煤矸石除杂及碱融活化制取硅酸钠的实验研究

摘要/Abstract

摘要： 研究利用煤矸石中的硅元素制取硅酸钠，先将煤矸石粉在750 ℃下煅烧2 h，除去有机质并破坏了煤矸石中的高岭石等矿物的晶型结构，再将煅烧过的煤矸石粉在95 ℃、液固比（mL/g）为8∶1、质量分数为40%的硫酸中酸浸5 h，煤矸石煅烧粉中的铁和铝等金属杂质离子的总去除率为86.93%；还研究了碱融活化条件对硅元素溶出率的影响，获得了适宜的碱融活化条件：m（酸浸粉）∶m（碳酸钠）=1∶1.5、碱融温度为800 ℃、碱融时间为2 h。在此条件下，硅元素溶出率大于75%，最终获得了硅酸钠溶液。

关键词: 煤矸石, 除杂, 碱融, 硅酸钠

Abstract: In order to utilize silicon in the coal gangue to prepare sodium silicate，the gangue powder was calcined at 750 ℃ for 2 h firstly，then the organic matters were removed and the crystal structures of the minerals，such as kaolin in the gangue were destroyed.The calcined gangue powder was leached in sulfuric acid with mass fraction of 40% and liquid to solid ratio of 8∶1 at 95 ℃ for 5 h.The total removal ratio of impurity metal ions，such as iron and aluminum was 86.93%；the influences of the alkali melting activation conditions on the dissolution ratios of silicon element were investigated，then the suitable activation conditions were obtained:the mass ratio of acid leaching powder to sodium carbonate was 1∶1.5，the alkali melting temperature was 800 ℃，and the alkali melting time was 2 h.Under these conditions silicon element dissolution ratio was more than 75% and the sodium silicate solution was obtained finally.

Key words: gangue, purification, alkali melting, sodium silicate

中图分类号:

TQ131.12

孔德顺, 吴红. 煤矸石除杂及碱融活化制取硅酸钠的实验研究[J]. 无机盐工业, 2013, 45(8): 42-.

KONG De-Shun, WU Hong. Experimental study on preparation of sodium silicate by purification of gangue and alkali melting activation[J]. INORGANICCHEMICALSINDUSTRY, 2013, 45(8): 42-.

[1]	黄振旭,陈凌霞,任丽,李颖欣,贾潘潘,张文慧. Na₂SiO₃/ZrO₂固体碱催化大豆油制备生物柴油的研究[J]. 无机盐工业, 2020, 52(6): 83-86.
[2]	刘小婷,温久然,王思雨,刘开平,高妮,钟佳墙. 原状煤矸石骨料强化工艺研究[J]. 无机盐工业, 2020, 52(4): 65-71.
[3]	吴宝建,吕昕峰,张清杰,易美桂,向兰. 磷石膏湿法偶联除杂规律初探[J]. 无机盐工业, 2020, 52(12): 55-58.
[4]	杨权成,弓志明,毛艳宇,李晓东,张闫城,石常省,曾鸣. 煤矸石提铝尾渣水热法制备介孔硅酸钙研究[J]. 无机盐工业, 2020, 52(11): 86-90.
[5]	谢娟,夏润南,杜红霞,许永权,赵树春,许红,康文通. α-Fe₂O₃/煤矸石复合光催化剂的制备及其降解五氯酚性能的研究[J]. 无机盐工业, 2019, 51(5): 74-77.
[6]	张萍花,燕云洁,陈建钧,王红艳,张春丽,吴宁. 高镁钙磷尾矿酸解制纳米级碳酸钙[J]. 无机盐工业, 2019, 51(3): 63-66.
[7]	陈云海，王海燕，周秀. 卤水结晶除杂工艺技术研究[J]. 无机盐工业, 2019, 51(11): 57-58.
[8]	范剑明1，2. 高铝煤矸石铝硅分级提取实验研究[J]. 无机盐工业, 2019, 51(11): 65-68.
[9]	张金山, 孙春宝, 曹钊, 范文阳, 郭振坤, 樊雪敏. 煤系高岭岩制备偏高岭土实验研究[J]. 无机盐工业, 2016, 48(9): 64-.
[10]	刘秋斌, 陈佚, 吴伯荣, 陈飞彪. 电解锰粉制备高纯氯化锰除杂工艺研究[J]. 无机盐工业, 2016, 48(6): 20-.
[11]	范雯阳, 李侠, 孙建岭. 内蒙古某煤矸石低温制备4A沸石实验[J]. 无机盐工业, 2016, 48(5): 44-.
[12]	张翔, 段建榜, 李瑞歌, 陈淼, 卢艳洁. 炼钙还原渣和煤矸石制备聚合氯化铝的研究[J]. 无机盐工业, 2016, 48(4): 66-.
[13]	田伟军. 用氨配合法从含锌废催化剂中回收锌[J]. 无机盐工业, 2016, 48(2): 49-.
[14]	王远望, 杨明平, 姚茂生, 王远鸿. 高纯偏钒酸钾制备工艺研究[J]. 无机盐工业, 2016, 48(10): 40-.
[15]	景艳伟, 乃学瑛, 党力, 李武, 吕智慧. 碳酸钙晶须的除杂工艺研究[J]. 无机盐工业, 2015, 47(7): 35-.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会