锑掺杂量对ATO薄膜结构及光、电性能的影响

Abstract

Abstract: Using sol-gel method and with SnCl₄ and SbCl₃as raw materials,antimony doped tin oxide (ATO) films with different Sb doping amounts were synthesized. Microstructure,film morphology,transmission,and sheet resistance were characterized by XRD,FESEM,UV-visible spectroscopy,and four-probe resistivity/square resistance tester,and the effects of Sb doping amounts on crystalline microstructure,crystal size,transmission,and conductivity properties of the ATO films were investigated systematically.Results showed that the prepared ATO films had tetragonal cassiterite structure and the preferred orientation was observed as (110)plane,the average crystal size was less than 26 nm,and its sheet resistance was obtained to be the lowest 60.1 Ω/□ when the Sb content was 10%(molar fraction),and the transmission was above 85% in the visible light range.

Key words: ATO films, Sb doping amounts, sol-gel method, transmission, sheet resistance

CLC Number:

TQ135.31

YANG Bao-Ping, ZHONG Xiao-Hua, ZHANG Xiao-Liang, CUI Jin-Feng, JIA Jun-Hong, YI Ge-Wen. Effects of Sb doping amount on structure and transmission,electric property of ATO films[J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(1): 19-.

[1]	LEI Xinyu, SUN Henghui, YUAN Xinqiang, ZHANG Wei, JIANG Peng, ZHANG Lizhai. Study on preparation of core-shell structure VO₂（M）@SiO₂ by silica sol-gel coating [J]. Inorganic Chemicals Industry, 2024, 56(6): 46-54.
[2]	WU Bingdang, PAN Yinglu, ZHAO Qinzheng, WU Wei, XU Xiaoyi, HUANG Tianyin. Preparation of novel lanthanum coagulants and their deep phosphorus removal properties in low temperature and turbidity water [J]. Inorganic Chemicals Industry, 2024, 56(2): 127-135.
[3]	FENG Lunwei, LIU Yan, XIE Yan. Study on preparation of high purity barium titanate powder by sol-gel method [J]. Inorganic Chemicals Industry, 2024, 56(12): 56-61.
[4]	SONG Zhi, LIU Boxia, CHEN Yaoyao. Study on synthesis of FeWO₄/WO₃ complex by sol-gel and degradation of textile dye wastewater [J]. Inorganic Chemicals Industry, 2022, 54(5): 131-137.
[5]	HAO Xiaodong,FENG Xinyi,XU Yang,ZHANG Xishu,LIU Wen,HAO Fangyuan,MA Shufang,XU Bingshe. Study on controllable synthesis and ultramicroscopic structure-activity relationship of cerium oxides nanocatalysts [J]. Inorganic Chemicals Industry, 2022, 54(3): 7-17.
[6]	BAN Liping,MA Min. Study on synthesis and photoluminescence mechanism of CuAl₂O₄ and CuAl₂O₄：Cr phosphors [J]. Inorganic Chemicals Industry, 2022, 54(1): 56-61.
[7]	Xia Miao,Nie Yimiao,Liu Panpan,Wang Ling,Liu Shuxian,Wang Sen,Wang Yingchun,Zhai Peixin,Liu Shuoyu. Research progress of preparation and synthesis process of SiO₂-Al₂O₃ system gel by sol-gel method [J]. Inorganic Chemicals Industry, 2021, 53(8): 8-14.
[8]	Zheng Wei,Hou Fang,Gao Xiping. Preparation of BaFe₂O₄/BaSO₄ composite photocatalyst and study on the photocatalytic activity of degrading rhodamine B wastewater discharged from food processing plant [J]. Inorganic Chemicals Industry, 2021, 53(7): 113-118.
[9]	Zhao Hongkai,Peng Zhenfeng,Chi Mingshuo. Research status of silicon oxide nanowires [J]. Inorganic Chemicals Industry, 2020, 52(11): 12-15.
[10]	Yu Tianhua,Ao Houyu,Huang Qipeng,Wu Jinglan. Preparation and catalytic hydroxylation performance of hierarchical titanium silicalite-1 [J]. Inorganic Chemicals Industry, 2019, 51(9): 102-105.
[11]	Zhou Peng1，2，Guo Qiushuang1，2，Li Xiaoyun1，2，Sun Yanmin1，2，Miao Jing1，Yu Haibin1，2. Application of mesoporous TiO2-SiO2 composite oxide inphotocatalytic degradation of Rhodamine B [J]. Inorganic Chemicals Industry, 2019, 51(7): 93-99.
[12]	WANG Guo-Ming, MA Xue-Ming, WU Ping, YANG Sheng-Bin. Magnetic and photo-catalytic properties of Zn-Mn co-doped BiFeO3 nano-crystals [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(9): 83-.
[13]	LI De-Gui, ZHANG Jin-Lei, QIN Ming, DENG Yu-Ping. Preparation of La2O3 powder and effect on grain size [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(11): 21-.
[14]	ZHU Jian-Jun, JIANG De-Li, WEI Wei, XIE Ji-Min. Analysis on transmittance of hydrophobic silica aerogels prepared at ambient pressure [J]. INORGANICCHEMICALSINDUSTRY, 2013, 45(12): 21-.
[15]	ZHANG Wang-Xi, YUAN Zu-Pei, WANG Yan-Zhi. Study on preparation process of yttria stabilized nano-sized zirconia [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(1): 22-.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Effects of Sb doping amount on structure and transmission,electric property of ATO films

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Metrics

Comments

Recommended 0