Study on preparation and modification of phosphogypsum-based architectural gypsum
Received date: 2023-03-14
Online published: 2023-12-14
Using phosphogypsum as raw material，the impurities in phosphogypsum were removed by water washing method，architectural gypsum was prepared by low-temperature calcination，and the effects of calcination temperature and calcination time on gypsum strength and three-phase component content were studied with the help of DSC-TG technology，and then the effects of additives such as sodium tripolyphosphate，fly ash reinforcing agent，melamine and polypropylene fiber of retarder were investigated on the physical and chemical properties of gypsum test block.The results showed that the mass fraction of β-CaSO4·0.5H2O prepared under the condition of low calcination at 170 ℃ and 3 h was 72.23%，and the mechanical properties of gypsum test block were better than those of grade 2.0 products in GB/T 9776—2008“Building Gypsum”The sodium tripolyphosphate with an added amount of 0.15%（mass fraction，the same below） was used as a retarder，and fly ash with an added amount of 5.00% was used as a reinforcing agent with an addition amount of 0.05% melamine was used as a water reducing agent and polypropylene fiber with an addition of 1.00% was modified to build gypsum powder，and the dry flexural strength and dry compressive strength of the prepared gypsum test block were 4.17 MPa and 12.97 MPa for 7 d.The role of various additives in the preparation of architectural gypsum powder using phosphogypsum as raw material was discussed，and the construction gypsum powder with good performance was prepared，which provided technical methods and theoretical basis for the comprehensive utilization of phosphogypsum.
Key words： phosphogypsum; gypsum hemihydrate; strength; construction plaster; low calcination
GUO Shuang , XING Dongxian , GUO Xiao , JI Xiaojie , TANG Jianwei , HUA Quanxian , WANG Baoming , LIU Yong . Study on preparation and modification of phosphogypsum-based architectural gypsum[J]. Inorganic Chemicals Industry, 2023 , 55(12) : 102 -110 . DOI: 10.19964/j.issn.1006-4990.2023-0138
| 1 | TAN Hongbo， LI Xiangguo， HE Chao， et al. Utilization of lithium slag as an admixture in blended cements：Physico-mechanical and hydration characteristics［J］. Journal of Wuhan University of Tech- nology-Mater.Sci.Ed.， 2015， 30（1）：129-133. |
| 2 | TAN Hongbo， ZHANG Xun， HE Xingyang， et al. Utilization of lithium slag by wet-grinding process to improve the early strength of sulphoaluminate cement paste［J］. Journal of Cleaner Production， 2018， 205：536-551. |
| 3 | 李东旭， 焦嘉伟， 廖大龙. 我国磷石膏在新型建筑材料行业的发展及思考［J］. 新型建筑材料， 2021， 48（11）：1-4，11. |
| LI Dongxu， JIAO Jiawei， LIAO Dalong. The development and thinking of phosphogypsum used in new building materials in China［J］. New Building Materials， 2021， 48（11）：1-4，11. | |
| 4 | LU Wenda， MA Baoguo， SU Ying， et al. Preparation of α-hemihydrate gypsum from phosphogypsum in recycling CaCl2 solution［J］. Construction and Building Materials， 2019， 214：399-412. |
| 5 | ZHOU Jun， GAO Hui， SHU Zhu， et al. Utilization of waste phosphogypsum to prepare non-fired bricks by a novel Hydration-Recrystallization process［J］. Construction and Building Materials， 2012， 34：114-119. |
| 6 | 叶学东. 2019年我国磷石膏利用现状及形势分析［J］. 磷肥与复肥， 2020， 35（7）：1-3. |
| YE Xuedong. Status and situation analysis of phosphogypsum utilization in China in 2019［J］. Phosphate & Compound Fertilizer， 2020， 35（7）：1-3. | |
| 7 | 胡宏， 何兵兵， 薛绍秀. α-半水石膏的制备与应用研究进展［J］. 新型建筑材料， 2015， 42（4）：44-48. |
| HU Hong， HE Bingbing， XUE Shaoxiu. Research progress on preparation and application of α-calcium sulfate hemihydrate［J］. New Building Materials， 2015， 42（4）：44-48. | |
| 8 | 李紫瑞， 邢冬娴， 汤建伟， 等. 磷石膏基复合相变材料的制备及储热性能研究［J］. 无机盐工业， 2022， 54（4）：34-39. |
| LI Zirui， XING Dongxian， TANG Jianwei， et al. Study on preparation and heat storage performance of phosphogypsum-based composite phase change materials［J］. Inorganic Chemicals Industry， 2022， 54（4）：34-39. | |
| 9 | 董泽， 翟延波， 任志威， 等. 磷石膏建材资源化利用研究进展［J］. 无机盐工业， 2022， 54（4）：5-9. |
| DONG Ze， ZHAI Yanbo， REN Zhiwei， et al. Research progress on phosphogypsum utilization in building materials［J］. Inorganic Chemicals Industry， 2022， 54（4）：5-9. | |
| 10 | 韩松， 赵志曼， 成耀华， 等. 关于利用云南磷石膏制备磷建筑石膏预处理实验研究［J］. 科学技术与工程， 2014， 14（30）：250-253. |
| HAN Song， ZHAO Zhiman， CHENG Yaohua， et al. On study of pretreatment for preparation of gypsum building plaster with Yunnan phosphorus［J］. Science Technology and Engineering， 2014， 14（30）：250-253. | |
| 11 | DE?IRMENCI N. Utilization of phosphogypsum as raw and calcined material in manufacturing of building products［J］. Construction and Building Materials， 2008， 22（8）：1857-1862. |
| 12 | 李恒， 张晖， 资学民. 磷石膏煅烧工艺进展分析［J］. 无机盐工业， 2023， 55（6）：27-35. |
| LI Heng， ZHANG Hui， ZI Xuemin. Analysis on calcination process of phosphogypsum［J］. Inorganic Chemicals Industry， 2023， 55（6）：27-35. | |
| 13 | 黄照昊， 罗康碧， 李沪萍. 磷石膏中杂质种类及除杂方法研究综述［J］. 硅酸盐通报， 2016， 35（5）：1504-1508. |
| HUANG Zhaohao， LUO Kangbi， LI Huping. Types of impurity in phosphogypsum and the method of removing impurity research review［J］. Bulletin of the Chinese Ceramic Society， 2016， 35（5）：1504-1508. | |
| 14 | 张太玥， 谢凡， 郭君渊. 磷石膏基复合胶凝材料的性能优化及机理研究［J］. 无机盐工业， 2022， 54（9）：136-142. |
| ZHANG Taiyue， XIE Fan， GUO Junyuan. Study on performance optimization and mechanism of phosphogypsum based composite cementitious materials［J］. Inorganic Chemicals Industry， 2022， 54（9）：136-142. | |
| 15 | 马保国， 孙仲达， 苏英， 等. 缓凝剂改性磷建筑石膏及其机理研究［J］. 硅酸盐通报， 2017， 36（12）：3978-3983，3992. |
| MA Baoguo， SUN Zhongda， SU Ying， et al. Mechanism research of phosphor building gypsum with retarder modified［J］. Bulletin of the Chinese Ceramic Society， 2017， 36（12）：3978-3983，3992. | |
| 16 | 张彪， 郑光亚， 刘家宁， 等. 减水剂对磷石膏基建筑石膏性能的影响［J］. 硅酸盐通报， 2020， 39（5）：1540-1546. |
| ZHANG Biao， ZHENG Guangya， LIU Jianing， et al. Effect of water reducing agent on properties of phosphogypsum based building gypsum［J］. Bulletin of the Chinese Ceramic Society， 2020， 39（5）：1540-1546. | |
| 17 | 谢元涛. 石膏材料增强增韧研究［D］. 唐山： 华北理工大学， 2022. |
| XIE Yuantao. Research on strengthening and toughening of gypsum materials［D］. Tangshan： North China University of Science and Technology， 2022. | |
| 18 | 张粤. 改性磷石膏在水泥基湿拌砂浆中影响研究［D］. 贵阳： 贵州大学， 2022. |
| ZHANG Yue. Study on the influence of modified phosphogypsum in cement-based wet-mixed mortar［D］. Guiyang： Guizhou University， 2022. | |
| 19 | 郑绍聪， 余强， 宁平， 等. 磷石膏制备β半水石膏粉的研究［J］. 现代化工， 2015， 35（5）：60-63，65. |
| ZHENG Shaocong， YU Qiang， NING Ping， et al. Preparation of β-hemihydrate gypsum with phosphogypsum［J］. Modern Chemical Industry， 2015， 35（5）：60-63，65. | |
| 20 | 彭家惠. 建筑石膏减水剂与缓凝剂作用机理研究［D］. 重庆： 重庆大学， 2004. |
| PENG Jiahui. Study on action mechanism of water reducers and retarders for building gypsum［D］. Chongqing： Chongqing University， 2004. | |
| 21 | 张伶俐， 罗慧， 夏伟军. 缓凝剂对不同种类石膏性能的影响［J］. 新型建筑材料， 2016， 43（9）：18-21. |
| ZHANG Lingli， LUO Hui， XIA Weijun. Effect of retarder on the properties of different kinds of gypsum［J］. New Building Materials， 2016， 43（9）：18-21. | |
| 22 | 彭家惠， 张建新， 瞿金东， 等. 三聚磷酸钠对建筑石膏水化进程的影响及缓凝机理研究［J］. 硅酸盐通报， 2007， 26（6）：1053-1057. |
| PENG Jiahui， ZHANG Jianxin， QU Jindong， et al. Effect of sodium tripolyphosphate on hydration process of building gypsum and its retarding mechanism［J］. Bulletin of the Chinese Ceramic Society， 2007， 26（6）：1053-1057. | |
| 23 | 陈明胜， 刘鹏， 孔德文， 等. 外掺料对磷石膏基胶凝材料力学及导热性能的影响［J］. 无机盐工业， 2022， 54（9）：113-118. |
| CHEN Mingsheng， LIU Peng， KONG Dewen， et al. Effect of external admixtures on mechanical and thermal conductivity of phosphogypsum composite cementitious materials［J］. Inorganic Che-Industry micals， 2022， 54（9）：113-118. | |
| 24 | 何玉龙， 陈德玉， 王舒州， 等. 磷石膏基胶凝材料的试验研究［J］. 非金属矿， 2015， 38（4）：19-22. |
| HE Yulong， CHEN Deyu， WANG Shuzhou， et al. Study on phosphogypsum cementitious materials［J］. Non-Metallic Mines， 2015， 38（4）：19-22. | |
| 25 | 王响， 张鹏， 吴鹏， 等. 不同结构聚羧酸减水剂对α-高强石膏性能的影响［J］. 新型建筑材料， 2019， 46（12）：73-75. |
| WANG Xiang， ZHANG Peng， WU Peng， et al. Effect of polycarboxylate superplasticizer with different molecular structures on the properties of α-type high-strength gypsum［J］. New Building Materials， 2019， 46（12）：73-75. | |
| 26 | 曾众， 赵志曼， 全思臣， 等. 减水剂与磷建筑石膏基胶凝材料兼容性研究［J］. 非金属矿， 2017， 40（5）：32-35. |
| ZENG Zhong， ZHAO Zhiman， QUAN Sichen， et al. Study on compatibility between superplasticizer and phosphor building gyps- | |
| umbased cementitious material［J］. Non-Metallic Mines， 2017， 40（5）：32-35. | |
| 27 | 陈明凤， 彭家惠， 瞿金东， 等. 减水剂对建筑石膏性能及水化进程的影响［J］. 新型建筑材料， 2003， 30（9）：24-27. |
| 28 | 郜峰， 赵志曼， 全思臣， 等. 不同减水剂对β型磷建筑石膏性能的影响［J］. 硅酸盐通报， 2017， 36（3）：960-964，978. |
| GAO Feng， ZHAO Zhiman， QUAN Sichen， et al. Different water reducing agents on the properties of β type building phosphogypsum［J］. Bulletin of the Chinese Ceramic Society， 2017， 36（3）：960-964，978. | |
| 29 | SINGH N B， MIDDENDORF B. Calcium sulphate hemihydrate hydration leading to gypsum crystallization［J］. Progress in Crystal Growth and Characterization of Materials， 2007， 53（1）：57-77. |
/
| 〈 |
|
〉 |