凹凸棒土,氧化锌,纳米复合材料,光催化,活性大红," /> 凹凸棒土,氧化锌,纳米复合材料,光催化,活性大红,"/> attapulgite;zinc oxide;nano composite material;photocatalysis;activeness scarlet,"/> 凹凸棒土负载氧化锌-二氧化钛的制备与性能
无机盐工业
主管：中海油天津化工研究设计院有限公司
主办：中海油天津化工研究设计院有限公司
　　　中海油炼油化工科学研究院（北京）有限公司
　　　中国化工学会无机酸碱盐专业委员会
ISSN 1006-4990 CN 12-1069/TQ

无机盐工业 ›› 2011, Vol. 43 ›› Issue (1): 33-35.

• 论文 • 上一篇    下一篇

凹凸棒土负载氧化锌-二氧化钛的制备与性能

李志林1，安青珍1，郝永亮2   

  1. （1．河北大学化学与环境科学学院，河北保定 071002；2．华东理工大学化学与分子工程学院）
  • 出版日期:2011-01-10 发布日期:2011-03-17

Preparation and performance of attapulgiteloaded zinc oxidetitania

 LI  Zhi-Lin-1, AN  Qing-Zhen-1, HAO  Yong-Liang-2   

  1. (1.School of Chemistry and Environmental Science,Hebei University，Baoding 071002,China;2.School of Chemistry and Molecular Engineering,East China University of Science and Technology)
  • Published:2011-01-10 Online:2011-03-17

摘要： 以凹凸棒土(ATP)作载体，硫酸氧钛、硫酸锌及碳酸铵为原料，采用化学沉淀法制备凹凸棒土负载氧化锌-二氧化钛(ATP/ZnO-TiO2)纳米复合材料，并用XRD，TEM测试手段对样品进行了表征。以其对活性大红(BES)的降解效果作为评价其光催化性能的标准，对制备条件进行了优化。结果表明：ATP与二氧化钛的质量比为20%、二氧化钛与氧化锌的物质的量比为10∶1、煅烧温度为450 ℃下制备的复合材料光催化降解活性大红的效果最佳；与凹凸棒土负载二氧化钛（ATP/TiO2）及凹凸棒土负载氧化锌（ATP/ZnO）相比，复合材料具有良好的可见光光催化性能。

关键词: font-family: 宋体, mso-bidi-font-size: 12.0pt, mso-ascii-font-family: 'Times New Roman', mso-hansi-font-family: 'Times New Roman', mso-bidi-font-family: 'Times New Roman', mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, 凹凸棒土')">mso-bidi-language: AR-SA">凹凸棒土, 氧化锌, 纳米复合材料, 光催化, 活性大红

Abstract: Attapulgite loaded zinc oxide-titania (ATP/ZnO-TiO2）nano composite material was prepared by chemical precipitation method with TiOSO4,ZnSO4,and (NH4)2CO3 as raw materials and ATP as carrier.Samples were characterized by XRD and TEM.Photocatalytic activities were evaluated by degradation of activeness scarlet (BES) and the conditions for preparing this composite material were optimized.Results showed that the optimum conditions for preparation of the nano composite material were as follows:mass ratio of ATP to TiO2 was 20%,amount substance ratio of TiO2 to ZnO was 10 ∶1,and calcined temperature was 450 ℃.Under these conditions,the effect of photocatalytic activity of the composite material to BES was the best.Compared with ATP/TiO2 and ATP/ZnO,the nano composite material had better photocatalytic material performance under visible light.

Key words: font-family: "Times New Roman", mso-bidi-font-size: 12.0pt, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, attapulgite;zinc oxide;nano composite material;photocatalysis;activeness scarlet')">mso-fareast-font-family: 宋体">attapulgite;zinc oxide;nano composite material;photocatalysis;activeness scarlet

主管：中海油天津化工研究设计院有限公司
主办：中海油天津化工研究设计院有限公司
　　　中海油炼油化工科学研究院（北京）有限公司
　　　中国化工学会无机酸碱盐专业委员会
出版单位：《无机盐工业》编辑部
ISSN　1006-4990
CN　12-1069/TQ
网站版权所有 © 2024《无机盐工业》编辑部
地址：中国天津红桥区丁字沽三号路85号 邮编：300131
电话：(022)26689297;26658343 传真：(022)26658343
E-mail:book@wjygy.com.cn http://www.wjygy.com.cn
本系统由北京玛格泰克科技发展有限公司设计开发
技术支持：support@magtech.com.cn
违法和不良信息举报电话: 022-26689297
津ICP备05000975号-8  津公网安备 12010602120338号   网站版权所有 ©《无机盐工业》编辑部