关键词: 高铁煤矸石, 酸浸液, 氧化铁红

Abstract: High-iron coal gangue was taken as the raw material to obtain ferric sulfate solution containing aluminum ions with sulfuric acid leaching method firstly.As totally turned into Fe（OH）₃ gel，the Fe³⁺ was separated from Al³⁺ by fractional precipitation，then the Fe（OH）₃ gel was calcined at high temperature after it was dried.At last，the iron oxide red was obtained after the calcined product being milled and sieved.The synthesis conditions of iron oxide red were determined: the concentration of Fe³⁺ in the acid leaching solution was 0.31 mol/L；the concentration of NaOH was 1 mol/L and the endpoint of the pH was about 3.0，when separating the Fe³⁺ from Al³⁺；the dry gel was calcined at 800 ℃ for 60 min.XRD and chemical analysis showed that the product was iron oxide red，and met the requirements of Iron Oxide Pigment，GB/T 1863—2008.

Key words: high-iron coal gangue, acid leaching solution, iron oxide red