球形LiMnPO4/C正极材料的喷雾干燥法制备及性能研究

doi:10.11962/1006-4990.2020-0101

Abstract

Abstract:

One-time spray-drying method was used to prepare spherical LiMnPO₄/C cathode materials with lithium hydroxide,manganese acetate,NH₄H₂PO₄ and polyethylene glycol as raw materials.The effect of calcination temperature on the morpho-logy,structure and electrochemical performance of spherical LiMnPO₄/C samples was studied.Its structure and morphology were characterized by X-ray diffraction（XRD）and field emission scanning electron microscopy（SEM）.The morphology and prechemical properties of LiMnPO₄/C obtained after calcination at different temperatures are quite different.The results showed that the spherical LiMnPO₄/C calcined at 700 ℃ had olivine-type crystal structure,and it showed a spherical shape composed of one-dimensional nano particles with a diameter of about 50 nm under SEM.The specific discharge capacity of this sample reached 148 mA·h/g for the first time at a rate of 0.1C at room temperature.After 80 cycles,the specific discharge capacity was still around 140 mA·h/g,and the capacity retention rate was 94.6%.

Key words: lithium-ion batteries, cathode material, LiMnPO₄, spray drying method

CLC Number:

TQ131.11

Zhang Kai,Jiang Ao. Preparation and properties of spherical LiMnPO₄/C cathode materials by spray drying method[J]. Inorganic Chemicals Industry, 2021, 53(1): 54-58.

Figures/Tables 8

References 20

[1]	Delacourt C, Laffont L, Bouchet R, et al. Toward understanding of electrical limitations(electronic,ionic) in LiMPO₄(M=Fe,Mn) el-ectrode materials[J]. Journal of the Electrochemical Society, 2005,152(5):A913-A921. doi: 10.1149/1.1884787
[2]	Padhi A K, Nanjundaswamy K S, Goodenough J B. Phospho-olivines as positive-electrode materials for rechargedeadle lithiu batteries[J]. Journal of the Electrochemical Society, 1997,144(4):1188-1194. doi: 10.1149/1.1837571
[3]	Yang C, Wang X, Liu G, et al. One-step hydrothermal synjournal of Ni-Co sulfide on Ni foam as a binder-free electrode for lithium-sulfur batteries[J]. Journal of Colloid and Interface Science, 2020,565(1):378-387. doi: 10.1016/j.jcis.2019.12.112
[4]	Padhi A K, Nanjundaswamy K S, Masquelier C, et al. Effect of struc-ture on the Fe²+/Fe³+ redox couple in iron phosphates[J]. Journal of the Electrochemical Society, 1997,144(5):1609-1613. doi: 10.1149/1.1837649
[5]	Yin S C, Grondey H, Strobel P, et al. Electrochemical property:St-ructure relationships in monoclinic Li_3-yV₂(PO₄)₃[J]. ChemInform, 2003,125(34):10402-10411.
[6]	Deng C, Zhang S, Ma L, et al. Effects of precipitator on the morpho-logical,structural and electrochemical characteristics of Li[Ni_1/3Co_1/3Mn_1/3]O₂ prepared via carbonate co-precipitation[J]. Jo-urnal of Alloys and Compounds, 2011,509(4):1322-1327.
[7]	Yang S Y, Wang X Y, Yang X K, et al. Influence of Li source on tap density and high rate cycling performance of spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ for advanced lithium-ion batteries[J]. Journal of Solid State Electrochemistry, 2012,16(3):1229-1237. doi: 10.1007/s10008-011-1513-6
[8]	Wang L, Zhang L, Lieberwirth I, et al. A Li₃V₂(PO₄)₃/C thin film with high rate capability as a cathode material for lithium-ion batteries[J]. Electrochemistry Communications, 2010,12(1):52-55. doi: 10.1016/j.elecom.2009.10.034
[9]	Malik R, Burch D, Bazant M, et al. Particle size dependence of the ionic diffusivity[J]. Nano Letters, 2010,10(10):4123-4127. pmid: 20795627
[10]	Kang B, Ceder G. Battery materials for ultrafast charging and disc-harging[J]. Nature, 2009,458(7235):190-193. doi: 10.1038/nature07853 pmid: 19279634
[11]	Wang L, He X, Sun W, et al. Crystal orientation tuning of LiFePO₄ nanoplates for high rate lithium battery cathode materials[J]. Nano Letters, 2012,12(11):5632-5636. doi: 10.1021/nl3027839 pmid: 23074971
[12]	Padhi A K, Archibald W B, Nanjundaswamy K S, et al. Ambient and high-pressure structures of LiMnVO₄ and its Mn³+/Mn²+ redox en-ergy[J]. Journal of Solid State Chemistry, 1997,128(2):267-272. doi: 10.1006/jssc.1996.7217
[13]	Wei Y J, Liang G C, Wang L, et al. Synjournal and electrochemical performance of LiFe_1-xMn_xPO₄/C cathode material[J]. Advanced Materials Research, 2011,347-353(1):3434-3438. doi: 10.4028/www.scientific.net/AMR.347-353
[14]	Jiang A, Wang X, Gao M, et al. Enhancement of electrochemical properties of niobium-doped LiFePO₄/C synthesized by sol-gel met-hod[J]. Journal of the Chinese Chemical Society, 2018,65(8):977-981. doi: 10.1002/jccs.2018.65.issue-8
[15]	Zhou F, Zhu P, Fu X, et al. Comparative study of LiMnPO₄ cathode materials synthesized by solvothermal methods using different manganese salts[J]. CrystEngComm, 2013,16(5):766-774. doi: 10.1039/C3CE41567H
[16]	Wang X, Zhao X, Wang J, et al. Electrospun Li₃V₂(PO₄)₃ nanobel-ts:synjournal and electrochemical properties as cathode materials of lithium-ion batteries[J]. Journal of the Chinese Chemical Socie-ty, 2017,64(5):97-104.
[17]	Hu P, Zhong K, Zhang C, et al. Spray drying synjournal and electro-chemical performance of lithium ion battery cathode materials LiNi_0.5Mn_1.5O₄[J]. Journal of Synthetic Crystals, 2015,44(8):2184-2190.
[18]	Wang Y, Wang X, Jiang A, et al. A versatile nitrogen-doped carbon coating strategy to improve the electrochemical performance of LiFePO₄ cathodes for lithium-ion batteries[J]. Journal of Alloys and Compounds, 2019,810(25):151889. doi: 10.1016/j.jallcom.2019.151889
[19]	Doan T N L, Bakenov Z, Taniguchi I. Preparation of carbon coated LiMnPO₄ powders by a combination of spray pyrolysis with dry ball-milling followed by heat treatment[J]. Advanced Powder Te-chnology, 2010,21(2):187-196.
[20]	Fan L, Wu L, Guan M, et al. Preparation of LiFe_(1-3y/2)Al_yPO₄ cathode material by precursor-doping combined room temperature reduc-tion via ball-milling[J]. The Chinese Journal of Nonferrous Metals, 2014,24(2):468-475.

样品	a/nm	b/nm	c/nm	晶胞体积/ nm³	D₁₃₁/nm
LMP-500	0.606 994	0.473 751	1.602 74	0.299 75	2.405 3
LMP-600	0.606 932	0.473 722	1.605 55	0.300 48	2.468 5
LMP-700	0.607 234	0.473 983	1.605 31	0.301 12	2.512 4
LMP-800	0.608 342	0.474 996	1.606 24	0.301 98	2.589 6
LMP-900	0.609 667	0.475 445	1.608 68	0.303 30	2.671 2

样品	R_e/Ω	R_ct/Ω	σ/ （Ω·s^-1/2）	D/ （cm²·s^-1）	i^o/ （mA·cm^-2）
LMP-600	7.025	308.52	79.44	1.82×10^-16	8.18×10^-5
LMP-700	3.480	82.548	135.6	1.04×10^-16	3.06×10^-4
LMP-800	4.658	98.206	78.21	1.85×10^-16	2.57×10^-4

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Preparation and properties of spherical LiMnPO₄/C cathode materials by spray drying method

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 20

Related Articles 15

Metrics

Comments

Recommended 10

[1]	Fan Qingke,Meng Qinghua,Luo Fengyu. Study on preparation and properties of cathode materials for vehicle lithium battery [J]. Inorganic Chemicals Industry, 2021, 53(1): 44-49.
[2]	Liu Peiwen,Dong Peng,Meng Qi,Yang Xuan,Zhou Siyuan. Research development of solid phase regeneration of cathode material of spent lithium iron phosphate batteries [J]. Inorganic Chemicals Industry, 2020, 52(9): 6-8.
[3]	Guo Ju,Jia Shuangzhu. Study of the method for the preparation of spherical-like and low sulfur FePO₄ [J]. Inorganic Chemicals Industry, 2020, 52(5): 31-34.
[4]	Wang Jiatai,Zhao Duan,Ma Lianhua,Zhang Caihong. Research progress of LiFePO₄ cathode materials for Li-ion battery [J]. Inorganic Chemicals Industry, 2020, 52(4): 18-22.
[5]	Long Yunfei,Su Jing,Lü Xiaoyan,Wen Yanxuan. Advances in transition metal fluoride phosphate cathode materials for lithium-ion batteries and sodium-ion batteries [J]. Inorganic Chemicals Industry, 2020, 52(3): 28-34.
[6]	Zhou Qiong,Du Shaolin,Xie Yinghao. Study on properties of lithium battery recycled graphite reinforced cement [J]. Inorganic Chemicals Industry, 2020, 52(11): 64-68.
[7]	Ye Jiaming,Li Changming. Research progress on anode material LiTi₂（PO₄）₃ for lithium-ion batteries [J]. Inorganic Chemicals Industry, 2019, 51(5): 17-22.
[8]	Liu Daliang1，2，Sun Guoping3，Liu Yafei1，2. Effect of blending process on properties of LiNi0.5Co0.2Mn0.3O2 cathode materials [J]. Inorganic Chemicals Industry, 2019, 51(10): 39-42.
[9]	XIA Ji-Ping, LI Xiao-Yun, GUO Qiu-Shuang. Effect of MgF2-coating on performance of LiNi1/3Co1/3Mn1/3O2 cathode materials [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(8): 79-.
[10]	GUO Hong-Xia, QIAO Yue-Chun, MU Pei-Zhen. Progress in research and application of cathode materials for lithium-ion battery [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(3): 5-.
[11]	MAO Jia-Yu, XIAO Yang. Research progress in doping modification of LiFePO4/C cathode materials [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(1): 13-.
[12]	. Technology research progress of cathode material of lithium ion battery [J]. INORGANICCHEMICALSINDUSTRY, 2015, 47(6): 1-.
[13]	HE Ai-Zhen, YE Xue-Hai, ZHI Xiao-Ke, LIU Chao, ZHAO Zhen, WANG Xu-Yang, ZHANG Su, SHI Jie. Influence of lithium content on electrochemical properties of Li1.2Mn0.6Ni0.2O2 material [J]. INORGANICCHEMICALSINDUSTRY, 2015, 47(4): 68-.
[14]	ZHANG Zheng-Guo. Preparation of ternary cathode material for lithium ion batteries assisted by surfactant [J]. INORGANICCHEMICALSINDUSTRY, 2015, 47(2): 67-.
[15]	ZHI Xiao-Ke, YE Xue-Hai, HE Ai-Zhen, ZHAO Zhen, ZHANG Su, SHI Jie, WANG Xu-Yang. Effects of annealing temperatures on electrochemical properties of LiNi0.5Mn1.5O4 cathode materials [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(8): 75-.

Preparation and properties of spherical LiMnPO4/C cathode materials by spray drying method