Cr对工业V-Mo/Ti脱硝催化剂的毒化作用研究

doi:10.19964/j.issn.1006-4990.2020-0543

Abstract

Abstract:

Industrial V-Mo-Cr/Ti catalysts loaded with different amounts of Cr₂O₃ were prepared by impregnation method.XRD,N₂-adsorption,NH₃-TPD,Raman,H₂-TPR and XPS were used to characterize the catalysts.Afterwards,the denitri-fication performance of the different catalysts was tested through a fixed-bed microreactor.It was found that Cr₂O₃ loaded on industrial V-Mo/Ti denitration catalysts had little impact on the pore properties of catalyst.By comparison with V-Mo/Ti cat-alyst,V-Mo-Cr/Ti catalyst presented more amount of acid sites.However,due to the influence of Cr₂O₃,the reduction perfor-mance of the catalyst was lower and the content of chemical adsorbed oxygen was less.V-Mo-Cr/Ti catalysts exhibited relative lower NO_x conversion and higher N₂O generation in the temperature range of 250 ℃ to 430 ℃ than that of the V-Mo/Ti cata-lyst.

Key words: selective catalytic reduction, V-Mo/Ti, chromium oxide, denitration catalyst

CLC Number:

TQ136.11

Huang Li,Wang Hu,Zong Yuhao,Chang Zhengfeng,Liu Yang,Li Jinke,Han Pei. Study on deactivation effect of chromium on industrial V-Mo/Ti De-NO_x catalyst[J]. Inorganic Chemicals Industry, 2021, 53(8): 112-116.

Figures/Tables 8

Fig.1

Table 1

Fig.2

Fig.3

Fig.4

Fig.5

Table 2

Fig.6

References 24

[1]	周惠, 黄华存, 董文华. SCR脱硝催化剂失活及再生技术的研究进展[J]. 无机盐工业, 2017, 49(5):9-13.
[2]	李想, 李俊华, 何煦, 等. 烟气脱硝催化剂中毒机制与再生技术[J]. 化工进展, 2015, 34(12):4129-4138.
[3]	贾勇, 周军, 柏家串, 等. 砷、钾复合中毒选择性催化还原脱硝催化剂的再生[J]. 硅酸盐学报, 2016, 44(7):1025-1032.
[4]	Xiao H P, Chen Y, Qi C, et al. Effect of Na poisoning catalyst(V₂O₅-WO₃/TiO₂) on denitration process and SO₃ formation[J]. Applied Surface Science, 2018, 433:341-348. doi: 10.1016/j.apsusc.2017.10.048
[5]	周学荣, 张晓鹏. SCR催化剂碱(土)金属中毒的研究进展[J]. 化学通报, 2015, 78(7):590-596.
[6]	Li X, Li X S, Yang R T, et al. The poisoning effects of calcium on V₂O₅-WO₃/TiO₂ catalyst for the SCR reaction:Comparison of diffe-rent forms of calcium[J]. Molecular Catalysis, 2017, 434:16-24. doi: 10.1016/j.mcat.2017.01.010
[7]	Castellino F, Rasmussen S B, Jensen A D, et al. Deactivation of vana-dia-based commercial SCR catalysts by polyphosphoric acids[J]. Applied Catalysis B:Environmental, 2008, 83:110-122. doi: 10.1016/j.apcatb.2008.02.008
[8]	沈伯雄, 熊丽仙, 刘亭. 负载型V₂O₅-WO₃/TiO₂催化剂的砷中毒研究[J]. 燃料化学学报, 2011, 39(11):856-859.
[9]	Jiang Y, Gao X, Zhang Y X, et al. Effects of PbCl₂ on selective cat-alytic reduction of NO with NH₃ over vanadia-based catalysts[J]. Journal of Hazardous Materials, 2014, 274:270-278. doi: 10.1016/j.jhazmat.2014.04.026 pmid: 24794983
[10]	Ali Z, Wu Y W, Wu Y, et al. Inhibition effects of Pb species on the V₂O₅-MoO₃/TiO₂ catalyst for selective catalytic reduction of NO_x with NH₃:A DFT supported experimental study[J]. Applied Surface Science, 2020, 525:146582-146592. doi: 10.1016/j.apsusc.2020.146582
[11]	Wu Y W, Zhou X Y, Han J, et al. Interaction mechanism between Se species in flue gas and V₂O₅-MoO₃/TiO₂ catalyst:An in-depth experimental and theoretical study[J]. Chemical Engineering Jo-urnal, 2020, 398:125615-125625.
[12]	Liu Z, Han J, Zhao L, et al. Effects of Se and SeO₂ on the denitrifica-tion performance of V₂O₅-WO₃/TiO₂ SCR catalyst[J]. Applied Ca-talysis A,General, 2019, 587:117263-117272.
[13]	石梦雅, 陈娟, 罗光前, 等. 西部低阶煤中铬赋存形态及燃烧排放特性研究[J]. 工程热物理学报, 2017, 38(6):1344-1350.
[14]	晁晶迪, 何洪, 宋丽云, 等. Pr掺杂对V₂O₅-MoO₃/TiO₂催化剂NH₃-SCR反应活性的影响[J]. 高等学校化学学报, 2015, 36(3):523-530.
[15]	Dong G J, Bai Y, Zhang Y F, et al. Effect of the V⁴⁺⁽³+)/V⁵+ ration on the denitration activity for V₂O₅-WO₃/TiO₂ catalysts[J]. New Jour-nal of Chemistry, 2015, 39:3588-3596.
[16]	Yu W C, Wu X D, Si Z C, et al. Influences of impregnation proce-dure on the SCR activity and alkali resistance of V₂O₅-WO₃/TiO₂ catalyst[J]. Applied Surface Science, 2013, 283:209-214. doi: 10.1016/j.apsusc.2013.06.083
[17]	Qiu Y, Liu B, Du J, et al. The monolithic cordierite supported V₂O₅-MoO₃/TiO₂ catalyst for NH₃-SCR[J]. Chemical Engineering Jour-nal, 2016, 294:264-272.
[18]	Casagrande L, Lietti L, Nova I, et al. SCR of NO by NH₃ over TiO₂-supported V₂O₅-MoO₃ catalysts:Reactivity and redox behavior[J]. Applied Catalysis B:Environmental, 1999, 22(1):63-77. doi: 10.1016/S0926-3373(99)00035-1
[19]	Huang L, Zong Y H, Wang H, et al. Influence of calcination tem-perature on the plate-type V₂O₅-MoO₃/TiO₂ catalyst for selective catalytic reduction of NO[J]. Reaction Kinetics,Mechanisms and Catalysis, 2018, 124(2):603-617. doi: 10.1007/s11144-018-1378-0
[20]	Al-Kandari H, Al-Kharafi F, Al-Awadi N, et al. The catalytic active sites in partially reduced MoO₃ for the hydroisomerization of 1-pentene and n-pentane[J]. Applied Catalysis A:General, 2005, 295:1-10. doi: 10.1016/j.apcata.2005.07.023
[21]	Shawn D L, Andreea C G, Bernard E N. Ammonia oxidation over Au/MO_x/γ-Al₂O₃-activity,selectivity and FTIR measurements[J]. Catalysis Today, 2004(9):3-14.
[22]	姚佳, 刘少光, 林文松, 等. Ce-Cr-Ni/TiO₂催化剂的CO-SCR性能研究[J]. 现代化工, 2019, 39(5):123-127.
[23]	Topsϕe N Y, Topsϕe H, Dumesic J A. Vanadia/titania catalysts for selective catalytic reduction(SCR) of nitric oxide by ammonia:Ⅰ. Combined temperature programmed in situ FTIR and on-line mass spectroscopy studies[J]. Journal of Catalysis, 1995, 151:226-240. doi: 10.1006/jcat.1995.1024
[24]	Topsϕe N Y, Dumesic J A, Topsϕe H. Vanadia/titania catalysts for selective catalytic reduction of nitric oxide by ammonia：Ⅱ.Studies of active sites and formulation of catalytic cycles[J]. Journal of catalysis, 1995, 151:241-252. doi: 10.1006/jcat.1995.1025

催化剂	比表面积/ （m²·g^-1）	孔容/ （cm³·g^-1）	平均孔径/ nm
V-Mo/Ti	73.2	0.301	15.4
V-Mo-Cr（0.2）/Ti	70.8	0.285	16.1
V-Mo-Cr（0.5）/Ti	67.1	0.272	16.9

催化剂	n（V⁴⁺+V³⁺）/ n（V⁵⁺）	n（Mo⁶⁺）/ n（Mo⁵⁺+Mo⁶⁺）	n（O_α）/ n（O_α+O_β）	n（Cr³⁺）/ n（Cr⁶⁺）
V-Mo/Ti	1.64	0.97	0.11	—
V-Mo-Cr（0.2）/Ti	1.60	0.96	0.09	0.92
V-Mo-Cr（0.5）/Ti	1.58	0.97	0.06	0.93

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on deactivation effect of chromium on industrial V-Mo/Ti De-NO_x catalyst

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 24

Related Articles 15

Metrics

Comments

Recommended 0

[1]	LAI Huilong, YU fei, YANG Dongxia, MA Jiangli, YIN Xuemei, CHANG Shiying. Research on NH₃-SCR performance and ammonia storage characteristics based on different Cu-CHA catalyst schemes [J]. Inorganic Chemicals Industry, 2024, 56(12): 159-166.
[2]	LI Peng, YANG Siyuan, LUO Shizhong, DU Peining, TAN Renjun, JING Fangli. Neodymium-modified iron-based catalysts for nitrogen oxides removal [J]. Inorganic Chemicals Industry, 2023, 55(3): 140-146.
[3]	ZHANG Zhiqiang, CUI Kangping, CHEN Xing, LI Haiyang. Optimization of preparation of ultrafine chromium oxide by carbothermal reduction of sodium dichromate by response surface methodology [J]. Inorganic Chemicals Industry, 2023, 55(10): 136-144.
[4]	XU Enhao, WU Kaipeng. Research progress of preparation and application of nano-sized chromium oxide [J]. Inorganic Chemicals Industry, 2023, 55(10): 24-34.
[5]	DU Peining,LUO Shizhong,Tan Renjun,JING Fangli. Study on denitration performance of Y doped Fe₂O₃ catalyst [J]. Inorganic Chemicals Industry, 2022, 54(11): 137-142.
[6]	Su Shaolong,Qu Xiaolong,Zhong Dule,Sun Yanmin,Nan Jun,Li Shipeng. Study on preparation and denitration performance of Cu-Ce/ZSM-5 zeolite catalyst [J]. Inorganic Chemicals Industry, 2021, 53(6): 190-193.
[7]	Liu Jijun,Lin Hongmei,Hu Guorong,Peng Zhongdong. Study on new process of producing chromium salt with ferrochrome alloy [J]. Inorganic Chemicals Industry, 2021, 53(6): 156-159.
[8]	HAN Xinyu,LIU Kaijie,BIAN Mengyao,ZHANG Yibo,YANG Xiangguang. Catalytic performance study of Ce-MnO_x for low-temperature purification of nitrogen oxides and carbon monoxide [J]. Inorganic Chemicals Industry, 2021, 53(12): 35-42.
[9]	SUN Chunhui,CHEN Yongsheng,LIU Wei,XU Yan,ZHANG Jingcheng,YU Ruixiang. Study on new preparation process and performance of V₂O₅ /（TiO₂-SiO₂） denitrification catalyst [J]. Inorganic Chemicals Industry, 2021, 53(12): 146-149.
[10]	Gong Peng,Zhang Bing,Liu Sihao. Status of regeneration and resource utilization of deactivated commercial SCR catalyst [J]. Inorganic Chemicals Industry, 2021, 53(1): 14-17.
[11]	Wei Xiao1，Liao Huiwei1，Chen Ning2，Dong Mingfu2，Huang Xiandong2，Huang Yuxi2. Process optimization of preparation of chromium hydroxide from sodium chromate carbonization mother liquor and effect of particle size distribution of chromium trioxide [J]. Inorganic Chemicals Industry, 2019, 51(11): 36-41.
[12]	Tian Sen1，2，3，Ye Xuemei1，2，3，Feng Haitao1，2，Dong Yaping1，2，Li Wu1，2，Zhang Bo1，2，Li Bo1，2. Effect of temperature on preparation of chromium oxide by thermal decomposition of ammonium dichromate [J]. Inorganic Chemicals Industry, 2019, 51(10): 60-63.
[13]	Liu Yuxin1，Shi Fengjuan2，Lü Yaohui1，Wei Shicheng1，Wang Yujiang1，He Dongyu1，Wang Wenyu1. Progress in preparation of nano?鄄sized or porous chromium oxide particles [J]. Inorganic Chemicals Industry, 2019, 51(10): 1-6.
[14]	WU Qi-Sheng- , CHEN Yi-Lin- . Synthesis， characterization，and de-NOx performance of lanthanum-doped MCM-41 [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(7): 71-.
[15]	XU Hong, LIAO Xin, QIN Jian-Feng, WU Tao, LI Yi-Ying, QIU Bin. Selection research on tungsten salt precursor of titanium tungsten powder used for denitration catalyst [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(5): 73-.

Study on deactivation effect of chromium on industrial V-Mo/Ti De-NOx catalyst