Investigation on industrial production process of magnesium fluorosilicate
Received date: 2020-09-18
Online published: 2021-08-11
Copyright
In order to reduce energy consumption and improve product quality,the best method for industrial production of magnesium fluorosilicate was explored.The process parameters for the production of magnesium fluorosilicate crystal particles by using by-product fluorosilicic acid from phosphate fertilizer industry from phosphate fertilizer industry and magnesia powder were systematically studied and optimized.The physicochemical properties such as particle size and particle size distribution of magnesium fluorosilicate were listed.The optimum process parameters to provide the maximum yield of magnesium fluosilicate products were obtained,directly adding MgO powder into the synthesis tank and its adding sequence were determined.The optimum parameters were as follows:the content of fluorosilicic H2SiF6,was 16%(mass fraction) the mass ratio of m(MgO)/m(H2SiF6) was controlled at 0.244~0.260,the synthesis temperature was controlled at 40~50 ℃,the product solution with high concentration was obtained,the evaporation temperature was 35~45 ℃,and the evaporated slurry entered the MSMPR cooling crystallization tank,the cooling crystallization temperature was controlled at 30 ℃,the rotation frequency of crystallizer agitator was controlled at 20~40 Hz,and the product particle size could be controlled at 0.16~0.37 mm.The above-mentioned studies could be used as process technological reference for the related manufacturers.
Zhao Ruixiang . Investigation on industrial production process of magnesium fluorosilicate[J]. Inorganic Chemicals Industry, 2021 , 53(8) : 79 -82 . DOI: 10.19964/j.issn.1006-4990.2020-0523
[1] | 刘晓华. 磷肥副产品-氟硅酸镁的生产[J]. 磷肥与复肥, 1995(2):26-27. |
[2] | 唐坤明, 方定远. 氟硅酸镁的真空浓缩生产工艺探讨[J]. 应用技术市场, 1996(9):12-13. |
[3] | Zhao R X. Process optimization in batch crystallization of sodium fluosilicate[J]. Journal of Experimental & Industrial Crystallograp-hy, 2005,40(3):243-247. |
[4] | Gurbuz H, Ozdemir B. Experimental determination of the metastable zone width of borax decahydrate by ultrasonic velocity measureme-nt[J]. Crystal Growth, 2003,252:343-349. |
[5] | 赵瑞祥. 加料方式对氟硅酸钠晶体微观结构的影响研究[J]. 磷肥与复肥, 2019(12):6-9. |
[6] | 龙丹. 氟硼酸钾制备工艺研究[J]. 山东化工, 2019,9(48):26-28. |
[7] | Everett J.H. Effects of supersaturation and temperature on nuclea-tion and crystal growth in a MSMPR crystallizer[Z/OL]. Retro-spective Theses and Dissertations,1976. [2020-09-28]. https//lib.dr.iastate.edu/rtd/6213. |
[8] | 黄凤鸣. 真空蒸发技术在氟硅酸镁生产中的应用[J]. 无机盐工业, 2007,39(6):54-56. |
[9] | Ali H. A.Preparation of potassium fluorosilicate(K2SiF6) from fluorosilicic acid produced in Iraq Phosphate Plant Al-Qadisiya[J]. Journal for Engineering Sciences, 2011,4(4):537-545. |
[10] | Akrap M, Kuzmanic N, Prlic Kardum J. Effect of mixing on the cry-stal size distribution of borax deca-hydrate in a batch cooling cryst allizer[J]. Journal of Crystal Growth, 2010,312(24):3603-3608. |
[11] | Jiang M, Braatz R D. Designs of continuous-flow pharmaceutical crystallizers:developments and practice[J]. Cryst Eng Comm, 2019,21:3534-3551. |
[12] | 隋岩峰, 刘松林, 杨帆. 氟硅酸铵氨化制备纳米二氧化硅的实验研究[J]. 无机盐工业, 2018,50(2):33-36. |
/
〈 |
|
〉 |