高钙镁磷矿预处理的硝酸钙镁浸取液制备氢氧化镁的研究

doi:10.19964/j.issn.1006-4990.2023-0391

摘要/Abstract

摘要：

通过煅烧高钙镁磷矿分解碳酸钙镁盐可有效提高磷矿品位。对煅烧后的磷矿进行水化、浸取得到低镁磷精矿和硝酸钙镁浸取液，对浸取液进一步沉淀以回收制备氢氧化镁。然而，在氢氧化镁生产过程中存在固液分离困难和产品纯度低的问题，系统研究了不同温度下湿滤饼的性质、比阻、沉降性能等。结果表明：较低温度下滤饼吸附水分大、过滤困难、洗涤负担大；当温度升高到70 ℃时，可有效破坏氢氧化镁胶体，从而减少滤饼对水分的吸附，减轻洗涤负担，显著改善氢氧化镁的沉降性能和过滤性能，沉降速率高达0.051 8 mL/min，过滤比阻低达（5.82±1.1）×10¹¹ m/kg，镁的回收率可达72%。进一步对沉淀过程进行模拟分析，提出以分步沉淀方式实现杂质的预分离，从而提高氢氧化镁纯度，使其达到工业级氢氧化镁Ⅲ类合格品的要求。

关键词: 氢氧化镁, 过滤比阻, 沉降性能, Visual MINTEQ模拟

Abstract:

The decomposition of calcium magnesium carbonate salts by calcining phosphate rock with high content of magnesium and calcium can effectively improve the grade of phosphate rock.Leachate and phosphate rock with low magnesium content are obtained by further hydrating and leaching the calcined phosphate rock.The leachate is further precipitated to prepare magnesium hydroxide.However，there are difficulties in solid-liquid separation and low product purity in the production process of magnesium hydroxide.The properties，specific resistance，and settling performance of wet filter cakes prepared at different temperatures were systematically studied.The results showed that the filter cakes adsorbed more water at lower temperatures，making filtration difficult and washing burdensome.When the temperature was rised to 70 ℃，the magnesium hydroxide colloid could be effectively destroyed，thus reducing the adsorption of water by filter cake，reducing the washing burden，and significantly improving the settlement and filtration performance of magnesium hydroxide.The sedimentation rate was up to 0.051 8 mL/min，and the minimum specific resistance of filtration was（5.82±1.1）×10¹¹ m/kg.The recovery ratio of magnesium could reach 72%.Further simulation analysis of the precipitation process showed that the two-step precipitation method could realize the pre-separation of impurities，thus improving the purity of magnesium hydroxide，and the product purity could meet the requirements of industrial magnesium hydroxide grade Ⅲ.

Key words: magnesium hydroxide, specific resistance of filtration, settlement performance, Visual MINTEQ simulation

中图分类号:

TQ132.2

唐彪, 唐盛伟. 高钙镁磷矿预处理的硝酸钙镁浸取液制备氢氧化镁的研究[J]. 无机盐工业, 2024, 56(5): 87-93.

TANG Biao, TANG Shengwei. Study on preparation of magnesium hydroxide from calcium magnesium nitrate leaching pretreatment of phosphate rock with high content of magnesium and calcium[J]. Inorganic Chemicals Industry, 2024, 56(5): 87-93.

图/表 13

图1

表 1

图2

图 3

图 4

图5

图 6

表 2

图7

图 8

图 9

图 10

表 3

参考文献 26

1	LIU Qiang， LIU Weizao， Li LÜ，et al.Study on reactions of gaseous P₂O₅ with Ca₃（PO₄）₂ and SiO₂ during a rotary kiln process for phosphoric acid production［J］.Chinese Journal of Chemical Engineering，2018，26（4）：795-805.
2	CHEN Fang， WANG Xiaomei， LIU Weizao，et al.Selective extraction of nitric and acetic acids from etching waste acid using N235 and MIBK mixtures［J］.Separation and Purification Technology，2016，169：50-58.
3	ABDEL-GHAFAR H M， ABDEL-AAL E A， IBRAHIM M A M，et al.Purification of high iron wet-process phosphoric acid via oxalate precipitation method［J］.Hydrometallurgy，2019，184：1-8.
4	BECKER P.Phosphates and phosphoric acid：Raw materials，technology，and economics of the wet process（Second edition）［M］.CRC Press，1989.
5	ZHANG P.Comprehensive recovery and sustainable development of phosphate resources［J］.Procedia Engineering，2014，83：37-51.
6	LI Hongqiang， GE Wu， ZHANG Jun，et al.Control foaming performance of phosphate rocks used for wet-process of phosphoric acid production by phosphoric acid［J］.Hydrometallurgy，2020，195：105364.
7	SILVA L F O， OLIVEIRA M L S， CRISSIEN T J，et al.A review on the environmental impact of phosphogypsum and potential health impacts through the release of nanoparticles［J］.Chemosphere，2022，286：131513.
8	TAYIBI H， CHOURA M， LÓPEZ F A，et al.Environmental impact and management of phosphogypsum［J］.Journal of Environmental Management，2009，90（8）：2377-2386.
9	何宾宾，魏立军，谢德龙，等.中国湿法磷加工产业现状与可持续发展［J］.无机盐工业，2020，52（1）：1-4，16.
	HE Binbin， WEI Lijun， XIE Delong，et al.Current situation and sustainable development of wet process phosphorus processing industry in China［J］.Inorganic Chemicals Industry，2020，52（1）：1-4，16.
10	LV Li， ZHENG Dongyao， TANG Shengwei，et al.Phosphate ore particles dissolution kinetics in hydrochloric acid based on a structure-related segmented model［J］.Powder Technology，2021，392：141-149.
11	方进，李菊，孟品品，等.冷冻法硝酸磷肥副产粗硝钙液用于磷矿脱镁的研究［J］.无机盐工业，2021，53（6）：180-184.
	FANG Jin， LI Ju， MENG Pinpin，et al.Study on by-product crude calcium nitrate solution of frozen nitrophosphate fertilizer for phosphate rock demagnesium［J］.Inorganic Chemicals Industry，2021，53（6）：180-184.
12	殷灵，李军，唐湘.硝酸磷肥生产新工艺研究［J］.无机盐工业，2014，46（12）：50-53.
	YIN Ling， LI Jun， TANG Xiang.Study on new production technology of nitrophosphate fertilizer［J］.Inorganic Chemicals Industry，2014，46（12）：50-53.
13	WU Junhu， XU Dehua， YANG Xiushan，et al.Determination and correlation of vapor-liquid equilibria for the nitric acid+water，nitric acid+water+phosphoric acid，and nitric acid+water+phosphoric acid+sulfuric acid system［J］.Journal of Chemical & Engineering Data，2023，68（3）：633-641.
14	向伟，王勃，应建康.硫酸铵法硝酸磷肥生产高品质硫酸钙工艺研究［J］.无机盐工业，2013，45（1）：17-20.
	XIANG Wei， WANG Bo， YING Jiankang.Study on producing process of high-quality calcium sulfate from nitric phosphate by ammonium sulfate method［J］.Inorganic Chemicals Industry，2013，45（1）：17-20.
15	李晓妍，刘佳，钟永恒，等.青海镁产业专利导航发展分析［J］.无机盐工业，2021，53（5）：26-32.
	LI Xiaoyan， LIU Jia， ZHONG Yongheng，et al.Analysis on patent navigation development of Qinghai magnesium industry［J］.Inorganic Chemicals Industry，2021，53（5）：26-32.
16	CHEN Zhan， ZHANG Weijun， WANG Dongsheng，et al.Enhancement of activated sludge dewatering performance by combined composite enzymatic lysis and chemical re-flocculation with inorganic coagulants：Kinetics of enzymatic reaction and re-flocculation morphology［J］.Water Research，2015，83：367-376.
17	MANTILAKA M M M G P G， PITAWALA H M T G A， KARUNARATNE D G G P，et al.Nanocrystalline magnesium oxide from dolomite via poly（acrylate） stabilized magnesium hydroxide colloids［J］.Colloids and Surfaces A：Physicochemical and Engineering Aspects，2014，443：201-208.
18	申红艳，刘有智，白俊红.改善氢氧化镁过滤性能的实验研究［J］.无机盐工业，2014，46（8）：33-36.
	SHEN Hongyan， LIU Youzhi， BAI Junhong.Study on improvement of magnesium hydroxide filtration performance［J］.Inorganic Chemicals Industry，2014，46（8）：33-36.
19	BATES R G， PINCHING G D.Dissociation constant of aqueous ammonia at 0 to 50° from E.m.f. studies of the ammonium salt of a weak acid［J］.Journal of the American Chemical Society，1950，72（3）：1393-1396.
20	LOCKWOOD A P G， PEAKALL J， WARREN N J，et al.Structure and sedimentation characterisation of sheared Mg（OH）₂suspensions flocculated with anionic polymers［J］.Chemical Engineering Science，2021，231：116274.
21	AGERAEK M L， KEIDING K.On the origin of specific resistance to filtration［J］.Water Science and Technology，1993，28（1）：159-168.
22	BAI Shaojun， YU Pan， DING Zhang，et al.New insights into lead ions activation for microfine particle ilmenite flotation in sulfuric acid system：Visual MINTEQ models，XPS，and TOF-SIMS studies［J］.Minerals Engineering，2020，155.
23	LV Li， LIAO Hang， TAO Zhang，et al.Separation of calcium chloride from waste acidic raffinate in HCl wet process for phosphoric acid manufacture：Simulated and experimental study［J］.Journal of Environmental Chemical Engineering，2022，10（5）： 108076.
24	FAN Tianbo， HAN Dongxue， JIA Xiaohui，et al.Study on preparation and growth mechanism of MgSO₄·5Mg（OH）₂·3H₂O whiskers in NH₄ ⁺-NH₃ buffer system［J］.Journal of Chemical Engineering of Japan，2020，53（10）：646-652.
25	KADUK J A， BILLINGE S J L， DINNEBIER R E，et al.Powder diffraction［J］.Nature Reviews Methods Primers，2021，1：77.
26	GOLUBEV S V， POKROVSKY O S， SAVENKO V S.Homogeneous precipitation of magnesium phosphates from seawater solutions［J］.Journal of Crystal Growth，2001，223（4）：550-556.

矿物总类	lg IPA （pH=8.3）	饱和指数（pH=8.3）	饱和指数=0 时的pH
氢氧化镁	14.915	-2.185	8.85
Ca₃（PO₄）₂（am1）	-20.471	5.029	5.15
Ca₃（PO₄）₂（am2）	-20.471	7.779	5.15
Ca₃（PO₄）₂（beta）	-20.471	8.449	5.10
Ca₄H（PO₄）₃∙3H₂O（s）	-38.197	9.753	4.95
CaHPO₄（s）	-17.704	1.571	4.50
CaHPO₄∙2H₂O（s）	-17.719	1.276	4.70
萤石	-8.058	2.442	1.25
羟基磷灰石	-23.245	21.088	4.30
Mg（OH）₂（active）	14.915	-3.879	10.10
Mg₃（PO₄）₂（s）	-20.493	2.787	6.65
MgF₂（s）	-8.065	0.045	6.80
MgHPO₄∙3H₂O（s）	-17.733	0.442	5.55
羟钙石	14.922	-7.782	11.95
鸟粪石	-10.416	2.844	5.75

[1]	杨恩, 申红艳, 刘有智. 硅聚醚原位改性超细氢氧化镁的制备[J]. 无机盐工业, 2024, 56(4): 42-49.
[2]	蒋德敏, 李顺梅, 李青青, 陈雨欣, 刘代俊. 氢氧化镁与七水硫酸镁水热法合成碱式硫酸镁晶须[J]. 无机盐工业, 2023, 55(12): 74-81.
[3]	庞洪昌,王智煜,田朋,宁桂玲. “一锅法”合成双组分镁基阻燃剂及性能研究[J]. 无机盐工业, 2022, 54(8): 54-58.
[4]	范天博,胡婷婷,韩冬雪,贾晓辉,赵一波,王新安,郭洪范,李莉,刘云义. 煅烧白云石粉制备微纳米级圆片状氢氧化镁[J]. 无机盐工业, 2022, 54(1): 29-33.
[5]	孔会民,邹来禧,刘远,曹雨微,林彦军,罗仙平. 以轻烧氧化镁制备六角片状氢氧化镁的研究[J]. 无机盐工业, 2022, 54(1): 39-44.
[6]	张靖,柯昌美,段国权,王静雯. 新型聚丙烯酸酯乳液对纳米氢氧化镁的改性研究[J]. 无机盐工业, 2021, 53(9): 35-39.
[7]	黄建翠,凌观爽,宗俊. 水菱镁矿制备高分散六角片状纳米氢氧化镁的新工艺条件探究[J]. 无机盐工业, 2021, 53(2): 55-60.
[8]	朱华阳,仲剑初,于本儒,刘建行,罗鑫虎. 球形氧化镁的控制合成研究[J]. 无机盐工业, 2020, 52(11): 33-36.
[9]	范天博,姜宇,陈思,由钢,丁珂,孙晓君,刘露萍,李莉,刘云义,胡开宙,马峻茹,郭曦遥. TRIZ理论在轻烧粉氨气法制备氢氧化镁过程中的应用研究[J]. 无机盐工业, 2019, 51(5): 23-27.
[10]	丁珂1，孙晓君1，李会杰1，黄娜娜1，仇龙1，刘云义1，2，李雪1，2. 氧化镁蒸氨反应的动力学和机理研究[J]. 无机盐工业, 2019, 51(11): 31-35.
[11]	刘兴，刘润静，赵华，韩晓娑，孙烨. 碱式碳酸镁微观结构对视比容影响[J]. 无机盐工业, 2019, 51(11): 42-45.
[12]	陈云海，王海燕，周秀. 卤水结晶除杂工艺技术研究[J]. 无机盐工业, 2019, 51(11): 57-58.
[13]	郑焱, 何伟艳. 氯化镁-白云石为原料制备氢氧化镁的研究[J]. 无机盐工业, 2016, 48(8): 52-.
[14]	吴健松, 黄雪清, 伍思韵, 潘琳清, 邓国丽. 徐闻盐场苦卤制备阻燃型氢氧化镁[J]. 无机盐工业, 2016, 48(3): 56-.
[15]	金维, 徐跃鑫, 周骏宏, 王珏. 磷尾矿水洗-碳化法制氢氧化镁和碳酸钙研究[J]. 无机盐工业, 2016, 48(3): 49-.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会