Study on permeability of mesoporous silica antireflective film regulated by conductivity
Received date: 2021-11-18
Online published: 2022-08-11
Supported by
Foundation Department,Hebei University of Water Resources and Electric Engineering,Cangzhou(061000);School of Transportation Engineering,Hebei University of Water Resources and Electric Engineering
Mesoporous silica antireflective film solution was prepared by sol-gel process in the form of acid catalysis with tetraethyl orthosilicate（TEOS） as precursor and triblock copolymer（F127） as template.The film was coated on borosilicate glass by dip coating method and curing treated by muffle furnace.Uv-visible spectrophotometer and conductivity meter were used to characterize transmittance of the films and electrical properties of the sol.The results showed that the conductivity of the sol increased from 243 μS/cm to 266 μS/cm under long?term exposure for 6 months，and the same pulling speed resulted in the increase of layer thickness.The transmittance peak showed a red shift and the average transmittance within the range of 300~2 500 nm decreased from 96.7% to 96.0%.Experimental data fitting showed that electric conductivity had a good linear relationship with SiO2 concentration and a good single exponential relationship with optimal pulling speed.The transmittance of the sol would be recovered by conductivity control using the method of dilution，it did not affect the production efficiency and could also guarantee the consistency of film products.
Yu ZHANG , Xiaoyu QI , Mengyao FENG , Nannan SUN , Cuilian ZHAO . Study on permeability of mesoporous silica antireflective film regulated by conductivity[J]. Inorganic Chemicals Industry, 2022 , 54(8) : 80 -84 . DOI: 10.19964/j.issn.1006-4990.2021-0701
| 1 | 王珊.溶胶-凝胶法制备低折射率SiO2薄膜的过程控制研究［J］.材料导报，2010，24（S1）∶47-49，59. |
| 1 | WANG Shan.Study of process control on sol-gel derived optical SiO2 thin films with low refractive index［J］.Materials Review，2010，24（S1）∶47-49，59. |
| 2 | 张弛，王德平，徐更生，等.溶胶-凝胶法制备平板玻璃减反射膜的工艺研究［J］.建筑材料学报，2004，7（4）∶479-482. |
| 2 | ZHANG Chi， WANG Deping， XU Gengsheng，et al.Study on the preparation of flat glass with antireflective coatings by sol-gel process［J］.Journal of Building Materials，2004，7（4）∶479-482. |
| 3 | 吴启坚，吴清仁，杨媛，等.酸-碱二步催化制备SiO2溶胶及其稳定性研究［J］.武汉理工大学学报，2011，33（7）∶14-19. |
| 3 | WU Qijian， WU Qingren， YANG Yuan，et al.Study on preparation and stability of silica Sol system by acid?base two?step catalytic process［J］.Journal of Wuhan University of Technology，2011，33（7）∶14-19. |
| 4 | 孙菁华，吕海兵，吴东，等.溶胶-凝胶法制备氧化硅光学减反射膜［J］.材料导报，2013，27（9）∶15-19，37. |
| 4 | SUN Jinghua， LV Haibing， WU Dong，et al.Preparation of silica optical antireflective films by sol-gel process［J］.Materials Review，2013，27（9）∶15-19，37. |
| 5 | 邹丽萍，李晓光，沈军.高强度有序介孔二氧化硅减反膜的制备及性能［J］.稀有金属材料与工程，2016，45（S1）∶472-476. |
| 5 | ZOU Liping， LI Xiaoguang， SHEN Jun.Preparation and properties of ordered mesoporous silica antireflective coating with high stren? |
| 5 | gth［J］.Rare Metal Materials and Engineering，2016，45（S1）∶472-476. |
| 6 | GUO Zhaolong， ZHAO Haixin， ZHAO Wei，et al.High?quality hollow closed?pore silica antireflection coatings based on styrene?acrylate emulsion @ organic?inorganic silica precursor［J］.ACS Applied Materials & Interfaces，2016，8（18）∶11796-11805. |
| 7 | 辛崇飞，彭诚，吴建青.醇硅比对太阳能玻璃用多孔SiO2减反膜性能的影响［J］.材料科学与工程学报，2012，30（1）∶9-13. |
| 7 | XIN Chongfei， PENG Cheng， WU Jianqing.Effects of EtOH/TEOS molar ratio on performance of porous SiO2 antireflective coatings for solar glass［J］.Journal of Materials Science and Engineering，2012，30（1）∶9-13. |
| 8 | 倪志龙，王彪，杨晔，等.溶胶粒径对氧化硅减反射膜结构和光学性能的影响［J］.材料研究学报，2010，24（5）∶478-482. |
| 8 | NI Zhilong， WANG Biao， YANG Ye，et al.Effect of colloid particle sizes on microstructure and optical properties of the silica antireflective coatings［J］.Chinese Journal of Materials Research，2010，24（5）∶478-482. |
| 9 | 商孟莹，曹林洪，刘淼，等.新型溶胶-凝胶二氧化硅微孔增透膜的制备及性能研究［J］.光谱学与光谱分析，2013，33（4）∶872-876. |
| 9 | SHANG Mengying， CAO Linhong， LIU Miao，et al.Study on the preparation and properties of novel silica microporous antireflective coating by sol-gel process［J］.Spectroscopy and Spectral An? |
| 9 | alysis，2013，33（4）∶872-876. |
| 10 | LIANG Zihui， LI Wei， DONG Binghai，et al.Double-function SiO2-DMS coating with antireflection and superhydrophobic surface［J］.Chemical Physics Letters，2019，716∶211-214. |
| 11 | 胡小娟，刘岚，罗远芳，等.溶胶-凝胶法制备超疏水PMHS-SiO2涂膜［J］.材料研究学报，2010，24（3）∶266-272. |
| 11 | HU Xiaojuan， LIU Lan， LUO Yuanfang，et al.Preparation of superhydrophobic PMHS-SiO2 coatings by sol-gel method［J］.Chinese Journal of Materials Research，2010，24（3）∶266-272. |
| 12 | 魏美英，王新敏，青双桂，等.KH560/KH570改性SiO2增透膜的制备［J］.材料导报，2012，26（14）∶39-42. |
| 12 | WEI Meiying， WANG Xinmin， QING Shuanggui，et al.Preparation of KH560/KH570 modified SiO2 antireflective coating［J］.Materials Review，2012，26（14）∶39-42. |
| 13 | LIU Zhaoyue， ZHANG Xintong， MURAKAMI T，et al.Sol-gel SiO2/TiO2 bilayer films with self?cleaning and antireflection properties［J］.Solar Energy Materials and Solar Cells，2008，92（11）∶1434-1438. |
| 14 | CHI Fangting， ZENG Yiyang， LIU Cheng，et al.Enhancing mechanical stability of sol-gel silica antireflection coatings via ammonia treatment at low temperature［J］.Results in Physics，2020，18.Doi∶10.1016/j.rinp.2020.103315. |
| 15 | ISO 9050 ∶Glass in building-Determination of light transmittance，solar direct transmittance，total solar energy transmittance，ultraviolet transmittance and related glazing factors［J］.International Organization for Standardization.Geneva.1990-01-01. |
| 16 | 张日东，严鸿维，吕海兵，等.提拉法SiO2化学膜厚度与折射率的变化规律研究［J］.强激光与粒子束，2014，26（7）∶70-74. |
| 16 | ZHANG Ridong， YAN Hongwei， Haibing Lü，et al.Changes of thickness and refractive index of silica sol-gel film by dip coating process［J］.High Power Laser and Particle Beams，2014，26（7）∶70-74. |
| 17 | 黎珊，戴红旗，姜兴茂，等.二氧化硅溶胶体系的电导行为［J］.化工进展，2015，34（8）∶3093-3098. |
| 17 | LI Shan， DAI Hongqi， JIANG Xingmao，et al.Study on the electric conductivity of silicasol system［J］.Chemical Industry and Engineering Progress，2015，34（8）∶3093-3098. |
/
| 〈 |
|
〉 |