羰基合成废铑液焙烧回收铑制备三氯化铑工艺研究

doi:10.19964/j.issn.1006-4990.2022-0761

Abstract

Abstract:

Rhodium resources are scarce and the price of rhodium is expensive.Rhodium trichloride is the raw material of rhodium catalyst and other rhodium compounds.The content of rhodium in waste rhodium solution of carbonyl synthesis is usually several hundred to several thousand milligrams per kilogram，the recovery of rhodium to prepare rhodium trichloride is of great significance.At present，the recovery of rhodium from waste rhodium liquid mainly adopts the incineration method，which has large rhodium loss and rhodium overfiring，subsequent processing difficulties and other problems.In order to solve these problems，a two-stage roasting process for recovery of rhodium from carbonyl synthesis by adding charcoal powder from aerobic roasting to oxygen-free roasting was explored.The process was simple and had a high recovery rate.The main process could be summarized as follows：the waste rhodium solution was distilled to obtain concentrated rhodium slag，and the rhodium slag was added with 0.6 times of charcoal powder，and roasted from room temperature to 600 ℃ under aerobic conditions.After being roasted at 600 ℃ for 3 h，the roasting temperature was rosed to 1 100 ℃ under the condition of no oxygen and remained at 1 100 ℃ for 1 h，the active rhodium ash was obtained when the temperature was lowered to room temperature.Then the active rhodium ash was dissolved in the acid.Finally，rhodium trichloride was obtained by purification and concentration，yield was higher than 99.0%.

Key words: waste rhodium solution of carbonyl synthesis, roasting, rhodium recovery, charcoal powder

CLC Number:

TQ138.22

WANG Benlei, ZHANG Guisheng, JIANG Lingyun, LI Chen, WANG Pengfei, LI Jixia, ZANG Jiazhong. Study on preparation process of rhodium trichloride by roasting recovery technology from waste rhodium solution of carbonyl synthesis[J]. Inorganic Chemicals Industry, 2023, 55(6): 104-108.

Figures/Tables 5

Table 1

Table 2

Fig.1

Fig.2

Fig.3

References 12

1	史宏星.丁辛醇工业发展状况及市场供需分析［J］.中国石油和化工经济分析，2019（5）：56-60.
	SHI Hongxing.Industrial development and market supply and demand analysis of butyl octanol［J］.China Petrochemical Industry Observer，2019（5）：56-60.
2	李继霞，白文玉，姜旭，等.羰基合成用废铑催化剂的再生与铑的回收［J］.贵金属，2008，29（1）：53-55.
	LI Jixia， BAI Wenyu， JIANG Xu，et al.Regeneration technique of waste rhodium catalysts and recovery of rhodium in carbonylation synthesis reaction［J］.Precious Metals，2008，29（1）：53-55.
3	裴洪营，赵家春，吴跃东，等.从有机废料中回收铑的技术进展［J］.贵金属，2019，40（4）：85-90.
	PEI Hongying， ZHAO Jiachun， WU Yuedong，et al.Technology progress on recovery of rhodium from organic wastes［J］.Precious Metals，2019，40（4）：85-90.
4	蒋凌云，李晨，李继霞，等.丁辛醇废铑催化剂消解液制备高纯三氯化铑研究［J］.无机盐工业，2017，49（11）：76-78.
	JIANG Lingyun， LI Chen， LI Jixia，et al.Study on preparing high-purity rhodium chloride by using digestion solution produced in dispelling waste catalyst containing rhodium from butyl octanol unit［J］.Inorganic Chemicals Industry，2017，49（11）：76-78.
5	蒋凌云，于海斌，李晨，等.丁辛醇废铑催化剂焙烧铑回收工艺研究［J］.无机盐工业，2015，47（4）：51-53.
	JIANG Lingyun， YU Haibin， LI Chen，et al.Study on rhodium recovery process by roasting rhodium containing waste catalyst from butyl octanol unit［J］.Inorganic Chemicals Industry，2015，47（4）：51-53.
6	李志，权凯栋，韩志敏.废贵金属催化剂中铑回收工艺研究进展［J］.石化技术，2020，27（12）：270-271，265.
	LI Zhi， QUAN Kaidong， HAN Zhimin.Research progress on rhodium recovery process from waste precious metal catalyst［J］.Petrochemical Industry Technology，2020，27（12）：270-271，265.
7	张林燕，郭喜文，谭学苓，等.一种含铑工作液中贵金属铑的回收方法：中国，115074544A［P］.2022-09-20.
8	M·A·比其，R·B·华生.从氢甲酰化方法回收铑的方法：中国，111278560A［P］.2020-06-12.
9	刘杨，范兴祥，董海刚，等.贵金属物料的溶解技术及进展［J］.贵金属，2013，34（4）：65-72.
	LIU Yang， FAN Xingxiang， DONG Haigang，et al.Dissolving techniques of precious metal materials and their development［J］.Precious Metals，2013，34（4）：65-72.
10	蒋凌云，李晨，于海斌，等.从羰基合成废铑催化剂中回收铑制备水合氯化铑的方法：中国，106319202B［P］.2018-04-20.
11	蒋凌云，李晨，于海斌，等.从羰基合成废铑催化剂中回收铑制备水合氯化铑的方法：中国，106319202B［P］.2018-04-20.
12	陈国祥，苑志伟，蒋绍洋，等.从废催化剂中回收贵金属铑的技术进展［J］.中外能源，2021，26（2）：65-69.
	CHEN Guoxiang， YUAN Zhiwei， JIANG Shaoyang，et al.Technical progress of recovering precious metal rhodium from spent catalyst［J］.Sino-Global Energy，2021，26（2）：65-69.

焙烧原料	实验编号	添加木炭粉/g	焙烧氛围	m（焙烧后焙烧料）/g	活性铑收率/%	备注
浓缩铑渣 20 g	1	0	有氧	1.6	2.5	盐酸双氧水溶解液黄色
	2	12	有氧	2.3	2.8	盐酸双氧水溶解液黄色
	3	0	有氧+无氧	3.9	70.8	盐酸双氧水溶解液红黑色
	4	12	有氧+无氧	10.1	99.5	盐酸双氧水溶解液红黑色

焙烧原料	m（炭粉）/ m（铑渣）	m（焙烧后焙烧料）/g	活性铑收率/%
浓缩铑渣20 g	0.0	3.9	70.8
	0.1	4.9	75.2
	0.2	5.8	79.4
	0.3	6.9	84.5
	0.4	8.1	90.2
	0.5	8.9	98.7
	0.6	10.1	99.5
	0.8	12.7	99.5
	1.0	15.1	99.4
	1.2	17.5	99.5

[1]	ZHANG Yaqi, CHEN Xiping, SUN Ningning. Study on preparation process of cryolite from anode carbon slag by catalytic decarburization [J]. Inorganic Chemicals Industry, 2024, 56(3): 91-97.
[2]	CHEN Yujue, ZHANG Liangjun, KUANG Huan, JIANG Manwen, XIAO Li. Study on roasting and recovery process of waste lithium iron phosphate powder with sodium bisulfate [J]. Inorganic Chemicals Industry, 2023, 55(3): 113-117.
[3]	GUO Ze, ZHANG Pengfei, YANG Fan, ZHANG Hanquan, LU Manman. Preparation of β-hemihydrate gypsum by phosphogypsum roasting [J]. Inorganic Chemicals Industry, 2023, 55(10): 106-113.
[4]	DING Yong,FENG Xiaorui,LU Xiangjie,GAO Xiaoqin,FENG Yan,HE Yan. Study on preparation of high purity micron nickel oxide powder by roasting carbonyl nickel powder [J]. Inorganic Chemicals Industry, 2022, 54(4): 119-122.
[5]	ZENG Yanjie,XU Tongfei,HUANG Ziliang,CHEN Zhipeng,LIU Xudong,YI Meigui. Study on removal of calcium impurities from magnesium waste residue by roasting-hydration complexing [J]. Inorganic Chemicals Industry, 2022, 54(11): 118-123.
[6]	Sun Shuangshuang,Zhong Jianchu,Wang Hongzhi. Study on desiliconization process of copper smelting slag [J]. Inorganic Chemicals Industry, 2021, 53(9): 83-87.
[7]	Yan Zhenzong,Wang Dong. Study on rotary kiln reduction roasting production process of barite in Tianzhu of Guizhou [J]. Inorganic Chemicals Industry, 2021, 53(4): 73-75.
[8]	He Xiaoying,Li Chen,Wang Pengfei,Jiang Lingyun,Zang Jiazhong,Wu Qing. Study on enrichment process of rhodium from rhodium containing solution by sodium sulfide precipitation [J]. Inorganic Chemicals Industry, 2021, 53(4): 81-85.
[9]	Shang Fangyu,Su Xuetong,Shang Suying. Study on recovery of barium from barium slag by chlorination roasting-water leaching process [J]. Inorganic Chemicals Industry, 2021, 53(3): 65-67.
[10]	Qing Penghui,Dong Yuming,Wang Xingrun,Zhu Kaisheng,Niu Renjie,Meng Jingjuan,Chen Xiaohong,Chen Huixia,Zhang Hongling,Xu Hongbin. Chromium extraction and detoxification of processing residue from lime-free roasting process of chromite ore [J]. Inorganic Chemicals Industry, 2020, 52(6): 63-67.
[11]	Du Xiaowang,Zhong Jianchu,Wang Xiaotian. Study on removal of silicon from high-silicon brucite by sodium roasting method [J]. Inorganic Chemicals Industry, 2020, 52(10): 92-95.
[12]	Huang Jiming,Liu Runqing,Wu Sizhan,Song Juan. Optimization of extraction process of chlorination roasting-water leaching process for low-grade rhodochrosite by response surface methodology [J]. Inorganic Chemicals Industry, 2019, 51(3): 34-37.
[13]	Qing Penghui1，2，3，Zhang Hongling1，2，Shi Yilang4，Cai Zaihua4，Mei Haijun5，Xu Hongbin1，2. Effect of additive on oxidative roasting process of chromite [J]. Inorganic Chemicals Industry, 2019, 51(12): 26-29.
[14]	Zhang Lizhen1，2，3，Zhang Yongxing1，2，3，Zhang Xiufeng1，2，3，Tan Xiumin1，2，3. Extraction of lithium，potassium，rubidium and cesium by chlorination roasting-water leaching process [J]. Inorganic Chemicals Industry, 2019, 51(10): 48-50.
[15]	LIU Qian-Qian, LIAO Xue-Feng, CHEN Guo, CHEN Hu-Fei, ZHANG Li-Bo, PENG Jin-Hui. Experimental study on acid soluble titanium slag by traditional heating [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(9): 61-.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on preparation process of rhodium trichloride by roasting recovery technology from waste rhodium solution of carbonyl synthesis

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 5

References 12

Related Articles 15

Metrics

Comments

Recommended 0