Experimental study on properties of iron tailings powder cement-based materials
Received date: 2022-03-03
Online published: 2023-06-14
In order to study the effect of iron tailings powder on the properties of cement-based materials，the effect of iron tailings powder mixing amount on the microstructure properties，hydration mechanism and changes in mineral composition after hydration was studied.Based on the physical and mechanical test results of cementitious materials，it was concluded that the optimal performance of cementitious materials was achieved when the content of iron tailings powder was 30%（mass fraction） and the specific surface area was 450 m2/kg.Under the same hydration time，the heat release rate and heat release of cement-based materials were decreased with increasing of the content of iron tailings.The change law of the porosity of cement-based materials showed a trend of firstly decreasing and then increasing.The XRD patterns of cement-based materials had similar changes in diffraction peaks，but the intensity of the diffraction peaks of Ca（OH）2 was continuously reduced.The change law of the intensity value of the silica diffraction peak showed an increasing trend.Both the diffraction peak intensity value of dicalcium silicate and the diffraction peak intensity value of tricalcium silicate showed decreasing trends.
XU Li , ZHANG Qiang . Experimental study on properties of iron tailings powder cement-based materials[J]. Inorganic Chemicals Industry, 2023 , 55(6) : 116 -123 . DOI: 10.19964/j.issn.1006-4990.2022-0093
| 1 | 李东波，董仓，芦苇，等.基于矿渣粉与氧化石墨烯协同效应的水泥基材料冻融损伤力学性能研究［J］.应用力学学报，2021，38（4）：1431-1440. |
| LI Dongbo， DONG Cang， LU Wei，et al.Study on the mechanical properties of freeze-thaw damage of cement-based materials based on the synergistic effect of slag powder and graphene oxide［J］.Chinese Journal of Applied Mechanics，2021，38（4）：1431-1440. | |
| 2 | 杨厚强，冯晓巍，闫石磊.基于新型水泥基材料的全长锚固系统测试研究［J］.煤矿安全，2021，52（8）：89-94，101. |
| YANG Houqiang， FENG Xiaowei， YAN Shilei.Experimental research on full-length anchoring system based on a new type of cement based materials［J］.Safety in Coal Mines，2021，52（8）：89-94，101. | |
| 3 | 王琴，齐国栋，王悦，等.氧化石墨烯在水泥基复合材料中应用的研究进展（英文）［J］.新型炭材料，2021，36（4）：729-750. |
| WANG Qin， QI Guodong， WANG Yue，et al.Research progress on the effect of graphene oxide on the properties of cement-based composites［J］.New Carbon Materials，2021，36（4）：729-750. | |
| 4 | 刘竞怡，孙志华，温久然，等.金尾矿砂作为混凝土集料的物化性质及其改性试验［J］.金属矿山，2021（5）：211-220. |
| LIU Jingyi， SUN Zhihua， WEN Jiuran，et al.Physical and chemical properties of gold tailing sand as concrete aggregate and its modification test［J］.Metal Mine，2021（5）：211-220. | |
| 5 | 朱街禄，肖莉娜，宋军伟.钨尾矿粉对水泥基材料性能和微观结构的影响［J］.非金属矿，2021，44（1）66-69. |
| ZHU Jielu， XIAO Lina， SONG Junwei.Effect of tungsten tailing powders on the properties and microstructure of cement based materials［J］.Non-Metallic Mines，2021，44（1）：66-69. | |
| 6 | 付云鹏，鲍文博.聚乙烯醇纤维增强尾矿砂水泥基复合材料的剪切和弯曲韧性［J］.工业建筑，2020，50（12）：82-87. |
| FU Yunpeng， BAO Wenbo.Shear and flexural toughness of tailings sand cement-based composites reinforced by pva［J］.Industrial Construction，2020，50（12）：82-87. | |
| 7 | 孙茹茹，王振，黄法礼，等.不同岩性石粉-水泥复合胶凝材料性能研究［J］.材料导报，2021，35（S1）：211-215. |
| SUN Ruru， WANG Zhen， HUANG Fali，et al.Study on properties of different lithology stone powder-cement composite cementitious materials［J］.Materials Reports，2021，35（S1）：211-215. | |
| 8 | 谢开仲，刘振威，朱茂金，等.不同石粉含量的机制砂混凝土高温后力学性能［J］.建筑科学与工程学报，2021，38（3）80-89. |
| XIE Kaizhong， LIU Zhenwei， ZHU Maojin，et al.Mechanical properties of manufactured sand concrete with different stone powder content after high temperatures［J］.Journal of Architecture and Civil Engineering，2021，38（3）：80-89. | |
| 9 | 杨迎春，毛宇光.不同细度铁尾矿粉对水泥基材料性能的影响［J］.西安建筑科技大学学报：自然科学版，2020，52（2）：241-247. |
| YANG Yingchun， MAO Yuguang.Influence of iron tailing powder of different fineness on properties of cement-based material［J］.Journal of Xi′an University of Architecture & Technology，2020，52（2）：241-247. | |
| 10 | 侯云芬，刘锦涛，赵思儒，等.铁尾矿粉对水泥砂浆性能的影响及机理分析［J］.应用基础与工程科学学报，2019，27（5）：1149-1157. |
| HOU Yunfen， LIU Jintao， ZHAO Siru，et al.Effect mechanism of iron tailing powder on cement mortar properties ［J］.Journal of Basic Science and Engineering，2019，27（5）：1149-1157. | |
| 11 | 余江滔，田力康，王义超，等.具有超高延性的再生微粉水泥基复合材料的力学性能［J］.材料导报，2019，33（8）：1328-1334. |
| YU Jiangtao， TIAN Likang， WANG Yichao，et al.Mechanical property of recycled micro-powder cementitious composites with ultra-high ductility［J］.Materials Reports，2019，33（8）：1328-1334. | |
| 12 | 周文娟，张晨，胡牛涛.再生微粉材料性能表征及其对混凝土性能的影响［J］.中国粉体技术，2022，28（5）：64-72. |
| ZHOU Wenjuan， ZHANG Chen， HU Niutao.Characterization of recycled micro-powders and their effects on concrete properti-es［J］.China power science and technology，2022，28（5）：64-72. | |
| 13 | 陈超，孙振平.硅灰对掺有无碱速凝剂水泥浆体性能的影响［J］.材料导报，2019，33（14）：2348-2353. |
| CHEN Chao， SUN Zhenping.Effect of silica fume on the properties of cement paste with alkali-free accelerator［J］.Materials Reports，2019，33（14）：2348-2353. | |
| 14 | 国家市场监督管理总局，国家标准化管理委员会. 水泥胶砂强度检验方法（ISO法）：GB/T 17671—2021［S］.北京：中国标准出版社，2021. |
| 15 | 王胜年，曾俊杰，范志宏.基于长期暴露试验的海工高性能混凝土耐久性分析［J］.土木工程学报，2021，54（10）：82-89. |
| WANG Shengnian， ZENG Junjie， FAN Zhihong. Analysis on durability of marine HPC based on long-term exposure experi-ment ［J］.China Civil Engineering Journal，2021，54（10）：82-89. | |
| 16 | 储洪强，王婷婷，张宇衡，等.氯盐-硫酸盐共存环境中杂散电流作用下提升砂浆中氯离子结合性能的研究［J］.材料导报，2021，35（18）：18069-18075. |
| CHU Hongqiang， WANG Tingting， ZHANG Yuheng，et al.Study on improving chloride binding capacity in mortar under stray current in chloride-sulfate coexisting environment［J］.Materials Reports，2021，35（18）：18069-18075. | |
| 17 | 申爱琴，杨景玉，郭寅川，等.SAP内养生水泥混凝土综述［J］.交通运输工程学报，2021，21（4）：1-31. |
| SHEN Aiqin， YANG Jingyu， GUO Yinchuan，et al.Review on cement concrete internally cured by SAP［J］.Journal of Traffic and Transportation Engineering，2021，21（4）：1-31. | |
| 18 | 王营，顾晓薇，张延年，等.铁尾矿砂水泥砂浆抗压强度及微观结构分析［J］.金属矿山，2022（1）：60-64. |
| WANG Ying， GU Xiaowei， ZHANG Yannian，et al.Analysis of compressive strength and microstructure of iron tailings sand cement mortar［J］.Metal Mine，2022（1）：60-64. | |
| 19 | 程和平，陆璐.铁尾矿砂掺量对混凝土力学性能、耐久性及水化特性的影响研究［J］.金属矿山，2021（11）：215-220. |
| CHENG Heping， LU Lu.Research on mechanical，impermeability and hydration characteristics of iron tailings concrete［J］.Metal Mine，2021（11）：215-220. | |
| 20 | NESVETAEV G， KORYANOVA Y， KOLLEGANOV A，et al.On the issue of standardizing concrete frost resistance to ensure the reinforced concrete structures durability［J］.Materials Science Forum，2021，1043：1-7. |
| 21 | 张登祥，蒋晓明.大流动性高强轻集料混凝土约束收缩及抗裂性能研究［J］.铁道学报，2021，43（5）：190-196. |
| ZHANG Dengxiang， JIANG Xiaoming.Study on constrained shrinkage and crack resistance of high workability and high strength lightweight aggregate concrete［J］.Journal of the China Railway Society，2021，43（5）：190-196. | |
| 22 | 龚建清，罗鸿魁，张阳，等.减缩剂和HCSA膨胀剂对UHPC力学性能和收缩性能的影响［J］.材料导报，2021，35（8）：8042-8048，8063. |
| GONG Jianqing， LUO Hongkui， ZHANG Yang，et al.Effect of shrinkage reducing agent and HCSA expansion agent on mechanical properties and shrinkage properties of UHPC［J］.Materials Reports，2021，35（8）：8042-8048，8063. | |
| 23 | 张意江，陈生水，傅中志.铁矿尾矿料微观结构与压缩特性试验研究［J］.岩土工程学报，2020，42（S2）：61-66. |
| ZHANG Yijiang， CHEN Shengshui， FU Zhongzhi.Experimental study on microstructure and compressibility of iron ore tailings［J］.Chinese Journal of Geotechnical Engineering，2020，42（S2）：61-66. | |
| 24 | 王凤丹，胥孝川，顾晓薇，等.基于不同机械活化方式的二元固废混凝土抗压性能研究［J］.金属矿山，2022（1）：65-70. |
| WANG Fengdan， XU Xiaochuan， GU Xiaowei，et al.Study on the compressive performance of binary solid wastes concrete based on different mechanical activation methods［J］.Metal Mine，2022（1）：65-70. | |
| 25 | 田耀刚，阎宝宝，陈惠坤，等.标准养护条件下铁尾矿制备RPC力学性能研究［J］.功能材料，2021，52（4）：4153-4159. |
| TIAN Yaogang， YAN Baobao， CHEN Huikun，et al.Study on the mechanical properties of RPC prepared from iron tailings under standard curing conditions［J］.Journal of Functional Materials，2021，52（4）：4153-4159. | |
| 26 | 查进，陈梦义，李北星，等.蒸压养护对富硅铁尾矿粉活性特性的影响［J］.混凝土，2015（8）：56-58，62. |
| ZHA Jin， CHEN Mengyi， LI Beixing，et al.Influence of autoclave curing on the activity characteristic of silicon-rich iron tailings powders［J］.Concrete，2015（8）：56-58，62. |
/
| 〈 |
|
〉 |