预成型高岭土干胶转化合成NaY型分子筛

doi:10.11962/1006-4990.2019-0495

无机盐工业 ›› 2020, Vol. 52 ›› Issue (8): 88-92.doi: 10.11962/1006-4990.2019-0495

预成型高岭土干胶转化合成NaY型分子筛

张耀日^1,²(),臧甲忠^1,²,张丽娟^1,²,洪美花^1,²,于海斌^1,²

1.中海油天津化工研究设计院有限公司,天津 300131
2.天津市炼化催化工程技术中心

收稿日期:2020-02-22 出版日期:2020-08-10 发布日期:2020-08-12
作者简介:张耀日（1984— ）,男,工程师,硕士研究生,从事分子筛合成以及择形催化方面的研究工作;E-mail： zhangyaoriraul@163.com
基金资助:
中海油能源发展股份有限公司科技项目(HFKJ-TJY1701)

Synthesis of NaY zeolite from preformed kaolin by dry gel conversion

Zhang Yaori^1,²(),Zang Jiazhong^1,²,Zhang Lijuan^1,²,Hong Meihua^1,²,Yu Haibin^1,²

1. CenerTech Tianjin Chemical Research and Design Institute Co.,Ltd.,Tianjin 300131,China
2. Tianjin Refining and Catalytic Technology Engineering Center

Received:2020-02-22 Published:2020-08-10 Online:2020-08-12

摘要/Abstract

摘要：

通过干胶转化法制备了整体式NaY分子筛,采用XRD、SEM及XRF分析表征原料及产物,系统考察了合成体系的n（SiO₂）/n（Al₂O₃）、n（Na₂O）/n（SiO₂）、水量、晶化温度和晶化时间对整体式NaY分子筛制备的影响。结果表明,合成体系n（SiO₂）/n（Al₂O₃）=7.5时,骨架硅铝比（二氧化硅与氧化铝物质的量比）最大为6.12;n（Na₂O）/n（SiO₂）逐渐增大,整体式NaY分子筛结晶度逐渐升高,当n（Na₂O）/n（SiO₂）增至0.35时,会导致P型分子筛的生成;晶化温度从90 ℃逐渐增至120 ℃时,整体式NaY分子筛结晶度也随之升高;在110 ℃下晶化20 h,产物的结晶度达到98%并趋于稳定。干胶转化制备整体式NaY分子筛必须有水的参与,n（H₂O）/n（SiO₂）为4.2左右对反应物的成型及整体式NaY分子筛的晶化较为适宜。

关键词: 整体式分子筛, 干胶转化, NaY分子筛, 高岭土

Abstract:

Monolithic NaY zeolite was synthesized by dry gel conversion method.XRD,SEM and XRD were used to study the raw materials and products.The influences of n（SiO₂）/n（Al₂O₃）,n（Na₂O）/n（SiO₂）,water content,crystallization temperature and crystallization time on the preparation of monolithic NaY zeolite were systematically investigated.Experimental results showed that when n（SiO₂）/n（Al₂O₃） of synthesis system was 7.5,the n（SiO₂）/n（Al₂O₃） of framework was 6.12.The crystallinity of the NaY zeolite increased with the amount of n（Na₂O）/n（SiO₂） firstly.If n（Na₂O）/n（SiO₂） was above 0.35,the NaY zeolite would turn to P zeolite.When the crystallization temperature increased from 90 ℃ to 120 ℃,the crystallinity of product increased accordingly.After crystallization at 110 ℃ for 20 h,the crystallinity of product was 98% and stated stable.Water was the key factor in the process of dry gel conversion.When the n（H₂O）/n（SiO₂） reached about 4.2,it was good for the synthesis of NaY zeolite.

Key words: monolithic zeolite, dry gel conversion, NaY zeolite, kaolin

中图分类号:

TQ131.12

张耀日,臧甲忠,张丽娟,洪美花,于海斌. 预成型高岭土干胶转化合成NaY型分子筛[J]. 无机盐工业, 2020, 52(8): 88-92.

Zhang Yaori,Zang Jiazhong,Zhang Lijuan,Hong Meihua,Yu Haibin. Synthesis of NaY zeolite from preformed kaolin by dry gel conversion[J]. Inorganic Chemicals Industry, 2020, 52(8): 88-92.

图/表 8

表1

图1

图2

图3

图4

图5

图6

图7

参考文献 14

[1]	Xu Ruren, Pang Wenqin, Yu Jihong, et al. Chemistry of zeolites and related porous materials:synbook and structure[M]. Singapore:Wiley, 2007.
[2]	Jin Junsu, Peng Chaoyun, Wang Jiujiang, et al. Facile synjournal of mesoporous zeolite Y with improved catalytic performace for heavy oil fluid catalytic cracking[J]. Industrial & Engineering Chemistry Research, 2014,53(8):3405-3411.
[3]	Xu Wenyang, Dong Jinxiang, Li Jinping, et al. A novel method for the preparation of zeolite ZSM-5[J].Journal of the Chemical Society Chemical Communications, 1990(10):755-756.
[4]	Zhou Jian, Hua Zile, Shi Jianlin, et al. Synjournal of a hierarchical micro/mesoporous structure by steam-assisted post-crystallization[J]. Chemistry, 2009,15(47):12949.
[5]	Koekkoek A J J, Degirmenci V, Hensen E J M. Dry gel conversion of organosilane templated mesoporous silica:From amorphous to crystalline catalysts for benzene oxidation[J]. Journal of Materials Chemistry, 2011,21(25):9279-9289.
[6]	Möller K, Yilmaz B, Jacubinas R M, et al. One-step synjournal of hierarchical zeolite beta via network formation of uniform nanocrystals[J]. Journal of the American Chemical Society, 2011,133(14):5284-5295.
[7]	Majano G, Mintova S, Bein T, Klapötke T. High-density energeticmaterial hosted in pure silica mfi-type zeolite nanocrystals[J]. Advanced Materials, 2006,18(18):2440-2443.
[8]	Chou C, Cundy C S, Garforth A A. A dry gel synjournal route to mesoporous ZSM-5 catalysts[J]. Studies in Surface Science & Catalysis, 2005,156:393-400.
[9]	Chou Y H, Cundy C S, Garforth A A, et al. Mesoporous ZSM-5 catalysts:Preparation,characterisation and catalytic properties.Part I:Comparison of different synjournal routes[J]. Microporous & Mesoporous Materials, 2006,89(1/2/3):78-87.
[10]	戴长禄, 钟洪祥, 潘杰文, 等. 高岭土[M]. 北京: 中国建筑出版社, 1983.
[11]	郑淑琴. 高岭土碱溶性能对原位晶化的影响[J]. 石油化工, 2003,32(增刊):942-943.
[12]	郑淑琴. FCC催化剂中高岭土的影响及应用[J]. 非金属矿, 2002,25(2):22-23.
[13]	Valtchev V P, Bozhilov K N. transmission electron microscopy study of the formation of fau-type zeolite at room temperature[J]. Journal of Physical Chemistry B, 2004,108(40):15587-15598.
[14]	Hu Dan, Xia Qinghua, Lu Xinhua, et al. Synjournal of ultrafine zeolites by dry-gel conversion without any organic additive[J]. Materials Research Bulletin, 2008,43(12):3553-3561.

样品	w （Al₂O₃）	w （SiO₂）	w （SO₃）	w （K₂O）	w （CaO）	w （TiO₂）	w （Fe₂O₃）
K	44.5	51.7	1.460	0.554	0.161	0.376	0.586
K-650	46.6	50.8	0.273	0.553	0.159	0.371	0.618
SK-650	23.6	74.1	0.313	0.253	0.127	0.451	0.285

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会

预成型高岭土干胶转化合成NaY型分子筛

Synthesis of NaY zeolite from preformed kaolin by dry gel conversion

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 8

参考文献 14

相关文章 14

Metrics

本文评价

推荐阅读 0

[1]	熊晓云, 曹庚振, 杜学敏, 王久江, 胡清勋. 炭黑模板法制备大孔原位晶化型催化裂化催化剂[J]. 无机盐工业, 2023, 55(9): 134-139.
[2]	赵红娟, 王久江, 刘宇航, 李宁, 曹庚振, 刘宏海. 异型晶种对NaY分子筛合成的影响[J]. 无机盐工业, 2023, 55(4): 120-124.
[3]	刘应强,呙润华,刘喜杰. 硅灰、偏高岭土对矿渣-粉煤灰微珠胶凝材料性能的影响[J]. 无机盐工业, 2022, 54(6): 102-108.
[4]	杨阳,张胜中,张延鹏,范得权,王红涛,张英. 碱度对A型分子筛成型体的影响研究[J]. 无机盐工业, 2021, 53(7): 48-52.
[5]	熊晓云,魏昭成,王久江,高雄厚,赵红娟,胡清勋. 合成条件对高岭土微球原位晶化NaY分子筛的影响[J]. 无机盐工业, 2020, 52(1): 99-102.
[6]	张金山, 孙春宝, 曹钊, 范文阳, 郭振坤, 樊雪敏. 煤系高岭岩制备偏高岭土实验研究[J]. 无机盐工业, 2016, 48(9): 64-.
[7]	李侠, 周珊, 张金山, 范雯阳, 邹东雪, 孙春宝. NaY分子筛导向剂的制备及其性能研究[J]. 无机盐工业, 2016, 48(8): 70-.
[8]	刘明慧, 魏振浩, 周茁, 朱学栋. 碱处理对高岭土微球上原位合成 ZSM-5分子筛的影响[J]. 无机盐工业, 2016, 48(7): 68-.
[9]	高文秋, 赵斯琴, 吴哈申, 德力格尔, 长山. 微波法改性煤系高岭土的制备及其性能[J]. 无机盐工业, 2016, 48(12): 72-.
[10]	张耀日, 裴仁彦, 霍志萍, 于海斌. 高岭土微球离子热法原位合成SAPO-34分子筛[J]. 无机盐工业, 2015, 47(4): 75-.
[11]	裴仁彦, 张耀日, 霍志萍, 于海斌. 高岭土微球原位合成纳米Y沸石[J]. 无机盐工业, 2013, 45(7): 61-.
[12]	庞娟, 朱岳麟, 常增花. 以高岭土和铝土矿制备4A沸石的研究[J]. 无机盐工业, 2011, 43(11): 37-.
[13]	沈王庆, 李道华, 卿东红. 碱性活化煤系高岭土吸附生活污水中磷的研究[J]. 无机盐工业, 2010, 0(12): 46-.
[14]	刘晓霞;李永强. 一种制取无水氟化铝的新工艺[J]. 无机盐工业, 2009, 0(7): 0-0.

首 页

预成型高岭土干胶转化合成NaY型分子筛

Synthesis of NaY zeolite from preformed kaolin by dry gel conversion

RichHTML

PDF (PC)

可视化

引用本文

使用本文

首页