Research on preparation and mechanism of superhydrophobic phosphogypsum products
Received date: 2024-03-05
Online published: 2024-04-10
In order to improve the water resistance of phosphogypsum products and the utilization rate of phosphogypsum，the effects of three activators（alcohol amine activator，calcium activator，and silicon aluminum activator） on the strength，water absorption rate，24 h water absorption rate，and softening coefficient of phosphogypsum products containing silicon oil were discussed in this paper.The water resistance of phosphogypsum products containing calcareous activator under different silicone oil content was further studied.Combined with contact angle and scanning electron microscope（SEM） test methods，the water resistance mechanism of calcium activator-silicon oil phosphogypsum products was revealed.The results showed that the strength of phosphogypsum products containing silicone oil was decreased gradually with the increase of the content of three activators.While the 24 h water absorption and softening coefficient showed different changing rules with the contents of three activators.Among them，phosphogypsum products containing silicone oil doped with 1% calcium activator had better strength，water absorption resistance and softening coefficient.When the content of calcium activator was 1% and the content of silicone oil was 0.10%，the water absorption rate of phosphogypsum was 3.38% for 24 h，13.97% for 14 d，and the softening coefficient was 0.86，showing superhydrophobicity.It was due to the chemical condensation reaction between calcium activator and silicone oil，which embedded/attached small synapses in the gypsum matrix，forming the “lotus leaf effect”.
TANG Kaijing , LIU Chuanbei , LI Yingding , JIANG Yong , WU Junnan , ZHANG Tao . Research on preparation and mechanism of superhydrophobic phosphogypsum products[J]. Inorganic Chemicals Industry, 2025 , 57(1) : 97 -102 . DOI: 10.19964/j.issn.1006-4990.2024-0123
| 1 | 李莹，段鹏选，倪文，等.基于生命周期的工业副产石膏制备胶凝材料碳足迹评价［J］.硅酸盐通报，2023，42（6）：1921-1930. |
| LI Ying， DUAN Pengxuan， NI Wen，et al.Carbon footprint assessment of cementitious materials prepared from industrial by-product gypsum based on life cycle［J］.Bulletin of the Chinese Ceramic Society，2023，42（6）：1921-1930. | |
| 2 | 郝建英，胡涛，程冠吉，等.脱硫石膏掺杂氧化锌转晶制备高性能建筑石膏［J］.无机盐工业，2022，54（6）：96-101. |
| HAO Jianying， HU Tao， CHENG Guanji，et al.Preparation of high-performance building gypsum by desulfurization gypsum doped with ZnO crystal transformation［J］.Inorganic Chemicals Industry，2022，54（6）：96-101. | |
| 3 | 谢浪，罗双，付汝宾，等.纤维-建筑石膏基复合材料力学及耐水性能研究进展［J］.新型建筑材料，2021，48（6）：34-39. |
| XIE Lang， LUO Shuang， FU Rubin，et al.Review of research progress on mechanical properties and water resistance of fiber-building gypsum based composites［J］.New Building Materials，2021，48（6）：34-39. | |
| 4 | 赵敏，张明涛，彭家惠，等.硫铝酸盐水泥增强建筑石膏的力学性能与耐水性能机理［J］.材料导报，2021，35（12）：12099-12102. |
| ZHAO Min， ZHANG Mingtao， PENG Jiahui，et al.Mechanisms for the improvement of mechanical properties and water resistance of building gypsum by sulphoaluminate cement［J］.Materials Reports，2021，35（12）：12099-12102. | |
| 5 | 郭会师，王庆佩，张果，等.普通硅酸盐水泥改性脱硫建筑石膏耐水性能［J］.硅酸盐通报，2021，40（7）：2288-2295. |
| GUO Huishi， WANG Qingpei， ZHANG Guo，et al.Water resistance of flue gas desulfurization building gypsum modified by ordinary Portland cement［J］.Bulletin of the Chinese Ceramic Society，2021，40（7）：2288-2295. | |
| 6 | 张峻，解维闵，董雄波，等.磷石膏材料化综合利用研究进展［J］.材料导报，2023，37（16）：167-178. |
| ZHANG Jun， XIE Weimin， DONG Xiongbo，et al.Research progress on comprehensive utilization of phosphogypsum for materials：A review［J］.Materials Reports，2023，37（16）：167-178. | |
| 7 | 周祥，李亮，张晓敏，等.硅酸盐水泥熟料和硅灰对磷建筑石膏耐水性和水化行为的影响［J］.新型建筑材料，2023，50（9）：77-81. |
| ZHOU Xiang， LI Liang， ZHANG Xiaomin，et al.Effect of silicate clinker and silica fume on water resistance and hydration behavior of phosphogypsum［J］.New Building Materials，2023，50（9）：77-81. | |
| 8 | 李桦军，刘东辉，王平艳，等.石膏防水剂的研究进展［J］.硅酸盐通报，2014，33（4）：831-835. |
| LI Huajun， LIU Donghui， WANG Pingyan，et al.Research progress on gypsum waterproofing agent［J］.Bulletin of the Chinese Ceramic Society，2014，33（4）：831-835. | |
| 9 | 齐艳涛，刘芳，张奔，等.激发剂对掺有机硅磷石膏制品耐水性的影响［J］.材料导报，2015，29（S2）：450-452，467. |
| QI Yantao， LIU Fang， ZHANG Ben，et al.Effects of activator on water resistance of phosphogypsum mixed with silicone［J］.Materials Reports，2015，29（S2）：450-452，467. | |
| 10 | 马红恩，吴其胜，钱旭阳，等.硅烷改性苯丙乳液对脱硫石膏防水性能的影响［J］.材料科学与工程学报，2020，38（2）：269-273，307. |
| MA Hongen， WU Qisheng， QIAN Xuyang，et al.Effect of silane modified styrene-acrylic emulsion on waterproof properties of desulfurized gypsum［J］.Journal of Materials Science and Engineering，2020，38（2）：269-273，307. | |
| 11 | 陈畅，邓逸豪，王绪富，等.含氢硅油乳液对脱硫石膏砌块耐水性能影响［J］.非金属矿，2021，44（5）：15-18. |
| CHEN Chang， DENG Yihao， WANG Xufu，et al.Effect of polymethylhydrosiloxane emulsion on hydrolytic resistance of FGD gypsum blocks［J］.Non-Metallic Mines，2021，44（5）：15-18. | |
| 12 | 延海龙.利用磷石膏制备建筑砌块的防水性能研究［D］.济南：济南大学，2020. |
| YAN Hailong.Study on waterproof performance of building blocks made of phosphogypsum［D］.Jinan：University of Jinan，2020. | |
| 13 | FERNANDEZ-TOLEDANO J C， BLAKE T D， LAMBERT P，et al.On the cohesion of fluids and their adhesion to solids：Young′s equation at the atomic scale［J］.Advances in Colloid and Interface Science，2017，245：102-107. |
| 14 | 刘子涵.地质聚合物基硅酮纳米纤维超疏水复合涂层的制备与性能研究［D］.南宁：广西大学，2019. |
| LIU Zihan.Preparation and properties of geopolymer-based silicone nanofilaments superhydrophobic composite coatings［D］.Nanning：Guangxi University，2019. | |
| 15 | NEINHUIS C， BARTHLOTT W.Characterization and distribution of water-repellent，self-cleaning plant surfaces［J］.Annals of Botany，1997，79（6）：667-677. |
| 16 | BARTHLOTT W， NEINHUIS C.Purity of the sacred lotus，or escape from contamination in biological surfaces［J］.Planta，1997，202（1）：1-8. |
/
| 〈 |
|
〉 |