碱激发矿渣水泥基材料收缩性能研究

doi:10.11962/1006-4990.2019-0586

摘要/Abstract

摘要：

通过XRD、SEM、TGA等方法研究了膨胀剂掺量、碱当量、水玻璃模数对碱矿渣水泥砂浆干燥收缩、质量损失的影响。结果表明：氧化钙膨胀剂的加入会使矿渣产生膨胀现象,且随膨胀剂掺量（6%~10%）的增加,膨胀值增大;而氧化钙-硫铝酸钙复合膨胀剂的加入对矿渣的收缩无改善效果。XRD及SEM测试结果表明,氢氧化钙是氧化钙膨胀剂在矿渣中的主要膨胀源;掺加氧化钙-硫铝酸钙复合膨胀剂后未生成钙矾石相,是其未能改善矿渣收缩的主要原因。水玻璃模数及碱当量都会影响膨胀剂在矿渣中的作用效果。膨胀剂的加入会降低矿渣在干燥条件下的质量损失及体系游离水含量,其中氧化钙膨胀剂对两者的降低幅度更大。

关键词: 碱矿渣水泥, 钙系膨胀剂, 干燥收缩

Abstract:

The influence of expansive agents dasages,alkali concentration and modulus of sodium silicate on drying shrinkage and mass loss of alkali activated slag was investigated by XRD,SEM and TG.The results indicated that the addition of CaO expansive agent caused swelling phenomenon on alkali activated slag,and the expansion value increased with the dosage of CaO expansive agent（6%~10%）.While the addition of calcium oxide-calcium sulphoaluminate expansive agent didn′t improve the shrinkage of alkali activated slag.The results of XRD and SEM tests showed that Ca（OH）₂ was the main expansion component in CaO expansive agent.Besides,no AFt prepared after the addition of calcium oxide-calcium sulphoaluminate expansive agent was the main reason that CS could not improve the shrinkage of slag.The effect of expansive agent in activated slag was affected by calcium oxide-calcium sulphoaluminate and alkali concentration.Expansive agents could decrease the mass loss and free water content of SG and CaO expansive agent could significant reduce that.

Key words: alkali activated slag cement, calcium series expansive agent, drying shrinkage

中图分类号:

TQ172.12

麻鹏飞,李爽,程宝军,康升荣,张萍,高育欣. 碱激发矿渣水泥基材料收缩性能研究[J]. 无机盐工业, 2020, 52(10): 145-150.

Ma Pengfei,Li Shuang,Cheng Baojun,Kang Shengrong,Zhang Ping,Gao Yuxin. Research on contractility of alkali activated slag mortar[J]. Inorganic Chemicals Industry, 2020, 52(10): 145-150.

图/表 11

表1

表2

表3

图1

图2

图3

图4

图5

表4

图6

图7

参考文献 23

[1]	Ye H, Cartwright C, Rajabipour F, et al. Understanding the drying shrinkage performance of alkali-activated slag mortars[J]. Cement & Concrete Composites, 2017,76:13-24.
[2]	Mastali M, Kinnunen P, Dalvand A, et al. Drying shrinkage in alkaliactivated binders-A critical review[J]. Construction & Building Materials, 2018,190:533-550.
[3]	Thomas R J, Lezama D, Peethamparan S. On drying shrinkage in allkali-activated concrete:Improving dimensional stability by aging or heat-curing[J]. Cement & Concrete Research, 2017,91:13-23.
[4]	Collins F, Sanjayan J G. Microcracking and strength development of alkali activated slag concrete[J]. Cement & Concrete Composites, 2001,23(4/5):345-352.
[5]	陈科, 杨长辉, 潘群, 等. 碱-矿渣水泥砂浆的干缩特性[J]. 重庆大学学报, 2012(5):64-68.
[6]	杨长辉, 陈科, 于泽东, 等. 矿物掺合料对碱矿渣水泥砂浆干缩性能的影响[C]// 中国硅酸盐学会水泥分会.中国硅酸盐学会水泥分会第三届学术年会暨第十二届全国水泥和混凝土化学及应用技术会议论文摘要集, 2011.
[7]	汪国华, 于泽东. 外加剂对碱矿渣水泥砂浆干缩性能的影响[J]. 土木建筑与环境工程, 2012(S2):115-116.
[8]	Lee N K, Jang J G, Lee H K. Shrinkage characteristics of alkali-activated fly ash/slag paste and mortar at early ages[J]. Cement & Concrete Composites, 2014,53:239-248.
[9]	Bakharev T, Sanjayan J G, Cheng Y B. Effect of admixtures on properties of alkali-activated slag concrete[J]. Cement & Concrete Research, 2000,30(9):1367-1374.
[10]	Palacios M, Puertas F. Effect of shrinkage-reducing admixtures on the properties of alkali-activated slag mortars and pastes[J]. Cement & Concrete Research, 2007,37(5):691-702.
[11]	Bilim C, Karahan O, Atis C D, et al. Influence of admixtures on the properties of alkali-activated slag mortars subjected to different curing conditions[J]. Materials & Design, 2013,44:540-547.
[12]	代明, 袁杏, 柯国军. 浅谈混凝土膨胀剂[J]. 硅谷, 2010(4):86-87.
[13]	吴中伟. 补偿收缩混凝土[M]. 北京: 中国建筑工业出版社, 1979.
[14]	Yuan X, Chen W, Lu Z, et al. Shrinkage compensation of alkaliactivated slag concrete and microstructural analysis[J]. Construction & Building Materials, 2014,66:422-428. doi: 10.1016/j.conbuildmat.2015.07.186 pmid: 26722191
[15]	杨长辉, 梅琳. 辅助胶凝材料对碱矿渣混凝土限制膨胀率的影响[J]. 混凝土, 2010（9）：42-45.
[16]	Ye H, Radlinska A. Shrinkage mitigation strategies in alkali-activated slag[J]. Cement & Concrete Composites, 2017,101:131-143.
[17]	李爽, 张之璐, 唐德莎, 等. CaO类膨胀剂对碱矿渣水泥砂浆限制膨胀率影响研究[J]. 硅酸盐通报, 2018,37(5):1747-1752.
[18]	Chen W, Brouwers H J H. The hydration of slag,part 1:reaction models for alkali-activated slag[J]. Journal of Materials Science, 2007,42(2):428-443.
[19]	梅琳. 碱矿渣混凝土干缩性能及改善措施研究[D]. 重庆:重庆大学, 2010.
[20]	Ferone C, Colangelo F, Roviello G. Application-oriented chemical optimization of a metakaolin based geopolymer[J]. Materials, 2013,6(5):1920-1939. doi: 10.3390/ma6051920 pmid: 28809251
[21]	楼宗汉, 徐先宇, 韩韧. 矿渣水泥中钙矾石形成条件及其作用[J]. 硅酸盐学报, 1981(3):295-301,376.
[22]	顾亚敏, 方永浩. 碱矿渣水泥的收缩与开裂特性及其减缩与增韧[J]. 硅酸盐学报, 2012,40(1):76-84.
[23]	牟善彬, 孙振亚, 苏小萍. 高游离氧化钙水泥的显微结构与膨胀机理研究[J]. 武汉理工大学学报, 2001(11):27-29.

材料	w（SiO₂）	w（Al₂O₃）	w（CaO）	w（MgO）	w（TiO₂）	w（Fe₂O₃）
SG	31.63	13.42	36.35	9.12	2.76	1.32
C	3.81	2.02	78.27	1.18	—	1.55
CS	4.97	1.29	50.07	2.05	—	1.15
材料	w（SO₃）	w（K₂O）	w（Na₂O）	烧失量	w（f-CaO）
SG	0.28	0.46	0.34	0.61	—
C	0.17	—	—	11.49	55.73
CS	20.65	—	—	18.84	—

样品编号	w（可蒸发水）	样品编号	w（可蒸发水）
SG	71.70	SG-CS-8%	69.23
SG-C-8%	62.86

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会