Study on effect of crystallizer on preparation of anhydrous calcium sulfate from phosphogypsum
Received date: 2023-06-01
Online published: 2024-05-15
The production of phosphogypsum（PG） is large，and its resource utilization is difficult，which seriously affects the development of phosphorus chemical industry.In order to improve the added value of PG application，anhydrous CaSO4 with high whiteness was prepared by normal pressure salt solution method with PG as raw material，NaCl and EDTA-2Na as crystallization agents.The effect of crystal transition agent on the preparation of anhydrous CaSO4 was studied by SEM，XRD，FT-IR and particle size analyzer.The results showed that when the mass fraction of NaCl was 15% and the mass fraction of EDTA-2Na was 0.5%，the dehydration time of PG crystal water was shortened from 120 min to 40 min，and the dehydration effect was remarkable.At the same time，the particle size distribution of anhydrous CaSO4 crystal was uniform，the particle surface was complete，the D50 was 5.26 μm，the whiteness was 92.5%，and the P2O5 content was only 0.045%.It was mainly because non-lattice Na+ reduced the activity of water in the system，and promoted the dehydration，crystallization and impurity removal of PG.The coordination ion layer formed by the coordination between carboxyl groups in EDTA-2Na and Ca2+on the surface of gypsum crystal could regulate the growth of anhydrous CaSO4 crystal and modify the crystal face.
WANG Mingshun , AO Xianquan , YUAN Xing , DONG Wenyan , CHEN Qianlin . Study on effect of crystallizer on preparation of anhydrous calcium sulfate from phosphogypsum[J]. Inorganic Chemicals Industry, 2024 , 56(5) : 101 -107 . DOI: 10.19964/j.issn.1006-4990.2023-0301
| 1 | CHEN Shun， CHEN Jizhan， HE Xingyang，et al.Micromicelle-mechanical coupling method for high-efficiency phosphorus removal and whiteness improvement of phosphogypsum［J］.Construction and Building Materials，2022，354：129220. |
| 2 | FANG Ji， GE Yingyong， CHEN Zhijie，et al.Flotation purification of waste high-silica phosphogypsum［J］.Journal of Environmental Management，2022，320：115824. |
| 3 | 吴宝建，吕昕峰，张清杰，等.磷石膏湿法偶联除杂规律初探［J］.无机盐工业，2020，52（12）：55-58. |
| WU Baojian， Xinfeng Lü， ZHANG Qingjie，et al.Primary exploration of removing impurities from phosphogypsum by wet coupling process［J］.Inorganic Chemicals Industry，2020，52（12）：55-58. | |
| 4 | CHEN Xuemei， GAO Jianming， ZHAO Yasong.Investigation on the hydration of hemihydrate phosphogypsum after post treatment［J］.Construction and Building Materials，2019，229：116864. |
| 5 | 顾青山，林喜华，赵士豪，等.不同预处理工艺对磷石膏性能的影响［J］.无机盐工业，2022，54（4）：17-23. |
| GU Qingshan， LIN Xihua， ZHAO Shihao，et al.Effect of different pretreatment processes on properties of phosphogypsum［J］.Inorganic Chemicals Industry，2022，54（4）：17-23. | |
| 6 | ROSALES J， PéREZ S M， CABRERA M，et al.Treated phosphogypsum as an alternative set regulator and mineral addition in cement production［J］.Journal of Cleaner Production，2020，244：118752. |
| 7 | RASHAD A M.Phosphogypsum as a construction material［J］.Journal of Cleaner Production，2017，166：732-743. |
| 8 | 王进明，董发勤，王肇嘉，等.磷石膏浮选增白净化新工艺研究［J］.非金属矿，2019，42（5）：1-5. |
| WANG Jinming， DONG Faqin， WANG Zhaojia，et al.Study on new technology of phosphogypsum whitening and purification by flotation［J］.Non-Metallic Mines，2019，42（5）：1-5. | |
| 9 | 方官涛，敖先权，刘境，等.磷石膏煅烧过程中添加剂对其杂质和白度影响［J］.非金属矿，2019，42（4）：10-12. |
| FANG Guantao， AO Xianquan， LIU Jing，et al.Effects of additives on impurities and whiteness of phosphogypsum during calcining［J］.Non-Metallic Mines，2019，42（4）：10-12. | |
| 10 | LIU Yikai， ZHANG Qinli， CHEN Qiusong，et al.Utilisation of water-washing pre-treated phosphogypsum for cemented paste backfill［J］.Minerals，2019，9（3）：175. |
| 11 | GONG Shang， LI Xiaolong， SONG Fangxiang，et al.Preparation and application in HDPE of nano-CaSO4 from phosphogypsum［J］.ACS Sustainable Chemistry & Engineering，2020，8（11）：4511-4520. |
| 12 | LIU Hao， NIE Chenchen， LI Hongping，et al.Hydrophobically modified phosphogypsum and its application in polypropylene composites［J］.Construction and Building Materials，2022，347：128500. |
| 13 | 田家新，彭伟军，苗毅恒，等.磷石膏漂白—煅烧增白工艺研究［J］.矿产保护与利用，2021，41（3）：76-80. |
| TIAN Jiaxin， PENG Weijun， MIAO Yiheng，et al.Study on whitening of phosphogypsum via bleaching and calcination［J］.Conservation and Utilization of Mineral Resources，2021，41（3）：76-80. | |
| 14 | XU Li， FANG Keneng， BI Yongxiang，et al.Preparation of anhydrous micron CaSO4 with different morphologies from phosphogypsum and its reinforcing in polyvinyl chloride［J］.Construction and Building Materials，2023，365：130126. |
| 15 | GUAN Qingjun， SUI Ying， YU Weijian，et al.Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions［J］.Separation and Purification Technology，2022，298：121592. |
| 16 | WALAWALKAR M， NICHOL C K， AZIMI G.Process investigation of the acid leaching of rare earth elements from phosphogypsum using HCl，HNO3，and H2SO4 ［J］.Hydrometallurgy，2016，166：195-204. |
| 17 | QI Mengyao， PENG Weijun， WANG Wen，et al.Simple and efficient method for purification and recovery of gypsum from phosphogypsum：Reverse-direct flotation and mechanism［J］.Journal of Molecular Liquids，2023，371.Doi：10.1016/j.molliq.2022.121111. |
| 18 | GUPTA K， SINGH S， RAMACHANDRA RAO M S.Direct and facile room-temperature synthesis of nanocrystalline calcium sulfate dihydrate（gypsum）［J］.Crystal Growth & Design，2016， 16（6）：3256-3261. |
| 19 | MA Baoguo， LU Wenda， SU Ying，et al.Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum［J］.Journal of Cleaner Production，2018，195：396-405. |
| 20 | LI Xianbo， ZHANG Qin， SHEN Zhihui，et al.L-aspartic acid：A crystal modifier for preparation of hemihydrate from phosphogypsum in CaCl2 solution［J］.Journal of Crystal Growth，2019，511：48-55. |
| 21 | YU Bingjie， MIAO Shanshan， DING Manxin，et al.Solubility and physical properties of α-calcium sulfate hemihydrate in NaCl and glycerol aqueous solutions at 303.15，323.15，and 343.15 K［J］.Journal of Chemical & Engineering Data，2021，66（10）：3686-3694. |
| 22 | JIANG Guangming， FU Hailu， SAVINO K，et al.Nonlattice cation-SO42- ion pairs in calcium sulfate hemihydrate nucleation［J］.Crystal Growth & Design，2013，13（11）：5128-5134. |
| 23 | 汪潇，曹博伦，金彪，等.添加剂调控半水石膏晶体生长研究进展［J］.硅酸盐学报，2020，48（1）：94-103. |
| WANG Xiao， CAO Bolun， JIN Biao，et al.Using additives to control crystal growth of hemihydrate gypsum：A short review［J］.Journal of the Chinese Ceramic Society，2020，48（1）：94-103. |
/
| 〈 |
|
〉 |