Study on rapid preparation process of high-density spherical basic nickel carbonate
Received date: 2020-08-24
Online published: 2021-05-12
According to the quality requirements of HG/T 4696—2014,Industrial Basic Nickel Carbonate,a production technology of high-density basic nickel carbonate with simple preparation process and easy industrialization was developed.This topic has studied a way to feed the reaction material through pressurized spray,making the material more uniform in the reaction system,which was easy to form large particles,thereby improving the apparent density of basic nickel carbonate products.By exploring the effects of reaction temperature,reaction pH,nickel sulfate concentration,sodium carbonate con-centration and reaction speed on apparent density,the best single-factor process conditions were found and orthogonal expe-riments were carried out to obtain the optimal process conditions: at 40 ℃,using 100 g/L nickel ion concentration nickel sulfate solution to feed by pressurized spray method,the reaction pH was controlled by the automatic control system with 106 g/L sodium carbonate solution at 8.0,and the reaction speed was controlled at 300 r/min during the reaction.The basic nickel carbonate with apparent density more than 0.7 g/cm3 and low impurity content and spherical shape could be prepared.
Weihui Ye , Qi Lü , Changjiang Long . Study on rapid preparation process of high-density spherical basic nickel carbonate[J]. Inorganic Chemicals Industry, 2021 , 53(5) : 69 -72 . DOI: 10.11962/1006-4990.2020-0364
[1] | 付向辉, 薛生晖, 张翔宇, 等. 连续工艺合成高纯碱式碳酸镍的研究[J]. 电子元件与材料, 2012,31(12):30-34. |
[2] | 刘元生, 刘小平, 蒋良华, 等. 碱式碳酸镍或碱式碳酸钴快速生产工艺:中国,101708868B[P].2011-06-15. |
[3] | 付向辉, 薛生晖, 张翔宇, 等. 高纯碱式碳酸镍制备及其除杂净化[J]. 科学技术与工程, 2018,18(35):196-200. |
[4] | 张银亮, 李钧, 周兆安, 等. 电子级碱式碳酸镍的制备工艺研究[J]. 化工科技, 2016,24(3):61-65. |
/
〈 |
|
〉 |