Study on preparation technology and waterproof property of fused magnesia coating
Received date: 2021-07-26
Online published: 2022-05-31
Fused magnesia，as an insulating material with high thermal conductivity and high temperature resistance，is prone to hydration deterioration and loss of insulation in humid air.The coating method was used to coat the fused magnesia，aluminum nitrate and melamine as raw materials under the condition of nitrogen and 1 250 ℃.Scanning electron microscope（SEM） was used to observe the formation of coating on the surface of fused magnesia particles.X-ray diffraction（XRD） analysis showed that the coating layer was magnesium aluminium spinel，and there was no magnesium nitride，aluminum nitride，carbon nitride.Through pore specific surface area analysis，the specific surface area of fully coated fused magnesite particles was increased by comparing to the previous.Vacuum water absorption drying method was used to test the water absorption performance.The test results showed that the water absorption rate of coated fused magnesite particles was reduced by 92.97%，and the lowest water absorption rate reached 0.167 2%.The water absorption rate could reach less than 0.17% after 7 cycles.This study provided a new way for fused magnesia waterproof technology.
Jianping TANG , Guosheng WANG . Study on preparation technology and waterproof property of fused magnesia coating[J]. Inorganic Chemicals Industry, 2022 , 54(5) : 90 -95 . DOI: 10.19964/j.issn.1006-4990.2021-0449
| 1 | 刘润静，徐恺，张腾腾.我国轻烧粉、重烧粉及电熔镁砂生产现状分析［C］∥2014年全国镁化合物行业年会暨技术设备交流会专辑.石家庄：中国无机盐工业协会镁化合物分会，2014：62- |
| 69 | LIU Runjing， XU Kai， ZHANG Tengteng.Analysis of production status of light burned powder、heavy burned powder and fused magnesia in China［C］∥2014 National Magnesium Compound Industry Annual Meeting and Technical Equipment Exchange Conference album.Shijiazhuang：China Inorganic Salt Industry Association Magnesium Compaunds Brarch，2014：62-69. |
| 2 | 侯庆冬，罗旭东，谢志鹏，等.镁橄榄石前驱体溶胶结合电熔镁砂基耐火材料基质的烧结性能［J］.耐火材料，2018，52（6）：426-429. |
| 2 | HOU Qingdong， LUO Xudong， XIE Zhipeng，et al.Sintering property of forsterite precursor Sol bonded fused magnesia refractory matrix［J］.Refractories，2018，52（6）：426-429. |
| 3 | POURRAHIMI A M， PALLON L K H， LIU Dongming，et al.Poly? |
| 3 | ethylene nanocomposites for the next generation of ultralow?trans? |
| 3 | transmission-loss HVDC cables：Insulation containing moisture? |
| 3 | resistant MgO nanoparticles［J］.ACS Applied Materials & Interfa? |
| 3 | ces，2016，8（23）：14824-14835. |
| 4 | 徐娜，李志坚，吴锋，等.复合添加剂对镁碳砖高温性能的影响［J］.无机盐工业，2015，47（8）：45-48，55. |
| 4 | XU Na， LI Zhijian， WU Feng，et al.Effect of combined additives on high?temperature properties of MgO-C brick［J］.Inorganic Chemicals Industry，2015，47（8）：45-48，55. |
| 5 | 刘景林.冶金设备用耐火材料［J］.耐火与石灰，2010，35（2）：65-66. |
| 5 | LIU Jinglin.Refractory materials used in metallurgical equipme? |
| 5 | nt［J］.Refractories & Lime，2010，35（2）：65-66. |
| 6 | 陈英春，周佳芬，路贵民，等.高纯镁砂及氧化镁陶瓷研究进展［J］.化工进展，2019，38（1）：505-515. |
| 6 | CHEN Yingchun， ZHOU Jiafen， LU Guimin，et al.A review on the production technologies of high?purity magnesia and magnesium oxide ceramics［J］.Chemical Industry and Engineering Progress，2019，38（1）：505-515. |
| 7 | 兰伟.以烧结镁砂为基质的人工湿地强化除磷效果及其作用机制［D］.济南：山东大学，2018. |
| 7 | LAN Wei.Phosphorus removal enhancement of magnesia modified constructed wetland microcosm and its mechanism study［D］.Jinan：Shandong University，2018. |
| 8 | 全跃.试论采用煤气发生炉治理轻烧镁砂窑烟尘［J］.辽宁经济，2001（5）：6-7，48. |
| 8 | QUAN Yue.Discussion on using gas producer to treat dust of light burned magnesia kiln［J］.Liaoning Economy，2001（5）：6-7，48. |
| 9 | 李军，宋伟.电熔镁产业发展研究［J］.冶金能源，2010，29（4）：8-10. |
| 9 | LI Jun， SONG Wei.Research on development of fused magnesia industry［J］.Energy for Metallurgical Industry，2010，29（4）：8-10. |
| 10 | 张芳.电熔镁砂市场分析及发展优势［J］.包钢科技，2003，29（1）：87-88，78. |
| 10 | ZHANG Fang.Development of electric melting magnesia mar? |
| 10 | ket［J］.Science & Technology of Baotou Steel（Group） Corporation，2003，29（1）：87-88，78. |
| 11 | 徐恺，赵华，杨翠杰，等.高活性氧化镁潮解及其活性递变规律研究［J］.无机盐工业，2016，48（10）：44-46. |
| 11 | XU Kai， ZHAO Hua， YANG Cuijie，et al.Study on high activity magnesium oxide deliquescence and its active change law［J］.Inorganic Chemicals Industry，2016，48（10）：44-46. |
| 12 | AMARAL L F， OLIVEIRA I R， BONADIA P，et al.Chelants to inhibit magnesia（MgO） hydration［J］.Ceramics International， 2011，37（5）：1537-1542. |
| 13 | 于秋月.MgO-CaO耐火材料抗水化性能研究进展［J］.有色矿冶，2018，34（2）：39-42. |
| 13 | YU Qiuyue.Progress in research on hydration resistance of MgO-CaO refractories［J］.Non-Ferrous Mining and Metallurgy，2018，34（2）：39-42. |
| 14 | 宋柯成，宿金栋，陈俊红，等.镁砂水化性能研究［J］.四川冶金，2013，35（2）：58-61. |
| 14 | SONG Kecheng， SU Jindong， CHEN Junhong，et al.A performance study for magnesia hydration［J］.Sichuan Metallurgy，2013，35（2）：58-61. |
| 15 | 尤士伟，孙荣海.B2O3含量对镁砂抗水化性能的影响［J］.耐火与石灰，2008，33（2）：18-22. |
| 15 | YOU Shiwei， SUN Ronghai.Influence of B2O3 content on hydration resistance of magnesia［J］.Refractories & Lime，2008，33（2）：18-22. |
| 16 | 桂明玺.添加氧化镍对提高镁砂抗水化性的效果［J］.国外耐火材料，2006，31（1）：57. |
| 16 | GUI Mingxi.Effect of adding nickel oxide on improving hydration resistance of magnesia［J］.Foreign Refractories，2006，31（1）：57. |
| 17 | 朴明伟.添加柠檬酸对含氧化镁耐火浇注料的抗水化性能影响［J］.耐火与石灰，2013，38（1）：33-35. |
| 17 | PIAO Mingwei.Effect of adding citric acid on hydration resistance of refractory castable containing magnesium oxide［J］.Refractories & Lime，2013，38（1）：33-35. |
| 18 | SAKO E Y， BRAULIO M A L， PANDOLFELLI V C.Microstruc? |
| 18 | tural evolution of magnesia?based castables containing microsili? |
| 18 | ica［J］.Ceramics International，2012，38（7）：6027-6033. |
| 19 | MURALI K P， RAJESH S， PRAKASH O，et al.Effects of silane coatings in aqueous and non?aqueous media on the properties of magnesia filled PTFE laminates［J］.Materials Chemistry and Physics，2010，122（2/3）：317-320. |
| 20 | OIKAWA Y， GOTO Y， NISHIDA M，et al.Preparation of morpholo? |
| 20 | gy?controlled fluoroalkyl end?capped vinyltrimethoxysilane oligomeric silica/magnesium oxide nanocomposite particles：Development of magnesium oxide nanocomposite particles possessing a water?resistance ability［J］.Journal of Sol-Gel Science and Technology，2019，89（1）：135-147. |
| 21 | MADEJ D， TYRA?A K.In situ spinel formation in a smart nano?structured matrix for no?cement refractory castables［J］.Materials，2020，13（6）：1403. |
| 22 | NASKAR M K， CHATTERJEE M.Magnesium aluminate |
| 22 | MgAl 2 O4） spinel powders from water?based sols［J］.Journal of the American Ceramic Society，2005，88（1）：38-44. |
| 23 | RAHMAT N， YAAKOB Z， PUDUKUDY M，et al.Single step so? |
| 23 | lid?state fusion for MgAl 2 O4 spinel synthesis and its influence on the structural and textural properties［J］.Powder Technology，2018，329：409-419. |
| 23 | 上接第 89 页） |
/
| 〈 |
|
〉 |