5％氯化钙存在下高硫煤还原磷石膏实验研究

Abstract

Abstract: Phosphogypsum，waste slag derived from phosphate fertilizer industry doping with 5%（mass fraction） CaCl₂ was used as raw material，purged with N₂ and then calcined under the presence of high-sulfur coal as reductant to prepare CaS and CaO.The contents of CaS and CaO in the product were analyzed by iodine quantity method so as to investigate the reduction rate of calcium sulfate.The effects of raw material mix ratio，calcining time，calcining temperature，and particle size etc. on the reduction of phosphogypsum were studied.Based on these studies，orthogonal experiments were conducted to find out the optimum process conditions for obtaining CaS and CaO by reducing phosphogypsum，which are as follows：amount-of-substance ratio of CaSO₄ to C was 1∶1.3，calcining temperature was 900 ℃，and calcining time was 2.5 h. Under those conditions the reduction rate of CaSO₄ in phosphogypsum could reach more than 98%.The doping of 5% CaCl₂ could decline the reductive decomposition temperature of phosphogypsum.

Key words: phosphogypsum, CaS, CaO, orthogonal experiments

CLC Number:

TQ132.32

WU Yu-Long, WU Qiong. Study on reducing phosphogypsum by high-sulfur coal in presence of 5% CaCl2[J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(12): 43-.

[1]	Yin Wei,Huang Jin,Xie Tian,He Bingbing. Experimental study on high efficiency decomposition of phosphate rock by phosphoric acid [J]. Inorganic Chemicals Industry, 2020, 52(9): 34-36.
[2]	Zhao Shihao,Lin Xihua,Ma Pengfei,Yuan Yijin,Gao Yuxin,Zhang Ping,Zhou Dali. Study on formulation calculation of phosphogypsum-based composite cementitious materials based on expansion and failure of critical AFt [J]. Inorganic Chemicals Industry, 2020, 52(9): 91-95.
[3]	Su Shaolong,Qu Xiaolong,Zhong Dule,Sun Yanmin,Ma Yueqian. Study on determination of CaO,Ca（OH）₂ and CaCO₃ in industrial calcium hydroxide [J]. Inorganic Chemicals Industry, 2020, 52(5): 75-77.
[4]	Wang Gang,Tang Shengwei,Chen Yanxiao,Zhang Tao. Effect of CTAB on crystal form of CaCO₃ in indirect mineralization of CO₂ by CaSO₄·2H₂O [J]. Inorganic Chemicals Industry, 2020, 52(3): 75-79.
[5]	Li Wenjun,Wang Jinyu,Li Hongling,Hong Chenglin,Dan Jianming,Qiao Xiuwen. Preparation of high concentration NaHSO₃ solution by two-step method of desulfurization intermediate CaSO₃ [J]. Inorganic Chemicals Industry, 2020, 52(3): 90-93.
[6]	Bian Chengli,Shi Huangang,Bao Wenyun,Zhang Dongping. Heat treatment of FGD gypsum and preparation of molds for slip casting [J]. Inorganic Chemicals Industry, 2020, 52(2): 54-57.
[7]	Wu Baojian,Lü Xinfeng,Zhang Qingjie,Yi Meigui,Xiang Lan. Primary exploration of removing impurities from phosphogypsum by wet coupling process [J]. Inorganic Chemicals Industry, 2020, 52(12): 55-58.
[8]	Luo Shuang,Fu Rubin,Kong Dewen,Xie Lang,Zhou Yinsheng,Zhao Yan. Summary on effects of admixtures on water resistance and strength of phosphogypsum-based composite cementitious materials [J]. Inorganic Chemicals Industry, 2020, 52(11): 6-6.
[9]	Zheng Shaocong,Wang Fan,Zhu Liping,Xu Chengkun. Experimental study on influence of phosphogypsum with modified phosphorus slag powder [J]. Inorganic Chemicals Industry, 2020, 52(1): 73-75.
[10]	Ding Feng,Dou Yan,Zheng Zhiyin,Liu Rong,Cui Peng. Effect of pH on α-CaSO₄·0.5H₂O in salt solution at atmospheric pressure-succinic acid crystal transfer system [J]. Inorganic Chemicals Industry, 2020, 52(1): 82-86.
[11]	Li Bing1，2，Wei Sha2. Modification of phosphogypsum cement retarder by carbide slag [J]. Inorganic Chemicals Industry, 2019, 51(7): 74-76.
[12]	Dong Yuming1，2，3，Zhu Guangjin1，2，3，Pei Lili1，2，Liu Honghui1，2，Yan Beilei4，Xu Hongbin1，2，Zhang Yi1，2. Removal of phosphorus from leaching solution of sodium roasted vanadium slag clinker [J]. Inorganic Chemicals Industry, 2019, 51(12): 75-79.
[13]	Huang Zhenxu，Gao Hairong，Chen Lingxia，Sun Haijie，Li Yongting，Li Yingxin. Preparation of CaO/La2O3 solid base catalysts and its catalytic performances for transesterification of soybean oil [J]. Inorganic Chemicals Industry, 2019, 51(12): 89-93.
[14]	LUO Shu-Feng, FU Quan-Jun, MA Xian-Lin, CHEN Wei, ZHANG Zhi-Ye, WANG Xin-Long, YANG Lin, SHENG Yong. Thermodynamic analysis of reductive reaction of phosphogypsum with pyrite [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(4): 57-.
[15]	WANG Di, DANG Ya-Gu, FEI De-Jun, SUN Xian. Preparation and mechanism analysis of silica-coated CaSO4 whisker [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(12): 37-.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on reducing phosphogypsum by high-sulfur coal in presence of 5% CaCl2

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Metrics

Comments

Recommended 10