Preparation of high purity ultrafine tin dioxide particles by liquid oxidation-spray drying method
Received date: 2022-06-30
Online published: 2023-04-13
To reduce the impact of nitrogen oxides（NO x ） emissions on the environment in the reaction，improve the purity of tin dioxide（SnO2） products，and reduce the particle size，the metal tin particles and dilute nitric acid were used as raw materials，and the liquid phase nitric acid oxidation method and spray drying in combination with the process were used.To prepare high-purity ultra-fine SnO2 particles.The influence of parameters such as tin source type，nitric acid concentration and dropping rate reaction temperature and calcination temperature on the product were investigated.The structure and properties of the prepared metastannic acid（H2SnO3） and SnO2 were characterized by X-ray diffractometer inductively coupled plas-ma emission spectrometer scanning electron microscope laser particle size analyzer and specific surface area analyzer.The results showed that using tin particles as the tin source，nitric acid mass concentration of 25%，adding speed of 30 mL/min，reaction temperature of 80 ℃，after spray drying process，and then 950 ℃ calcination，the final purity of SnO2 was 99.997%，D50 was 1.15 μm，D90 was 2.44 μm，with a specific surface area of 3.86 m2/g.This products had important applications in the field of screen display technology and could be used to prepare indium tin oxide powder materials（ITO）.
MA Dianpu , PU Youfu , LI Jun , CHEN Lishi , LIU Hengyu , QIN Deqing , FU Zewei , PENG Jubo . Preparation of high purity ultrafine tin dioxide particles by liquid oxidation-spray drying method[J]. Inorganic Chemicals Industry, 2023 , 55(4) : 54 -59 . DOI: 10.19964/j.issn.1006-4990.2022-0396
| 1 | KHAJUEE S， MEMARIAN N.Hydrothermal synthesis of ultrafine SnO2 nanospheres：Effect of reaction time on physical properties[J].The European Physical Journal Plus，2021，136（5）.Doi：10.1140/epjp/s13360-021-01563-0. |
| 2 | SHARMA S， CHHOKER S.CVD grown doped and Co-doped SnO2 nanowires and its optical and electrical studies[J].Materials Today：Proceedings，2020，28：375-378. |
| 3 | CHEEMA H， DELCAMP J H.SnO2 transparent printing pastes from powders for photon conversion in SnO2-based dye-sensitized solar cells[J].Chemistry，2019，25（62）：14205-14213. |
| 4 | KHALAMEIDA S V， SAMSONENKO M N， SYDORCHUK V V，et al.Photocatalytic properties of tin dioxide doped with chromi-um（Ⅲ），silver and zinc compounds in the oxidation of organic substrates by the action of visible light[J].Theoretical and Experimental Chemistry，2017，53（1）：40-46. |
| 5 | LIU Duanduan， JIN Zhiliang， ZHANG Yongke，et al.Light harvesting and charge management by Ni4S3 modified metal-organic fra-meworks and rGO in the process of photocatalysis[J].Journal of Colloid and Interface Science，2018，529：44-52. |
| 6 | ZHANG Miao， WANG Xianhui， YANG Xiaohong，et al.Arc erosion behaviors of AgSnO2 contact materials prepared with different SnO2 particle sizes[J].Transactions of Nonferrous Metals Society of China，2016，26（3）：783-790. |
| 7 | SEBASTIAN B， THOMAS C G， MANOJ B.Synthesis of nano-crystalline tin dioxide and its effect on calcination[J].Asian Journal of Chemistry，2017，29（4）：875-878. |
| 8 | MARTIN N P， VOLKRINGER C， HENRY N，et al.Formation of a new type of uranium（Ⅳ） poly-oxo cluster｛U38｝based on a controlled release of water via esterification reaction[J].Chemical Science，2018，9（22）：5021-5032. |
| 9 | 马春红.ITO透明导电薄膜中毒及掺杂改性研究[D].北京：北京科技大学，2018. |
| MA Chunhong.Research on poisoning and doping effects by Nb/Ti of ITO films[D].Beijing：University of Science and Technology Beijing，2018. | |
| 10 | 李晓晖，宋凯强，丛大龙，等.高透明低发射率ITO薄膜的制备及其光电性能研究[J].表面技术，2020，49（7）：126-132. |
| LI Xiaohui， SONG Kaiqiang， CONG Dalong，et al.Preparation and photoelectric properties of ITO thin films with high transparency and low emissivity[J].Surface Technology，2020，49（7）：126-132. | |
| 11 | 许永姿，彭巨擘，蔡珊珊，等.市售高端电子陶瓷用二氧化锡粉体产品对比分析[J].有色矿冶，2021，37（6）：54-58. |
| XU Yongzi， PENG Jubo， CAI Shanshan，et al.Comparative analysis of tin dioxide powder products for commercial high-end electronic ceramics[J].Non-Ferrous Mining and Metallurgy，2021，37（6）：54-58. | |
| 12 | LU Han， HAN Gengxin， CAO Jieping，et al.Large-area and patternable nano-dot array from electrolysis of ITO film for surface-enhanced Raman spectroscopy[J].Nanoscale Research Letters，2020，15（1）.Doi：10.1186/s11671-019-3239-9. |
| 13 | 徐伟玲，李延升.液相共沉淀法制备氧化铟锡超细粉体材料的研究进展[J].应用化工，2005，34（7）：404-407. |
| XU Weiling， LI Yansheng.The research of manufacture super thin tin indium oxide powder by co-precipitation method in solution[J].Applied Chemical Industry，2005，34（7）：404-407. | |
| 14 | 陈晓宇，李詠侠，邹丹，等.超细Co-Cr-V复合金属粉末的制备与表征[J].中南大学学报：自然科学版，2017，48（2）：302-309. |
| CHEN Xiaoyu， LI Yongxia， ZOU Dan，et al.Preparation and characterization of ultrafine Co-Cr-V alloy powders[J].Journal of Central South University：Science and Technology，2017，48（2）：302-309. | |
| 15 | 熊华亮.一种利用锡电解阳极泥直接制取二氧化锡的方法：中国，104876260B[P].2017-04-19. |
| 16 | 苏瑞春，张旭，刘新阳.加压合成偏锡酸（二氧化锡）工艺实验研究[J].中国石油和化工标准与质量，2021，41（22）：50-51. |
| SU Ruichun， ZHANG Xu， LIU Xinyang.Experimental study on synthesis of stannic acid（tin dioxide） under pressure[J].China Petroleum and Chemical Standard and Quality，2021，41（22）：50-51. | |
| 17 | 黄娟，钟小华，朱刘.高纯纳米二氧化锡球形粉末的制备[J].广东化工，2017，44（14）：49-50. |
| HUANG Juan， ZHONG Xiaohua， ZHU Liu.Synthesis of high purity spherical SnO2 nanoparticles[J].Guangdong Chemical Industry，2017，44（14）：49-50. | |
| 18 | DAIDECHE K， AZIZI A.Electrodeposition of tin oxide thin film from nitric acid solution：The role of pH[J].Journal of Materials Science：Materials in Electronics，2017，28（11）：8051-8060. |
| 19 | 纪守峰，李桂春.超细粉体团聚机理研究进展[J].中国矿业，2006，15（8）：54-56，90. |
| JI Shoufeng， LI Guichun.Progress on agglomeration mechanism of the superfine powders[J].China Mining Magazine，2006，15（8）：54-56，90. | |
| 20 | 李国栋，熊翔，黄伯云.纳米粉体大气环境团聚机理及无团聚纳米粉体的制备[J].中南大学学报：自然科学版，2004，35（4）：527-531. |
| LI Guodong， XIONG Xiang， HUANG Boyun.Agglomerate mechanism of nanometer powders in atmosphere and methods of preparation of nan-agglomerate nanometer powders[J].Journal of Central South University of Technology：Natural Science，2004，35（4）：527-531. | |
| 21 | 亢思莹，顾宙辉，黄鑫.喷雾干燥技术在固体分散体制备中的应用[J].药学与临床研究，2022，30（2）：159-161. |
| KANG Siying， GU Zhouhui， HUANG Xin.Application of spray dry technology in preparation of solid dispersion[J].Pharmaceutical and Clinical Research，2022，30（2）：159-161. | |
| 22 | 陈杨，陈志刚，刘强，等.超声雾化法制备单分散纳米CeO2粉体研究[J].化学工程，2009，37（11）：55-58. |
| CHEN Yang， CHEN Zhigang， LIU Qiang，et al.Preparation of single dispersed nano-CeO2 particles by ultrasonic atomization method[J].Chemical Engineering（China），2009，37（11）：55-58. |
/
| 〈 |
|
〉 |