Effect of sealing treatment on properties of zinc phosphate conversion film on building structural steel
Received date: 2020-11-11
Online published: 2021-10-11
Zinc phosphate conversion film was prepared on building structural steel,and it was sealed with different types of sealing solution.The effect of sealing treatment on the microstructure,surface components,thickness and corrosion resistance of phosphate conversion film were studied.The results showed that sealing treatment had no significant influence on the macrostructure and thickness of phosphate conversion film,but there were some differences in the microstructure,surface components and corrosion resistance of phosphate conversion film.The surface components of unsealed and sealed phosphate conversion film were mainly Zn,O and P.After sealing treatment,the surface of phosphate conversion film tended to be flat,the compactness was improved,and the corrosion resistance was significantly improved,which was mainly attributed to that different types of sealing solution play a role in filling the grain gaps and preventing the corrosive medium from penetrating into the phosphate conversion film.The phosphate conversion film sealed with the sealing solution containing sodium silicate and cerium nitrate had smoother surface,the solution resistance and charge transfer resistance were the biggest,which was 58.2 Ω·cm 2 and 4.02×103 Ω·cm 2 respectively,and it had the greatest phase angle and the widest range of frequency.This phosphating film exhibited excellent corrosion resistance and ideal corrosion durability with application potential,and was expected to be used as the surface protection layer for building structural steel.
Danjing Wang , Jingkui Li . Effect of sealing treatment on properties of zinc phosphate conversion film on building structural steel[J]. Inorganic Chemicals Industry, 2021 , 53(10) : 92 -97 . DOI: 10.19964/j.issn.1006-4990.2020-0606
[1] | 王瑶, 邵忠财, 王鑫, 等. 稀土元素对镁合金磷酸盐转化膜性能的影响[J]. 电镀与环保, 2019, 39(2):30-33. |
[2] | Verbruggen H, Baert K, Terryn H, et al. Molybdate-phosphate conv-ersion coatings to protect steel in a simulated concrete pore soluti-on[J]. Surface and Coatings Technology, 2019, 361:280-291. |
[3] | Lin B L, Lu J T. Self-healing mechanism of composite coatings obta-ined by phosphating and silicate sol post-sealing[J]. Transactions of Nonferrous Metals Society of China, 2014(24):2723-2728. |
[4] | An K, An C Q, Yang C N, et al. Effect of phosphating and post-se-aling on the corrosion resistance of electro-galvanized steel[J]. International Journal of Electrochemical Science, 2017, 12(3):2102-2111. |
[5] | 林碧兰, 卢锦堂, 孔纲. 几种改进磷化膜耐蚀性对比和自修复性初探[J]. 表面技术, 2010, 39(1):37-40. |
[6] | 邵红红, 陈婷婷, 祁昌洋, 等. 封闭处理对316L不锈钢超声场下磷化膜性能的影响[J]. 中国表面工程, 2017, 30(1):63-69. |
[7] | Abdel-Gawad S A. Enhancing corrosion resistance of galvanized steel by phosphating and silicate post-sealing[J]. International Jo-urnal of Eelectrochemical Science, 2018, 13(3):2688-2704. |
[8] | Saraswathy V, Karthick S P. Effect of ecofriendly sealing coat agai-nst corrosion protection of steel rebars in concrete[J]. Corrosion En-gineering,Science and Technology, 2014, 49(5):327-334. |
[9] | 孔纲, 林碧兰, 刘军. 热镀锌层磷化膜硝酸铈封闭后处理的研究[J]. 材料保护, 2008, 41(2):8-10. |
[10] | 牟世辉. 锌锰系磷化膜硅烷封闭工艺研究[J]. 电镀与精饰, 2012, 34(7):41-43. |
[11] | 刘新院. 24Cr2Ni4W合金钢黑色磷化膜的制备及性能研究[D]. 沈阳:沈阳理工大学, 2012. |
[12] | 吴海江, 卢锦堂. 钼酸盐封闭后处理的热镀锌钢板硅烷膜的耐蚀性[J]. 物理化学学报, 2009, 25(9):1743-1748. |
[13] | Dong Q, Ba Z, Jia Y, et al. Effect of solution concentration on seal-ing treatment of Mg-Al hydrotalcite film on AZ91D Mg alloy[J]. Journal of Magnesium and Alloys, 2017, 5(3):320-325. |
[14] | 徐伟, 薛茂权, 白建波. 铝添加量对烧结合成Ti3SiC2的影响及其耐蚀性研究[J]. 无机盐工业, 2019, 51(4):23-26. |
[15] | Kong W C, Shen H, Gao J X, et al. Electrochemical corrosion be-havior of HVOF sprayed WC-12Co coating on H13 hot work mould steel[J]. Anti-Corrosion Methods and Materials, 2019, 66(6):827-834. |
[16] | 阳建君, 旷焕, 田金旺, 等. 2A96铝合金表面含三价铬转化膜制备及其电化学性能研究[J]. 包装学报, 2019, 11(1):80-86. |
[17] | 杨少华, 张丹城, 田亚斌, 等. 5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究[J]. 有色金属科学与工程, 2018, 9(2):1-5. |
[18] | 曾凤春, 谢万如, 任旺, 等. 氯碱生产环境下金属阳极电解槽的腐蚀探讨与防护方法研究[J]. 无机盐工业, 2015, 47(5):45-47. |
/
〈 |
|
〉 |