal of Materials Research，2011，25（6）：566-572.
13	LIU Xianfeng， PENG Jiahui， ZHANG Jianxin，et al.Effect of organic diacid carbon chain length on crystal morphology of α-calcium sulfate hemihydrate in preparation from flue gas desulphurization gypsum［J］.Applied Mechanics and Materials，2012，
	253-255：542-545.
14	SHAO Duoduo， ZHAO Bin， GAO Lili，et al.Preparation of whitening dihydrate gypsum and short columnar α-hemihydrate gypsum with FGD gypsum［J］.Crystal Research and Technology，2017，52（9）.Doi：10.1002/crat.201700166 . doi: 10.1002/crat.201700166
15	SUN Xiangbin， ZHANG Genlei， CUI Peng.Aspect ratio-controlled
	preparation of α-CaSO 4·0.5 H₂O from phosphogypsum in potassium tartrate aqueous solution［J］.RSC Advances，2019，9（38）：21601-21607.

水平	因素
水平	A 共沸溶剂体积分数/%	B 反应温度/℃	C 固液比
1	60	110	1∶5
2	70	120	1∶6
3	80	130	1∶7

试验号	因素			转化率/ %
试验号	A	B	C	转化率/ %
1	1	1	1	3.1
2	1	2	2	10.6
3	1	3	3	4.2
4	2	1	2	82.0
5	2	2	3	50.4
6	2	3	1	52.0
7	3	1	3	5.8
8	3	2	1	90.3
9	3	3	2	85.1
K1	17.90	90.90	145.40
K2	184.40	151.30	177.70
K3	181.20	141.30	60.40
k1	5.97	30.30	48.47
k2	61.47	50.43	59.23
k3	60.40	47.10	20.13
极差	55.49	20.13	39.10
优化方案	A₂	B₂	C₂

序号	抗折强度/MPa	抗压强度/MPa
1	5.6	43.0
2	5.4	42.8
3	5.7	43.4
标准	5.0	40.0

[1]	HU Cheng, LIU Meng, XIANG Weiheng, CHEN Ping, WANG Neng, LU Guanju, ZHOU Jinlan. Preparation of α-hemihydrous gypsum from CaCl₂ and MgCl₂ and their composite solution [J]. Inorganic Chemicals Industry, 2024, 56(7): 112-117.
[2]	HU Cheng, LIU Meng, XIANG Weiheng, DUAN Pengxuan, LI Shunkai, MING Yang, WANG Neng, LU Guanju. Effect of NaCl solution concentration on transcrystallization behavior of α-hemihydrate gypsum from phosphogypsum [J]. Inorganic Chemicals Industry, 2024, 56(6): 87-93.
[3]	YANG Fengling, QIAO Guoxin, YANG Pu, REN Lei, WANG Qiong, WU Haibin, CHENG Fangqin. Research progress and application of α-hemihydrate gypsum preparation from desulfurization gypsum [J]. Inorganic Chemicals Industry, 2024, 56(2): 11-20.
[4]	LI Peng, WANG Likun, MENG Qiuyan. Study on effect of α-hemihydrate gypsum on performance of cement mortar and its hydration mechanism [J]. Inorganic Chemicals Industry, 2023, 55(3): 98-103.
[5]	LIU Chao, FAN Chuigang, LIU Runguo, YU Dongxue, LI Songgeng. Preparation of α-hemihydrate gypsum from phosphogypsum by flotation and atmospheric trans-crystallization in solution [J]. Inorganic Chemicals Industry, 2023, 55(11): 107-114.
[6]	LI Yunfei, LIU Shuqing, TANG Shengwei, ZHANG Tao. Preparation of α-hemihydrate gypsum in Mg-Na mixed salt solution system under atmospheric pressure [J]. Inorganic Chemicals Industry, 2023, 55(11): 100-106.
[7]	LI Mingchuan,WEI Jiazhan,CHEN Ping,DUAN Pengxuan. Effect of crystal modifier and autoclave parameters on preparation of α-hemihydrate gypsum from phosphogypsum [J]. Inorganic Chemicals Industry, 2022, 54(8): 132-137.
[8]	JIANG Hanning,LI Yuping,WANG Zhiyun,WEN Huimin,YE Baoquan. Effect of potassium oxalate and aluminum sulfate and their compounds on preparation and properties of α-hemihydrate gypsum [J]. Inorganic Chemicals Industry, 2022, 54(10): 121-126.
[9]	Chen Ping,Tian Yu,Hu Cheng. Effect of type and concentration of salt solution on synthesis of α-semi-water desulfurization gypsum [J]. Inorganic Chemicals Industry, 2020, 52(10): 130-134.
[10]	HE Yu-Xin, HUA Su-Dong, QU Xian. Research progress of gypsum slag green material [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(5): 13-.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on process of preparing α-hemihydrate gypsum by azeotropic reflux method

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 21

References 15

Related Articles 10

Metrics

Comments

Recommended 0