Research progress and application of α-hemihydrate gypsum preparation from desulfurization gypsum
Received date: 2023-04-26
Online published: 2024-02-06
With the continuous development of China's industry，a large amount of desulphurization gypsum has been produced.At present，although the current comprehensive utilization of desulfurization gypsum is increasing year by year，its utilization rate is decreasing，and it is indispensable to explore the high-value utilization path of desulfurization gypsum.One of the ways to resource utilization of desulfurization gypsum is to dehydrate and convert it into α-hemihydrate gypsum.Using desulfurization gypsum to prepare high-performance and high-value-added α-hemihydrate gypsum can reduce the environmental pollution caused by gypsum accumulation，reduce the mining of natural gypsum and bring new economic benefits.Based on this，the current research status of the methods of preparing α-hemihydrate gypsum from desulphurization gypsum at home and abroad and its influencing factors were systematically reviewed，its production process path and its applications were summarized，and the prospect of promoting the reduction and resource utilization of desulfurization gypsum were put forward，aiming to improve the utilization rate of solid waste and promote“carbon neutrality and carbon emission reduction”.
YANG Fengling , QIAO Guoxin , YANG Pu , REN Lei , WANG Qiong , WU Haibin , CHENG Fangqin . Research progress and application of α-hemihydrate gypsum preparation from desulfurization gypsum[J]. Inorganic Chemicals Industry, 2024 , 56(2) : 11 -20 . DOI: 10.19964/j.issn.1006-4990.2023-0242
| 1 | 中华人民共和国生态环境部.2014—2020年全国大中城市固体废物污染环境防治年报［EB/OL］.［2020-12-28］.https://www.mee.gov.cn/hjzl/sthjzk/gtfwwrfz/. |
| 2 | 中商产业研究院.2021年中国新型建材产业链上中下游市场剖析［EB/OL］.［2021-9-26］.https://www.askci.com/news/chanye/20210926/1500221603972_5.shtml. |
| 3 | 高子栋，展琳琳.浅谈我国脱硫石膏环保资源化综合利用现状［J］.砖瓦，2022（6）：44-46，49. |
| GAO Zidong， ZHAN Linlin.Current situation of comprehensive utilization of desulfurization gypsum environmental protection resources［J］.Brick-Tile，2022（6）：44-46，49. | |
| 4 | 张志明，桂联政，廖达琛，等.燃煤电厂粉煤灰高值化利用研究进展［J］.能源环境保护，2023，37（4）：1-11. |
| ZHANG Zhiming， GUI Lianzheng， LIAO Dachen，et al.Advances in high-value utilization of fly ash from coal-fired power plants［J］.Energy Environmental Protection，2023，37（4）：1-11. | |
| 5 | 赵龙广，艾勇.火电厂脱硫石膏的产生与利用现状［J］.科技视界，2017（7）：209-210. |
| ZHAO Longguang， AI Yong.Research progress for comprehensive utilization of FGD gypsum［J］.Science & Technology Vision， 2017（7）：209-210. | |
| 6 | GUAN Qingjun， SUI Ying， ZHANG Fang，et al.Preparation of α-calcium sulfate hemihydrate from industrial by-product gypsum：A review［J］.Physicochemical Problems of Mineral Processing，2020，57（1）：168-181. |
| 7 | 胡宏，何兵兵，薛绍秀. α-半水石膏的制备与应用研究进展［J］.新型建筑材料，2015，42（4）：44-48. |
| HU Hong， HE Bingbing， XUE Shaoxiu.Research progress on pre-paration and application of α-calcium sulfate hemihydrate［J］.New Building Materials，2015，42（4）：44-48. | |
| 8 | ZHANG Xiaofei， WANG Jinshu， WU Junshu，et al.Phase-and morphology-controlled crystallization of gypsum by using flue-gas-desulfurization gypsum solid waste［J］.Journal of Alloys and Compounds，2016，674：200-206. |
| 9 | SCHMIDT H， PASCHKE I， FREYER D，et al.Water channel structure of bassanite at high air humidity：Crystal structure of CaSO4·0.625H2O［J］.Acta Crystallographica Section B Structural Science，2011，67（6）：467-475. |
| 10 | JACQUES S D M， GONZáLEZ-SABORIDO A， LEYNAUD O，et al.Structural evolution during the dehydration of gypsum materials［J］.Mineralogical Magazine，2009，73（3）：421-432. |
| 11 | BALLIRANO P， MARAS A， MELONI S，et al.The monoclinic I2 structure of bassanite，calcium sulphate hemihydrate（CaSO4·0.5H2O）［J］.European Journal of Mineralogy，2001，13（5）：985-993. |
| 12 | BEZOU C， NONAT A， MUTIN J C，et al.Investigation of the crystal structure of γ-CaSO4，CaSO4·0.5H2O，and CaSO4·0.6H2O by powder diffraction methods［J］.Journal of Solid State Chemistry，1995，117（1）：165-176. |
| 13 | 郭会宾.脱硫石膏制备α-半水石膏工艺研究［D］.西宁：青海大学，2013. |
| GUO Huibin.Research of process conditions on the preparation of hemi hydrate gypsum from desulfurization gypsum［D］.Xining：Qinghai University，2013. | |
| 14 | 董一苇，徐祖顺，杨婷婷，等.化学石膏制备α-半水石膏的研究进展［J］.材料导报，2021，35（S2）：241-247. |
| DONG Yiwei， XU Zushun， YANG Tingting，et al.Research progress on the preparation of α-calcium sulfate hemihydrate from chemical gypsum［J］.Materials Reports，2021，35（S2）：241- 247. | |
| 15 | YANG Baojun， DONG Yinzhe， WANG Bainian，et al.A mild alcohol-salt route to synthesize α-hemihydrate gypsum microrods from flue gas desulfurization gypsum in large scale［J］.Materials Research Express，2019，6（4）：045507. |
| 16 | 龚小梅，宾晓蓓，杨少博，等.脱硫石膏转化为半水石膏的过程及机理［J］.硅酸盐通报，2015，34（9）：2491-2495. |
| GONG Xiaomei， Xiaobei BIN， YANG Shaobo，et al.Preparation and mechanism of hemihydrate gypsum with FGD gypsum［J］.Bulletin of the Chinese Ceramic Society，2015，34（9）：2491-2495. | |
| 17 | 吴晓琴，杨有余，裘建军.常压盐溶液法转化脱硫石膏制备α-半水石膏的相变机理［J］.武汉科技大学学报，2011，34（1）：37-41. |
| WU Xiaoqin， YANG Youyu， QIU Jianjun.Mechanism of α-calcium sulfate hemihydrate produced from FGD gypsum in thermal solution［J］.Journal of Wuhan University of Science and Technology，2011，34（1）：37-41. | |
| 18 | 邵朵朵.脱硫石膏制备大颗粒α-半水石膏及其增白工艺的研究［D］.天津：河北工业大学，2018. |
| SHAO Duoduo.Study on the preparation of large-grained α-calcium sulfate hemihydrate and the whitening process of flue gas desulfurization gypsum［D］.Tianjin：Hebei University of Technology，2018. | |
| 19 | 董胤喆.常压醇盐体系由脱硫石膏制备α-半水石膏的工艺条件研究［D］.合肥：合肥工业大学，2019. |
| DONG Yinzhe.Study on the prepartion conditions of α-hemihydrate gypsum from flue gas desulfurization gypsum in alcohol-salt system under normal pressure［D］.Hefei：Hefei University of Technology，2019. | |
| 20 | SAKAKIBARA S.Method of producing a gypsum plaster board：US，4392896［P］.1983-07-12. |
| 21 | 赵辉. α半水石膏的制备及其改性［D］.武汉：湖北大学，2015. |
| ZHAO Hui.Preparation and modification of α hemihydrate gypsum［D］.Wuhan：Hubei University，2015. | |
| 22 | 吴传龙.常压醇水法α-半水石膏的形貌调控及性能研究［D］.绵阳：西南科技大学，2016. |
| WU Chuanlong.Study on morphology control and performance of α-hemihydrate gypsum by the glycerol water method at atmospheric pressure［D］.Mianyang：Southwest University of Science and Technology，2016. | |
| 23 | 陈金文，易芸，张慧，等.蒸压参数与杂质对磷石膏制备α-半水石膏的影响［J］.无机盐工业，2022，54（3）：91-96. |
| CHEN Jinwen， YI Yun， ZHANG Hui，et al.Effect of autoclave parameters and impurities on preparation of α-hemihydrate gypsum from phosphogypsum［J］.Inorganic Chemicals Industry，2022，54（3）：91-96. | |
| 24 | 黎明川，韦家崭，陈平，等.转晶剂与蒸压参数对磷石膏制备α半水石膏的影响［J］.无机盐工业，2022，54（8）：132-137. |
| LI Mingchuan， WEI Jiazhan， CHEN Ping，et al.Effect of crystal modifier and autoclave parameters on preparation of α-hemihydrate gypsum from phosphogypsum［J］.Inorganic Chemicals Industry，2022，54（8）：132-137. | |
| 25 | KAMAROU M， KOROB N， KWAPINSKI W，et al.High-quality gypsum binders based on synthetic calcium sulfate dihydrate produced from industrial waste［J］.Journal of Industrial and Engineering Chemistry，2021，100：324-332. |
| 26 | 陈勇，张毅，李东旭.利用脱硫石膏制备α-半水石膏的蒸压制度研究［J］.硅酸盐通报，2015，34（5）：1241-1245. |
| CHEN Yong， ZHANG Yi， LI Dongxu.Autoclaved system research of calcium sulfate prepared with desulfurization gypsum［J］.Bulletin of the Chinese Ceramic Society，2015，34（5）：1241-1245. | |
| 27 | 徐成.石膏固废制备α-半水石膏工艺及性能研究［D］.常州：常州大学，2022. |
| XU Cheng.Study on the technology and performance of α-hemihydrate gypsum prepared from gypsum solid waste［D］.Changzhou：Changzhou University，2022. | |
| 28 | 韩康，管学茂，王燕峰，等.加压水溶液法制备工艺对α型高强石膏性能的影响［J］.硅酸盐通报，2021，40（5）：1620-1630，1645. |
| HAN Kang， GUAN Xuemao， WANG Yanfeng，et al.Effect of preparation process of pressurized aqueous solution method on properties of α-high strength gypsum［J］.Bulletin of the Chinese Ceramic Society，2021，40（5）：1620-1630，1645. | |
| 29 | 岳文海，王志. α半水石膏晶形转化剂作用机理的探讨［J］.武汉工业大学学报，1996，18（2）：1-4. |
| YUE Wenhai， WANG Zhi.Investigation on the mechanism of crystal shape modifying agent of α-hemihydrate［J］.Journal of Wuhan University of Technology，1996，18（2）：1-4. | |
| 30 | 胡俊要，李军，金央，等.盐种类对常压盐溶液法制备半水石膏的影响［J］.无机盐工业，2018，50（6）：47-50. |
| HU Junyao， LI Jun， JIN Yang，et al.Effect of salt species on preparation of hemihydrate gypsum by atmospheric salt solution method［J］.Inorganic Chemicals Industry，2018，50（6）：47-50. | |
| 31 | 丁峰，窦焰，郑之银，等.常压盐溶液-丁二酸转晶体系中pH对α-CaSO4·0.5H2O的影响［J］.无机盐工业，2020，52（1）：82-86，98. |
| DING Feng， DOU Yan， ZHENG Zhiyin，et al.Effect of pH on α-CaSO4·0.5H2O in salt solution at atmospheric pressure-succinic acid crystal transfer system［J］.Inorganic Chemicals Industry，2020，52（1）：82-86，98. | |
| 32 | 胡成，向玮衡，陈平，等.丁二酸对水热合成α-半水脱硫石膏微晶形貌及力学强度的影响［J］.无机盐工业，2021，53（4）：76-80. |
| HU Cheng， XIANG Weiheng， CHEN Ping，et al.Effects of succinic acid on crystallite morphology and mechanical strength of α-hemihydrate desulfurized gypsum synthesized by hydrothermal method［J］.Inorganic Chemicals Industry，2021，53（4）：76-80. | |
| 33 | MA Baoguo， LU Wenda， SU Ying，et al.Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum［J］.Journal of Cleaner Production，2018，195：396-405. |
| 34 | 杨后文，刘丰，江郡，等.常压水热法制备半水脱硫石膏的工艺因素研究［J］.矿产综合利用，2021（1）：140-143，198. |
| YANG Houwen， LIU Feng， JIANG Jun，et al.Research on process condition on the preparation of hemihydrate desulfurization gypsum with hydrothermal method under atmospheric pressure［J］.Multipurpose Utilization of Mineral Resources，2021（1）：140-143，198. | |
| 35 | 吴传龙，董发勤，陈德玉，等.常压醇水法制备α-高强石膏的工艺条件研究［J］.西南科技大学学报，2016，31（4）：33- 37. |
| WU Chuanlong， DONG Faqin， CHEN Deyu，et al.Study on process conditions for preparation of α-high strength gypsum by the glycerol water method under atmospheric pressure［J］.Journal of Southwest University of Science and Technology，2016，31（4）：33-37. | |
| 36 | 李德星，郭荣鑫，林志伟，等.常压微波醇水法制备α半水硫酸钙晶须的研究［J］.非金属矿，2022，45（1）：46-50，55. |
| LI Dexing， GUO Rongxin， LIN Zhiwei，et al.Study on preparation of α-calcium sulfate hemihydrate whiskers by atmospheric microwave glycerol water method［J］.Non-Metallic Mines，2022，45（1）：46-50，55. | |
| 37 | 杨月静.丙烯酰胺在离子液体1-丁基-3-甲基四氟硼酸盐中的分散聚合研究［D］.青岛：青岛科技大学，2014. |
| YANG Yuejing.Study on dispersion polymerization of acrylamide in ionic liquids［D］.Qingdao：Qingdao University of Science & Technology，2014. | |
| 38 | 孔宝.反相微乳液法合成α-半水石膏及其形貌控制［D］.杭州：浙江大学，2012. |
| KONG Bao.Synthesis and morphology control of α-calcium sulfate hemihydrate in a reverse microemulsion［D］.Hangzhou：Zhejiang University，2012. | |
| 39 | 郭荣鑫，林志伟，杨洋，等.一种反相微乳液体系中磷石膏制备纳米级α型半水硫酸钙晶须的方法：中国，110835780B［P］. 2021-11-09. |
| 40 | 卢佳艳.微波辅助微乳液法制备脱水相硫酸钙［D］.湘潭：湘潭大学，2021. |
| LU Jiayan.Preparation of dehydrated calcium sulfate by micro-wave-assisted microemulsion method［D］.Xiangtan：Xiangtan University，2021. | |
| 41 | 陈星宇，林志伟，郭荣鑫，等.以磷石膏为原料在反相微乳液体系中制备α型半水石膏及晶体调控［J］.硅酸盐通报，2020，39（11）：3542-3548. |
| CHEN Xingyu， LIN Zhiwei， GUO Rongxin，et al.Preparation of α-hemihydrate gypsum and crystal regulation with phosphogypsum as raw material in reverse microemulsion system［J］.Bulletin of the Chinese Ceramic Society，2020，39（11）：3542-3548. | |
| 42 | 郭宇.脱硫石膏含水量对微波加热特性的影响［D］.太原：太原理工大学，2016. |
| GUO Yu.Effect of water content in FGD gypsum on microwave heating characteristics［D］.Taiyuan：Taiyuan University of Technology，2016. | |
| 43 | 张绍奇，郭荣鑫，林志伟，等.微波醇水体系下制备α-半水石膏晶须的研究［J］.非金属矿，2020，43（2）：84-87. |
| ZHANG Shaoqi， GUO Rongxin， LIN Zhiwei，et al.Study on preparation of α-calcium sulfate hemihydrate whiskers under microwave alcohol-water system［J］.Non-Metallic Mines，2020，43（2）：84-87. | |
| 44 | 冯焱，张绍奇，林志伟，等.微波辐照下丁二酸对磷石膏制备半水石膏的影响［J］.硅酸盐通报，2020，39（11）：3535-3541，3556. |
| FENG Yan， ZHANG Shaoqi， LIN Zhiwei，et al.Effect of succinic acid on preparation of hemihydrate gypsum from phosphogypsum under microwave irradiation［J］.Bulletin of the Chinese Ceramic Society，2020，39（11）：3535-3541，3556. | |
| 45 | SHAO Duoduo， ZHAO Bin， GAO Lili，et al.Preparation of whitening dihydrate gypsum and short columnar α-hemihydrate gypsum with FGD gypsum［J］.Crystal Research and Technology，2017，52（9）：1700166. |
| 46 | 汪潇，曹博伦，金彪，等.添加剂调控半水石膏晶体生长研究进展［J］.硅酸盐学报，2020，48（1）：94-103. |
| WANG Xiao， CAO Bolun， JIN Biao，et al.Using additives to control crystal growth of hemihydrate gypsum：A short review［J］.Journal of the Chinese Ceramic Society，2020，48（1）：94-103. | |
| 47 | 尹诗诗.石膏二水相-半水相转化过程调控研究［D］.湘潭：湘潭大学，2020. |
| YIN Shishi.Study on contronlling the transformation process from dihydrate to hemihydrate gypsum［D］.Xiangtan：Xiangtan University，2020. | |
| 48 | 陈平，田宇，胡成.盐溶液种类和浓度对α-半水脱硫石膏合成的影响［J］.无机盐工业，2020，52（10）：130-134. |
| CHEN Ping， TIAN Yu， HU Cheng.Effect of type and concentration of salt solution on synthesis of α-semi-water desulfurization gypsum［J］.Inorganic Chemicals Industry，2020，52（10）：130- 134. | |
| 49 | 韩康.加压水热法制备高强石膏［D］.焦作：河南理工大学，2021. |
| HAN Kang.Preparation of high strength gypsum by pressurized hydrothermal method［D］.Jiaozuo：Henan Polytechnic University，2021. | |
| 50 | 赵云龙.建筑石膏生产与应用技术［M］.北京：中国建材工业出版社，2019：258-279. |
| 51 | 雷中明，苏根华，郭栋，等.石膏煅烧回转窑生产线系统：中国，114893960A［P］.2022-08-12. |
| 52 | 蔡彦煌.脱硫石膏蒸汽二步法生产建筑石膏粉工艺简介［J］.福建建材，2019（4）：102-103，84. |
| CAI Yanhuang.Brief introduction to the process of producing building gypsum powder by steam two-step method of desulfurization gypsum［J］.Fujian Building Materials，2019（4）：102-103，84. | |
| 53 | 陈燕，岳文海，董若兰.石膏建筑材料［M］.2版.北京：中国建材工业出版社，2012：380-393. |
| 54 | 中华人民共和国工业和信息化部. α型高强石膏：JC/T 2038—2010［S］.北京：中国建材工业出版社，2011. |
| 55 | 中华人民共和国工业和信息化部. 石膏型熔模铸造用铸型粉：JB/T 11734—2013［S］.北京：机械工业出版社，2014. |
| 56 | 中华人民共和国工业和信息化部. 陶瓷模用石膏粉：QB/T 1639—2014［S］.北京：中国轻工业出版社，2014. |
/
| 〈 |
|
〉 |