Study on preparation of magnesium hydroxide from calcium magnesium nitrate leaching pretreatment of phosphate rock with high content of magnesium and calcium
Received date: 2023-07-27
Online published: 2024-05-15
The decomposition of calcium magnesium carbonate salts by calcining phosphate rock with high content of magnesium and calcium can effectively improve the grade of phosphate rock.Leachate and phosphate rock with low magnesium content are obtained by further hydrating and leaching the calcined phosphate rock.The leachate is further precipitated to prepare magnesium hydroxide.However，there are difficulties in solid-liquid separation and low product purity in the production process of magnesium hydroxide.The properties，specific resistance，and settling performance of wet filter cakes prepared at different temperatures were systematically studied.The results showed that the filter cakes adsorbed more water at lower temperatures，making filtration difficult and washing burdensome.When the temperature was rised to 70 ℃，the magnesium hydroxide colloid could be effectively destroyed，thus reducing the adsorption of water by filter cake，reducing the washing burden，and significantly improving the settlement and filtration performance of magnesium hydroxide.The sedimentation rate was up to 0.051 8 mL/min，and the minimum specific resistance of filtration was（5.82±1.1）×1011 m/kg.The recovery ratio of magnesium could reach 72%.Further simulation analysis of the precipitation process showed that the two-step precipitation method could realize the pre-separation of impurities，thus improving the purity of magnesium hydroxide，and the product purity could meet the requirements of industrial magnesium hydroxide grade Ⅲ.
TANG Biao , TANG Shengwei . Study on preparation of magnesium hydroxide from calcium magnesium nitrate leaching pretreatment of phosphate rock with high content of magnesium and calcium[J]. Inorganic Chemicals Industry, 2024 , 56(5) : 87 -93 . DOI: 10.19964/j.issn.1006-4990.2023-0391
| 1 | LIU Qiang， LIU Weizao， Li Lü，et al.Study on reactions of gaseous P2O5 with Ca3（PO4）2 and SiO2 during a rotary kiln process for phosphoric acid production［J］.Chinese Journal of Chemical Engineering，2018，26（4）：795-805. |
| 2 | CHEN Fang， WANG Xiaomei， LIU Weizao，et al.Selective extraction of nitric and acetic acids from etching waste acid using N235 and MIBK mixtures［J］.Separation and Purification Technology，2016，169：50-58. |
| 3 | ABDEL-GHAFAR H M， ABDEL-AAL E A， IBRAHIM M A M，et al.Purification of high iron wet-process phosphoric acid via oxalate precipitation method［J］.Hydrometallurgy，2019，184：1-8. |
| 4 | BECKER P.Phosphates and phosphoric acid：Raw materials，technology，and economics of the wet process（Second edition）［M］.CRC Press，1989. |
| 5 | ZHANG P.Comprehensive recovery and sustainable development of phosphate resources［J］.Procedia Engineering，2014，83：37-51. |
| 6 | LI Hongqiang， GE Wu， ZHANG Jun，et al.Control foaming performance of phosphate rocks used for wet-process of phosphoric acid production by phosphoric acid［J］.Hydrometallurgy，2020，195：105364. |
| 7 | SILVA L F O， OLIVEIRA M L S， CRISSIEN T J，et al.A review on the environmental impact of phosphogypsum and potential health impacts through the release of nanoparticles［J］.Chemosphere，2022，286：131513. |
| 8 | TAYIBI H， CHOURA M， LóPEZ F A，et al.Environmental impact and management of phosphogypsum［J］.Journal of Environmental Management，2009，90（8）：2377-2386. |
| 9 | 何宾宾，魏立军，谢德龙，等.中国湿法磷加工产业现状与可持续发展［J］.无机盐工业，2020，52（1）：1-4，16. |
| HE Binbin， WEI Lijun， XIE Delong，et al.Current situation and sustainable development of wet process phosphorus processing industry in China［J］.Inorganic Chemicals Industry，2020，52（1）：1-4，16. | |
| 10 | LV Li， ZHENG Dongyao， TANG Shengwei，et al.Phosphate ore particles dissolution kinetics in hydrochloric acid based on a structure-related segmented model［J］.Powder Technology，2021，392：141-149. |
| 11 | 方进，李菊，孟品品，等.冷冻法硝酸磷肥副产粗硝钙液用于磷矿脱镁的研究［J］.无机盐工业，2021，53（6）：180-184. |
| FANG Jin， LI Ju， MENG Pinpin，et al.Study on by-product crude calcium nitrate solution of frozen nitrophosphate fertilizer for phosphate rock demagnesium［J］.Inorganic Chemicals Industry，2021，53（6）：180-184. | |
| 12 | 殷灵，李军，唐湘.硝酸磷肥生产新工艺研究［J］.无机盐工业，2014，46（12）：50-53. |
| YIN Ling， LI Jun， TANG Xiang.Study on new production technology of nitrophosphate fertilizer［J］.Inorganic Chemicals Industry，2014，46（12）：50-53. | |
| 13 | WU Junhu， XU Dehua， YANG Xiushan，et al.Determination and correlation of vapor-liquid equilibria for the nitric acid+water，nitric acid+water+phosphoric acid，and nitric acid+water+phosphoric acid+sulfuric acid system［J］.Journal of Chemical & Engineering Data，2023，68（3）：633-641. |
| 14 | 向伟，王勃，应建康.硫酸铵法硝酸磷肥生产高品质硫酸钙工艺研究［J］.无机盐工业，2013，45（1）：17-20. |
| XIANG Wei， WANG Bo， YING Jiankang.Study on producing process of high-quality calcium sulfate from nitric phosphate by ammonium sulfate method［J］.Inorganic Chemicals Industry，2013，45（1）：17-20. | |
| 15 | 李晓妍，刘佳，钟永恒，等.青海镁产业专利导航发展分析［J］.无机盐工业，2021，53（5）：26-32. |
| LI Xiaoyan， LIU Jia， ZHONG Yongheng，et al.Analysis on patent navigation development of Qinghai magnesium industry［J］.Inorganic Chemicals Industry，2021，53（5）：26-32. | |
| 16 | CHEN Zhan， ZHANG Weijun， WANG Dongsheng，et al.Enhancement of activated sludge dewatering performance by combined composite enzymatic lysis and chemical re-flocculation with inorganic coagulants：Kinetics of enzymatic reaction and re-flocculation morphology［J］.Water Research，2015，83：367-376. |
| 17 | MANTILAKA M M M G P G， PITAWALA H M T G A， KARUNARATNE D G G P，et al.Nanocrystalline magnesium oxide from dolomite via poly（acrylate） stabilized magnesium hydroxide colloids［J］.Colloids and Surfaces A：Physicochemical and Engineering Aspects，2014，443：201-208. |
| 18 | 申红艳，刘有智，白俊红.改善氢氧化镁过滤性能的实验研究［J］.无机盐工业，2014，46（8）：33-36. |
| SHEN Hongyan， LIU Youzhi， BAI Junhong.Study on improvement of magnesium hydroxide filtration performance［J］.Inorganic Chemicals Industry，2014，46（8）：33-36. | |
| 19 | BATES R G， PINCHING G D.Dissociation constant of aqueous ammonia at 0 to 50° from E.m.f. studies of the ammonium salt of a weak acid［J］.Journal of the American Chemical Society，1950，72（3）：1393-1396. |
| 20 | LOCKWOOD A P G， PEAKALL J， WARREN N J，et al.Structure and sedimentation characterisation of sheared Mg（OH）2 suspensions flocculated with anionic polymers［J］.Chemical Engineering Science，2021，231：116274. |
| 21 | AGERAEK M L， KEIDING K.On the origin of specific resistance to filtration［J］.Water Science and Technology，1993，28（1）：159-168. |
| 22 | BAI Shaojun， YU Pan， DING Zhang，et al.New insights into lead ions activation for microfine particle ilmenite flotation in sulfuric acid system：Visual MINTEQ models，XPS，and TOF-SIMS studies［J］.Minerals Engineering，2020，155. |
| 23 | LV Li， LIAO Hang， TAO Zhang，et al.Separation of calcium chloride from waste acidic raffinate in HCl wet process for phosphoric acid manufacture：Simulated and experimental study［J］.Journal of Environmental Chemical Engineering，2022，10（5）： 108076. |
| 24 | FAN Tianbo， HAN Dongxue， JIA Xiaohui，et al.Study on preparation and growth mechanism of MgSO4·5Mg（OH）2·3H2O whiskers in NH4 +-NH3 buffer system［J］.Journal of Chemical Engineering of Japan，2020，53（10）：646-652. |
| 25 | KADUK J A， BILLINGE S J L， DINNEBIER R E，et al.Powder diffraction［J］.Nature Reviews Methods Primers，2021，1：77. |
| 26 | GOLUBEV S V， POKROVSKY O S， SAVENKO V S.Homogeneous precipitation of magnesium phosphates from seawater solutions［J］.Journal of Crystal Growth，2001，223（4）：550-556. |
/
| 〈 |
|
〉 |