改性球形活性炭对氨气吸附性能的研究

doi:10.11962/1006-4990.2020-0318

Abstract

Abstract:

The adsorption performance of spherical activated carbon impregnated with different metal salt solutions for ammonia and the optimal ratio of the same impregnant were studied.The influence of different impregnation ratio on the surface morphology, phase structure and pore size distribution on impregnated carbon samples were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and Quanta adsorption instrument.The adsorption performance of the unmodified carbon and impregnated carbon for ammonia was studied by the fixed bed adsorption device.The results showed that the type of impregnant had a great influence on the adsorption performance of ammonia.Under the same impregnation conditions, the activated carbon impregnated with cobalt chloride had the best adsorption performance for ammonia.The sample with 50% impregnation ratio of cobalt chloride had the highest ammonia adsorption capacity up to 54.05 mg/mL, which was 37 times of the unmodified carbon.The physicochemical properties and temperature programmed desorption characteristics of the samples after ammonia adsorption were analyzed.The results showed that[Co（NH₃）₆]Cl₃ was formed by the reaction of cobalt chloride with ammonia.

Key words: spherical activated carbon, cobalt chloride, impregnated carbon, ammonia, adsorption capacity

CLC Number:

O647.32

Jin Qingqing,Liang Xiaoyi,Zhang Jia′nan,Zhou Xiaolong. Study on adsorption performance of modified spherical activated carbon for ammonia[J]. Inorganic Chemicals Industry, 2021, 53(4): 61-66.

Figures/Tables 13

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Table 1

Fig.8

Fig.9

Fig.10

Fig.11

Fig.12

References 17

[1]	Rodrigues C C, de Moraes D, da Nobrega S W , et al. Ammonia adsorption in a fixed bed of activated carbon[J]. Bioresource Technology, 2006,98(4):886-891.
[2]	Petit C, Karwacki C, Peterson G . Interactions of ammonia with the surface of microporous carbon impregnated with transition metal chlorides[J]. The Journal of Physical Chemistry C, 2007,111:12705-12714.
[3]	傅成诚, 梅凡民, 周亮 . 柠檬酸改性对活性炭吸附氨气的研究[J]. 黑龙江科技信息, 2008(34):46.
[4]	盛丽丽, 唐颖, 尹魏能 , 等. 改性活性炭对氨气吸附性能研究[J]. 林产化学与工业, 2010,30(5):35-39.
[5]	要栋梁 . 硅胶和活性炭对氨气的吸附研究[D]. 北京:首都经济贸易大学, 2007.
[6]	Jia G, Wang S X, Yan L C , et al. Adsorption of NH₃ onto activatedcarbon prepared from palm shells impregnated with H₂SO₄[J]. Journal of Colloid and Interface Science, 2005,281(2):285-290.
[7]	Park S J, Jin S Y . Effect of ozone treatment on ammonia removal of activated carbons[J]. Journal of Colloid and Interface Science, 2005,286(1):417-419.
[8]	Le Leuch L M, Bandosz T J . The role of water and surface acidity on the reactive adsorption of ammonia on modified activated carbons[J]. Carbon, 2007,45(3):568-570.
[9]	Huang C C, Li H S, Chen C H . Effect of surface acidic oxides of activated carbon on adsorption of ammonia[J]. Elsevier, 2008,159(2/3):523-527.
[10]	Shan X M, Zhu S Q, Zhang W H . Effect of surface modification of activated carbon on its adsorption capacity for NH₃[J].Journal of China University of Mining & Technology, 2008(2):261-265.
[11]	Petit C, Bandosz T J . Activated carbons modified with aluminiumzirconium polycations as adsorbents for ammonia[J]. Microporous and Mesoporous Materials, 2008(114):137-147.
[12]	Petit C, Bandosz T J . Complexity of ammonia interactions on activated carbons modified with V₂O₅[J]. Journal of Colloid and Interface Science, 2008,325(2):301-308.
[13]	Bandosz T J, Petit C . On the reactive adsorption of ammonia on activated carbons modified by impregnation with inorganic compounds[J]. Journal of Colloid and Interface Science, 2009,338(2):329-345.
[14]	Wang J T, Jiang W Y, Zhang Z X , et al. Mesoporous carbon beads impregnated with transition metal chlorides for regenerative removal of ammonia in the atmosphere[J]. Industrial and Engineering Chemistry Research, 2017,56(12):3283-3290.
[15]	唐有祺, 谢有畅, 桂琳琳 . 氧化物和盐类在载体表面的自发单层分散及其应用[J]. 自然科学进展, 1994(6):4-14.
[16]	谢有畅, 杨乃芳, 刘英骏 , 等. 某些催化剂活性组份在载体表面分散的自发倾向[J]. 中国科学, 1982(8):673-682.
[17]	吴平, 任红, 曹雪玲 , 等. 三氯化六氨合钴(Ⅲ)制备方法的改进研究[J]. 化学试剂, 2014,37(7):670-672.

浸渍比/ %	比表面积/（m²·g^-1）		总孔容/（cm³·g^-1）		微孔孔容/（cm³·g^-1）
浸渍比/ %	吸附前	吸附后	吸附前	吸附后	吸附前	吸附后
0	1 595.62	1 544.10	1.063	0.913	0.620	0.596
10	1 393.31	1 234.10	0.877	0.787	0.537	0.483
20	1 207.72	964.56	0.751	0.702	0.466	0.374
30	1 086.06	815.13	0.622	0.523	0.424	0.309
40	963.66	424.51	0.524	0.396	0.376	0.149
50	851.91	447.08	0.470	0.359	0.333	0.308
60	792.10	471.60	0.472	0.381	0.308	0.172

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on adsorption performance of modified spherical activated carbon for ammonia

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 13

References 17

Related Articles 15

Metrics

Comments

Recommended 0

[1]	SHI Yunpeng, GUO Ze, ZHANG Hanquan, LU Manman. Study on treatment of ammonia nitrogen wastewater by roasted phosphorus tailings [J]. Inorganic Chemicals Industry, 2025, 57(3): 94-100.
[2]	ZHANG Jinjun, GUO Linlin, MIAO Chengpeng, LI Xingyu, PANG Yaheng, YANG Rongkai, YU Yasen. Study on preparation of spherical calcium carbonate for coating fillers based on carbide slag as raw materials [J]. Inorganic Chemicals Industry, 2025, 57(2): 113-119.
[3]	SHEN Haiyan, LI Fangqin, REN Jianxing, WU Jiang, GUAN Zhenzhen, PAN Weiguo. Research progress on chemical absorption method for capturing carbon dioxide [J]. Inorganic Chemicals Industry, 2024, 56(5): 11-19.
[4]	LAI Huilong, YU fei, YANG Dongxia, MA Jiangli, YIN Xuemei, CHANG Shiying. Research on NH₃-SCR performance and ammonia storage characteristics based on different Cu-CHA catalyst schemes [J]. Inorganic Chemicals Industry, 2024, 56(12): 159-166.
[5]	YUAN Jinghua, WU Junhu, YANG XiuShan, XU Dehua, ZHANG Zhiye. Research on process of production ammonium dihydrogen phosphate by ammonia purification of nitro-phosphoric acid [J]. Inorganic Chemicals Industry, 2023, 55(9): 50-56.
[6]	HAN Hongjing, ZHANG Jingze, LAMAO Zhuoma, HAN Jizhe, WU Yongmin, TANG Weiping. Preparation of Al-Co co-doped lithium manganese oxide and its adsorption performance of lithium [J]. Inorganic Chemicals Industry, 2023, 55(7): 38-44.
[7]	DONG Xinyu, WANG Haifeng, HE Yue, YANG Pan, WANG Song, YANG Chunyuan, WANG Qin, HUANG Bifang, WANG Jiawei. Exleaching toxicity analysis and harmless treatment of electrolytic manganese residue [J]. Inorganic Chemicals Industry, 2023, 55(5): 85-90.
[8]	ZHANG Lingfeng, FAN Yajuan, MAO Chenchen, WU Shiguo, GU Hongxia. Research progress of cocatalyst of nicke-based catalyst system for hydrogen production from ammonia decomposition [J]. Inorganic Chemicals Industry, 2023, 55(3): 21-27.
[9]	HU Yue, MO Hengliang, LI Tianyu, PENG Wenjuan, SUN Guangdong, XIAO Hongkang, CHEN Yili, LI Suoding, TANG Yang. Study on spinning molding and performance of Ti-based lithium ion sieve powder and PVDF resin [J]. Inorganic Chemicals Industry, 2023, 55(11): 58-63.
[10]	QIU Xiaokui, ZHANG Ruofan, WANG Xiaoyan, WANG Hailong, ZHANG Qixue, WAN Chao, XU Lixin. Research on bamboo shavings carbon supported ruthenium catalysts for hydrogen generation from photocatalytic hydrolysis of ammonia borane [J]. Inorganic Chemicals Industry, 2023, 55(10): 153-158.
[11]	LI Sen, WANG Jin, WANG Yingying, CAI Mingfang. Synthesis and modification of NaA zeolite and its application in polyurethane system [J]. Inorganic Chemicals Industry, 2023, 55(10): 78-85.
[12]	WANG Zhiyuan,DOU Zewei,XIONG Lijia,FAN Tianbo,LIU Yunyi,GUO Hongfan. Principle and application of ammonium（ammonia） circulation process [J]. Inorganic Chemicals Industry, 2022, 54(8): 47-53.
[13]	ZHANG Shaokang,ZHAO Hua,LIU Runjing. Study on macro?kinetics of carbonization reaction of ammonia alkali salt sludge [J]. Inorganic Chemicals Industry, 2022, 54(6): 120-124.
[14]	ZHANG Shaokang,ZHAO Hua,LIU Runjing. Study on macro?kinetics of carbonization reaction of ammonia alkali salt sludge [J]. Inorganic Chemicals Industry, 2022, 54(6): 120-124.
[15]	LI Yajiao,ZHAO Yiwei,JU Kai,TANG Renlong,LI Longqing,SHAO Xiaoping,ZHANG Gaofeng,REN Wuang. Study on optimization of extraction conditions in process of determination of ammonia content in fly ash based on response surface method [J]. Inorganic Chemicals Industry, 2022, 54(4): 145-151.