Study on thermal decomposition behaviour of ultrafine cerium oxide with reticulated framework
Received date: 2024-06-06
Online published: 2025-06-25
Aiming at the agglomeration and sintering problems generated during the roasting process of ultrafine cerium oxide precursor，a new idea of using multifunctional reticulated framework polyethylene glycol（PEG） to prepare the precursor cerium carbonate salts of ultrafine cerium oxide powder was proposed，and the thermal decomposition process and kinetic analysis of the precursor were studied by using the TG-DSC thermal analyser and the effect of the roasting temperature，the rate of heating and the holding time on the particle size，morphology and crystal structure of the ultrafine cerium oxide were investigated.The effects of temperature，morphology and crystal structure were investigated.The experimental results showed that the thermal decomposition of the precursor was divided into three stages.The first stage at 25~258 ℃ was the stage of demineralised water，with a weight loss of 2.94%.The second stage was at 258~422 ℃ with a weight loss of 11.86%，and the precursors Ce（CO3）2O·H2O and Ce2（CO3）2O·H2O were decomposed into CeCO3OH and CeO2.The third stage was at 422~630 ℃，the residual PEG was volatilised by high temperature oxidative decomposition，and part of the rare earth cerium carbonate salt CeCO3OH was decomposed to produce perfectly crystalline cerium oxide with a weight loss of 10.29%.Using the Freeman-Carroll method，the activation energy（E） of the second reaction stage was determined to be 166.68 kJ/mol，and the number of reaction stages（n） was 19.27.The activation energy（E） of the third reaction stage was determined to be 101.95 kJ/mol，and the number of reaction stages（n） was 14.75.It was found that under the roasting system with a roasting temperature of 1 000 ℃，a temperature rise rate of 300 ℃/h and a holding time of 3 h，the mean particle size D50≤0.50 µm of the ultrafine ceria powder could be obtained.
MENG Longhui , HU Yanhong , YANG Guosheng , ZHAO Yan , ZHANG Xiaowei , LIU Zhaogang , WANG Ruifen . Study on thermal decomposition behaviour of ultrafine cerium oxide with reticulated framework[J]. Inorganic Chemicals Industry, 2025 , 57(6) : 77 -84 . DOI: 10.19964/j.issn.1006-4990.2024-0313
| 1 | 郝晓东，冯心怡，徐阳，等.二氧化铈纳米催化剂可控合成及超微观构效关系研究［J］.无机盐工业，2022，54（3）：7-17. |
| HAO Xiaodong， FENG Xinyi， XU Yang，et al.Study on controllable synthesis and ultramicroscopic structure-activity relationship of cerium oxides nanocatalysts［J］.Inorganic Chemicals Industry，2022，54（3）：7-17. | |
| 2 | WANG Xingzi， WANG Ning， ZHANG Zhenyu，et al.Controlled synthesis of triangular submicron-sized CeO2 and its polishing performance［J］. Materials，2024，17（9）：2001. |
| 3 | 刘翠翠，李梅，胡艳宏，等.聚苯乙烯磺酸钠调控制备球状碳酸铈颗粒研究［J］.无机盐工业，2012，44（8）：13-15. |
| LIU Cuicui， LI Mei， HU Yanhong，et al.Research in preparation of spherical Ce2（CO3）3 particles under control of PSS［J］.Inorganic Chemicals Industry，2012，44（8）：13-15. | |
| 4 | JAVID H， AMIRI H， HASHEMI S F，et al.Sol-gel synthesis and cytotoxicity evaluation of selenium-doped cerium oxide nanoparticles for biomedical applications［J］.Naunyn-Schmiedeberg′s Archives of Pharmacology，2024，397（5）：3437-3447. |
| 5 | ALSHARIF N B， SAMU G F， SáRINGER S，et al.Antioxidant colloids via heteroaggregation of cerium oxide nanoparticles and latex beads［J］.Colloids and Surfaces B：Biointerfaces，2022，216：112531. |
| 6 | 周薇.光学透镜用铈基稀土抛光粉的制备研究［D］.包头：内蒙古科技大学，2020. |
| ZHOU Wei.Study on preparation of cerium-based rare earth polishing powder for optical lens［D］.Baotou：Inner Mongolia University of Science & Technology，2020. | |
| 7 | 贾慧灵，徐阳，吴锦绣，等.制备条件对二氧化铈稀土抛光粉性能的影响［J］.稀土，2022，43（4）：37-45. |
| JIA Huiling， XU Yang， WU Jinxiu，et al.Effect of preparation conditions on the properties of cerium oxide polishing powder［J］.Chinese Rare Earths，2022，43（4）：37-45. | |
| 8 | JANO? P， EDERER J， PILA?OVá V，et al.Chemical mechanical glass polishing with cerium oxide：Effect of selected physico-chemical characteristics on polishing efficiency［J］.Wear，2016，362：114-120. |
| 9 | MA Jiahui， XU Ning， LUO Yuxin，et al.Defect generation and morphology transformation mechanism of CeO2 particles prepared by molten salt method［J］.Ceramics International，2023，49（3）：4929-4943. |
| 10 | 贾红伟，贾艳虹，李斌，等.甲酸铈煅烧制备二氧化铈［J］.核化学与放射化学，2022，44（3）：347-355. |
| JIA Hongwei， JIA Yanhong， LI Bin，et al.Preparation of cerium dioxide by calcination of cerium formate［J］.Journal of Nuclear and Radiochemistry，2022，44（3）：347-355. | |
| 11 | 吴婷，李静，朱敏萱，等.湿固相机械法制备氧化铈抛光粉［J］.稀土，2020，41（5）：1-10. |
| WU Ting， LI Jing， ZHU Minxuan，et al.Preparation of ceria polishing powder by wet solid phase mechanical method［J］.Chinese Rare Earths，2020，41（5）：1-10. | |
| 12 | LI Mei， LIU Zhaogang， HU Yanhong，et al.Effects of the synthesis methods on the physicochemical properties of cerium dioxide powder［J］.Colloids and Surfaces A：Physicochemical and Engineering Aspects，2007，301（1/2/3）：153-157. |
| 13 | CHAFIQ M， CHAOUIKI A， KO Y G.Recent advances in multifunctional reticular framework nanoparticles：A paradigm shift in materials science road to a structured future［J］.Nano-Micro Letters，2023，15（1）：213. |
| 14 | 李学舜.稀土碳酸盐制备铈基稀土抛光粉的研究［D］.沈阳：东北大学，2008. |
| LI Xueshun.Study on preparation of cerium-based rare earth polishing powder from rare earth carbonate［D］.Shenyang：Northeastern University，2008. | |
| 15 | 周强，武斌，陈葵，等.磷尾矿热分解动力学机理与煅烧工艺研究［J］.无机盐工业，2023，55（3）：47-54. |
| ZHOU Qiang， WU Bin， CHEN Kui，et al.Study on thermal decomposition kinetic mechanism and calcination process of phosphorus tailings［J］.Inorganic Chemicals Industry，2023，55（3）：47-54. | |
| 16 | 卢博，刘宜强，蒋威，等.大颗粒氧化镧粉体制备研究进展［J］.稀土，2022，43（6）：119-124. |
| LU Bo， LIU Yiqiang， JIANG Wei，et al.Research progress on preparation of large-grained lanthanum oxide powder［J］.Chinese Rare Earths，2022，43（6）：119-124. | |
| 17 | 梅燕，陈文娟，陈学安.氟化镧铈抛光粉的焙烧制备及抛光性能研究［J］.功能材料，2024，55（1）：1010-1015. |
| MEI Yan， CHEN Wenjuan， CHEN Xue′an.Preparation and polishing performance of lanthanum cerium fluoride polishing powder［J］.Journal of Functional Materials，2024，55（1）：1010-1015. | |
| 18 | 范娜，陈传东，于健飞，等.基于氟硅混酸制备稀土抛光粉及其抛光性能研究［J］.中国稀土学报，2024，42（2）：261-267. |
| FAN Na， CHEN Chuandong， YU Jianfei，et al.Preparation of rare earth polishing powder based on fluorosilicate mixed acid and its polishing performance［J］.Journal of the Chinese Society of Rare Earths，2024，42（2）：261-267. | |
| 19 | 李学舜.稀土抛光粉的生产及应用［J］.中国稀土学报，2002，20（5）：392-397. |
| LI Xueshun.Preparation and application of rare earth polishing powder［J］.Journal of the Chinese Rare Earth Society，2002，20（5）：392-397. | |
| 20 | 杨国胜，边雪，崔凌霄，等.氯化铈溶液喷雾焙烧制备纳米氧化铈实心粉体的研究［J］.稀土，2017，38（1）：72-78. |
| YANG Guosheng， BIAN Xue， CUI Lingxiao，et al.Study on preparation of nano cerium oxide powder by spray roasting of cerium chloride solution［J］.Chinese Rare Earths，2017，38（1）：72-78. | |
| 21 | ZHAN Guang， YU Junxia， XU Zhigao，et al.Kinetics of thermal decomposition of lanthanum oxalate hydrate［J］.Transactions of Nonferrous Metals Society of China，2012，22（4）：925-934. |
| 22 | 丁勇，冯晓锐，鲁相杰，等.羰基镍粉焙烧制备高纯度微米氧化亚镍粉体的研究［J］.无机盐工业，2022，54（4）：119-122，140. |
| DING Yong， FENG Xiaorui， LU Xiangjie，et al.Study on preparation of high purity micron nickel oxide powder by roasting carbonyl nickel powder［J］.Inorganic Chemicals Industry，2022，54（4）：119-122，140. | |
| 23 | 饶明璐，高国华，陈金发，等.超细碳酸钇热分解行为及焙烧工艺的研究［J］.中国稀土学报，2022，40（2）：276-285. |
| RAO Minglu， GAO Guohua， CHEN Jinfa，et al.Thermal decomposition behavior and roasting process of ultrafine yttrium carbonate［J］.Journal of the Chinese Society of Rare Earths，2022，40（2）：276-285. | |
| 24 | 朱钰方，方莹，张少明.低温固相反应制备氧化锌微粉研究［J］.南京工业大学学报（自然科学版），2002，24（6）：70-73. |
| ZHU Yufang， FANG Ying， ZHANG Shaoming.Preparation of ultrafine ZnO by solid state reaction under low temperature［J］.Journal of Nanjing University（Natural Science Edition），2002，24（6）：70-73. | |
| 25 | 张超，谢永纯，喻航，等.焙烧时间对喷雾干燥制备LiMnPO4/C多孔微球的影响［J］.无机盐工业，2018，50（2）：24-28. |
| ZHANG Chao， XIE Yongchun， YU Hang，et al.Influence of calcination time on preparation porous LiMnPO4/C microspheres by spray drying process［J］.Inorganic Chemicals Industry，2018，50（2）：24-28. |
/
| 〈 |
|
〉 |