基于阴离子交换反应的NiMn-LDH电极电容性能提升研究

doi:10.19964/j.issn.1006-4990.2021-0223

Abstract

Abstract:

NiMn-LDH nanosheet arrays on Ni foam were synthesized via one-step hydrothermal method,and the capacitive performance was enhanced by soaking the nanoarrays on KOH solution.The as-obtained electrode before and after the soaking process were characterized by SEM,XRD,TEM and XPS technologies.The results showed that the morphology of NiMn-LDH electrode did not change before and after immersion,but anion exchange reaction between CO₃^2- and OH^- anions was occurred in the electrode materials obviously,which reduced the distribution quantity of large CO₃^2- between LDH layers,made the space in the layer become the“reservoir”of OH^-,and reduced the migration distance of OH^- in the charge storage process.Therefore,the capacitance performance had been significantly improved.The electrochemical test results showed that the speci-fic capacitance of the electrode increased from 18.0 F/g to 766.6 F/g（1.69 F/cm²） at the current density of 5 mA/cm².When the power density of the all solid-state asymmetric supercapacitor assembled with the electrode and activated carbon was 900 W/kg,the displayed energy density was 35.9 W·h/kg,and the cycle stability of the device was good.

Key words: NiMn-LDH, electrode activation, supercapacitor, anions exchange reaction.

CLC Number:

TQ138.13

LIANG Qunfang,XU Xuetang,WANG Fan. Study on improvement of capacitance performance of NiMn-LDH electrode material by anions exchange[J]. Inorganic Chemicals Industry, 2022, 54(2): 38-44.

Figures/Tables 8

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Table 1

References 24

[1]	NGUYEN T, MONTEMOR M. Metal oxide and hydroxide-based aqueous supercapacitors:From charge storage mechanisms and functional electrode engineering to need-tailored devices[J]. Adva-nced Science, 2019, 6.Doi: 10.1002/advs.201801797. doi: 10.1002/advs.201801797
[2]	张硕嘉, 杨玉彬, 唐宇, 等. 高活性Fe₂O₃@Ni复合电极制备及电化学性能研究[J]. 无机盐工业, 2019, 51(7):24-27.
[3]	CHOUDHARY N, LI C, MOORE J, et al. Supercapacitors:Asymme-tric supercapacitor electrodes and devices[J]. Advanced Materials, 2017, 29.Doi: 10.1002/adma.201605336. doi: 10.1002/adma.201605336
[4]	赵杰, 郭月, 沈桢, 等. 高倍率容量层状双金属氢氧化物超级电容材料的研究进展[J]. 化工学报, 2020, 71(11):4851-4872.
[5]	王文聪. 层状双金属氢氧化物超级电容器电极材料的制备和电化学性能研究[D]. 杭州:浙江大学, 2019.
[6]	WANG R, YAO M, NIU Z. Smart supercapacitors from materials to devices[J]. InfoMat, 2020, 2:113-125. doi: 10.1002/inf2.v2.1
[7]	朱基亮. 超级电容器用金属层状双氢氧化物电极材料研究进展[J]. 四川师范大学学报:自然科学版, 2020, 43(3):285-296.
[8]	雷娜, 马翩翩. Ni-Co LDHs纳米片阵列用于超级电容器电极的研究[J]. 浙江理工大学学报:自然科学版, 2020, 43(6):58-64.
[9]	XU R, DU L, ADEKOYA D, et al. Well-defined nanostructures for electrochemical energy conversion and storage[J]. Advanced Ener-gy Materials, 2020, 10.Doi: 10.1002/aenm.202001537. doi: 10.1002/aenm.202001537
[10]	李宫, 陈昆峰, 金京一, 等. La³+掺杂NiCo层状双金属氢氧化物纳米片的合成及其电化学性能[J]. 应用化学, 2017(34):71-75.
[11]	LIU H B, LI J C, YE L, et al. Co₁-_x-_yNi_xZn_y(CO₃)_0.5(OH)·0.11H₂O nanoneedles-NiCo-layered double hydroxide nanosheet compos-ites on vulcanized Ni foams for supercapacitors[J]. ACS Applied Nano Materials, 2021, 4(2):1743-1753. doi: 10.1021/acsanm.0c03200
[12]	WANG Y, YAN D, EL HANKARI S, et al. Recent progress on lay-ered double hydroxides and their derivatives for electrocatalytic water splitting[J]. Advanced Science, 2018, 5(8).Doi: 10.1002/advs.201800064. doi: 10.1002/advs.201800064
[13]	WANG X L, ZHANG J Q, YANG S B, et al. Interlayer space regu- lating of NiMn layered double hydroxides for supercapacitors by controlling hydrothermal reaction time[J]. Electrochimica Acta, 2019, 295:1-6. doi: 10.1016/j.electacta.2018.10.021
[14]	TANG Y Q, SHEN H M, CHENG J Q, et al. Fabrication of oxygen-vacancy abundant NiMn-layered double hydroxides for ultrahigh capacity supercapacitors[J]. Advanced Functional Materials, 2020, 30.Doi: 10.1002/adfm.201908223. doi: 10.1002/adfm.201908223
[15]	邹文茹. 阴离子交换法增强Ni-Co基纳米阵列电极性能的研究[D]. 南宁:广西大学, 2019.
[16]	YANG T Y, YE J, CHEN S H, et al. Construction of nanowall-su-pported-nanorod nico ldh array electrode with high mass-loadingon carbon cloth for high-performance asymmetric supercapacitors[J]. Electrochimica Acta, 2020, 362.Doi: 10.1016/j.electacta.2020.137081. doi: 10.1016/j.electacta.2020.137081
[17]	ZANG Y, LUO H, ZHANG H, et al. Polypyrrole nanotube-interco-nnected NiCo-LDH nanocages derived by ZIF-67 for supercapac-itors[J]. ACS Applied Energy Materials, 2021, 4(2):1189-1198. doi: 10.1021/acsaem.0c02465
[18]	LIU X, ZHOU A, PAN T, et al. Ultrahigh-rate-capability of a layered double hydroxide supercapacitor based on a self-generated elec-trolyte reservoir[J]. Journal of Materials Chemistry A, 2016(4):8421-8427.
[19]	WEI M, MA R, WU J, et al. Development of efficient electrocataly-sts via molecular hybridization of NiMn layered double hydroxide nanosheets and graphene[J]. Nanoscale, 2016, 8(19):10425-10432. doi: 10.1039/C6NR00988C
[20]	CHEN D M, YAN S, CHEN H J, et al. Hierarchical Ni-Mn layered double hydroxide grown on nitrogen-doped carbon foams as high-performance supercapacitor electrode[J]. Electrochimica Acta, 2018, 292:374-382. doi: 10.1016/j.electacta.2018.07.042
[21]	YU M, LIU R L, LIU J H, et al. Polyhedral-like NiMn-layered dou-ble hydroxide/porous carbon as electrode for enhanced electroche-mical performance supercapacitors[J]. Small, 2017, 13(44).Doi: 10.1002/smll.201702616. doi: 10.1002/smll.201702616
[22]	CHEN H Y, AI Y N, LIU F, et al. Carbon-coated hierarchical Ni-Mn layered double hydroxide nanoarrays on Ni foam for flexible high-capacitance supercapacitors[J]. Electrochimica Acta, 2016, 213:55-65. doi: 10.1016/j.electacta.2016.06.038
[23]	SUN L, ZHANG Y X, ZHANG Y, et al. Reduced graphene oxide nanosheet modified NiMn-LDH nanoflake arrays for high-perfor-mance supercapacitors[J]. Chemical Communications, 2018, 54(72):10172-10175. doi: 10.1039/C8CC05745A
[24]	XU T, LI G, YANG X, et al. Design of the seamless integrated C@NiMn-OH-Ni₃S₂/Ni foam advanced electrode for supercapaci-tors[J]. Chemical Engineering Journal, 2019, 362:783-793. doi: 10.1016/j.cej.2019.01.083

正极	负极	能量密度/ （W·h·kg^-1）	功率密度/ （W·kg^-1）
a-NiMn LDH	AC	35.9	900.00
NiMn-LDH/NCF^[20]	NCF	34.1	350.10
NiMn-LDH/PC-1^[21]	RGO/CNT	18.6	225.03
NiMn-LDH/PPy/BC^[22]	Fe₃O₄@C/MWCNTs	29.8	299.00
rGO@NiMn-LDH@NF^[23]	AC	22.5	700.00
carbon-NiMn-LDH/NF^[24]	AC	37.7	378.13

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on improvement of capacitance performance of NiMn-LDH electrode material by anions exchange

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 24

Related Articles 15

Metrics

Comments

Recommended 0

[1]	ZHANG Feigang, LIU Zhongli. Study on application of CuO/g-C₃N₄ composites in organic dye degradation and supercapacitors [J]. Inorganic Chemicals Industry, 2025, 57(1): 129-136.
[2]	WU Qingqing, XU Xuetang, WANG Fan. Study on capacitor performance of high⁃mass⁃loading ZnCo-based carbonate hydroxide electrode materials [J]. Inorganic Chemicals Industry, 2024, 56(7): 46-54.
[3]	WANG Jianfang, YANG Heping, LI Kaibin, CONG Shiqiang, ZHANG Bojie, GUO Shan. Study on preparation of C₃N₄/MnCo₂S₄ composites and their capacitive properties [J]. Inorganic Chemicals Industry, 2023, 55(7): 70-74.
[4]	XU Xuetang, WANG Xukai, ZHANG Shenhe, HUANG Meixiang, NONG Shuliu, XU Nuo. Study on preparation and properties of vanadate doped NiCo-LDH electrode [J]. Inorganic Chemicals Industry, 2023, 55(5): 52-58.
[5]	JIANG Tiantian,XU Xuetang,WANG Fan. Research on growth and supercapacitance of NiCo based electrode materials regulated by halogen ions [J]. Inorganic Chemicals Industry, 2022, 54(8): 66-73.
[6]	Zhang Tianliang,Li Jun,Xiong Wei,Zhang Haiyan,Tao Xiaoqiu. Study on one-step preparation of activated carbon with high specific surface by K₂CO₃ activation and its capacitance performance [J]. Inorganic Chemicals Industry, 2022, 54(4): 159-164.
[7]	WANG Dian,SU Qiong,PANG Shaofeng,CAO Shijun,KANG Lihui,LIANG Lichun,WANG Yanbin,LI Zhaoxia. Study on high-performance supercapacitors based on Fe₂O₃/biomass carbon composites [J]. Inorganic Chemicals Industry, 2022, 54(3): 59-65.
[8]	ZHAO Zhichao,WANG Honglin,WANG Xia,SUN Gang,ZHAO Cuilian,SUN Nannan. Controllable preparation of NiMoO₄ nanosheets-based microspheres by hydrothermal method and their supercapacitor properties [J]. Inorganic Chemicals Industry, 2022, 54(2): 60-64.
[9]	YI Jinliang,YANG Min,SONG Fangxiang,CHEN Qianlin. Study on preparation and electrochemical properties of agaric carbon-based cobalt sulfide composites [J]. Inorganic Chemicals Industry, 2022, 54(12): 60-67.
[10]	Shen Wei,Wang Sinan,Liang Xuemei,Wei Jinyun,Pan Yujie,Nong Tiantian,Zhou Yan,Tan Xuecai,Huang Zaiyin. Research progress of nano MOFs and their derivatives for supercapacitors [J]. Inorganic Chemicals Industry, 2021, 53(6): 79-86.
[11]	Wang Yuexiang,Shao Lanyan,Xu Tiannan,Cai Caihong,Yuan Junsheng,Zhang Yingwu. Study on existing speciation and deep dechlorination of chlorine in waste incineration fly ash [J]. Inorganic Chemicals Industry, 2021, 53(5): 78-83.
[12]	Zhang Hao,Wang Liyan,Li Yingqi,Xiao Shanshan,Bi Fei,Zhao Li. Nano-flowered ZnCo LDHs electrode material grown in situ on nickel foam and its electrochemical properties [J]. Inorganic Chemicals Industry, 2021, 53(5): 61-65.
[13]	Zhang Shuojia，Yang Yubin，Tang Yu，Chi Liping，Xu Bing. Synthesis and electrochemical properties of high?鄄activity Fe2O3@Ni composite electrode [J]. Inorganic Chemicals Industry, 2019, 51(7): 24-27.
[14]	Zhao Yu,Zhang Shuojia,Xu Bing,Yu Yue,Sun Xiaohui. Fabrication and electrochemical properties of Zn-based electrode materials [J]. Inorganic Chemicals Industry, 2019, 51(6): 21-24.
[15]	Luo Xiqing，Wang Tongzhen，Jiang Miaomiao，Xiong Fan，Cheng Fengru. Study on preparation of NiS2/Ni（OH）2 hollow spheres and its capacitor performance [J]. Inorganic Chemicals Industry, 2019, 51(12): 35-38.