Inorganic Chemicals Industry >

2024 , Vol. 56 >Issue 10: 103 - 109

DOI: https://doi.org/10.19964/j.issn.1006-4990.2024-0119

Environment·Health·Safety

Study on application of phosphogypsum oxalic acid pretreatment liquid in oriented silicon steel coatings

  • XIANG Linghui ,
  • WU Lin ,
  • LIU Ying ,
  • HU Ya
Expand
  • 1.School of Chemistry and Chemical Engineering, Wuhan University of Science and Technology, Wuhan 430081, China
    2.Academy of Green Manufacturing Engineering, Wuhan University of Science and Technology, Wuhan 430081, China
    3.College of Resource and Environmental Engineering, Wuhan University of Science and Technology, Wuhan 430081, China

Received date: 2024-03-04

  Online published: 2024-11-05

Fold

Abstract

Pretreatment is necessary for high value utilization of phosphogypsum，and the filtrate produced by water washing pre⁃treatment has not yet been well utilized.After component analysis，it was found that the filtrate contained components such as phosphates and aluminum，which were effective components for improving the corrosion resistance of coatings.The present study involved the preparation of phosphogypsum pretreatment filtrate and its incorporation into an inorganic chromium⁃free anti⁃corrosion coating for oriented silicon steel.A comparative analysis was conducted to evaluate the impact of pretreatment filtrate generated using water and oxalic acid solution at different temperatures on the corrosion resistance properties of the coating，and the substances present in the filtrate and their improvement mechanism on the anti⁃corrosion performance of the coatings were studied.Under the pretreatment of oxalic acid solution，pretreatment temperature of 20 ℃，and the addition of 5% pretreatment solution，the neutral salt spray experiment of oriented silicon steel sheet coating was decreased from 11% corrosion area after 36 hours to less than 1% corrosion area，and the corrosion current density was decreased to 0.317 1 μA/cm2，overall impedance modulus of coating was increased by 17%.The orthophosphate generated by the reaction between oxalic acid and phosphorus impurities accounted for more than 95% of the total phosphorus in the filtrate.The filtrate promoted deep cross⁃linking of the AlPO4 network to form the main network structure of the coating，highlights the role of MgO，and generated Mg3（PO4）2 network branches at high temperatures，forming microcrystalline Mg2P2O7 and AlF3 to fill the network pores，jointly improving the corrosion resistance of the coating.

Key words： phosphogypsum; oxalic acid; oriented silicon steel; coating; phosphate network

Cite this article

XIANG Linghui , WU Lin , LIU Ying , HU Ya . Study on application of phosphogypsum oxalic acid pretreatment liquid in oriented silicon steel coatings[J]. Inorganic Chemicals Industry, 2024 , 56(10) : 103 -109 . DOI: 10.19964/j.issn.1006-4990.2024-0119

References

1 匡国明.湿法磷酸工艺路线的探讨［J］.无机盐工业，2013， 45（4）：1-4.
  KUANG Guoming.Discussion on process routes of wet?process phosphoric acid［J］.Inorganic Chemicals Industry，2013，45（4）：1-4.
2 贺雷，朱干宇，郑光明，等.湿法磷酸体系磷石膏结晶过程与机理研究［J］.无机盐工业，2022，54（7）：110-116.
  HE Lei， ZHU Ganyu， ZHENG Guangming，et al.Study on crystallization process and mechanism of phosphogypsum in wet process phosphoric acid system［J］.Inorganic Chemicals Industry，2022，54（7）：110-116.
3 张峻，解维闵，董雄波，等.磷石膏材料化综合利用研究进展［J］.材料导报，2023，37（16）：163-174.
  ZHANG Jun， XIE Weimin， DONG Xiongbo，et al.Research progress on comprehensive utilization of phosphogypsum for materials：A review［J］.Materials Reports，2023，37（16）：163-174.
4 李东旭，焦嘉伟，廖大龙.我国磷石膏在新型建筑材料行业的发展及思考［J］.新型建筑材料，2021，48（11）：1-4，11.
  LI Dongxu， JIAO Jiawei， LIAO Dalong.The development and thinking of phosphogypsum used in new building materials in China［J］.New Building Materials，2021，48（11）：1-4，11.
5 姚炜栋，石林.低品位磷矿的资源化利用研究［J］.矿业研究与开发，2022，42（10）：63-68.
  YAO Weidong， SHI Lin.Resource utilization of low?grade phosphate rock［J］.Mining Research and Development，2022，42（10）：63-68.
6 张利珍，张永兴，吴照洋，等.脱除磷石膏中水溶磷、水溶氟的实验研究［J］.无机盐工业，2022，54（4）：40-45.
  ZHANG Lizhen， ZHANG Yongxing， WU Zhaoyang，et al.Experimental study on removal of water?soluble phosphorus and water?soluble fluorine from phosphogypsum［J］.Inorganic Chemicals Industry，2022，54（4）：40-45.
7 董泽，翟延波，任志威，等.磷石膏建材资源化利用研究进展［J］.无机盐工业，2022，54（4）：5-9.
  DONG Ze， ZHAI Yanbo， REN Zhiwei，et al.Research progress on phosphogypsum utilization in building materials［J］.Inorganic Chemicals Industry，2022，54（4）：5-9.
8 王秀秀.磷石膏渗滤液除磷研究［D］.重庆：重庆大学，2021.
  WANG Xiuxiu.Study on phosphorus removal from phosphogypsum leachate［D］.Chongqing：Chongqing University，2021.
9 SONG Xiaoyan， PAN Yanqiu， WU Quyin，et al.Phosphate removal from aqueous solutions by adsorption using ferric sludge［J］.Desalination，2011，280（1/2/3）：384-390.
10 杨浩，王成，肖小波，等.添加硼酸和钨酸铵对取向硅钢无铬绝缘涂层的影响［J］.材料导报，2021，35（22）：22141-22145.
  YANG Hao， WANG Cheng， XIAO Xiaobo，et al.Effects of boric acid and ammonium tungstate additions on the chromium?free insulating coating of grain?oriented silicon steel［J］.Materials Reports，2021，35（22）：22141-22145.
11 CHENG Ling， MENG Li， GUO Dawei，et al.Deterioration law and evaluation of insulation coating of grain?oriented silicon steel in service［J］.Iron & Steel，2019，54（1）：79-84.
12 LIU Ying， WU Lin， CHEN Ao，et al.Component design of environmentally friendly high?temperature resistance coating for oriented silicon steel and effects on anti?corrosion property［J］.Coatings，2022，12（7）：959.
13 CAI Qiang， JIANG Jun， MA Bing，et al.Efficient removal of phosphate impurities in waste phosphogypsum for the production of cement［J］.Science of the Total Environment，2021，780：146600.
14 曹京宜，熊金平，李水冰，等.利用EIS高频区参数评价两种环氧涂层的性能［J］.化工学报，2008，59（11）：2851-2856.
  CAO Jingyi， XIONG Jinping， LI Shuibing，et al.Evaluation of protective performance of organic coatings by EIS parameters at high frequency zone［J］.CIESC Journal，2008，59（11）：2851-2856.
15 翁诗甫.傅里叶变换红外光谱分析［M］.2版.北京：化学工业出版社，2010：348-352.
16 史学海，陈志宇，周斌，等.无机磷酸盐耐高温涂料的防腐机理及研究进展［J］.电镀与涂饰，2021，40（14）：1110-1118.
  SHI Xuehai， CHEN Zhiyu， ZHOU Bin，et al.Anticorrosion mechanism and research progress of high?temperature?resistant inorganic phosphate coatings［J］.Electroplating & Finishing，2021，40（14）：1110-1118.
17 陈洋，丁军，邓承继，等.室温固化磷酸二氢铝-硅溶胶复合高温黏结剂的制备及物理性能［J］.硅酸盐学报，2018，46（12）：1762-1770.
  CHEN Yang， DING Jun， DENG Chengji，et al.Preparation and physical properties of room?temperature curing aluminum dihydrogen phosphate-silica sol composite high temperature adhesi?ve［J］.Journal of the Chinese Ceramic Society，2018，46（12）：1762-1770.
18 张全利，陈长林.偏磷酸镁修饰钨铝复合氧化物载铂催化剂的稳定性研究［J］.南京工业大学学报（自然科学版），2022， 44（1）：36-44.
  ZHANG Quanli， CHEN Changlin.Study on stability of platinum supported on tungsten-aluminum composite oxide modified by magnesium metaphosphate［J］.Journal of Nanjing Tech University（Natural Science Edition），2022，44（1）：36-44.
19 杨淑莉，李富天，邓毅，等.酸性高氯介质中氟离子对Incoloy825合金腐蚀行为的影响［J］.焊管，2023，46（10）：8-13.
  YANG Shuli， LI Futian， DENG Yi，et al.Effect of fluoride ions on corrosion behavior of Incoloy825 alloy in acidic high chloride solution［J］.Welded Pipe and Tube，2023，46（10）：8-13.
20 XIAO Wei， WANG Ying.Corrosion resistance of aluminum fluoride modified 6061 aluminum alloy［J］.Materials Letters，2021，298：129932.
21 WANG Zhijiang， WU Lina， CAI Wei，et al.Effects of fluoride on the structure and properties of microarc oxidation coating on aluminium alloy［J］.Journal of Alloys and Compounds，2010，505（1）：188-193.
Options
Outlines

/

〈 〉



Copyright © 2021 Editorial Office of Inorganic Chemicals Industry

Add:No.3 Road Dingzigu,Hongqiao District,Tianjin,China

E-mail：book@wjygy.com.cn 违法和不良信息举报电话: 022-26689297