Preparation of α-hemihydrate gypsum from phosphogypsum by flotation and atmospheric trans-crystallization in solution
Received date: 2023-03-16
Online published: 2023-11-16
In order to realize the high value utilization of phosphogypsum，froth flotation-atmospheric Na2SO4 solution crystallization method was used to convert phosphogypsum sampled from Hubei province into α-hemihydrate gypsum.The morphology，composition and mechanical strength of the product were characterized through various characterization methods（like SEM-EDS，XRF，XRD，FT-IR，TG-DSC，whiteness test and mechanical strength test）.Experimental data revealed that the final product had uniform particle size with aspect ratio of 1.50±0.271.Whiteness and purity（based on CaSO4） of the product was found to be around 84.6% and 95%，respectively.Most of the Si，F and P impurities was removed during the treatment，and final impurity level met the requirement of Grade I phosphogypsum in the National Standard GB/T 23456—2018 as the raw material of gypsum building materials.The compressive and 2 h flexural strength of hardened body of the crystallized product were higher than 36.3 MPa and 7.7 MPa，respectively，which met the requirements of the relevant national and industrial standards for the mechanical strength grade of high strength gypsum.The research was illustrated that α-hemihydrate gypsum with high whiteness，high purity，and high mechanical strength could synthesize by the process，and could be considered as a potential option for phosphogypsum.
Key words： phosphogypsum; α-hemihydrate gypsum; flotation; saline solution; crystal modifier
LIU Chao , FAN Chuigang , LIU Runguo , YU Dongxue , LI Songgeng . Preparation of α-hemihydrate gypsum from phosphogypsum by flotation and atmospheric trans-crystallization in solution[J]. Inorganic Chemicals Industry, 2023 , 55(11) : 107 -114 . DOI: 10.19964/j.issn.1006-4990.2023-0063
| 1 | LI Xibing， DU Jing， GAO Li，et al.Immobilization of phosphogypsum for cemented paste backfill and its environmental effect［J］.Journal of Cleaner Production，2017，156：137-146. |
| 2 | 杨兆娟，向兰.磷石膏综合利用现状评述［J］.无机盐工业，2007，39（1）：8-10. |
| YANG Zhaojuan， XIANG Lan.Review of comprehensive utilization of phosphogypsum［J］.Inorganic Chemicals Inoustry，2007，39（1）：8-10. | |
| 3 | TIAN Tian， YAN Yun， HU Zhihua，et al.Utilization of original phosphogypsum for the preparation of foam concrete［J］.Construction and Building Materials，2016，115：143-152. |
| 4 | YANG Lin， CAO Jianxin， LI Caiyu.Enhancing the hydration reactivity of hemi-hydrate phosphogypsum through a morphology-controlled preparation technology［J］.Chinese Journal of Chemical Engineering，2016，24（9）：1298-1305. |
| 5 | CHERNYSH Y， YAKHNENKO O， CHUBUR V，et al.Phosphogypsum recycling：A review of environmental issues，current trends，and prospects［J］.Applied Sciences，2021，11（4）：1575. |
| 6 | DU Mingxia， WANG Jinming， DONG Faqin，et al.The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum［J］.Scientific Reports，2022，12：95. |
| 7 | MA Baoguo， JIN Zihao， SU Ying，et al.Utilization of hemihydrate phosphogypsum for the preparation of porous sound absorbing material［J］.Construction and Building Materials，2020，234：117346. |
| 8 | 韩青，罗康碧，李沪萍，等.磷石膏开发利用现状［J］.化工科技，2012，20（1）：53-58. |
| HAN Qing， LUO Kangbi， LI Huping，et al.Development and utilization status on the phosphogypsum［J］.Science & Technology in Chemical Industry，2012，20（1）：53-58. | |
| 9 | RU Xiaohong， MA Baoguo， HUANG Jian，et al.Phosphogypsum transition to α-calcium sulfate hemihydrate in the presence of omongwaite in NaCl solutions under atmospheric pressure［J］.Journal of the American Ceramic Society，2012，95（11）：3478-3482. |
| 10 | 胡宏，何兵兵，薛绍秀. α-半水石膏的制备与应用研究进展［J］.新型建筑材料，2015，42（4）：44-48. |
| HU Hong， HE Bingbing， XUE Shaoxiu.Research progress on preparation and application of α-calcium sulfate hemihydrate［J］.New Building Materials，2015，42（4）：44-48. | |
| 11 | MAO Jingwei， JIANG Guangming， CHEN Qiaoshan，et al.Influences of citric acid on the metastability of α-calcium sulfate hemihydrate in CaCl2 solution［J］.Colloids and Surfaces A：Physicochemical and Engineering Aspects，2014，443：265-271. |
| 12 | 王鑫，纪利俊，陈葵，等.pH与Ca2+浓度对磷石膏常压制备α-半水硫酸钙的影响［J］.无机盐工业，2017，49（11）：54-58. |
| WANG Xin， JI Lijun， CHEN Kui，et al.Effects of pH and Ca2+ concentration on formation of α-hemihydrate calcium sulfate by phosphogypsum under atmospheric pressure［J］.Inorganic Chemicals Industry，2017，49（11）：54-58. | |
| 13 | 陈金文，易芸，张慧，等.蒸压参数与杂质对磷石膏制备α-半水石膏的影响［J］.无机盐工业，2022，54（3）：91-96. |
| CHEN Jinwen， YI Yun， ZHANG Hui，et al.Effect of autoclave parameters and impurities on preparation of α-hemihydrate gypsum from phosphogypsum［J］.Inorganic Chemicals Industry，2022，54（3）：91-96. | |
| 14 | 丁峰，窦焰，郑之银，等.常压盐溶液-丁二酸转晶体系中pH对α-CaSO4·0.5H2O的影响［J］.无机盐工业，2020，52（1）：82-86，98. |
| DING Feng， DOU Yan， ZHENG Zhiyin，et al.Effect of pH on α-CaSO4·0.5H2O in salt solution at atmospheric pressure-succinic acid crystal transfer system［J］.Inorganic Chemicals Industry，2020，52（1）：2-86，98. | |
| 15 | FELDMANN T， DEMOPOULOS G P.Influence of impurities on crystallization kinetics of calcium sulfate dihydrate and hemihydrate in strong HCl-CaCl2 solutions［J］.Industrial & Engineering Chemistry Research，2013，52（19）：6540-6549. |
| 16 | 马保国，茹晓红，邹开波，等.常压水热Ca-Na-Cl溶液中用磷石膏制备α-半水石膏［J］.化工学报，2013，64（7）：2701-2707. |
| MA Baoguo， RU Xiaohong， ZOU Kaibo，et al.Preparation of α-calcium sulfate hemihydrate from phosphogypsum in Ca-Na-Cl solutions under atmospheric pressure［J］.CIESC Journal，2013，64（7）：2701-2707. | |
| 17 | KONG Xia， LUO Kangbi， LI Huping，et al.Removing impurity fluorine from phosphogypsum by sulfuric acid leaching method［J］.Chemical Engineering，2012，40（8）：65-68. |
| 18 | KONG Bao， GUAN Baohong， YATES M Z，et al.Control of α-calcium sulfate hemihydrate morphology using reverse microemulsions［J］.Langmuir，2012，28（40）：14137-14142. |
| 19 | 陈燕，岳文海，董若兰.石膏建筑材料［M］.2版.北京：中国建材工业出版社，2012. |
| 20 | POWELL D A.The α- and β-forms of calcium sulphate hemihydrate［J］.Nature，1960，185（4710）：375-376. |
| 21 | CLIFTON J R.Thermal analysis of calcium sulfate dihydrate and supposed a and forms of calcium sulfate hemihydrate from 25 to 500 C［J］.Journal of Research of the National Bureau of Standards Section A：Physics and Chemistry，1972，76A（1）：41. |
| 22 | POWELL D A.Transformation of the α- and β-forms of calcium sulphate hemihydrate to insoluble anhydrite［J］.Nature，1958，182（4638）：792. |
| 23 | LI Xianbo， ZHANG Qin.Effect of molecular structure of organic acids on the crystal habit of α-CaSO4·0.5H2O from phosphogypsum［J］.Crystals，2020，10（1）：24. |
| 24 | SHAO Duoduo， ZHAO Bin， ZHANG Hongqi，et al.Preparation of large-grained α-high strength gypsum with FGD gypsum［J］.Crystal Research and Technology，2017，52（7）：1700078. |
| 25 | 陈星宇，陈德玉，米阳，等.丁二酸对磷石膏制备α-半水石膏晶体生长的影响［J］.四川建材，2022，48（1）：22-23. |
| CHEN Xingyu， CHEN Deyu， MI Yang，et al.Effect of succinic acid on crystal growth of α-hemihydrate gypsum prepared from phosphogypsum［J］.Sichuan Building Materials，2022，48（1）：22-23. |
/
| 〈 |
|
〉 |